CN103613808A - 一种安全环保橡胶密封垫材料及其制备方法 - Google Patents

一种安全环保橡胶密封垫材料及其制备方法 Download PDF

Info

Publication number
CN103613808A
CN103613808A CN201310561262.0A CN201310561262A CN103613808A CN 103613808 A CN103613808 A CN 103613808A CN 201310561262 A CN201310561262 A CN 201310561262A CN 103613808 A CN103613808 A CN 103613808A
Authority
CN
China
Prior art keywords
parts
environment
safe
sealing gasket
mixing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310561262.0A
Other languages
English (en)
Inventor
孔华英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGLING SIDE TECHNOLOGY Co Ltd
Original Assignee
TONGLING SIDE TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING SIDE TECHNOLOGY Co Ltd filed Critical TONGLING SIDE TECHNOLOGY Co Ltd
Priority to CN201310561262.0A priority Critical patent/CN103613808A/zh
Publication of CN103613808A publication Critical patent/CN103613808A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种安全环保橡胶密封垫材料，其特征在于，由下列重量份的原料制成：氯丁橡胶（CR121）75-85、氧化锌4-5、陶瓷空心微球40-45、硅酸铝12-15、白碳黑20-25、氢化腰果酚3-4、儿茶酚1-2、乙酰柠檬酸三乙酯4-6、氧化镁2-3、硬脂酸钙1-2、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯1-2、抗氧剂DSTP1-2、硫磺1-2、改性凹凸棒土10-12；本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明配方合理，安全无毒，具有良好的耐油性以及绝缘性能。

Description

一种安全环保橡胶密封垫材料及其制备方法
技术领域
本发明涉及橡胶复合材料加工领域，特别是一种安全环保橡胶密封垫材料及其制备方法。
背景技术
密封垫，是一种用于机械、设备、管道等内部，起密封作用的材料。目前使用的密封垫多为橡胶密封垫，其特点是：耐高温、耐臭氧、耐天然老化、耐真空、耐燃料油、耐润滑油、耐强氧化剂、耐药品性和电绝缘性能好，广泛用于国防工业和民用工业。但是现有的橡胶密封垫密封效果不理想、耐磨性较差、强度低等缺陷，已远不能满足现实要求。因此研发一种高性能橡胶密封垫已成为当务之急。氯丁橡胶有良好的物理机械性能，耐油，耐热，耐燃，耐日光，耐臭氧，耐酸碱，耐化学试剂。
发明内容
本发明的目的是提供一种安全环保橡胶密封垫材料及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种安全环保橡胶密封垫材料，由下列重量份的原料制成：氯丁橡胶（CR121）75-85、氧化锌4-5、陶瓷空心微球40-45、硅酸铝12-15、白碳黑20-25、氢化腰果酚3-4、儿茶酚1-2、乙酰柠檬酸三乙酯4-6、氧化镁2-3、硬脂酸钙1-2、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯1-2、抗氧剂DSTP1-2、硫磺1-2、改性凹凸棒土10-12；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、甲苯二异氰酸酯3-4、三羟甲基丙烷三丙烯酸酯2-3、薏仁油2-3、柠檬酸2-3、纳米二氧化钛1-2、三氧化二铝2-3、甲基三乙氧基硅烷1-2、促进剂TMTM1-2、刚玉粉2-3、花椒籽油1-2；制备方法是将凹凸棒土放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述安全环保橡胶密封垫材料，由以下具体步骤制成：将氯丁橡胶（CR121）、乙酰柠檬酸三乙酯、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至90-110℃，再加入氧化锌、陶瓷空心微球、硅酸铝、白碳黑、氢化腰果酚、儿茶酚，混炼6-8min，再加入氧化镁、硬脂酸钙、抗氧剂DSTP继续混炼4-6min；加入其余剩余成分混炼5-6min，即得混炼胶料。
本发明的优异效果是：本发明添加改性凹凸棒土，改善了胶料的工艺性能，使用环保型配合剂，减少其毒副作用和对环境的污染；本发明配方合理，安全无毒，具有良好的耐油性以及绝缘性能。
具体实施方式
下面通过具体实例对本发明进行详细说明。
一种安全环保橡胶密封垫材料，由下列重量份（公斤）的原料制成：氯丁橡胶（CR121）75、氧化锌4、陶瓷空心微球40、硅酸铝12、白碳黑20、氢化腰果酚3、儿茶酚1、乙酰柠檬酸三乙酯4、氧化镁2、硬脂酸钙1、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯1、抗氧剂DSTP1、硫磺1、改性凹凸棒土10；
所述改性凹凸棒土由下列重量份（公斤）的原料制成：凹凸棒土20、甲苯二异氰酸酯3、三羟甲基丙烷三丙烯酸酯2、薏仁油2、柠檬酸2、纳米二氧化钛1、三氧化二铝2、甲基三乙氧基硅烷1、促进剂TMTM1、刚玉粉2、花椒籽油1；制备方法是将凹凸棒土放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
本发明所述安全环保橡胶密封垫材料，由以下具体步骤制成：将氯丁橡胶（CR121）、乙酰柠檬酸三乙酯、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至90-110℃，再加入氧化锌、陶瓷空心微球、硅酸铝、白碳黑、氢化腰果酚、儿茶酚，混炼6-8min，再加入氧化镁、硬脂酸钙、抗氧剂DSTP继续混炼4-6min；加入其余剩余成分混炼5-6min，即得混炼胶料。
用本发明的橡胶密封垫材料与普通胶料物理性能对比如下表。
Figure BDA0000412244290000031
从表中可以看出用本发明的橡胶密封垫材料，综合性能比较好。

Claims (2)

1.一种安全环保橡胶密封垫材料，其特征在于，由下列重量份的原料制成：氯丁橡胶（CR121）75-85、氧化锌4-5、陶瓷空心微球40-45、硅酸铝12-15、白碳黑20-25、氢化腰果酚3-4、儿茶酚1-2、乙酰柠檬酸三乙酯4-6、氧化镁2-3、硬脂酸钙1-2、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯1-2、抗氧剂DSTP 1-2、硫磺1-2、改性凹凸棒土10-12；
所述改性凹凸棒土由下列重量份的原料制成：凹凸棒土20-24、甲苯二异氰酸酯3-4、三羟甲基丙烷三丙烯酸酯2-3、薏仁油2-3、柠檬酸2-3、纳米二氧化钛1-2、三氧化二铝2-3、甲基三乙氧基硅烷1-2、促进剂TMTM1-2、刚玉粉2-3、花椒籽油1-2；制备方法是将凹凸棒土放入煅烧炉中在700-720℃下煅烧3-4小时，冷却，放入10-12%盐酸溶液中浸泡1-2小时，过滤取出，用清水洗净烘干，粉碎成200-300目粉末，与其它剩余成分混合，研磨分散1-2小时，即得。
2.根据权利要求1所述安全环保橡胶密封垫材料，其特征在于，由以下具体步骤制成：将氯丁橡胶（CR121）、乙酰柠檬酸三乙酯、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯加入密炼机中，加热至80-90℃，混炼3-5min；然后升温至90-110℃，再加入氧化锌、陶瓷空心微球、硅酸铝、白碳黑、氢化腰果酚、儿茶酚，混炼6-8min，再加入氧化镁、硬脂酸钙、抗氧剂DSTP继续混炼4-6min；加入其余剩余成分混炼5-6min，即得混炼胶料。
CN201310561262.0A 2013-11-12 2013-11-12 一种安全环保橡胶密封垫材料及其制备方法 Pending CN103613808A (zh)