CN103643109A - Wear-resisting lining board with long service life - Google Patents

Wear-resisting lining board with long service life Download PDF

Info

Publication number
CN103643109A
CN103643109A CN201310727204.0A CN201310727204A CN103643109A CN 103643109 A CN103643109 A CN 103643109A CN 201310727204 A CN201310727204 A CN 201310727204A CN 103643109 A CN103643109 A CN 103643109A
Authority
CN
China
Prior art keywords
abrasion
backing block
proof backing
service life
wear
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310727204.0A
Other languages
Chinese (zh)
Other versions
CN103643109B (en
Inventor
鲁进
杨明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MAANSHAN SHENGLEI WEAR-RESISTANT ALLOY MANUFACTURING Co Ltd
Original Assignee
MAANSHAN SHENGLEI WEAR-RESISTANT ALLOY MANUFACTURING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by MAANSHAN SHENGLEI WEAR-RESISTANT ALLOY MANUFACTURING Co Ltd filed Critical MAANSHAN SHENGLEI WEAR-RESISTANT ALLOY MANUFACTURING Co Ltd
Priority to CN201310727204.0A priority Critical patent/CN103643109B/en
Publication of CN103643109A publication Critical patent/CN103643109A/en
Application granted granted Critical
Publication of CN103643109B publication Critical patent/CN103643109B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a wear-resisting lining board with a long service life, belonging to the technical field of wear-resisting lining boards. An installation hole is formed in the wear-resisting lining board, and the wear-resisting lining board consists of the following components in percent by mass: 3.0%-3.2% of C, 0.3%-0.4% of Si, 0.5%-0.7% of Mn, 2%-3% of Cr, 2.8%-3.1% of Mo, 0.8%-1.2% of Cu, 8%-9% of V, 0.002%-0.003% of B, 0.04%-0.05% of Sn, 0.02%-0.03% of Te, 0.01%-0.02% of Ce, 0.03%-0.04% of Zr, 0.004%-0.005% of Y, 0.01%-0.02% of P, 0.001%-0.002% of S and the balance of Fe and inevitable impurities, wherein Cu/Sn is equal to 20-24. The grinding bowl lining board finished product disclosed by the invention is good in quality, and has a service life prolonged by nearly three times; the service life of the existing grinding bowl lining board is only 3000 hours, and the service life of the existing grinding bowl lining board disclosed by the invention reaches 9000 hours-11000 hours.

Description

A kind of abrasion-proof backing block of long service life
Technical field
The present invention relates to abrasion-proof backing block technical field, more particularly, relate to a kind of abrasion-proof backing block of long service life.
Background technology
High-abrasive material is the comparatively special material of a class, and it is used for existing the occasion of wearing and tearing, as: in mining machinery, engineering machinery, powder equipment with the interactional mechanical component of material such as native sand, ore, rock, cement; The agricultural machine such as grain and oil processing, farming harvesting; Many components of machine in water conservancy and steam power plant; The tooth of human body, sole, nib and multiple life product etc.Can say, high-abrasive material is ubiquity in each industrial circles such as metallurgy, building materials, mine, harbour, oil, electric power, coal, chemical industry and military affairs, and everyone life is closely bound up.
The Working environment of high-abrasive material is very complicated, some high-abrasive material need to be worked under the bad working environments conditions such as heavy duty, impact, burn into dust, steam, dregs, usually for occasions such as mine, machinery, water power, coal, harbour, metallurgy, these environment can cause huge loss and the energy dissipation of high-abrasive material, this part high-abrasive material, in occupation of the main body of high-abrasive material, comprises antifriction cast iron and wearable cast steel two parts.
Coal-grinding process is that coal is broken and the ever-increasing process of surface-area.Increase new surface-area, must overcome the intermolecular bonding force of solid, thereby need consumed energy.Coal by being ground into coal dust, is mainly by crushing, smashes and grind three kinds of modes and carry out in coal pulverizer.The pattern of coal pulverizer is a lot, and the rotating speed of massage coal working part can be divided into three types, i.e. low-speed coal mill, medium-speed pulverizer and high speed coal mill.Abrasion-proof backing block in bowl pulverizer is its important abrasion-proof backing block, generally only has 3000 hours the work-ing life of abrasion-proof backing block at present, and be that the technical barrier solving is badly in need of in machinery manufacturing industry field the work-ing life of how to improve abrasion-proof backing block.
By patent retrieval, Chinese Patent Application No. 201310051686.2 discloses a kind of abrasion-proof backing block and preparation method thereof, and the component of this abrasion-proof backing block and mass percent are: carbon: 0.25~0.30%, manganese: 0.70~0.90%, silicon: 0.30~0.60%, chromium: 0.8~1.10%, molybdenum: 0.15~0.25%, aluminium: 0.015~0.050%, zirconium: 0.025~0.050%, copper≤0.50%, niobium≤0.020%, tin≤0.020%, surplus is iron and inevitable impurity.Its preparation method comprises the following steps: S1, preparation of raw material: according to the component of abrasion-proof backing block and mass percent preparation raw material; S2, casting: by the above-mentioned raw material preparing smelt, casting, obtain moulding liner plate; The cutting of S3, dead head: by above-mentioned moulding liner plate preheating after heat cut, heat plane; S4, thermal treatment: the moulding liner plate after above-mentioned heat plane is carried out to surface finish processing, while being then warming up to 950~1000 ℃, carry out normalizing, when being 900~950 ℃, temperature quenches, insulation after quenching, then the air cooling of coming out of the stove, in temperature, be tempering under the condition of 190~220 ℃, after tempering, be incubated, obtain finished product abrasion-proof backing block.In high-abrasive material, need to take into full account the impact of various elements, ability is excavated material potentiality fully, obtain the material of good comprehensive mechanical property, component about abrasion-proof backing block in this application case still needs further improvement, and in conjunction with appropriate thermal treatment process, could obtain the abrasion-proof backing block in higher work-ing life.
Summary of the invention
1. the technical problem that invention will solve
The object of the invention is to overcome the abrasion-proof backing block shorter deficiency in work-ing life in coal pulverizer in prior art, a kind of abrasion-proof backing block of long service life is provided, adopt technical scheme of the present invention, the hardness of abrasion-proof backing block is high, toughness is good, hardening capacity good, wear resistance is strong and high comprehensive performance, thus the work-ing life of greatly having improved abrasion-proof backing block.
2. technical scheme
For achieving the above object, technical scheme provided by the invention is:
The abrasion-proof backing block of a kind of long service life of the present invention, on this abrasion-proof backing block, offer open holes, abrasion-proof backing block is comprised of following component and mass percent thereof: C:3.0~3.2%, Si:0.3~0.4%, Mn:0.5~0.7%, Cr:2~3%, Mo:2.8~3.1%, Cu:0.8~1.2%, V:8~9%, B:0.002~0.003%, Sn:0.04~0.05%, Te:0.02~0.03%, Ce:0.01~0.02%, Zr:0.03~0.04%, Y:0.004~0.005%, P:0.01~0.02%, S:0.001~0.002%, surplus is Fe and inevitable impurity, wherein: Cu/Sn=20~24.
Preferably, abrasion-proof backing block is comprised of following component and mass percent thereof: C:3.1%, Si:0.34%, Mn:0.62%, Cr:2.6%, Mo:2.93%, Cu:1.0%, V:8.7%, B:0.0025%, Sn:0.043%, Te:0.025%, Ce:0.017%, Zr:0.033%, Y:0.0046%, P:0.015%, S:0.0018%, surplus is Fe and inevitable impurity.
Preferably, abrasion-proof backing block is comprised of following component and mass percent thereof: C:3.0%, Si:0.4%, Mn:0.5%, Cr:3%, Mo:2.8%, Cu:1.2%, V:8%, B:0.003%, Sn:0.05%, Te:0.03%, Ce:0.01%, Zr:0.04%, Y:0.004%, P:0.02%, S:0.001%, surplus is Fe and inevitable impurity.
Preferably, abrasion-proof backing block is comprised of following component and mass percent thereof: C:3.2%, Si:0.3%, Mn:0.7%, Cr:2%, Mo:3.1%, Cu:0.8%, V:9%, B:0.002%, Sn:0.04%, Te:0.02%, Ce:0.02%, Zr:0.03%, Y:0.005%, P:0.01%, S:0.002%, surplus is Fe and inevitable impurity.
3. beneficial effect
Adopt technical scheme provided by the invention, compared with prior art, there is following unusual effect:
The abrasion-proof backing block of a kind of long service life of the present invention, by adding with Si in mill bowl liner plate molten metal, Mn, Cr is master's alloying element and a small amount of Mo, Cu, V, B, Sn, Te, Ce, Zr, y alloy element, and control Cu/Sn=20~24, mill bowl liner plate is carried out to complex intensifying processing, tissue and the hardening capacity of mill bowl liner plate have been improved, adopt rational casting process simultaneously, by fusion process and heat treatment process, give full play to Cr, Mo, Cu, V, B, Sn, Te, Ce, Zr, the effect of Y, toughness and the wear resisting property of mill bowl liner plate have been improved, reached the required over-all properties of mill bowl liner plate for coal pulverizer far away, the quality of the mill bowl liner plate finished product making is good, improve nearly three times work-ing life, generally only have 3000 hours the work-ing life of existing mill bowl liner plate, mill bowl liner plate of the present invention reaches 9000~11000 hours work-ing life.
Embodiment
For further understanding content of the present invention, below in conjunction with embodiment, the invention will be further described.
Embodiment 1
The abrasion-proof backing block of a kind of long service life of the present embodiment, offers open holes on this abrasion-proof backing block.In the present invention, abrasion-proof backing block is comprised of following component and mass percent thereof: C:3.0~3.2%, Si:0.3~0.4%, Mn:0.5~0.7%, Cr:2~3%, Mo:2.8~3.1%, Cu:0.8~1.2%, V:8~9%, B:0.002~0.003%, Sn:0.04~0.05%, Te:0.02~0.03%, Ce:0.01~0.02%, Zr:0.03~0.04%, Y:0.004~0.005%, P:0.01~0.02%, S:0.001~0.002%, surplus is Fe and inevitable impurity, wherein: Cu/Sn=20~24.Specifically abrasion-proof backing block is comprised of following component and mass percent thereof in the present embodiment: C:3.1%, Si:0.34%, Mn:0.62%, Cr:2.6%, Mo:2.93%, Cu:1.0%, V:8.7%, B:0.0025%, Sn:0.043%, Te:0.025%, Ce:0.017%, Zr:0.033%, Y:0.0046%, P:0.015%, S:0.0018%, surplus is Fe and inevitable impurity.
The preparation method of the abrasion-proof backing block of a kind of long service life of this embodiment, the steps include:
The preparation of step 1, casting sand type
The material of manufacturing sand mold is comprised of following material: casting model powder, furane resin and sulfonic acid solid agent, casting model powder in the present embodiment is comprised of following component and mass percent thereof: 25% natural silica Sand, 34% chromite sand, 15% olivine sand, 16% mound sand and 10% magnesia, casting model powder in the present embodiment adopts polytype casting model powder to coordinate and forms, the molten metal temperature that can prevent casting is balanced, prevents shrinkage cavity.Wherein: the weight of described furane resin is 1.15% of casting model powder weight, described sulfonic acid solid agent and the mass ratio of furane resin are 2:5, and above-mentioned casting model powder, furane resin and sulfonic acid solid agent are stirred and within 28 minutes, obtain moulding sand for casting in stirrer for mixing; Adopt the casting sand type of the moulding sand for casting making abrasion-proof backing block of above-mentioned preparation, latter standing 2 hours of casting sand type finishing; After standing, brushing the first layer coating on casting sand type, this first layer coating is comprised of brown corundum and alcohol, wherein: the mass percent that brown corundum accounts for the first layer coating is 65%, the thickness of the first layer coating is 1.1mm, after brushing, the first layer coating point is burnt to knot; After the first layer coating point is burnt knot, use gas purging casting sand type, and on casting sand type brushing second layer coating, this second layer coating is comprised of brown corundum and alcohol, wherein: the mass percent that brown corundum accounts for second layer coating is 45%, the thickness of second layer coating is 0.9mm, after brushing, second layer coating point is burnt to knot; After second layer coating point is burnt knot, brushing releasing agent in casting sand type, releasing agent in the present embodiment is comprised of following component and mass percent thereof: 10% furnace cloth bag dust-removing ash, 7% titanium dioxide, 5% are without calcium chromium slag, 18% white fused alumina, 23% Wingdale, 22% methyl-silicone oil, 15% hydroxy silicon oil, adopt the releasing agent of the present embodiment configuration, can guarantee the smooth finish of cast(ing) surface, and then reduce the polishing time, improved casting product quality.
Step 2, fusion process
Adopt smelting furnace to carry out fusion smelting, first steel scrap is added to smelting furnace, when the temperature in smelting furnace reaches 1520~1530 ℃, in smelting furnace, add alloy carry out alloying and add slag former, after deoxidation treatment, the metal after melting is poured and contains V, B, Sn, Te, Ce, Zr, in the casting ladle of Y batching, molten metal is consisted of: C:3.1% following component and mass percent thereof, Si:0.34%, Mn:0.62%, Cr:2.6%, Mo:2.93%, Cu:1.0%, V:8.7%, B:0.0025%, Sn:0.043%, Te:0.025%, Ce:0.017%, Zr:0.033%, Y:0.0046%, P:0.015%, S:0.0018%, surplus is Fe and inevitable impurity.Partial Elements about molten metal in this present invention is described in detail as follows: 1) Cr is one of fundamental element of high-abrasive material, can solution strengthening matrix, improve hardening capacity, wear resistance and the erosion resistance of steel, when improving hardness and intensity, do not reduce impact toughness, have higher tempering resistivity, chrome content is controlled at 2~3%.2) Cu can increase the hardening capacity of steel, refinement matrix, and the nano level Cu phase particle of Precipitation has stronger precipitation strength effect, and copper content is controlled at 0.8~1.2%.3) V energy crystal grain thinning, improve matrix strength and impelling strength, the carbide of vanadium all has higher hardness, can significantly improve the wear resisting property of material, meanwhile, vanadium solid solution can obviously improve hardening capacity in steel, also has certain precipitation hardening effect, but too high vanadium strengthening effect is saturated, therefore, vanadiumcontent is controlled at 8~9%.4) Te, Ce, Zr, Y element all have very strong solution strengthening effect, Te, Ce, Zr, Y can form non-spontaneous nucleation center, thereby crystal grain thinning, improve the comprehensive mechanical property of material, but its ratio must be controlled in the scope of Te:0.02~0.03%, Ce:0.01~0.02%, Zr:0.03~0.04%, Y:0.004~0.005%; In addition the Te that, adds 0.02~0.03% weight in the present embodiment can be used for controlling the crystallisation by cooling degree of depth.5) B is surface active element, and very easily segregation, to crystal boundary, effectively suppresses the forming core of proeutectoid ferrite and grows up, and strongly inhibited ferrite transformation improves the strength of materials, and the interaction of B and Y can also obviously improve the low-temperature flexibility of material.6) both ratios of Cu, Sn must be controlled at Cu/Sn=20~24, could coordinate under suitable thermal treatment process excavated material potentiality to greatest extent, obtain the material of good comprehensive mechanical property.
Step 3, casting cycle
The molten metal of step 2 melting is cast in the die cavity of step 1 casting sand type, pouring temperature is 1495~1510 ℃ and all can, pouring temperature in the present embodiment is 1500 ℃, and casting finishes rear naturally cooling 1.5 hours, coolingly unpacks and foundry goods is cleared up afterwards.
Step 4, thermal treatment
The abrasion-proof backing block foundry goods that step 3 is obtained is heat-treated, and its process is as follows:
1) abrasion-proof backing block foundry goods is packed in heat treatment furnace, with the temperature rise rate of 5 ℃/min, control and be warming up to 180 ℃, be incubated 160 minutes; With the temperature rise rate of 7 ℃/min, control and be warming up to 350 ℃ again, be incubated 120 minutes; With the temperature rise rate of 10 ℃/min, control and be warming up to 610 ℃ again, be incubated 100 minutes; With the temperature rise rate of 6 ℃/min, control and be warming up to 860 ℃ again, be incubated 80 minutes; With the temperature rise rate of 3 ℃/min, control and be warming up to 1018 ℃ again, be incubated and go out heat treatment furnace after 250 minutes;
2) the abrasion-proof backing block foundry goods after step 1) is processed carries out the wind processing of quenching, wind is quenched to process on vibration workplatform and is carried out, before abrasion-proof backing block foundry goods is poured over vibration workplatform, open vibration workplatform, the vibrational frequency that makes to vibrate workplatform is 16~18Hz, the amplitude of vertical direction is that 10~20cm all can, the vibrational frequency of vibrating workplatform in the present embodiment is 17Hz, the amplitude of vertical direction is 15cm, and open temperature-dropping fan simultaneously and carry out the wind processing of quenching, when the surface temperature of abrasion-proof backing block foundry goods is down to 610 ℃, closing temperature-dropping fan, to make abrasion-proof backing block foundry goods naturally cool to surface temperature be 350 ℃, now, close the vibrating device of vibration workplatform and reopen temperature-dropping fan, until abrasion-proof backing block foundry goods is cooled to normal temperature,
3) by step 2) abrasion-proof backing block foundry goods after processing again packs in heat treatment furnace, is handled as follows:
Tempering for the first time: control and be warming up to 170 ℃ with the temperature rise rate of 15 ℃/min, be incubated 20 minutes; With the temperature rise rate of 20 ℃/min, control and be warming up to 310 ℃ again, be incubated 25 minutes; With the temperature rise rate of 10 ℃/min, control and be warming up to 400 ℃ again, be incubated 240 minutes, insulating process finishes rear furnace cooling;
Tempering for the second time: control and be warming up to 180 ℃ with the temperature rise rate of 12 ℃/min, be incubated 25 minutes; With the temperature rise rate of 18 ℃/min, control and be warming up to 320 ℃ again, be incubated 27 minutes; With the temperature rise rate of 13 ℃/min, control and be warming up to 390 ℃ again, be incubated 230 minutes, insulating process finishes rear furnace cooling;
Tempering for the third time: control and be warming up to 200 ℃ with the temperature rise rate of 17 ℃/min, be incubated 30 minutes; With the temperature rise rate of 18 ℃/min, control and be warming up to 300 ℃ again, be incubated 35 minutes; With the temperature rise rate of 8 ℃/min, control and be warming up to 400 ℃ again, be incubated 220 minutes, insulating process finishes rear furnace cooling, obtains abrasion-proof backing block.
The thermal treatment process of the present embodiment, for the component of abrasion-proof backing block molten metal in the present invention and mass percent particular design thereof, test-results confirms, in the present invention, in abrasion-proof backing block molten metal, add with Si, Mn, Cr is master's alloying element and a small amount of Mo, Cu, V, B, Sn, Te, Ce, Zr, y alloy element, and control Cu/Sn=20~24, abrasion-proof backing block is carried out to complex intensifying processing, tissue and the hardening capacity of abrasion-proof backing block have been improved, adopt rational casting process simultaneously, by fusion process and specific heat treatment process, give full play to Cr, Mo, Cu, V, B, Sn, Te, Ce, Zr, the effect of Y, toughness and the wear resisting property of abrasion-proof backing block have been improved, make the abrasion-proof backing block significant prolongation in work-ing life of the present embodiment.
The abrasion-proof backing block of the present embodiment, its hardness is 62HRC, and tensile strength is 1541Mpa, and yield strength is 1257Mpa, and unit elongation is 9%, when temperature is-40 ℃, impelling strength is 19J/cm 2, reach 11000 hours the work-ing life in coal pulverizer.
Embodiment 2
The abrasion-proof backing block of a kind of long service life of the present embodiment, this abrasion-proof backing block is comprised of following component and mass percent thereof: C:3.0%, Si:0.4%, Mn:0.5%, Cr:3%, Mo:2.8%, Cu:1.2%, V:8%, B:0.003%, Sn:0.05%, Te:0.03%, Ce:0.01%, Zr:0.04%, Y:0.004%, P:0.02%, S:0.001%, surplus is Fe and inevitable impurity.The preparation method of the present embodiment and result of use thereof are substantially with embodiment 1.
The abrasion-proof backing block of the present embodiment, its hardness is 62HRC, and tensile strength is 1538Mpa, and yield strength is 1260Mpa, and unit elongation is 9%, when temperature is-40 ℃, impelling strength is 21J/cm 2, reach 9300 hours the work-ing life in coal pulverizer.
Embodiment 3
The abrasion-proof backing block of a kind of long service life of the present embodiment, this abrasion-proof backing block is comprised of following component and mass percent thereof: C:3.2%, Si:0.3%, Mn:0.7%, Cr:2%, Mo:3.1%, Cu:0.8%, V:9%, B:0.002%, Sn:0.04%, Te:0.02%, Ce:0.02%, Zr:0.03%, Y:0.005%, P:0.01%, S:0.002%, surplus is Fe and inevitable impurity.The preparation method of the present embodiment and result of use thereof are substantially with embodiment 1.
The abrasion-proof backing block of the present embodiment, its hardness is 63HRC, and tensile strength is 1539Mpa, and yield strength is 1261Mpa, and unit elongation is 9%, when temperature is-40 ℃, impelling strength is 20J/cm 2, reach 9800 hours the work-ing life in coal pulverizer.

Claims (4)

1. the abrasion-proof backing block of a long service life, it is characterized in that: on this abrasion-proof backing block, offer open holes, abrasion-proof backing block is comprised of following component and mass percent thereof: C:3.0~3.2%, Si:0.3~0.4%, Mn:0.5~0.7%, Cr:2~3%, Mo:2.8~3.1%, Cu:0.8~1.2%, V:8~9%, B:0.002~0.003%, Sn:0.04~0.05%, Te:0.02~0.03%, Ce:0.01~0.02%, Zr:0.03~0.04%, Y:0.004~0.005%, P:0.01~0.02%, S:0.001~0.002%, surplus is Fe and inevitable impurity, wherein: Cu/Sn=20~24.
2. the abrasion-proof backing block of a kind of long service life according to claim 1, it is characterized in that: abrasion-proof backing block is comprised of following component and mass percent thereof: C:3.1%, Si:0.34%, Mn:0.62%, Cr:2.6%, Mo:2.93%, Cu:1.0%, V:8.7%, B:0.0025%, Sn:0.043%, Te:0.025%, Ce:0.017%, Zr:0.033%, Y:0.0046%, P:0.015%, S:0.0018%, surplus is Fe and inevitable impurity.
3. the abrasion-proof backing block of a kind of long service life according to claim 1 and 2, it is characterized in that: abrasion-proof backing block is comprised of following component and mass percent thereof: C:3.0%, Si:0.4%, Mn:0.5%, Cr:3%, Mo:2.8%, Cu:1.2%, V:8%, B:0.003%, Sn:0.05%, Te:0.03%, Ce:0.01%, Zr:0.04%, Y:0.004%, P:0.02%, S:0.001%, surplus is Fe and inevitable impurity.
4. according to the abrasion-proof backing block of a kind of long service life described in claim 2 or 3, it is characterized in that: abrasion-proof backing block is comprised of following component and mass percent thereof: C:3.2%, Si:0.3%, Mn:0.7%, Cr:2%, Mo:3.1%, Cu:0.8%, V:9%, B:0.002%, Sn:0.04%, Te:0.02%, Ce:0.02%, Zr:0.03%, Y:0.005%, P:0.01%, S:0.002%, surplus is Fe and inevitable impurity.
CN201310727204.0A 2013-12-25 2013-12-25 A kind of abrasion-proof backing block of long service life Active CN103643109B (en)