CN103616565A - 一种石英材料电导率的检测方法 - Google Patents

一种石英材料电导率的检测方法 Download PDF

Info

Publication number
CN103616565A
CN103616565A CN201310663679.8A CN201310663679A CN103616565A CN 103616565 A CN103616565 A CN 103616565A CN 201310663679 A CN201310663679 A CN 201310663679A CN 103616565 A CN103616565 A CN 103616565A
Authority
CN
China
Prior art keywords
quartz
sample
conductivity
mesh standard
mill
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310663679.8A
Other languages
English (en)
Other versions
CN103616565B (zh
Inventor
李冬芹
曹家凯
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Lianyungang Donghai Silica Powder Co Ltd
Original Assignee
Lianyungang Donghai Silica Powder Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lianyungang Donghai Silica Powder Co Ltd filed Critical Lianyungang Donghai Silica Powder Co Ltd
Priority to CN201310663679.8A priority Critical patent/CN103616565B/zh
Publication of CN103616565A publication Critical patent/CN103616565A/zh
Application granted granted Critical
Publication of CN103616565B publication Critical patent/CN103616565B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明是一种石英材料电导率的检测方法，其步骤包括磨介准备、石英砂样品准备、研磨和电导率检测等。当检测样品为石英砂时，取石英砂样品，用8目和16目标准筛过筛，将8目和16目标准筛中的石英砂作为样品；当样品为石英块时，将石英块预碎到粒径为1-3cm小石英块，再用硅石进行破碎，破碎方式将硅石衬砖作为底板，用硅石敲击小石英块，致使小石英块破碎；最后将破碎好的石英砂过8目和16目标准筛，取8目和16目标准筛中部分进行除铁处理，取得样品。本发明方法适用性强，它可以对大小石英块原料进行导电率检测，检测方法操作简单、方便，检测结果准确性高。解决了现在技术中无法对石英块原料进行导电率检测的技术难题。

Description

一种石英材料电导率的检测方法
技术领域
本发明涉一种检测方法，特别是一种石英材料电导率的检测方法。
背景技术
电导率是指在介质中该量与电场强度之积等于传导电流密度。对于各向同性介质，电导率是标量；对于各向异性介质，电导率是张量。生态学中，电导率是以数字表示的溶液传导电流的能力。单位以S/m，μS/cm等表示。
石英材料的电导率是它的一个重要指标。现有技术中，对于石英块或者稍粗一点的石英砂材料，无法对其进行电导率的检测，导致在选择石英材料时无法对其电导率进行评估测定，影响了原料使用前对原料的有效检测。
发明内容
本发明所要解决的技术问题是针对现有技术的不足，提供一种操作方便、检测结果准确的一种石英材料电导率的检测方法。
本发明所要解决的技术问题是通过以下的技术方案来实现的。本发明是一种石英材料电导率的检测方法，其特点是，其步骤如下：
（1）磨介准备：按磨介Φ15mm：Φ10mm：Φ8mm=39-41：69-71：89-91称取磨介；用去离子水清洗研磨罐和磨介，然后将研磨罐、磨介一同放入105℃恒温干燥箱中烘干，冷却到室温后备用；
（2）石英砂样品准备：
当检测样品为石英砂时，取适量的石英砂样品，用8目和16目标准筛过筛，将8目和16目标准筛中的石英砂作为样品；
当样品为石英块时，将石英块预碎到粒径为1-3cm小石英块，再用硅石进行破碎，破碎方式将硅石衬砖作为底板，放在聚氨酯收集槽中，在硅石衬砖上放适量的石英块，然后用硅石敲击小石英块，致使小石英块破碎；最后将破碎好的石英砂过8目和16目标准筛，取8目和16目标准筛中部分进行除铁处理，取得样品；
（3）研磨：将样品100g置于经步骤（1）准备的研磨罐中，加入磨介后固定在行星球磨机上研磨50-70分钟，取下研磨罐将研磨好的物料用80目标准筛过筛，收集过筛后的材料作待测样品；
（4）电导率检测：
a.量取两份100ml的去离子水分别装入两个250ml烧杯中，测量去离子水的电导率，至两电导率相差小于0.1us/cm后进入下一步；
b.准确称取10g待测样品加入其中一烧杯中，另一烧杯纯水做空白，分别置于电磁搅拌器上搅拌30min；搅拌结束后，用温度计测量空白纯水的温度，设定温度补偿，然后测量空白去离子水电导率Ec1,将电极用去离子水冲洗2～3次，测量萃取液的电导率Ec2。
分析结果的表述，以EC样品表示样品的电导率，按下式计算：
             EC样品  = Ec2-Ec1
式中：  Ec1 ——搅拌30min后去离子水的电导率，μS/cm；
        Ec2 ——搅拌30min后萃取液的电导率， μS/cm。
本发明所述的石英砂电导率的检测方法的步骤（1）中，磨介准备中优选按磨介Φ15mm：Φ10mm：Φ8mm=40：70：90称取磨介。
与现有技术相比，本发明方法适用性强，它可以对大小石英块原料进行导电率检测，检测方法操作简单、方便，检测结果准确性高。解决了现在技术中无法对石英块原料进行导电率检测的技术难题。
具体实施方式
以下对本发明技术方案进行进一步的描述，以使本领域技术人员进一步的理解本发明，而不构成对本发明权利的限制。
实施例1，一种石英材料电导率的检测方法，其步骤如下：
（1）磨介准备：按磨介Φ15mm：Φ10mm：Φ8mm=39-41：69-71：89-91称取磨介；用去离子水清洗研磨罐和磨介，然后将研磨罐、磨介一同放入105℃恒温干燥箱中烘干，冷却到室温后备用；
（2）石英砂样品准备：
当检测样品为石英砂时，取适量的石英砂样品，用8目和16目标准筛过筛，将8目和16目标准筛中的石英砂作为样品；
当样品为石英块时，将石英块预碎到粒径为1-3cm小石英块，再用硅石进行破碎，破碎方式将硅石衬砖作为底板，放在聚氨酯收集槽中，在硅石衬砖上放适量的石英块，然后用硅石敲击小石英块，致使小石英块破碎；最后将破碎好的石英砂过8目和16目标准筛，取8目和16目标准筛中部分进行除铁处理，取得样品；
（3）研磨：将样品100g置于经步骤（1）准备的研磨罐中，加入磨介后固定在行星球磨机上研磨50-70分钟，取下研磨罐将研磨好的物料用80目标准筛过筛，收集过筛后的材料作待测样品；
（4）电导率检测：
a.量取两份100ml的去离子水分别装入两个250ml烧杯中，测量去离子水的电导率，至两电导率相差小于0.1us/cm后进入下一步；
b.准确称取10g待测样品加入其中一烧杯中，另一烧杯纯水做空白，分别置于电磁搅拌器上搅拌30min；搅拌结束后，用温度计测量空白纯水的温度，设定温度补偿，然后测量空白去离子水电导率Ec1,将电极用去离子水冲洗2～3次，测量萃取液的电导率Ec2。
分析结果的表述，以EC样品表示样品的电导率，按下式计算：
             EC样品  = Ec2-Ec1
式中：  Ec1 ——搅拌30min后去离子水的电导率，μS/cm；
        Ec2 ——搅拌30min后萃取液的电导率， μS/cm。
实施例2，实施例1所述的石英砂电导率的检测方法中：步骤（1）磨介准备中按磨介Φ15mm：Φ10mm：Φ8mm=40：70：90称取磨介。其余与实施例1同。

Claims (2)

1.一种石英材料电导率的检测方法，其特征在于，其步骤如下：
（1）磨介准备：按磨介Φ15mm：Φ10mm：Φ8mm=39-41：69-71：89-91称取磨介；用去离子水清洗研磨罐和磨介，然后将研磨罐、磨介一同放入105℃恒温干燥箱中烘干，冷却到室温后备用；
（2）石英砂样品准备：
当检测样品为石英砂时，取适量的石英砂样品，用8目和16目标准筛过筛，将8目和16目标准筛中的石英砂作为样品；
当样品为石英块时，将石英块预碎到粒径为1-3cm小石英块，再用硅石进行破碎，破碎方式将硅石衬砖作为底板，放在聚氨酯收集槽中，在硅石衬砖上放适量的石英块，然后用硅石敲击小石英块，致使小石英块破碎；最后将破碎好的石英砂过8目和16目标准筛，取8目和16目标准筛中部分进行除铁处理，取得样品；
（3）研磨：将样品100g置于经步骤（1）准备的研磨罐中，加入磨介后固定在行星球磨机上研磨50-70分钟，取下研磨罐将研磨好的物料用80目标准筛过筛，收集过筛后的材料作待测样品；
（4）电导率检测：
a.量取两份100ml的去离子水分别装入两个250ml烧杯中，测量去离子水的电导率，至两电导率相差小于0.1us/cm后进入下一步；
b.准确称取10g待测样品加入其中一烧杯中，另一烧杯纯水做空白，分别置于电磁搅拌器上搅拌30min；搅拌结束后，用温度计测量空白纯水的温度，设定温度补偿，然后测量空白去离子水电导率Ec1,将电极用去离子水冲洗2～3次，测量萃取液的电导率Ec2；
分析结果的表述，以EC样品表示样品的电导率，按下式计算：
             EC样品  = Ec2-Ec1
式中：  Ec1 ——搅拌30min后去离子水的电导率，μS/cm；
        Ec2 ——搅拌30min后萃取液的电导率， μS/cm。
2.根据权利要求1所述的石英砂电导率的检测方法，其特征在于：步骤（1）磨介准备中按磨介Φ15mm：Φ10mm：Φ8mm=40：70：90称取磨介。
CN201310663679.8A 2013-12-10 2013-12-10 一种石英材料电导率的检测方法 Active CN103616565B (zh)