CN103632687A - CD (Compact Disc) optical disk electroplating material - Google Patents

CD (Compact Disc) optical disk electroplating material Download PDF

Info

Publication number
CN103632687A
CN103632687A CN201310702370.5A CN201310702370A CN103632687A CN 103632687 A CN103632687 A CN 103632687A CN 201310702370 A CN201310702370 A CN 201310702370A CN 103632687 A CN103632687 A CN 103632687A
Authority
CN
China
Prior art keywords
parts
nickelous
optical disk
silit
electroplating material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310702370.5A
Other languages
Chinese (zh)
Inventor
刘思荣
刘宁宇
蔡洛波
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGDONG JINCHAO GROUP CO Ltd
Original Assignee
GUANGDONG JINCHAO GROUP CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGDONG JINCHAO GROUP CO Ltd filed Critical GUANGDONG JINCHAO GROUP CO Ltd
Priority to CN201310702370.5A priority Critical patent/CN103632687A/en
Publication of CN103632687A publication Critical patent/CN103632687A/en
Pending legal-status Critical Current

Abstract

The invention relates to a CD (Compact Disc) optical disk electroplating material, and belongs to the technical field of chemical material processing. The CD optical disk electroplating material comprises the following components in parts by weight: 40-80 parts of silicon carbide, 30-40 parts of zinc oxide, 1-10 parts of nickel carbonate and 20-40 parts of nickel sulphate. The CD optical disk electroplating material disclosed by the invention has the advantages of low cost and good property and is suitable for industrial popularization; an optical disk prepared by utilizing the CD optical disk electroplating material is good in appearance and difficult to scrape.

Description

A kind of CD CD plated material
Technical field
The present invention relates to a kind of plated material, be specifically related to a kind of CD CD plated material, belong to chemical materials manufacture field.
Background technology
CD is the equipment that utilizes Principles of Laser to read and write, it is a kind of supplementary storage developing rapidly, can deposit the multimedia digital information such as various words, sound, figure, image and animation, it is the optical memory that RECENT DEVELOPMENTS gets up to be different from complete magnetic carrier, medium (for example: magneto-optic disk is also CD), method storage and regenerating information with the hydrogen ion laser beam treatment recording medium focusing on, claim again laser-optical disk.Because the capacity of floppy disk is too little, CD relies on large capacity to be widely used.The CD that we listen is a kind of CD, and the VCD seeing, DVD are also a kind of CDs.
CD is a general designation, and it is divided into two classes, and a class is CD-ROM, comprising CD-Audio, CD-Video, CD-ROM, DVD-Audio, DVD-Video, DVD-ROM etc.; Another kind of is recordable disc, and it comprises all kinds such as CD-R, CD-RW, DVD-R, DVD+R, DVD+RW, DVD-RAM, Double layer DVD+R.
Common CD CD is very thin, and it only has 1.2mm thick, but has comprised a lot of contents.CD CD is mainly divided into five layers, comprising substrate, recording layer, reflection horizon, protective seam, printed layers etc.The place of this imprinting signal while being burning of recording layer wherein, its main principle of work is to be coated with and to spread special-purpose organic dyestuff on substrate, for laser recorded information.Because the reflectivity before and after burning is different, while reading the signal of different length via laser, by variation formation 0 and 1 signal of reflectivity, so as to reading information.By 2013, on market, there is three major types organic dyestuff: Hua Jing (Cyanine), phthalocyanine (Phthalocyanine) and azo (AZO).The CD-R CD of disposable recording mainly adopts (phthalocyanine) organic dyestuff, when this CD is when carrying out burning, laser will be to the organic dyestuff being coated with on substrate, carry out burning, direct burning becomes " hole " one by one, have like this state in " hole, hole " and not having " " just to form ' 0' and the ' signal of 1', this one by one " hole " is irreclaimable, namely when burning till, after " hole ", will permanently keep present situation, it is erasable that this also just means that this CD can not repeat.This series of " 0 ", " 1 " information, just formed binary code, thereby represent specific data.For can repeating erasable CD-RW, what smear is not just organic dyestuff, but certain carbon material, when laser is during in burning, not just to burn till " hole " one by one, but the polarity of change carbon material, by changing the polarity of carbon material, forms specific " 0 ", " 1 " code sequence.The polarity of this carbon material can repeat to change, and it is erasable that this also just represents that this CD can repeat.
CN201210589295.1 discloses a kind of preparation method of cd-recordable, wherein the process of electroplated metal layer will be for sending into one by one and electroplate in workstation through the dyestuff video disc of drying, metal cladding under the state of vacuum, preparation cost is high and performance is stable not, can not meet consumer demand.The invention provides a kind of CD CD plated material, superior performance, with low cost, suitablely industrial, promote the use of.
Summary of the invention
The object of this invention is to provide a kind of CD CD plated material, this plated material preparation cost is low, and performance is good, is suitable for promoting the use of industrial, utilizes its CD of preparing, and product lover, is difficult for scratching.
In order to address the above problem, the technical solution adopted in the present invention is:
A CD CD plated material, the weight portion of each component is:
40 ~ 80 parts, silit, 30 ~ 40 parts, zinc paste, 1 ~ 10 part of nickelous carbonate, 20 ~ 40 parts of nickelous sulfates;
40 ~ 60 parts, silit, 30 ~ 35 parts, zinc paste, 5 ~ 10 parts of nickelous carbonates, 30 ~ 40 parts of nickelous sulfates;
70 ~ 80 parts, silit, 35 ~ 40 parts, zinc paste, 5 ~ 10 parts of nickelous carbonates, 30 ~ 40 parts of nickelous sulfates;
60 ~ 70 parts, silit, 35 ~ 40 parts, zinc paste, 1 ~ 5 part of nickelous carbonate, 20 ~ 30 parts of nickelous sulfates;
55 ~ 65 parts, silit, 35 ~ 40 parts, zinc paste, 1 ~ 5 part of nickelous carbonate, 20 ~ 30 parts of nickelous sulfates;
55 parts, silit, 40 parts, zinc paste, 5 parts of nickelous carbonates, 20 parts of nickelous sulfates, 3 parts of sodium perborate;
65 parts, silit, 35 parts, zinc paste, 1 part of nickelous carbonate, 200 parts of nickelous sulfates, 3 parts of sodium perborate.
The invention has the beneficial effects as follows:
the invention provides a kind of CD CD plated material, this plated material preparation cost is low, and performance is good, is suitable for promoting the use of industrial, utilizes its CD of preparing, and product lover, is difficult for scratching, and DEVELOPMENT PROSPECT is good.
Embodiment
Below by embodiment, the present invention is described in further details, these embodiment are only used for illustrating the present invention, do not limit the scope of the invention.
embodiment 1
A CD CD plated material, the weight portion of each component is:
55 parts, silit, 40 parts, zinc paste, 5 parts of nickelous carbonates, 20 parts of nickelous sulfates, 3 parts of sodium perborate.
embodiment 2
A CD CD plated material, the weight portion of each component is:
65 parts, silit, 35 parts, zinc paste, 1 part of nickelous carbonate, 200 parts of nickelous sulfates, 3 parts of sodium perborate.
embodiment 3
A CD CD plated material, the weight portion of each component is:
40 parts, silit, 35 parts, zinc paste, 10 parts of nickelous carbonates, 40 parts of nickelous sulfates.
embodiment 4
A CD CD plated material, the weight portion of each component is:
80 parts, silit, 40 parts, zinc paste, 10 parts of nickelous carbonates, 40 parts of nickelous sulfates.
embodiment 5
A CD CD plated material, the weight portion of each component is:
70 parts, silit, 35 parts, zinc paste, 5 parts of nickelous carbonates, 20 parts of nickelous sulfates.

Claims (7)

1. a CD CD plated material, is characterized in that: the weight portion of each component is:
40 ~ 80 parts, silit, 30 ~ 40 parts, zinc paste, 1 ~ 10 part of nickelous carbonate, 20 ~ 40 parts of nickelous sulfates.
2. a CD CD plated material, is characterized in that: the weight portion of each component is:
40 ~ 60 parts, silit, 30 ~ 35 parts, zinc paste, 5 ~ 10 parts of nickelous carbonates, 30 ~ 40 parts of nickelous sulfates.
3. a CD CD plated material, is characterized in that: the weight portion of each component is:
70 ~ 80 parts, silit, 35 ~ 40 parts, zinc paste, 5 ~ 10 parts of nickelous carbonates, 30 ~ 40 parts of nickelous sulfates.
4. a CD CD plated material, is characterized in that: the weight portion of each component is:
60 ~ 70 parts, silit, 35 ~ 40 parts, zinc paste, 1 ~ 5 part of nickelous carbonate, 20 ~ 30 parts of nickelous sulfates.
5. a CD CD plated material, is characterized in that: the weight portion of each component is:
55 ~ 65 parts, silit, 35 ~ 40 parts, zinc paste, 1 ~ 5 part of nickelous carbonate, 20 ~ 30 parts of nickelous sulfates.
6. a CD CD plated material, is characterized in that: the weight portion of each component is:
55 parts, silit, 40 parts, zinc paste, 5 parts of nickelous carbonates, 20 parts of nickelous sulfates, 3 parts of sodium perborate.
7. a CD CD plated material, is characterized in that: the weight portion of each component is:
65 parts, silit, 35 parts, zinc paste, 1 part of nickelous carbonate, 200 parts of nickelous sulfates, 3 parts of sodium perborate.
CN201310702370.5A 2013-12-19 2013-12-19 CD (Compact Disc) optical disk electroplating material Pending CN103632687A (en)