CN103613898A - 一种电容器用多种橡胶混炼胶密封圈及其制备方法 - Google Patents

一种电容器用多种橡胶混炼胶密封圈及其制备方法 Download PDF

Info

Publication number
CN103613898A
CN103613898A CN201310561261.6A CN201310561261A CN103613898A CN 103613898 A CN103613898 A CN 103613898A CN 201310561261 A CN201310561261 A CN 201310561261A CN 103613898 A CN103613898 A CN 103613898A
Authority
CN
China
Prior art keywords
parts
rubber
mixing
attapulgite
hour
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310561261.6A
Other languages
English (en)
Inventor
孔华英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGLING SIDE TECHNOLOGY Co Ltd
Original Assignee
TONGLING SIDE TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING SIDE TECHNOLOGY Co Ltd filed Critical TONGLING SIDE TECHNOLOGY Co Ltd
Priority to CN201310561261.6A priority Critical patent/CN103613898A/zh
Publication of CN103613898A publication Critical patent/CN103613898A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种混炼胶密封垫材料，其特征在于，由下列重量份的原料制成：氯磺化聚乙烯橡胶105-115、氯丁橡胶（S40V）10-15、甲基丙烯酸正丁酯3-5、碳酸氢钠1-2、硫磺1.5-2、松香2-4、二氧化钛12-15、三氧化二锑6-8、硫酸钡12-15、EVA树脂3-4、促进剂TMTD1-2、促进剂TETD1-2、N330炭黑30-35、改性凹凸棒土10-12；本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明具有良好的力学性能以及耐油性，成本低，适合广泛推广。

Description

一种电容器用多种橡胶混炼胶密封圈及其制备方法
技术领域
本发明涉及橡胶复合材料加工领域，特别是一种混炼胶密封垫材料及其制备方法。
背景技术
密封垫，是一种用于机械、设备、管道等内部，起密封作用的材料。目前使用的密封垫多为橡胶密封垫，其特点是：耐高温、耐臭氧、耐天然老化、耐真空、耐燃料油、耐润滑油、耐强氧化剂、耐药品性和电绝缘性能好，广泛用于国防工业和民用工业。但是现有的橡胶密封垫密封效果不理想、耐磨性较差、强度低等缺陷，已远不能满足现实要求。因此研发一种高性能橡胶密封垫已成为当务之急。
发明内容
本发明的目的是提供一种混炼胶密封垫材料及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种混炼胶密封垫材料，由下列重量份的原料制成：氯磺化聚乙烯橡胶105-115、氯丁橡胶（S40V）10-15、甲基丙烯酸正丁酯3-5、碳酸氢钠1-2、硫磺1.5-2、松香2-4、二氧化钛12-15、三氧化二锑6-8、硫酸钡12-15、EVA树脂3-4、促进剂TMTD1-2、促进剂TETD1-2、N330炭黑30-35、改性凹凸棒土10-12；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、甲苯二异氰酸酯3-4、三羟甲基丙烷三丙烯酸酯2-3、薏仁油2-3、柠檬酸2-3、纳米二氧化钛1-2、三氧化二铝2-3、甲基三乙氧基硅烷1-2、促进剂TMTM1-2、刚玉粉2-3、花椒籽油1-2；制备方法是将凹凸棒土放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述混炼胶密封垫材料，由以下具体步骤制成：将氯磺化聚乙烯橡胶、氯丁橡胶（S40V）、甲基丙烯酸正丁酯、碳酸氢钠、硫磺加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至100-120℃，再加入松香、二氧化钛、三氧化二锑、硫酸钡、EVA树脂、促进剂TMTD，混炼6-8min，再加入促进剂TETD、N330炭黑继续混炼3-5min；加入其余剩余成分混炼5-6min，即得混炼胶料。
本发明的优异效果是：本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明具有良好的力学性能以及耐油性，成本低，适合广泛推广。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种混炼胶密封垫材料，由下列重量份（公斤）的原料制成：氯磺化聚乙烯橡胶105、氯丁橡胶（S40V）10、甲基丙烯酸正丁酯3、碳酸氢钠1、硫磺1.5、松香2、二氧化钛12、三氧化二锑6、硫酸钡12、EVA树脂3、促进剂TMTD1、促进剂TETD1、N330炭黑30、改性凹凸棒土10；
所述改性凹凸棒土由下列重量份（公斤）的原料制成：凹凸棒土20、甲苯二异氰酸酯3、三羟甲基丙烷三丙烯酸酯2、薏仁油2、柠檬酸2、纳米二氧化钛1、三氧化二铝2、甲基三乙氧基硅烷1、促进剂TMTM1、刚玉粉2、花椒籽油1；制备方法是将凹凸棒土放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述混炼胶密封垫材料，由以下具体步骤制成：将氯磺化聚乙烯橡胶、氯丁橡胶（S40V）、甲基丙烯酸正丁酯、碳酸氢钠、硫磺加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至100-120℃，再加入松香、二氧化钛、三氧化二锑、硫酸钡、EVA树脂、促进剂TMTD，混炼6-8min，再加入促进剂TETD、N330炭黑继续混炼3-5min；加入其余剩余成分混炼5-6min，即得混炼胶料。
用本发明的密封垫材料与普通胶料物理性能对比如下表。
Figure BDA0000412399820000021
从表中可以看出用本发明的密封垫材料，综合性能比较好。

Claims (2)

1.一种混炼胶密封垫材料，其特征在于，由下列重量份的原料制成：氯磺化聚乙烯橡胶105-115、氯丁橡胶（S40V）10-15、甲基丙烯酸正丁酯3-5、碳酸氢钠1-2、硫磺1.5-2、松香2-4、二氧化钛12-15、三氧化二锑6-8、硫酸钡12-15、EVA树脂3-4、促进剂TMTD 1-2、促进剂TETD 1-2、N330炭黑30-35、改性凹凸棒土10-12；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、甲苯二异氰酸酯3-4、三羟甲基丙烷三丙烯酸酯2-3、薏仁油2-3、柠檬酸2-3、纳米二氧化钛1-2、三氧化二铝2-3、甲基三乙氧基硅烷1-2、促进剂TMTM1-2、刚玉粉2-3、花椒籽油1-2；制备方法是将凹凸棒土放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
2.根据权利要求1所述混炼胶密封垫材料，其特征在于，由以下具体步骤制成：将氯磺化聚乙烯橡胶、氯丁橡胶（S40V）、甲基丙烯酸正丁酯、碳酸氢钠、硫磺加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至100-120℃，再加入松香、二氧化钛、三氧化二锑、硫酸钡、EVA树脂、促进剂TMTD，混炼6-8min，再加入促进剂TETD、N330炭黑继续混炼3-5min；加入其余剩余成分混炼5-6min，即得混炼胶料。
CN201310561261.6A 2013-11-12 2013-11-12 一种电容器用多种橡胶混炼胶密封圈及其制备方法 Pending CN103613898A (zh)