CN103627186A - Method for applying difficultly-regenerative rubber and plastic waste to paving asphalt filler - Google Patents
Method for applying difficultly-regenerative rubber and plastic waste to paving asphalt filler Download PDFInfo
- Publication number
- CN103627186A CN103627186A CN201310533380.0A CN201310533380A CN103627186A CN 103627186 A CN103627186 A CN 103627186A CN 201310533380 A CN201310533380 A CN 201310533380A CN 103627186 A CN103627186 A CN 103627186A
- Authority
- CN
- China
- Prior art keywords
- rubber
- asphalt
- filler
- waste
- plastics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for applying difficultly-regenerative rubber and plastic waste to a paving asphalt filler, relating to the technical field of resource recycling. The method comprises the following steps of: 1, selecting shoe soles and vamps or leftover materials of waste rubber rain shoes or rubber slippers, placing in a cleaning machine and adding a surfactant for cleaning, removing stains on the surface, and then dewatering through a dewatering machine to obtain a material a, 2, placing the material a in a crusher for being crushed into particles with the particle diameters of less than 3mm to obtain a material b; 3, adding the material b in a process of heating asphalt, and uniformly mixing to obtain a material c, wherein 150-300 kilograms of material b is added in per ton of asphalt; 4, raising the temperature of the material c to 50-90 DEG C, and paving on a pavement. According to the method, waste rubber and plastics and the asphalt are petroleum products, and have compatibility, the waste rubber and plastics are crushed to be used as a filler, and the filler is uniformly added in the asphalt, thus the elasticity, the abrasion resistance and the bonding property of the asphalt are improved, the combustion pollution is prevented, the way is found for the waste rubber and plastics which can not be regenerated, and thus the utilization rate of resources is increased.
Description
Technical field
The present invention relates to resource reutilization technical field, be specifically related to a kind of will be difficult to the rubber and plastic waste material of regeneration for the method for road oil filler.
Background technology
Along with the high speed development of Chinese national economy, the volume of traffic and traffic intensity are increasing day by day, highway fast development.Bituminous pavement because of its surfacing, without seam, drive a vehicle comfortable, vibrate little, noise is low, wear-resisting, airborne dust easy cleaning is not extensively favored, increasing in road construction medium pitch demand, and performance need further improves, but existing pitch resource wretched insufficiency, performance is in urgent need to be improved.
And along with economic fast development, petroleum resources as basic energy resource face exhaustion, the plastic, rubber cost relevant to petroleum products is more and more higher, the recycle of waste or used plastics rubber is paid attention to, in reprocessed plastic(s) industry fast development process, inevitably assemble produce much cannot regeneration plastic cement leftover bits, accumulate over a long period and be piled into mountain, hesitate to discard, how the pollution of burning, dispose and the utilization difficult problem that becomes a reality.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of method simple, good a kind of of practical application effect will be difficult to the rubber and plastic waste material of regeneration for the method for road oil filler.
Technical problem to be solved by this invention realizes by the following technical solutions:
To be difficult to the method for the rubber and plastic waste material of regeneration for road oil filler, its method steps is as follows,
1) sole and vamp or the scrap stock of selecting waste old rain boots or rubber to take off one's shoes, put into cleaning machine and add tensio-active agent to clean, and removes surface blot, then, through water extracter dehydration, obtains material a;
2) material a is put into pulverizer and be ground into particle, particle diameter is less than 3mm, obtains material b;
3) in the process of asphalt heating, material b is added wherein, uniform stirring, obtains material c, and b150-300 kilogram adds materials in 1 ton of pitch;
4) material c is warming up to 50-90 ℃, is layed on road surface.
The invention has the beneficial effects as follows: the waste and old plastic of utilization of the present invention and pitch are all petroleum productss, there is compatibility, waste and old plastic is pulverized and evenly joined in pitch as stopping composition, elasticity, wear resistance and the bond properties of pitch have not only been increased, avoided Air–pollution From Combustion simultaneously, for unrenewable waste and old plastic has found outlet, improved the utilization ratio of resource.
Embodiment
For technique means, creation characteristic that the present invention is realized, reach object and effect is easy to understand, below in conjunction with specific embodiment, further set forth the present invention.
To be difficult to the method for the rubber and plastic waste material of regeneration for road oil filler, its method steps is as follows,
1) sole and vamp or the scrap stock of selecting waste old rain boots or rubber to take off one's shoes, put into cleaning machine and add tensio-active agent to clean, and removes surface blot, then, through water extracter dehydration, obtains material a;
2) material a is put into pulverizer and be ground into particle, particle diameter is less than 3mm, obtains material b;
3) in the process of asphalt heating, material b is joined in pitch, stir, obtain material c, b150 kilogram adds materials in 1 ton of pitch;
4) material c is warming up to 50-90 ℃, is layed on road surface.
More than show and described ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; that in above-described embodiment and specification sheets, describes just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (1)
1. by being difficult to the method for the rubber and plastic waste material of regeneration for road oil filler, it is characterized in that: method steps is as follows,
1) sole and vamp or the scrap stock of selecting waste old rain boots or rubber to take off one's shoes, put into cleaning machine and add tensio-active agent to clean, and removes surface blot, then, through water extracter dehydration, obtains material a;
2) material a is put into pulverizer and be ground into particle, particle diameter is less than 3mm, obtains material b;
3) material b is fused into slurry, in the process of asphalt heating, joins in pitch, stir, obtain material c, b150 kilogram adds materials in 1 ton of pitch;
4) in material c, add tackiness agent and thickening material, make material c be thick, obtain material d;
5) material d is warming up to 50-90 ℃, is layed on road surface.