CN103589203A - Seal primer and preparation method thereof - Google Patents
Seal primer and preparation method thereof Download PDFInfo
- Publication number
- CN103589203A CN103589203A CN201310466216.2A CN201310466216A CN103589203A CN 103589203 A CN103589203 A CN 103589203A CN 201310466216 A CN201310466216 A CN 201310466216A CN 103589203 A CN103589203 A CN 103589203A
- Authority
- CN
- China
- Prior art keywords
- parts
- hour
- add
- primer
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a seal primer. The invention is characterized in that the primer is prepared from the following raw materials in parts by weight: 30-35 parts of ethyl methacrylate, 12-14 parts of butyl acrylate, 10-12 parts of hollow microbead, 0.4-0.8 part of cyclohexanone peroxide, 2.0-3.0 parts of benzotriazole, 2-3 parts of fatty acid polyethylene glycol ester, 45-50 parts of E-44 epoxy resin, 1-2 parts of anilinomethyl triethoxy silane, 3-4 parts of 1,6-hexanediol diacrylate, 1-2 parts of benzoin, 15-20 parts of amino resin, 5-10 parts of propylene glycol methyl ether acetate, 2-5 parts of polydimethylsiloxane and 3-4 parts of dispersing aid. The product can effectively resist alkalis and salts in the base layer from precipitation, has very high binding power with the elastic paint, and enhances the adhesive force between the base layer and the topcoat; the seal primer has the advantages of high water resistance, high moldproof and antimicrobial effects, high permeability and high adhesive force; and the seal primer can effectively prevent the finish coat from being corroded by soluble substances on the wall, thereby enhancing the quality of the topcoat.
Description
Technical field
The present invention relates to a kind of paint and preparation method thereof, particularly a kind of seal coat and preparation method thereof.
Background technology
Priming paint is the first layer of paint system, for improving the sticking power of finish paint, increase finish paint fullness ratio, alkali-resistivity is provided, anti-corrosion function etc. is provided, can guarantee the even absorption of finish paint simultaneously, make paint system performance best effect.Seal coat composition one is by hypertonicity epoxy resin liquid, and composition two is special curing agent, is applicable to the substrate surfaces such as concrete, timber, terrazzo, iron and steel and makes seal coat.Seal coat is attached directly in substrate, on it, be attached with middle painting, face painting, play a part to form a connecting link, good coat system does not have the interface of layer between layer and coating film, coating application requires can effectively interpenetrate between every procedure, whole coating becomes as a whole, seal coat is the first film being attached on base material, thereby the specification of quality of seal coat is very high, there are good water-fast, alkali resistance, saline and alkaline the oozing out of waterproof isolation, have good sticking power and ply adhesion.
Summary of the invention
The object of this invention is to provide a kind of good penetrability, strong adhesion, Salt And Alkali Tolerance, water-fast Eng than priming paint and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
A kind of seal coat, raw material by following weight part is made: β-dimethyl-aminoethylmethacrylate 30-35, butyl acrylate 12-14, cenosphere 10-12, cyclohexanone peroxide 0.4-0.8, benzotriazole 2.0-3.0, fatty acid polyglycol ester 2-3, E-44 epoxy resin 45-50, anilinomethyl triethoxysilane 1-2,1,6 hexanediol diacrylate 3-4, st-yrax 1-2, aminoresin 15-20,1-Methoxy-2-propyl acetate 5-10, polydimethylsiloxane 2-5, dispersing auxiliary 3-4.
Described dispersing auxiliary makes by the following method: the weight part of its each feed composition is: diatomite 200-210, nano-sized carbon 4-5, jade powder 12-13, Zinc Gluconate 2-3, xitix 1-2, pentaerythritol triacrylate 1-2, Zirconium tetrafluoride 1-2, alum 3-4, polyoxyethylene octylphenol ether 1-2, Silane coupling agent KH550 1-2; Preparation method adds diatomite in 12-15% hydrochloric acid soln and soaks 3-4 hour, takes out, and with clear water, cleans, and calcines 3-4 hour with sending in calcining furnace at 530-550 ℃, cooling, merges and grinds to form 300-400 order powder with jade; Add Zirconium tetrafluoride, nano-sized carbon, polyoxyethylene octylphenol ether to continue grinding distribution 2-3 hour, then add other remaining component to be ground to fully to disperse to obtain 300-400 order powder, obtain.
Seal coat of the present invention, by following concrete steps, made:
(1) β-dimethyl-aminoethylmethacrylate, butyl acrylate, cenosphere, cyclohexanone peroxide are added in reactor and stirred, temperature of reaction is controlled at below 40-60 ℃, stirs 0.5-1 hour;
(2) in reactor, add benzotriazole, fatty acid polyglycol ester, E-44 epoxy resin, anilinomethyl triethoxysilane, 1,6 hexanediol diacrylate again, temperature of reaction is controlled at below 70-80 ℃, stirs 0.5-1 hour;
(3) finally add all the other remaining components, mix, stir, grind, obtain the slurry of 20-40 μ m, filter and get final product.
Product of the present invention can effectively be resisted separating out of alkali salt in basic unit, has extremely strong cohesive force with elastic coating, improves the sticking power of basic unit and face painting; Water-fast, antimildew and antibacterial, seepage force, strong adhesion; Outstanding closure, alkali burnout resistance, salting-out resistance, can effectively prevent that finish paint is corroded by body of wall soluble substance, the quality that raising face is coated with.
Specific embodiments
Below by specific examples, the present invention is described in detail.
A kind of seal coat, by following weight part (kilogram) raw material make: β-dimethyl-aminoethylmethacrylate 30, butyl acrylate 12, cenosphere 10, cyclohexanone peroxide 0.4, benzotriazole 2, fatty acid polyglycol ester 2, E-44 epoxy resin 45, anilinomethyl triethoxysilane 1,1,6 hexanediol diacrylate 3, st-yrax 1, aminoresin 15,1-Methoxy-2-propyl acetate 5, polydimethylsiloxane 2, dispersing auxiliary 3.
Described dispersing auxiliary makes by the following method: the weight part of its each feed composition (kilogram) be: diatomite 200, nano-sized carbon 4, jade powder 12, Zinc Gluconate 2, xitix 1, pentaerythritol triacrylate 1, Zirconium tetrafluoride 1, alum 3, polyoxyethylene octylphenol ether 1, Silane coupling agent KH550 1; Preparation method adds diatomite in 12-15% hydrochloric acid soln and soaks 3-4 hour, takes out, and with clear water, cleans, and calcines 3-4 hour with sending in calcining furnace at 530-550 ℃, cooling, merges and grinds to form 300-400 order powder with jade; Add Zirconium tetrafluoride, nano-sized carbon, polyoxyethylene octylphenol ether to continue grinding distribution 2-3 hour, then add other remaining component to be ground to fully to disperse to obtain 300-400 order powder, obtain.
Seal coat of the present invention, by following concrete steps, made:
(1) β-dimethyl-aminoethylmethacrylate, butyl acrylate, cenosphere, cyclohexanone peroxide are added in reactor and stirred, temperature of reaction is controlled at below 40-60 ℃, stirs 0.5-1 hour;
(2) in reactor, add benzotriazole, fatty acid polyglycol ester, E-44 epoxy resin, anilinomethyl triethoxysilane, 1,6 hexanediol diacrylate again, temperature of reaction is controlled at below 70-80 ℃, stirs 0.5-1 hour;
(3) finally add all the other remaining components, mix, stir, grind, obtain the slurry of 20-40 μ m, filter and get final product.
Product performance index of the present invention:
1, time of drying (25 ℃): surface drying 28min, does solid work 42h
2, snappiness mm≤1
3, hardness >=2H
4, high temperature resistant (130 ℃) >=490h
5, shock-resistance 50
6, salt spray resistance (120h level) >=3
7, water tolerance (29 ± 1 ℃ of 240h): non-foaming, do not come off
8, oil resistant (90# gasoline, 56h): non-foaming, do not come off
9, alkali resistance (GB/T9755-2001): by 48 hours
10, artificial weathering ageing resistance (GB/T9755-2001): by 1200 hours.
Claims (2)
1. a seal coat, it is characterized in that, raw material by following weight part is made: β-dimethyl-aminoethylmethacrylate 30-35, butyl acrylate 12-14, cenosphere 10-12, cyclohexanone peroxide 0.4-0.8, benzotriazole 2.0-3.0, fatty acid polyglycol ester 2-3, E-44 epoxy resin 45-50, anilinomethyl triethoxysilane 1-2,1,6 hexanediol diacrylate 3-4, st-yrax 1-2, aminoresin 15-20,1-Methoxy-2-propyl acetate 5-10, polydimethylsiloxane 2-5, dispersing auxiliary 3-4;
Described dispersing auxiliary makes by the following method: the weight part of its each feed composition is: diatomite 200-210, nano-sized carbon 4-5, jade powder 12-13, Zinc Gluconate 2-3, xitix 1-2, pentaerythritol triacrylate 1-2, Zirconium tetrafluoride 1-2, alum 3-4, polyoxyethylene octylphenol ether 1-2, Silane coupling agent KH550 1-2; Preparation method adds diatomite in 12-15% hydrochloric acid soln and soaks 3-4 hour, takes out, and with clear water, cleans, and calcines 3-4 hour with sending in calcining furnace at 530-550 ℃, cooling, merges and grinds to form 300-400 order powder with jade; Add Zirconium tetrafluoride, nano-sized carbon, polyoxyethylene octylphenol ether to continue grinding distribution 2-3 hour, then add other remaining component to be ground to fully to disperse to obtain 300-400 order powder, obtain.
2. seal coat according to claim 1, is characterized in that, by following concrete steps, is made:
(1) β-dimethyl-aminoethylmethacrylate, butyl acrylate, cenosphere, cyclohexanone peroxide are added in reactor and stirred, temperature of reaction is controlled at below 40-60 ℃, stirs 0.5-1 hour;
(2) in reactor, add benzotriazole, fatty acid polyglycol ester, E-44 epoxy resin, anilinomethyl triethoxysilane, 1,6 hexanediol diacrylate again, temperature of reaction is controlled at below 70-80 ℃, stirs 0.5-1 hour;
(3) finally add all the other remaining components, mix, stir, grind, obtain the slurry of 20-40 μ m, filter and get final product.