CN103612482B - A kind of detection method of electrochemical aluminium thermoprinting performance - Google Patents
A kind of detection method of electrochemical aluminium thermoprinting performance Download PDFInfo
- Publication number
- CN103612482B CN103612482B CN201310601428.7A CN201310601428A CN103612482B CN 103612482 B CN103612482 B CN 103612482B CN 201310601428 A CN201310601428 A CN 201310601428A CN 103612482 B CN103612482 B CN 103612482B
- Authority
- CN
- China
- Prior art keywords
- gold stamping
- version
- pressure
- checking
- stamping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of detection method of electrochemical aluminium thermoprinting performance, utilize the part electrochemical aluminium thermoprinting that there is display and regulate blocking point, pressure of hot stamping and the gold stamping device of combined pressure time to intercept, if thermoprint is clear, then electrochemical aluminium thermoprinting performance is qualified, and records described blocking point, pressure of hot stamping and the parameter of combined pressure time; If thermoprint is fuzzy, then anodized aluminium performance inconsistency lattice.The waste of anodized aluminium can be avoided to anodized aluminium Performance Detection before manufacture and take the production time of production equipment, raising the efficiency.
Description
Technical field
The present invention relates to printing technology, especially relate to a kind of detection method of electrochemical aluminium thermoprinting performance.
Background technology
Post-press finishing technology is as the later process of printing, among the production technology being widely used in various printed matter, wherein gilding technology is especially widely used, and gold stamping have that pattern is bright-coloured, edge clear, picture and text can be interspersed and play crucial touch, increase the effect of added value of product.
Gold stamping adopted material mainly anodized aluminium material, the structure of this material and complex manufacturing, the thermoprint performance of production process factors to the quality of product especially product plays significant impact, therefore, how quick and precisely to identify that the thermoprint performance of anodized aluminium becomes manufacturer, the problem that applying unit is paid close attention to the most, and in the use of reality, applying unit is all often in production application, just find that electrochemical aluminium thermoprinting performance is not good, need of production can not be met, but now, anodized aluminium slitting becomes the product that fabric width is very little, substantially cannot return to production firm, cause waste.
Summary of the invention
The object of the present invention is to provide a kind of detection method of electrochemical aluminium thermoprinting performance, solve after anodized aluminium being put into production in the past and could find the problem that thermoprint performance is not good and cause anodized aluminium to waste.
The technical scheme that technical solution problem of the present invention adopts is: a kind of detection method of electrochemical aluminium thermoprinting performance, comprises the steps:
The gold stamping checking version of A, preparation band picture and text;
B, be arranged in the honeycomb version under gold stamping device heater by described gold stamping checking version, described gold stamping device is have display and regulate blocking point, pressure of hot stamping and the gold stamping device of combined pressure time;
C, intercepting part anodized aluminium are as detected object;
D, described pressure of hot stamping to be made zero, set described blocking point and combined pressure time;
E, by described gold stamping device, described gold stamping checking version and described anodized aluminium are pressed to stock, increase pressure of hot stamping gradually, and pressure uniform is consistent everywhere to keep thermoprint face, carries out examination thermoprint;
F, regulate described blocking point, combined pressure time and pressure of hot stamping, thermoprint is carried out to described stock;
G, judge according to hot stamping effects, if each region of picture and text on described stock is clear, then electrochemical aluminium thermoprinting performance is qualified, and records described blocking point, pressure of hot stamping and the parameter of combined pressure time; If there is fuzzy region in the picture and text on described stock, then anodized aluminium performance inconsistency lattice.
In the detection method of electrochemical aluminium thermoprinting performance of the present invention, in steps A, the thickness of described gold stamping checking version is 1.5mm-7.0mm, and the length of described gold stamping checking version is 5cm-15cm, and the width of described gold stamping checking version is 5cm-15cm.
In the detection method of electrochemical aluminium thermoprinting performance of the present invention, in steps A, the picture and text in described gold stamping checking version comprise the different lines of thickness, and the thickness scope of described lines is 0.1mm-2.0mm.
In the detection method of electrochemical aluminium thermoprinting performance of the present invention, the spacing between adjacent described lines is different, and described spacing range is 0.05mm-1.0mm.
In the detection method of electrochemical aluminium thermoprinting performance of the present invention, in steps A, the picture and text in described gold stamping checking version comprise area on the spot, and described area is on the spot for being more than or equal to 2cm × 2cm.
In the detection method of electrochemical aluminium thermoprinting performance of the present invention, in steps A, described gold stamping checking version is copperplate, steel version or photo zincography.
In the detection method of electrochemical aluminium thermoprinting performance of the present invention, in step B, described gold stamping checking version is fixedly mounted in the honeycomb version under described gold stamping device heater by private code son.
In the detection method of electrochemical aluminium thermoprinting performance of the present invention, described gold stamping checking version is arranged on the center of described honeycomb version.
In the detection method of electrochemical aluminium thermoprinting performance of the present invention, in step F, the adjustable range of described blocking point is 60 DEG C-200 DEG C, and the adjustable range of described combined pressure time is 0.1 second-5 seconds, and the adjustable range of described pressure of hot stamping is 0.01mm-0.3mm.
In the detection method of electrochemical aluminium thermoprinting performance of the present invention, step e also comprises: in thermoprint process, when described stock presenting the 70%-80% effect of described gold stamping checking domain literary composition, stop increasing pressure of hot stamping, adopt the mode of local pad pressure to fill described gold stamping checking version and/or described stock, to keep thermoprint face, pressure uniform is consistent everywhere.
Implement the detection method of electrochemical aluminium thermoprinting performance of the present invention, there is following beneficial effect: first, the detection method of electrochemical aluminium thermoprinting performance of the present invention is simple, accurate and efficient, can before anodized aluminium puts into production the thermoprint performance of just Testing and appraisal anodized aluminium rapidly, can find that thermoprint performance has problems as early as possible, reduce the waste of anodized aluminium, and only need intercept a fritter from the anodized aluminium of entire volume when detecting, save the material of anodized aluminium; The second, in testing process, the blocking point obtained when anodized aluminium performance is qualified, the thermoprint degree of depth and combined pressure time parameter, can directly be converted in production operation, and time when producing is saved in parameter adjustment when speed production uses; 3rd, the gold stamping device of the detection that the present invention is used does not need big scale production equipment, regulates display blocking point, pressure of hot stamping and the gold stamping device of combined pressure time, effectively can save the holding time to production equipment, in order to avoid delay production as long as have.
Accompanying drawing explanation
Fig. 1 is the flow chart of the detection method of electrochemical aluminium thermoprinting performance of the present invention.
Detailed description of the invention
Below in conjunction with drawings and Examples, the specific implementation of the detection method of electrochemical aluminium thermoprinting performance of the present invention is described further:
The present invention, in testing process, does not need with large-scale gold stamping production equipment, as long as gold stamping device is the gold stamping device having display and regulate blocking point, pressure of hot stamping and the function of combined pressure time.The first, can avoid taking production equipment and delaying the production time; Second, by often comparatively large for anodized aluminium consumption on big scale production equipment, can produce more serious waste, and the present invention only needs intercepting fritter anodized aluminium namely can detect its performance; 3rd, the lay day of anodized aluminium on big scale production equipment can be saved.Wherein gold stamping device has the scope of display and adjustment blocking point is 0 DEG C-300 DEG C, and the scope with display and adjustment pressure of hot stamping is 0.01mm-1mm, and having the scope showing and regulate the combined pressure time is 0.1 second-10 seconds.
In addition, for those skilled in the art it is clear that namely the pressure of hot stamping of indication of the present invention refers to the gold stamping checking version thermoprint degree of depth on the substrate, therefore use " mm " as measurement unit.
As shown in Figure 1, the roughly step of the detection method of electrochemical aluminium thermoprinting performance of the present invention comprises; Prepare the gold stamping device of anodized aluminium checking, check that whether each device on gold stamping device is normal; The gold stamping checking version of preparation band picture and text, wherein picture and text can be the lines that thickness is different, and also can be area on the spot, wherein area refers to the picture and text of out and out area on the spot, refers to do not have space etc. in picture and text; Gold stamping checking version is arranged in the honeycomb version under gold stamping device heater; Intercept part anodized aluminium as detected object; Pressure of hot stamping is made zero, setting blocking point and combined pressure time, increases pressure of hot stamping gradually, carry out examination thermoprint; Blocking point, combined pressure time and pressure of hot stamping is regulated to carry out thermoprint to stock, can be that blocking point, combined pressure time and pressure of hot stamping are finely tuned, also can be that after fine setting, the picture and text of thermoprint are fuzzy, setting can be readjusted to blocking point, combined pressure time and pressure of hot stamping; Judgement is carried out and recording parameters according to hot stamping effects.Wherein stock can be paper, millboard, PVC sheet or PET sheet.
Be described further below by the detection method of multiple embodiment to electrochemical aluminium thermoprinting performance of the present invention:
Embodiment 1:
A detection method for electrochemical aluminium thermoprinting performance, comprises the steps, and is specifically described each step.
The gold stamping device of S1, the checking of preparation anodized aluminium, checks that whether temperaturecontrol sensor, pressure sensor and combined pressure persond eixis be normal, checks that whether electric wiring and safety device etc. be normal.
The gold stamping checking version of S2, preparation band picture and text, gold stamping checking version is red copper version, and its thickness is 1.5mm, and length is 12cm, and width is 8cm; Wherein in gold stamping checking version, the making of picture and text adopts the mode of the micro-finishing impression of conputer controlled to complete, picture and text comprise the different lines of thickness and area on the spot, the thickness of lines includes the lines of the lines of 0.1mm, the lines of 0.25mm, the lines of 0.4mm and 0.5mm, and the spacing between adjacent described lines includes the spacing of the spacing of 0.05mm, the spacing of 0.08mm, the spacing of 0.15mm and 0.3mm.
S3, be arranged on gold stamping checking version under gold stamping device heater honeycomb version on, preferably, be arranged on the center of honeycomb version, be conducive to gold stamping checking version to be like this heated and uniform force, wherein gold stamping checking version is fixedly mounted in honeycomb version by private code son, also gold stamping checking version can be bonded in honeycomb version by the mode using heat-curable glue to paste, can guarantee that gold stamping checking version directly contacts with the heater on gold stamping device like this.The mode that private code son is fixedly mounted on honeycomb version is well known to those skilled in the art, and is no longer described in further details here.
S4, intercepting part anodized aluminium, as detected object, only need intercept a fritter anodized aluminium, preferably, suitable with the size of described gold stamping checking version.
S5, the pressure of hot stamping of gold stamping device to be made zero, setting blocking point 120 DEG C and 0.3 second combined pressure time.
S6, by gold stamping device, gold stamping checking version and anodized aluminium are pressed to stock, in thermoprint process, increase pressure of hot stamping gradually, when stock presenting 70% effect of gold stamping checking domain literary composition, stop increasing pressure of hot stamping, paste the peeling paper with standard thickness according to actual conditions in the uneven part of gold stamping checking version and stock, with the thermoprint face keeping between gold stamping checking version and stock, pressure uniform is consistent everywhere.Mainly due to uneven part can be there is when installing gold stamping checking version and place stock in this, so adopt the mode of local pad pressure to fill uneven part, gold stamping checking version after filling carries out examination thermoprint in art post paperboard, to verify that whether pressure is consistent in thermoprint face everywhere, if inconsistent need again re-start according to actual needs and fill, till the picture and text of the thermoprint in art post paperboard are clear, namely to thermoprint face everywhere pressure consistent.
S7, to finely tune according to hot stamping effects fine setting blocking point 120 DEG C ± 10 DEG C, 0.3 second ± 0.2 second combined pressure time and pressure of hot stamping, the adjustable range of pressure of hot stamping is 0.01mm-0.1mm, by the picture and text thermoprint in gold stamping checking version on stock, find that the rear line weight of fine setting is 0.5mm, line pitch is less than the region blur of 0.15mm, occurs scumming phenomenon;
S8, readjust setting blocking point be 80 DEG C, the combined pressure time is still 0.3 second, at this moment the picture and text that thermoprint goes out are all very clear, anodized aluminium performance is qualified, record blocking point 80 DEG C, pressure of hot stamping 0.01mm-0.1mm and the parameter of 0.3 second combined pressure time, these parameters can be converted into production operation parameter simultaneously, can speed production use time parameter adjustment, save the time before producing, enhance productivity.
Embodiment 2:
A detection method for electrochemical aluminium thermoprinting performance, comprises the steps, and is specifically described each step.
The gold stamping device of S1, the checking of preparation anodized aluminium, checks that whether temperaturecontrol sensor, pressure sensor and combined pressure persond eixis be normal, checks that whether electric wiring and safety device etc. be normal.
The gold stamping checking version of S2, preparation band picture and text, gold stamping checking version is brass version, and its thickness is 3.0mm, and length is 5cm, and width is 5cm; Wherein in gold stamping checking version, the making of picture and text adopts the mode of the micro-finishing impression of conputer controlled to complete, picture and text comprise the different lines of thickness and area on the spot, the thickness of lines includes the lines of the lines of 0.6mm, the lines of 0.7mm, the lines of 0.9mm and 1.0mm, spacing between adjacent described lines includes the spacing of the spacing of 0.1mm, the spacing of 0.2mm, the spacing of 0.4mm and 0.5mm, and area is 2cm × 2cm on the spot.
S3, be arranged on gold stamping checking version under gold stamping device heater honeycomb version on, preferably, be arranged on the center of honeycomb version, be conducive to gold stamping checking version to be like this heated and uniform force, wherein gold stamping checking version is fixedly mounted in honeycomb version by private code son, also gold stamping checking version can be bonded in honeycomb version by the mode using heat-curable glue to paste, can guarantee that gold stamping checking version directly contacts with the heater on gold stamping device like this.The mode that private code son is fixedly mounted on honeycomb version is well known to those skilled in the art, and is no longer described in further details here.
S4, intercepting part anodized aluminium, as detected object, only need intercept a fritter anodized aluminium, preferably, suitable with the size of described gold stamping checking version.
S5, the pressure of hot stamping of gold stamping device to be made zero, regulate setting blocking point 150 DEG C and 1 second combined pressure time.
S6, by gold stamping device, gold stamping checking version and anodized aluminium are pressed to stock, in thermoprint process, increase pressure of hot stamping gradually, when stock presenting 75% effect of gold stamping checking domain literary composition, stop increasing pressure of hot stamping, paste the peeling paper with standard thickness according to actual conditions in the uneven part of gold stamping checking version and stock, with the thermoprint face keeping between gold stamping checking version and stock, pressure uniform is consistent everywhere.Mainly due to uneven part can be there is when installing gold stamping checking version and place stock in this, so adopt the mode of local pad pressure to fill uneven part, gold stamping checking version after filling carries out examination thermoprint in art post paperboard, to verify that whether pressure is consistent in thermoprint face everywhere, if inconsistent need again re-start according to actual needs and fill, till the picture and text of the thermoprint in art post paperboard are clear, namely to thermoprint face everywhere pressure consistent.
S7, to finely tune according to hot stamping effects fine setting blocking point 150 DEG C ± 5 DEG C, 1 second ± 0.2 second combined pressure time and pressure of hot stamping, the adjustable range of pressure of hot stamping is 0.1mm-0.25mm, by the picture and text thermoprint in gold stamping checking version on stock, the picture and text that thermoprint goes out are all very clear, anodized aluminium performance is qualified, record blocking point 150 DEG C, pressure of hot stamping and the parameter of 1 second combined pressure time simultaneously, these parameters can be converted into production operation parameter, can speed production use time parameter adjustment, save the time before producing, enhance productivity.
Embodiment 3:
A detection method for electrochemical aluminium thermoprinting performance, comprises the steps, and is specifically described each step.
The gold stamping device of S1, the checking of preparation anodized aluminium, checks that whether temperaturecontrol sensor, pressure sensor and combined pressure persond eixis be normal, checks that whether electric wiring and safety device etc. be normal.
The gold stamping checking version of S2, preparation band picture and text, gold stamping checking version is steel version, and its thickness is 5.0mm, and length is 15cm, and width is 15cm; Wherein in gold stamping checking version, the making of picture and text adopts the mode of the micro-finishing impression of conputer controlled to complete, picture and text comprise the different lines of thickness and area on the spot, the thickness of lines includes the lines of the lines of 1.5mm, the lines of 1.65mm, the lines of 1.8mm and 2.0mm, and the spacing between adjacent described lines includes the spacing of the spacing of 0.5mm, the spacing of 0.6mm, the spacing of 0.8mm and 1.0mm.
S3, be arranged on gold stamping checking version under gold stamping device heater honeycomb version on, preferably, be arranged on the center of honeycomb version, be conducive to gold stamping checking version to be like this heated and uniform force, wherein gold stamping checking version is fixedly mounted in honeycomb version by private code son, also gold stamping checking version can be bonded in honeycomb version by the mode using heat-curable glue to paste, can guarantee that gold stamping checking version directly contacts with the heater on gold stamping device like this.The mode that private code son is fixedly mounted on honeycomb version is well known to those skilled in the art, and is no longer described in further details here.
S4, intercepting part anodized aluminium, as detected object, only need intercept a fritter anodized aluminium, preferably, suitable with the size of described gold stamping checking version.
S5, the pressure of hot stamping of gold stamping device to be made zero, regulate setting blocking point 190 DEG C and 0.5 second combined pressure time.
S6, by gold stamping device, gold stamping checking version and anodized aluminium are pressed to stock, in thermoprint process, increase pressure of hot stamping gradually, when stock presenting 80% effect of gold stamping checking domain literary composition, stop increasing pressure of hot stamping, paste the peeling paper with standard thickness according to actual conditions in the uneven part of gold stamping checking version and stock, with the thermoprint face keeping between gold stamping checking version and stock, pressure uniform is consistent everywhere.Mainly due to uneven part can be there is when installing gold stamping checking version and place stock in this, so adopt the mode of local pad pressure to fill uneven part, gold stamping checking version after filling carries out examination thermoprint in art post paperboard, to verify that whether pressure is consistent in thermoprint face everywhere, if inconsistent need again re-start according to actual needs and fill, till the picture and text of the thermoprint in art post paperboard are clear, namely to thermoprint face everywhere pressure consistent.
S7, to finely tune according to hot stamping effects fine setting blocking point 190 DEG C ± 10 DEG C, 0.5 second ± 0.4 second combined pressure time and pressure of hot stamping, the adjustable range of pressure of hot stamping is 0.01mm-0.3mm, by the picture and text thermoprint in gold stamping checking version on stock, after finding fine setting, picture and text are fuzzy;
S8, as shown in table 1, readjust setting blocking point and combined pressure time, by the picture and text thermoprint in gold stamping checking version on stock, the lines of picture and text 1.8mm, it is still fuzzy that spacing is less than 0.8mm region, therefore anodized aluminium performance inconsistency lattice, regulates result as follows:
Table 1
Note: pressure of hot stamping adjustable range in above-mentioned thermoprint process is 0.01mm-0.3mm.
Embodiment 4:
A detection method for electrochemical aluminium thermoprinting performance, comprises the steps, and is specifically described each step.
The gold stamping device of S1, the checking of preparation anodized aluminium, checks that whether temperaturecontrol sensor, pressure sensor and combined pressure persond eixis be normal, checks that whether electric wiring and safety device etc. be normal.
The gold stamping checking version of S2, preparation band picture and text, gold stamping checking version is photo zincography, and its thickness is 7.0mm, and length is 8cm, and width is 6cm; Wherein in gold stamping checking version, the making of picture and text adopts the mode of the micro-finishing impression of conputer controlled to complete, and picture and text comprise area on the spot, and area is 2cm × 2cm on the spot.
S3, be arranged on gold stamping checking version under gold stamping device heater honeycomb version on, preferably, be arranged on the center of honeycomb version, be conducive to gold stamping checking version to be like this heated and uniform force, wherein gold stamping checking version is fixedly mounted in honeycomb version by private code son, also gold stamping checking version can be bonded in honeycomb version by the mode using heat-curable glue to paste, can guarantee that gold stamping checking version directly contacts with the heater on gold stamping device like this.The mode that private code son is fixedly mounted on honeycomb version is well known to those skilled in the art, and is no longer described in further details here.
S4, intercepting part anodized aluminium, as detected object, only need intercept a fritter anodized aluminium, preferably, suitable with the size of described gold stamping checking version.
S5, the pressure of hot stamping of gold stamping device to be made zero, regulate setting blocking point 70 DEG C and 4.5 seconds combined pressure time.
S6, by gold stamping device, gold stamping checking version and anodized aluminium are pressed to stock, in thermoprint process, increase pressure of hot stamping gradually, when stock presenting 80% effect of gold stamping checking domain literary composition, stop increasing pressure of hot stamping, paste the peeling paper with standard thickness according to actual conditions in the uneven part of gold stamping checking version and stock, with the thermoprint face keeping between gold stamping checking version and stock, pressure uniform is consistent everywhere.Mainly due to uneven part can be there is when installing gold stamping checking version and place stock in this, so adopt the mode of local pad pressure to fill uneven part, gold stamping checking version after filling carries out examination thermoprint in art post paperboard, to verify that whether pressure is consistent in thermoprint face everywhere, if inconsistent need again re-start according to actual needs and fill, till the picture and text of the thermoprint in art post paperboard are clear, namely to thermoprint face everywhere pressure consistent.
S7, according to hot stamping effects fine setting blocking point 70 DEG C ± 10 DEG C, 4.5 seconds ± 0.5 second combined pressure time and pressure of hot stamping are finely tuned, the adjustable range of pressure of hot stamping is 0.1mm-0.3mm, by the picture and text thermoprint in gold stamping checking version on stock, find that the picture and text that thermoprint goes out are smudgy clear, readjust blocking point 100 DEG C, the combined pressure time is still 4.5 seconds, then the picture and text that go out of thermoprint are very clear, anodized aluminium performance is qualified, record blocking point 100 DEG C simultaneously, the parameter of pressure of hot stamping 0.1mm-0.3mm and 4.5 seconds combined pressure time, these parameters can be converted into production operation parameter, can speed production use time parameter adjustment, save the time before producing, enhance productivity.
Be understandable that; the type of the present invention's gold stamping checking version used is not limited to cited by above-described embodiment; without prejudice under the prerequisite of spirit and scope of the invention, any replacement that those skilled in the art make gold stamping checking version used, adjustment or equivalent replacement are all included in protection scope of the present invention.
The present invention has the following advantages: first, the detection method of electrochemical aluminium thermoprinting performance of the present invention is simple, accurate and efficient, can before anodized aluminium puts into production the thermoprint performance of just Testing and appraisal anodized aluminium rapidly, can find that thermoprint performance has problems as early as possible, reduce the waste of anodized aluminium, and only need intercept a fritter from the anodized aluminium of entire volume when detecting, save the material of anodized aluminium; The second, in testing process, the blocking point obtained when anodized aluminium performance is qualified, pressure of hot stamping and combined pressure time parameter, can directly be converted in production operation, and time when producing is saved in parameter adjustment when speed production uses; 3rd, the gold stamping device of the detection that the present invention is used does not need big scale production equipment, regulates display blocking point, pressure of hot stamping and the gold stamping device of combined pressure time, effectively can save the holding time to production equipment, in order to avoid delay production as long as have.
Should be understood that, for those of ordinary skills, can be improved according to the above description or convert, all these improve or conversion all should belong within the protection domain of claims of the present invention.
Claims (4)
1. a detection method for electrochemical aluminium thermoprinting performance, is characterized in that, comprises the steps:
The gold stamping checking version of A, preparation band picture and text, the thickness of described gold stamping checking version is 1.5mm-7.0mm, the length of described gold stamping checking version is 5cm-15cm, the width of described gold stamping checking version is 5cm-15cm, picture and text in described gold stamping checking version comprise the different lines of thickness, the thickness scope of described lines is 0.1mm-2.0mm, spacing between adjacent described lines is different, described spacing range is 0.05mm-1.0mm, picture and text in described gold stamping checking version comprise area on the spot, and described area is on the spot for being more than or equal to 2cm × 2cm;
B, be arranged in the honeycomb version under gold stamping device heater by described gold stamping checking version, described gold stamping device is have display and regulate blocking point, pressure of hot stamping and the gold stamping device of combined pressure time;
C, intercept part anodized aluminium as detected object, the size of the anodized aluminium of intercepting and the size of described gold stamping checking version suitable;
D, described pressure of hot stamping to be made zero, set described blocking point and combined pressure time;
E, by described gold stamping device, described gold stamping checking version and described anodized aluminium are pressed to stock, increase pressure of hot stamping gradually, and pressure uniform is consistent everywhere to keep thermoprint face, carry out examination thermoprint, in thermoprint process, when described stock presenting the 70%-80% effect of described gold stamping checking domain literary composition, stop increasing pressure of hot stamping, paste the peeling paper with standard thickness in the uneven part of gold stamping checking version and stock, to keep thermoprint face, pressure uniform is consistent everywhere;
F, regulate described blocking point, combined pressure time and pressure of hot stamping, thermoprint is carried out to described stock, the adjustable range of described blocking point is 60 DEG C-200 DEG C, and the adjustable range of described combined pressure time is 0.1 second-5 seconds, and the adjustable range of described pressure of hot stamping is 0.01mm-0.3mm;
G, judge according to hot stamping effects, if each region of picture and text on described stock is clear, then electrochemical aluminium thermoprinting performance is qualified, and records described blocking point, pressure of hot stamping and the parameter of combined pressure time; If there is fuzzy region in the picture and text on described stock, then anodized aluminium performance inconsistency lattice.
2. the detection method of electrochemical aluminium thermoprinting performance according to claim 1, is characterized in that, in steps A, described gold stamping checking version is copperplate, steel version or photo zincography.
3. the detection method of electrochemical aluminium thermoprinting performance according to claim 1, is characterized in that, in step B, described gold stamping checking version is fixedly mounted in the honeycomb version under described gold stamping device heater by private code son.
4. the detection method of electrochemical aluminium thermoprinting performance according to claim 3, is characterized in that, described gold stamping checking version is arranged on the center of described honeycomb version.