CN103602152B - The coating that a kind of cracking resistance is durable - Google Patents
The coating that a kind of cracking resistance is durable Download PDFInfo
- Publication number
- CN103602152B CN103602152B CN201310580635.9A CN201310580635A CN103602152B CN 103602152 B CN103602152 B CN 103602152B CN 201310580635 A CN201310580635 A CN 201310580635A CN 103602152 B CN103602152 B CN 103602152B
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- durable
- cracking resistance
- nitrile rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the coating that a kind of cracking resistance is durable; be made up of the raw material of following parts by weight: alkali earth metal aluminate 2.3-3.8 part, 2; 4,6-trimethylbenzoy-dipheny phosphine oxide 1.5-2.6 part, dihydroxyl Polymethyl methacrylate 2.6-4.7 part, oxalic dialdehyde 1.3-1.8 part, softening water 4-10 part, carboxy nitrile rubber 3-5.8 part, isopropyl benzene hydroperoxide 2.5-3.2 part and hydrogenated castor oil 1.3-3.8 part.The present invention, compared with existing waterproof paint, has the following advantages: paint film is hard, wear resistance good, strong adhesion, and has good water tolerance, is specially adapted to interior wall, the coating such as exterior wall and roof; And carboxy nitrile rubber is added in food ingredient, cohesive force is good, and cracking resistance is durable in use.
Description
Technical field
The present invention relates to the coating that a kind of cracking resistance is durable, belong to building material field.
Background technology
So-called coating refers to that coating body surface can form film under certain conditions and play protection, the class I liquid I of decoration or other specific functions (insulation, antirust, mildew-resistant, heat-resisting etc.) or solid material.Be main raw material mainly with vegetables oil greatly because of early stage coating, therefore also known as painting.Present synthetic resins is most of or all instead of vegetables oil, therefore is called coating.The broad varietys such as decorative paint, protective system, electrically conducting coating, rust proof paint, high-temperature resistant coating, thermo-paint, thermal insulating coating, frie retardant coating, waterproof paint can be divided into by function, the kind of waterproof paint has a lot, but the weather resistance of most of waterproof paint is poor, waterproof effect is not strong.
Summary of the invention
For the deficiency that prior art exists, technical problem to be solved by this invention is, provides the coating that a kind of cracking resistance is durable, and smear sticking power better, film coated surface is smooth, weather resistance and water-repellancy excellence.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is, the coating that a kind of cracking resistance is durable,
Be made up of the raw material of following parts by weight: alkali earth metal aluminate 2.3-3.8 part, 2; 4,6-trimethylbenzoy-dipheny phosphine oxide 1.5-2.6 part, dihydroxyl Polymethyl methacrylate 2.6-4.7 part, oxalic dialdehyde 1.3-1.8 part, softening water 4-10 part, carboxy nitrile rubber 3-5.8 part, isopropyl benzene hydroperoxide 2.5-3.2 part and hydrogenated castor oil 1.3-3.8 part.
Optimize, the coating that above-mentioned cracking resistance is durable, be made up of the raw material of following parts by weight:
Alkali earth metal aluminate 3.2 parts, 2; 4,6-trimethylbenzoy-dipheny phosphine oxide 1.9 parts, dihydroxyl Polymethyl methacrylate 3.7 parts, oxalic dialdehyde 1.6 parts, softening water 6 parts, carboxy nitrile rubber 5.2 parts, isopropyl benzene hydroperoxide 2.9 parts and hydrogenated castor oil 3.2 parts.
The present invention, compared with existing waterproof paint, has the following advantages: paint film is hard, wear resistance good, strong adhesion, and has good water tolerance, is specially adapted to interior wall, the coating such as exterior wall and roof; And carboxy nitrile rubber is added in food ingredient, cohesive force is good, and cracking resistance is durable in use.
Embodiment
embodiment 1
The present invention is the durable coating of a kind of cracking resistance, is made up of the raw material of following parts by weight:
Alkali earth metal aluminate 3.2 parts, 2; 4,6-trimethylbenzoy-dipheny phosphine oxide 1.9 parts, dihydroxyl Polymethyl methacrylate 3.7 parts, oxalic dialdehyde 1.6 parts, softening water 6 parts, carboxy nitrile rubber 5.2 parts, isopropyl benzene hydroperoxide 2.9 parts and hydrogenated castor oil 3.2 parts.
embodiment 2
The present invention is the durable coating of a kind of cracking resistance, is made up of the raw material of following parts by weight:
Alkali earth metal aluminate 2.3 parts, 2; 4,6-trimethylbenzoy-dipheny phosphine oxide 1.5 parts, dihydroxyl Polymethyl methacrylate 2.6 parts, oxalic dialdehyde 1.3 parts, softening water 4 parts, carboxy nitrile rubber 3 parts, isopropyl benzene hydroperoxide 2.5 parts and hydrogenated castor oil 1.3 parts.
embodiment 3
The present invention is the durable coating of a kind of cracking resistance, is made up of the raw material of following parts by weight:
Alkali earth metal aluminate 3.8 parts, 2; 4,6-trimethylbenzoy-dipheny phosphine oxide 2.6 parts, dihydroxyl Polymethyl methacrylate 4.7 parts, oxalic dialdehyde 1.8 parts, softening water 10 parts, carboxy nitrile rubber 5.8 parts, isopropyl benzene hydroperoxide 3.2 parts and hydrogenated castor oil 3.8 parts.
The present invention, compared with existing waterproof paint, has the following advantages: paint film is hard, wear resistance good, strong adhesion, and has good water tolerance, is specially adapted to interior wall, the coating such as exterior wall and roof; And carboxy nitrile rubber is added in food ingredient, cohesive force is good, and cracking resistance is durable in use.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned citing; those skilled in the art; in essential scope of the present invention, the change made, remodeling, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (2)
1. the coating that cracking resistance is durable, is characterized in that: be made up of the raw material of following parts by weight:
Alkali earth metal aluminate 2.3-3.8 part, 2; 4,6-trimethylbenzoy-dipheny phosphine oxide 1.5-2.6 part, dihydroxyl Polymethyl methacrylate 2.6-4.7 part, oxalic dialdehyde 1.3-1.8 part, softening water 4-10 part, carboxy nitrile rubber 3-5.8 part, isopropyl benzene hydroperoxide 2.5-3.2 part and hydrogenated castor oil 1.3-3.8 part.
2. the coating that cracking resistance according to claim 1 is durable, is characterized in that:
Be made up of the raw material of following parts by weight: alkali earth metal aluminate 3.2 parts, 2; 4,6-trimethylbenzoy-dipheny phosphine oxide 1.9 parts, dihydroxyl Polymethyl methacrylate 3.7 parts, oxalic dialdehyde 1.6 parts, softening water 6 parts, carboxy nitrile rubber 5.2 parts, isopropyl benzene hydroperoxide 2.9 parts and hydrogenated castor oil 3.2 parts.