CN103570332A - Colored environmental-friendly flame retardant material - Google Patents
Colored environmental-friendly flame retardant material Download PDFInfo
- Publication number
- CN103570332A CN103570332A CN201210268549.XA CN201210268549A CN103570332A CN 103570332 A CN103570332 A CN 103570332A CN 201210268549 A CN201210268549 A CN 201210268549A CN 103570332 A CN103570332 A CN 103570332A
- Authority
- CN
- China
- Prior art keywords
- flame retardant
- retardant material
- pigment
- kilograms
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a colored environmental friendly flame retardant material which is composed of the following raw materials by weight: 20-50 parts of magnesium oxide, 10-20 parts of low calcium fly ash, 5-9 parts of magnesium hydroxide, 3-6 parts of a pigment and 30-60 parts of water, the low calcium fly ash comprises stove ash or stove slag, the pigment is a chromium salt pigment, the colored environmental friendly flame retardant material is flame retardant and does not release toxic gases when burned, the stove ash or stove slag is turned from waste to treasure, the colored environmental friendly flame retardant material is energy-saving and environmental friendly, and the colored environmental friendly flame retardant material is no longer single in color due to the use of the pigment.
Description
Technical field
The present invention relates to a kind of material of construction, be specifically related to a kind of coloured environmental protection flame retardant material.
Background technology
Fire retardant material is a kind of protecting materials, and it is can stop burning and own and be not easy the material of burning, have solid as said the materials such as cement, steel, glass; Have liquidly, also referred to as fire retardant, if needing to coat fire retardant on the various material surfaces such as fire-proof wall, it can guarantee do not burnt on fire, also can not make combustion range aggravation, expand; At present fire retardant material mainly contain organic and inorganic, halogen and non-halogen, high flame retardant material is organic be take that bromine is, some fire retardants that nitrogen system and red phosphorus and compound are representative, inorganic is mainly the flame-retardant systems such as antimonous oxide, magnesium hydroxide, aluminium hydroxide, silicon system; Organic fire-resisting has good avidity in general, in plastics, adds and uses, and bromide fire retardant occupies absolute predominance in organic fire-resisting system, but " blame " is many in environmental issue.
Enhancing day by day along with people's environmental protection, safety, health perception, countries in the world start using environment friendly flame retardant as research and development and the emphasis of application, cement, mortar always are the most traditional raw material, but its price is not cheap, most material of construction all has potential safety hazard, even fire-retardant, but when being heated to certain temperature, these material easy firings and discharge toxic gas, and in material of construction, general fire retardant material color and luster is single.
Summary of the invention
In order to solve deficiency of the prior art, the invention provides the material of construction that a kind of flame retardant properties is good and coloured.
The object of the invention is to be achieved through the following technical solutions.
A material, it is comprised of following raw materials by weight portion ratio: magnesium oxide: 20-50 part, low calcium fly ash: 10-20 part, magnesium hydroxide: 5-9 part, pigment: 3-6 part, water: 30-60 part.
Described low calcium fly ash is comprised of ashes or slag.
Described pigment is chromic salts pigment.
The present invention has flame retardant resistance, and does not discharge toxic gas when burning; And ashes or slag are turned waste into wealth, energy-saving and environmental protection; Use pigment to make material color no longer single.
Embodiment
Embodiment 1:
A material, it is comprised of following raw materials by weight portion:
Magnesium oxide: 20 kilograms;
Ashes: 10 kilograms;
Magnesium hydroxide: 5 kilograms;
Chromic salts pigment: 3 kilograms;
Water: 30 kilograms;
After above-mentioned raw materials is mixed, can prepare this material of 68 kilograms.
Embodiment 2:
A material, it is comprised of following raw materials by weight portion:
Magnesium oxide: 50 kilograms;
Slag: 20 kilograms;
Magnesium hydroxide: 9 kilograms;
Chromic salts pigment: 6 kilograms;
Water: 60 kilograms;
After above-mentioned raw materials is mixed, can prepare this material of 45 kilograms.
Embodiment 3:
A material, it is comprised of following raw materials by weight portion:
Magnesium oxide: 35 kilograms;
Ashes: 15 kilograms;
Magnesium hydroxide: 7 kilograms;
Chromic salts pigment: 4.5 kilograms;
Water: 45 kilograms;
After above-mentioned raw materials is mixed, can prepare this material of 106.5 kilograms.
Embodiment 4:
A material, it is comprised of following raw materials by weight portion:
Magnesium oxide: 40 kilograms;
Slag: 18 kilograms;
Magnesium hydroxide: 8 kilograms;
Chromic salts pigment: 5 kilograms;
Water: 40 kilograms;
After above-mentioned raw materials is mixed, can prepare this material of 111 kilograms.
The present invention has flame retardant resistance, and does not discharge toxic gas when burning; And ashes or slag are turned waste into wealth, energy-saving and environmental protection; Use pigment to make material color no longer single.
Above content is in conjunction with concrete embodiment further description made for the present invention, can not assert that specific embodiment of the invention is confined to these explanations.For general technical staff of the technical field of the invention, without departing from the inventive concept of the premise, can also make some simple deduction or replace, all should be considered as belonging to protection scope of the present invention.
Claims (3)
1. a coloured environmental protection flame retardant material, is characterized in that: it is comprised of following raw materials by weight portion ratio: magnesium oxide: 20-50 part, low calcium fly ash: 10-20 part, magnesium hydroxide: 5-9 part, pigment: 3-6 part, water: 30-60 part.
2. a kind of coloured environmental protection flame retardant material as claimed in claim 1, is characterized in that: described low calcium fly ash is comprised of ashes or slag.
3. a kind of coloured environmental protection flame retardant material as claimed in claim 1, is characterized in that: described pigment is chromic salts pigment.