CN103642428A - 一种扬声器组装用防水胶黏剂及其制备方法 - Google Patents

一种扬声器组装用防水胶黏剂及其制备方法 Download PDF

Info

Publication number
CN103642428A
CN103642428A CN201410005040.5A CN201410005040A CN103642428A CN 103642428 A CN103642428 A CN 103642428A CN 201410005040 A CN201410005040 A CN 201410005040A CN 103642428 A CN103642428 A CN 103642428A
Authority
CN
China
Prior art keywords
resin
agent
mixture
water
loud speaker
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410005040.5A
Other languages
English (en)
Other versions
CN103642428B (zh
Inventor
刘群柱
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU DONGHE SPEAKER PARTS CO Ltd
Original Assignee
JIANGSU DONGHE SPEAKER PARTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU DONGHE SPEAKER PARTS CO Ltd filed Critical JIANGSU DONGHE SPEAKER PARTS CO Ltd
Priority to CN201410005040.5A priority Critical patent/CN103642428B/zh
Publication of CN103642428A publication Critical patent/CN103642428A/zh
Application granted granted Critical
Publication of CN103642428B publication Critical patent/CN103642428B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种扬声器组装用防水胶黏剂，按重量份组成如下：氯丁橡胶10～15份；SBS8～12份；SIS8～12份；增粘树脂8～12份；增塑剂1～2份；稳定剂0.5～1.5份；防水剂0.2～0.8份；填料10～15份；溶剂30～50份。本发明提供的胶黏剂防水效果佳。

Description

一种扬声器组装用防水胶黏剂及其制备方法
技术领域
本发明涉及一种胶黏剂，具体的说，涉及到一种扬声器组装用防水胶黏剂及其制备方法。
背景技术
扬声器又称“喇叭”，是一种十分常用的电声换能器件，在发声的电子电气设备中都能见到它。扬声器的种类很多，按其换能原理可分为电动式（即动圈式）、静电式（即电容式）、电磁式（即舌簧式）、压电式（即晶体式）等几种，后两种多用于农村有线广播网中；按频率范围可分为低频扬声器、中频扬声器、高频扬声器，这些常在音箱中作为组合扬声器使用。传统的扬声器的音盆都是纸材质的，普通胶黏剂就可以粘接，但是像汽车上面的扬声器并要求有防水特性的扬声器都是采用聚丙烯塑料材质的音盆，就对粘接的胶黏剂提出很高的要求，既要能粘接聚丙烯等塑料，又要胶黏剂具有防水特性，像聚丙烯这类塑料，特别是经过成型后，表面很光滑，普通的胶黏剂根本粘不住。扬声器组装工程中迫切需要不用处理聚丙烯等塑料音盆表面，又能防水的粘接方式。
发明内容
有鉴于此，本发明创造的目的之一是提供一种扬声器组装用防水胶黏剂，目的之二是提供该胶黏剂的制备方法。
本发明创造解决其技术问题所采用的技术方案是：一种扬声器组装用防水胶黏剂，其特征在于，按重量份组成如下：
Figure BDA0000453753340000011
Figure BDA0000453753340000021
优选的，所述SBS为充油型，且为线型、星型结构中的一种或几种混合；
所述SIS为线型、星型结构中的一种或几种的混合；
所述增粘树脂为松香改性酚醛树脂、松香改性萜烯树脂、萜烯酚醛树脂、松香树脂、酚醛树脂、古马隆树脂、氢化石油树脂、石油树脂、烷基酚醛树脂、萜烯树脂、苯乙烯树脂中的一种或几种的混合物；
所述增塑剂为碳酸二苯酯、白油、液体石蜡、已二酸二丁酯、碳酸丙烯酯中的一种或几种的混合物；
所述稳定剂为抗氧剂BHT、抗氧剂1010、抗氧剂4010、紫外线吸收剂UV-9、紫外线吸收剂UV-531中的一种或几种的混合物；
所述防水剂为纳米碳硅酸盐化合物共聚合防水剂、硅烷偶联防水剂、铝盐防水剂、高级脂肪酸防水剂中的一种或几种的混合物；
所述填料为碳酸钙、二氧化硅、有机膨润土、高岭土、氧化铝、硅灰石粉、滑石粉、活性氧化镁、硅微粉、立德粉、超细硫酸钡中的一种或几种的混合物；
所述溶剂为甲苯、醋酸乙酯、二氯甲烷、异丙醇、丁酮、丙酮、乙醇、甲醇、环己酮、碳酸二甲酯、醋酸甲酯、环己烷、正己烷、正庚烷、二甲苯、溶剂油中的一种或几种的混合物。
优选的，扬声器组装用防水胶黏剂按重量份组成如下：
Figure BDA0000453753340000031
一种扬声器组装用防水胶黏剂制备方法，包括如下步骤：在15℃～40℃下，先加入溶剂，再按照比例加入氯丁橡胶、SBS和SIS，搅拌4～6小时，待其溶剂后，依次加入增粘树脂、增塑剂、稳定剂、填料，再在恒定的速度下搅拌2～4小时，并在搅拌的时候缓慢加入防水剂，在搅拌的过程快结束的时候抽真空20～30分钟，即得产品。
本发明解决了现有粘接纸质音盆用胶黏剂无法粘接聚丙烯等材质音盆，以及不防水的缺点等问题。本发明提供的胶黏剂不用处理聚丙烯等塑料音盆表面就能对其进行粘接，方法简便，容易操作，简化生产工艺。本发明提供的胶黏剂防水效果佳，特别是汽车扬声器和室外使用的扬声器都要求防水性，正好解决了这个难题。
具体实施方式
本发明提供的扬声器组装用防水胶黏剂制备方法，包括如下步骤：在15℃～40℃下，先加入溶剂，再按照比例加入氯丁橡胶、SBS和SIS，搅拌4～6小时，待其溶剂后，依次加入增粘树脂、增塑剂、稳定剂、填料，再在恒定的速度下搅拌2～4小时，并在搅拌的时候缓慢加入防水剂，在搅拌的过程快结束的时候抽真空20～30分钟，即得产品。
实施例1
实施例2
Figure BDA0000453753340000042
实施例3
Figure BDA0000453753340000051
实施例4
Figure BDA0000453753340000052
在实施例1～4中，所述氯丁橡胶为日本东曹株式会社G40T、日本电气化学株式会社A-90、山纳合成橡胶股份有限公司SN242、重庆长寿化工有限责任公司CR244-1、德国拜耳公司公司320中的一种或几种的混合物；
所述SBS为充油型，且为线型、星型结构中的一种或几种混合；
所述SIS为线型、星型结构中的一种或几种的混合。
在实施例1、2、4中，所述增粘树脂为松香改性酚醛树脂、松香改性萜烯树脂、萜烯酚醛树脂、松香树脂、酚醛树脂、古马隆树脂、氢化石油树脂、石油树脂、烷基酚醛树脂、萜烯树脂、苯乙烯树脂中的一种或几种的混合物；
所述增塑剂为碳酸二苯酯、白油、液体石蜡、已二酸二丁酯、碳酸丙烯酯中的一种或几种的混合物；
所述稳定剂为抗氧剂BHT、抗氧剂1010、抗氧剂4010、紫外线吸收剂UV-9、紫外线吸收剂UV-531中的一种或几种的混合物；
所述防水剂为纳米碳硅酸盐化合物共聚合防水剂、硅烷偶联防水剂、铝盐防水剂、高级脂肪酸防水剂中的一种或几种的混合物；
所述填料为碳酸钙、二氧化硅、有机膨润土、高岭土、氧化铝、硅灰石粉、滑石粉、活性氧化镁、硅微粉、立德粉、超细硫酸钡中的一种或几种的混合物；
所述溶剂为甲苯、醋酸乙酯、二氯甲烷、异丙醇、丁酮、丙酮、乙醇、甲醇、环己酮、碳酸二甲酯、醋酸甲酯、环己烷、正己烷、正庚烷、二甲苯、溶剂油中的一种或几种的混合物。
上述实施例产品的对未处理的塑料表面粘接和防水型的测试结果如下：
Figure BDA0000453753340000061
Figure BDA0000453753340000071
从上表表明，本发明提供的防水胶黏剂具有良好的防水性，保证了扬声器工作的稳定性。
以上述依据本发明创造的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明创造技术思想的范围内，进行多样的变更以及修改。本项发明创造的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。

Claims (4)

1.一种扬声器组装用防水胶黏剂，其特征在于，按重量份组成如下：
Figure FDA0000453753330000011
2.根据权利要求1所述的扬声器组装用防水胶黏剂，其特征在于，
所述SBS为充油型，且为线型、星型结构中的一种或几种混合；
所述SIS为线型、星型结构中的一种或几种的混合；
所述增粘树脂为松香改性酚醛树脂、松香改性萜烯树脂、萜烯酚醛树脂、松香树脂、酚醛树脂、古马隆树脂、氢化石油树脂、石油树脂、烷基酚醛树脂、萜烯树脂、苯乙烯树脂中的一种或几种的混合物；
所述增塑剂为碳酸二苯酯、白油、液体石蜡、已二酸二丁酯、碳酸丙烯酯中的一种或几种的混合物；
所述稳定剂为抗氧剂BHT、抗氧剂1010、抗氧剂4010、紫外线吸收剂UV-9、紫外线吸收剂UV-531中的一种或几种的混合物；
所述防水剂为纳米碳硅酸盐化合物共聚合防水剂、硅烷偶联防水剂、铝盐防水剂、高级脂肪酸防水剂中的一种或几种的混合物；
所述填料为碳酸钙、二氧化硅、有机膨润土、高岭土、氧化铝、硅灰石粉、滑石粉、活性氧化镁、硅微粉、立德粉、超细硫酸钡中的一种或几种的混合物；
所述溶剂为甲苯、醋酸乙酯、二氯甲烷、异丙醇、丁酮、丙酮、乙醇、甲醇、环己酮、碳酸二甲酯、醋酸甲酯、环己烷、正己烷、正庚烷、二甲苯、溶剂油中的一种或几种的混合物。
3.根据权利要求2所述的扬声器组装用防水胶黏剂，其特征在于，按重量份组成如下：
Figure FDA0000453753330000021
4.如权利要求1～3所述所述的扬声器组装用防水胶黏剂，其特征在于，包括如下步骤：在15℃～40℃下，先加入溶剂，再按照比例加入氯丁橡胶、SBS和SIS，搅拌4～6小时，待其溶剂后，依次加入增粘树脂、增塑剂、稳定剂、填料，再在恒定的速度下搅拌2～4小时，并在搅拌的时候缓慢加入防水剂，在搅拌的过程快结束的时候抽真空20～30分钟，即得产品。
CN201410005040.5A 2014-01-06 2014-01-06 一种扬声器组装用防水胶黏剂及其制备方法 Active CN103642428B (zh)