CN103555926A - Atmosphere replacement method for continuous annealing furnace - Google Patents
Atmosphere replacement method for continuous annealing furnace Download PDFInfo
- Publication number
- CN103555926A CN103555926A CN201310550386.9A CN201310550386A CN103555926A CN 103555926 A CN103555926 A CN 103555926A CN 201310550386 A CN201310550386 A CN 201310550386A CN 103555926 A CN103555926 A CN 103555926A
- Authority
- CN
- China
- Prior art keywords
- furnace
- atmosphere
- continuous annealing
- annealing furnace
- protective atmosphere
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to an atmosphere replacement method for a continuous annealing furnace. The atmosphere replacement method is characterized in that protective atmosphere replacement is finished in a mutual conversion between a stainless steel belt annealing mode and a titanium belt annealing mode in the continuous annealing furnace by means of a protective atmosphere replacement system arranged in the furnace body of the continuous annealing furnace, and the protective atmosphere in the furnace is quickly replaced to a required protective atmosphere in the furnace according to process requirements so as to adjust the protective atmosphere in the furnace; the protective atmosphere replacement system is communicated with an external protective gas supply system; and the protective atmosphere in the furnace can be flexibly replaced to mixed atmosphere of hydrogen and nitrogen or argon atmosphere according to production requirements so as to meet the stainless steel belt annealing and titanium belt annealing demands. A titanium belt and a stainless steel belt are annealed on a continuous annealing line, so that no special annealing furnace is constructed for annealing and producing titanium belts.
Description
Technical field
Protective atmosphere method of replacing when the invention belongs to titanium band and Stainless Steel Band and annealing in continuous annealing furnace, belongs to the method for continuous annealing furnace for titanium band and the Stainless Steel Band annealing protective atmosphere displacement when changing the annealing of titanium band with Stainless Steel Band annealing especially.
Background technology
In existing titanium plate production process, anneal mostly adopts vacuum coil annealing, vacuum coil annealing is periodic annealing, and the annealing cycle is long, because of in vacuum annealing process, titanium plate is outside, inequality is heated by middle part and heart portion, makes sheet material Internal and external cycle microstructure and property homogeneity poor.At present a lot of technique is subject to thermal effect to promote titanium plate by strengthen atmosphere convection current under argon gas atmosphere in annealing process, although promoted to a certain extent tissue and the performance uniformity of vacuum annealing titanium plate, but fail fundamentally to solve the problem of titanium plate annealing ununiformity, annealing sheet material exists the problems such as performance difference and surface quality defect at different positions.The invention that application number is 201110003672.4 provides a kind of, with continuous bright annealing furnace, Cold-rolled Pure titanium, Ti Alloy Strip is involved in to the technique that row continuous bright annealing is processed, according to the thick difference of volume, with the speed of 2 ~ 6m/min successively process, clean, dry up, finally introduce continuous bright annealing furnace; In annealing furnace, fill inert protective gas argon gas.Continuous annealing has solved the unequal problem of being heated that periodic annealing easily causes, but because titanium plate rolling drawability is special, titanium Strip building of production line difficulty is large, titanium plate costliness and consumption are little, the special strip producing line of building titanium plate is not only invested huge, and produces to a certain degree surplus of line throughput.At present mostly utilize steel sheet production line to carry out the rolling of titanium plate, follow-up vacuum coil annealing or the continuous annealing mode taked.
The utility model that application number is 201220023604.4 provides a kind of stainless steel and titanium steel continuous annealing furnace spray device for cooling, and this device relates to a kind of spray device for cooling, is specifically related to a kind of stainless steel and titanium steel continuous annealing furnace spray device for cooling.In order to solve the one-piece construction of existing annealing furnace spray device for cooling, be unfavorable for the quick cooling process behind the quick cooling and titanium steel slow cooling section after stainless steel heating, and the very inconvenient problem of installation and maintenance.The stainless steel that this utility model is studied and titanium steel continuous annealing furnace, be to carry out continuous annealing to stainless steel with containing the steel of the alloying element titanium adding, and is not the continuous annealing furnace that can carry out continuous annealing to stainless steel and titanium plate.
The continuous annealing of titanium plate adopts argon gas atmosphere protection; stainless steel plate adopts the annealing of perhydro atmosphere protection; after titanium plate being rolled on existing steel sheet production line, steel sheet production line continuous annealing furnace cannot carry out continuous annealing to titanium plate; if the special newly-built continuous annealing line that can be used for the annealing of titanium plate; invest huge; and because titanium plate demand is little, the easy superfluous interim stopping production problem of continuous annealing furnace that also therefore causes of continuous annealing line throughput; less economical, and may Yin Lu district location problem affect production scheduling etc.
Inhomogeneous and have problems such as surface quality defect for overcoming titanium plate microstructure and property in vacuum coil annealing, huge and the overcapacity problem of the investment of simultaneously avoiding newly-built titanium band continuous annealing furnace to cause, therefore propose a kind of continuous annealing furnace that is applicable to titanium band and Stainless Steel Band annealing, can be used for the continuous annealing of titanium plate and stainless steel plate.When titanium band and Stainless Steel Band are annealed variety exchanging in continuous annealing, need to change protective atmosphere in continuous annealing furnace.
Summary of the invention
Problem to be solved by this invention is: a kind of atmosphere method of replacing that is applicable to vertical or Horizontal Continuous Furnace is provided; guaranteeing under the prerequisite of continuous annealing furnace use safety and titanium band, Stainless Steel Band annealing quality, the protective atmosphere to the continuous annealing furnace for titanium band and Stainless Steel Band annealing when changing the annealing of titanium band or Stainless Steel Band annealing is replaced.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A kind of atmosphere method of replacing of continuous annealing furnace, it is characterized in that: the protective atmosphere exchange system being equipped with by continuous annealing furnace body, in continuous annealing furnace, by Stainless Steel Band annealing pattern, when titanium band annealing pattern is changed mutually, completing protective atmosphere replaces, according to technique, need to be protective atmosphere in needed stove by the protective atmosphere Rapid replacement in stove, thereby complete the adjustment of protective atmosphere in stove; Described protective atmosphere exchange system is connected with outer protection gas airing system; Mainly comprise the steps:
A: it is creep mode that continuous annealing furnace operational mode is set, furnace annealing product is stainless-steel roll or titanium volume;
B: pass into nitrogen purging annealing furnace with displacement furnace atmosphere after reducing furnace temperature;
C: according to annealing product protective atmosphere needs, pass into the protective atmosphere needing, furnace atmosphere is replaced;
D: after furnace atmosphere is replaced, heats up, and change annealing product, adjustment annealing furnace is normal operation mode, anneals in continuous annealing furnace;
Described continuous annealing furnace be when Stainless Steel Band anneal after changing annealing product, and for preventing Stainless Steel Band heat-tinting, the interior employing of stove hydrogen nitrogen mixture is protective atmosphere, and hydrogen volume is than 75% ~ 100%; When titanium band is annealed, hydrogen nitrogen mixture in continuous annealing furnace need be purged totally, guarantee that argon gas atmosphere is protective atmosphere, purity of argon is greater than 99%.
By technique scheme, described atmosphere method of replacing specifically comprises the steps:
When continuous annealing furnace is produced steel band, in stove, adopting hydrogen nitrogen mixture is protective atmosphere; When this continuous annealing furnace need to be for the production of titanium band, it is creep mode that continuous annealing furnace operational mode is set, and reduces continuous annealing furnace furnace temperature; When each district's furnace temperature of annealing furnace is down to 800 ℃, utilize protective atmosphere exchange system to carry out nitrogen purging, progressively the hydrogen nitrogen mixture protective atmosphere in stove is replaced into nitrogen, with protective atmosphere exchange system, carry out again the high-purity argon gas purging of volume fraction 99.99%, progressively protective atmosphere in stove is replaced into needed argon gas, thereby meets the continuous annealing protective atmosphere needs of titanium band; After furnace atmosphere displacement completely, after argon content reaches 99%, in continuous annealing furnace, heat up, and connect steel band and titanium band by processing apparatus before continuous annealing furnace entrance, annealing product is replaced by titanium band; Adjustment annealing furnace is normal operation mode, carries out the annealing of titanium band in continuous annealing furnace;
When continuous annealing furnace is produced titanium band, in stove, adopting argon gas is protective atmosphere; When production line changes into, produce steel band and this continuous annealing furnace need to be for the production of steel band time, it is creep mode that continuous annealing furnace operational mode is set, and reduces continuous annealing furnace furnace temperature; Utilize protective atmosphere exchange system to carry out nitrogen purging, progressively the argon shield atmosphere in stove is replaced into nitrogen; When each district's furnace temperature of annealing furnace rises to 800 ℃, utilize protective atmosphere exchange system to pass into hydrogen, progressively protective atmosphere in stove is replaced into needed hydrogen nitrogen mixture, thereby meet the continuous annealing protective atmosphere needs of steel band; After furnace atmosphere displacement completely, hydrogen volume, than after 75% ~ 100%, heats up in continuous annealing furnace, and by processing apparatus connection titanium band and steel band before continuous annealing furnace entrance, annealing product is replaced by steel band; Adjustment annealing furnace is normal operation mode, carries out the annealing of steel band in continuous annealing furnace.
By technique scheme, protective atmosphere exchange system divides two subsystems, is respectively main airing system and time airing system; Main airing system passes into fast protective atmosphere in atmosphere displacement in the stage in stove, inferior airing system in production phase regulating stove internal pressure to guarantee furnace pressure state.
By technique scheme, protective atmosphere exchange system is configured in heating zone or the cooling section of continuous annealing furnace, or is configured in the transition section between heating zone and cooling section; The protective atmosphere recycle system is configured in heating zone or the cooling section of continuous annealing furnace, or is configured in the transition section between heating zone and cooling section.
By technique scheme, heating zone is retort furnace; When heating zone is retort furnace, described protective atmosphere exchange system and the protective atmosphere recycle system are not all arranged on heating zone.
With respect to prior art; beneficial effect of the present invention is: the atmosphere method of replacing that a kind of continuous annealing furnace is provided; can replace flexibly protective atmosphere in stove according to need of production is hydrogen nitrogen mixture or argon gas atmosphere, thereby meets the annealing of Stainless Steel Band annealing and titanium band.Realization is annealed to titanium band and Stainless Steel Band on a continuous annealing line, avoided as to carry out the annealing of titanium band and to produce special newly-built annealing furnace, the problems such as the interim stopping production of equipment of also having avoided special newly-built titanium band annealing furnace and having caused because of demand deficiency, promote the utilising efficiency of production line and annealing furnace, promoted greatly economical efficiency and workshop service efficiency; And can promote the efficiency of production Stainless Steel Band-titanium band composition board.
Accompanying drawing explanation
Fig. 1 is the structural representation of the 1st embodiment of the present invention.
Fig. 2 is the structural representation of the 2nd embodiment of the present invention.
In Fig. 1-2, each Reference numeral is corresponding as follows: inlet seal 1, heating zone 2, transition section 3, gas ventilator 4, the protective atmosphere recycle system 5, steering gear 6, passage 7, exit seal 8,, cooling section 9.
Fig. 3 is the structural representation of the 3rd embodiment of the present invention.
Fig. 4 is the structural representation of the 4th embodiment of the present invention.
In Fig. 3-4, each Reference numeral is corresponding as follows: inlet seal 1, preheating section 2, heating zone 3, cooling section 4, exit seal 5, gas ventilator 6, gas-circulating system 7, air cushion airing system 8.
Embodiment
In order to understand better the present invention, below in conjunction with embodiment, further illustrate content of the present invention, but content of the present invention is not only confined to the following examples.
Embodiment 1:
In the present embodiment, the applicable vertical continuous annealing furnace of atmosphere exchange system, comprises inlet seal 1, heating zone 2; transition section 3, cooling section 9, steering gear 6 and passage 7; exit seal 8, is arranged in the gas ventilator 4 on cooling section 9 and is arranged on the protective atmosphere recycle system 5 in heating zone 2.
When vertical continuous annealing furnace is produced steel band, in stove, adopting hydrogen nitrogen (hydrogen volume is than 99.99%) gas mixture is protective atmosphere, when needs change production titanium band into, it is creep mode that continuous annealing furnace operational mode is set, reduce continuous annealing furnace furnace temperature, when each district's furnace temperature of annealing furnace is down to 800 ℃, utilize gas ventilator 4 to carry out nitrogen purging and progressively the hydrogen nitrogen mixture protective atmosphere in stove is replaced into nitrogen, use again high-purity (volume fraction 99.99%) argon purge, progressively nitrogen protection atmosphere in stove is replaced into needed argon gas, in replacement process, by the protective atmosphere recycle system 5, strengthening furnace atmosphere circulates, the main airing system of the gas ventilator 4 being equipped with by continuous annealing furnace passes into fast argon shield atmosphere in stove, complete the displacement to furnace atmosphere, thereby meet the continuous annealing protective atmosphere needs of titanium band.After furnace atmosphere displacement complete (argon content reaches 99%), heat up, and connect steel band and titanium band by processing apparatus before continuous annealing furnace entrance, annealing product is replaced by titanium band, adjustment annealing furnace is normal operation mode, carries out the annealing of titanium band in continuous annealing furnace;
When vertical continuous annealing furnace is produced titanium band, in stove, adopting argon gas is protective atmosphere; When needs production line changes production steel band into, it is creep mode that continuous annealing furnace operational mode is set, and reduces continuous annealing furnace furnace temperature, utilizes nitrogen purging progressively the argon shield atmosphere in stove to be replaced into nitrogen; When rising to 800 ℃, each district's furnace temperature of annealing furnace passes into hydrogen; progressively nitrogen protection atmosphere in stove is replaced into needed hydrogen nitrogen (hydrogen volume is than 99.99%) gas mixture; in replacement process, by the protective atmosphere recycle system 5, strengthening furnace atmosphere circulates; the main airing system of the gas ventilator 4 being equipped with by continuous annealing furnace passes into fast protective atmosphere in stove; complete the displacement to furnace atmosphere, thereby meet the continuous annealing protective atmosphere needs of steel band.After furnace atmosphere displacement complete (hydrogen volume is than 99.99%), heat up, and connect titanium band and steel band by processing apparatus before continuous annealing furnace entrance, annealing product is replaced by steel band, adjustment annealing furnace is normal operation mode, carries out the annealing of steel band in continuous annealing furnace.
Preferably, gas ventilator 4 of the present invention is preferably air exchange system.
According to above-mentioned technique, according to need of production, replacing flexibly protective atmosphere in stove is hydrogen nitrogen mixture or argon gas atmosphere, reaches the object of the annealing that meets steel band annealing and titanium band; And can to titanium band and steel band, carry out after continuous annealing respectively, produce titanium-steel-titanium composition board.The function that realization is rolled and anneals titanium band and steel band on a continuous annealing line, need not be for carrying out the annealing of titanium band and producing special newly-built annealing furnace.And the quality problems such as while there will not be periodic annealing after titanium band annealing sheet material Internal and external cycle microstructure and property homogeneity is poor; Utilising efficiency and the economical efficiency in production line, annealing furnace and workshop have been promoted; And can promote the efficiency of production titanium-steel-titanium composition board.
Embodiment 2:
The vertical continuous annealing furnace that the present embodiment atmosphere exchange system is applicable; comprise inlet seal 1; heating zone 2; transition section 3, cooling section 9, steering gear and passage 7; exit seal 8; heating zone is retort furnace, has muffle tube 10 in heating zone, is arranged in gas ventilator 4 and the protective atmosphere recycle system 5 on cooling section 9.
When vertical continuous annealing furnace is produced steel band, in stove, adopting hydrogen nitrogen (hydrogen volume is than 80%) gas mixture is protective atmosphere, when needs change production titanium band into, it is creep mode that continuous annealing furnace operational mode is set, reduce continuous annealing furnace furnace temperature, when each district's furnace temperature of annealing furnace is down to 800 ℃, utilize nitrogen purging progressively the hydrogen nitrogen mixture protective atmosphere in stove to be replaced into nitrogen, use again high-purity (volume fraction 99.99%) argon purge, progressively protective atmosphere in stove is replaced into needed argon gas, in replacement process, by the protective atmosphere recycle system, strengthening furnace atmosphere circulates, the main airing system of the protective atmosphere exchange system being equipped with by continuous annealing furnace passes into fast protective atmosphere in stove, complete the displacement to furnace atmosphere, thereby meet the continuous annealing protective atmosphere needs of titanium band.After furnace atmosphere displacement complete (argon content reaches 99%), heat up, and connect steel band and titanium band by processing apparatus before continuous annealing furnace entrance, annealing product is replaced by titanium band, adjustment annealing furnace is normal operation mode, carries out the annealing of titanium band in continuous annealing furnace;
When vertical continuous annealing furnace is produced titanium band, in stove, adopting argon gas is protective atmosphere, when needs production line changes production steel band into, it is creep mode that continuous annealing furnace operational mode is set, reduce continuous annealing furnace furnace temperature, utilize nitrogen purging progressively the argon shield atmosphere in stove to be replaced into nitrogen, when rising to 800 ℃, each district's furnace temperature of annealing furnace passes into hydrogen, progressively protective atmosphere in stove is replaced into needed hydrogen nitrogen (hydrogen volume is than 80%) gas mixture, in replacement process, by the protective atmosphere recycle system, strengthening furnace atmosphere circulates, the main airing system of the protective atmosphere exchange system being equipped with by continuous annealing furnace passes into fast protective atmosphere in stove, complete the displacement to furnace atmosphere, thereby meet the continuous annealing protective atmosphere needs of steel band.After furnace atmosphere displacement complete (hydrogen volume is than 80%), heat up, and connect titanium band and steel band by processing apparatus before continuous annealing furnace entrance, annealing product is replaced by steel band, adjustment annealing furnace is normal operation mode, carries out the annealing of steel band in continuous annealing furnace.
According to above-mentioned technique, according to need of production, replacing flexibly protective atmosphere in stove is hydrogen nitrogen mixture or argon gas atmosphere, reaches the object of the annealing that meets steel band annealing and titanium band; And can to titanium band and steel band, carry out after continuous annealing respectively, produce titanium-steel-titanium composition board.The function that realization is rolled and anneals titanium band and steel band on a vertical continuous annealing line, need not be for carrying out the annealing of titanium band and producing special newly-built annealing furnace.And the quality problems such as while there will not be periodic annealing after titanium band annealing sheet material Internal and external cycle microstructure and property homogeneity is poor; Utilising efficiency and the economical efficiency in production line, annealing furnace and workshop have been promoted; And can promote the efficiency of production titanium-steel-titanium composition board.
It is as follows that the atmosphere exchange system of above-mentioned two embodiment carries out the concrete grammar of atmosphere displacement: furnace annealing product is stainless-steel roll, protective atmosphere is perhydro atmosphere, it is creep mode that continuous annealing furnace operational mode is set, reduce after continuous annealing furnace furnace temperature, pass into nitrogen purging annealing furnace with displacement furnace atmosphere; Pass into again argon gas atmosphere, furnace atmosphere is replaced again; Furnace atmosphere displacement after (argon content reaches 99%), heats up completely, and to change annealing product be titanium band, and adjustment annealing furnace is normal operation mode, carries out the annealing of titanium band in continuous annealing furnace;
Furnace annealing product is titanium volume, and protective atmosphere is argon gas atmosphere, and it is creep mode that continuous annealing furnace operational mode is set, and reduces after continuous annealing furnace furnace temperature, passes into nitrogen purging annealing furnace with displacement furnace atmosphere; Pass into again hydrogen atmosphere, furnace atmosphere is replaced again; After furnace atmosphere hydrogen content reaches 90%, heat up, and to change annealing product be Stainless Steel Band, adjustment annealing furnace is normal operation mode, carries out the annealing of Stainless Steel Band in continuous annealing furnace.
Embodiment 3:
The Horizontal Continuous Furnace that the present embodiment atmosphere exchange system is applicable, comprises inlet seal 1, preheating section 2, and heating zone 3, cooling section 4, exit seal 5, is arranged in the gas ventilator 6 in heating zone, gas-circulating system 7 and air cushion airing system 8.In described Horizontal Continuous Furnace stove, be equipped with air cushion airing system 8, the nozzle of the air cushion airing system layout that is staggered up and down, guarantees that annealing band hoverheight is suitable, stable; And the nozzle wind velocity of air cushion airing system is adjustable, according to the thickness of annealing band, tension condition, adjust wind speed, guarantee buoyancy and heat to annealing band; Described air cushion airing system is connected with outside inert protective gas airing system, when Horizontal Continuous Furnace is produced titanium band or steel band, selects respectively corresponding Annealing Protection atmosphere (argon gas or hydrogen) to carry out air feed.Air cushion airing system 8 mainly plays with blowing gas and forms air cushion effect with steel from bottom picking-up in horizontal chamber oven, thereby avoids the surface with steel with carrying roller damage.
Described gas-circulating system 7 is set in the adjustment and replacement process of protective atmosphere in stove, by furnace atmosphere being carried out to flow-disturbing reinforcement furnace atmosphere in annealing furnace different zones, circulates.
When Horizontal Continuous Furnace is produced steel band, in stove, adopting hydrogen nitrogen (hydrogen volume is than 99.99%) gas mixture is protective atmosphere, when needs change production titanium band into, it is creep mode that continuous annealing furnace operational mode is set, reduce continuous annealing furnace furnace temperature, when each district's furnace temperature of annealing furnace is down to 800 ℃, the main airing system of the gas ventilator 6 being equipped with by continuous annealing furnace passes into fast nitrogen in stove, air cushion airing system 8 also makes steel band keep overhang by nitrogen-blow simultaneously, progressively complete the displacement to furnace atmosphere, use again high-purity (volume fraction 99.99%) argon purge, the main airing system of the gas ventilator 6 being equipped with by continuous annealing furnace passes into fast argon gas in stove, air cushion airing system 8 also makes steel band keep overhang by winding-up argon gas simultaneously, progressively protective atmosphere in stove is replaced into needed argon gas, in replacement process, by gas-circulating system 7, strengthening furnace atmosphere circulates, complete the displacement to furnace atmosphere, thereby meet the continuous annealing protective atmosphere needs of titanium band.After furnace atmosphere displacement complete (argon content reaches 99%), heat up, and connect steel band and titanium band by processing apparatus before continuous annealing furnace entrance, annealing product is replaced by titanium band, adjustment annealing furnace is normal operation mode, carries out the annealing of titanium band in continuous annealing furnace;
When Horizontal Continuous Furnace is produced titanium band, in stove, adopting argon gas is protective atmosphere, when needs production line changes production steel band into, it is creep mode that continuous annealing furnace operational mode is set, reduce continuous annealing furnace furnace temperature, the main airing system of the gas ventilator 6 being equipped with by continuous annealing furnace passes into fast nitrogen in stove, air cushion airing system 8 also makes steel band keep overhang by nitrogen-blow simultaneously, progressively complete the displacement to furnace atmosphere, when rising to 800 ℃, each district's furnace temperature of annealing furnace passes into hydrogen, the main airing system of the gas ventilator 6 being equipped with by continuous annealing furnace passes into fast hydrogen in stove, air cushion airing system 8 also makes steel band keep overhang by winding-up hydrogen simultaneously, progressively protective atmosphere in stove is replaced into needed hydrogen nitrogen (hydrogen volume is than 99.99%) gas mixture, in replacement process, by gas-circulating system 7, strengthening furnace atmosphere circulates, the main airing system of the gas ventilator being equipped with by continuous annealing furnace passes into fast protective atmosphere in stove, complete the displacement to furnace atmosphere, thereby meet the continuous annealing protective atmosphere needs of steel band.After furnace atmosphere displacement complete (hydrogen volume is than 99.99%), heat up, and connect titanium band and steel band by processing apparatus before continuous annealing furnace entrance, annealing product is replaced by steel band, adjustment annealing furnace is normal operation mode, carries out the annealing of steel band in continuous annealing furnace.
According to above-mentioned technique, thereby realize, according to need of production, to replace flexibly protective atmosphere in stove be hydrogen nitrogen mixture or argon gas atmosphere, reaches the object of the annealing that meets steel band annealing and titanium band; And can to titanium band and steel band, carry out after continuous annealing respectively, produce titanium-steel-titanium composition board.The function that realization is rolled and anneals titanium band and steel band on a continuous annealing line, need not be for carrying out the annealing of titanium band and producing special newly-built annealing furnace.And the quality problems such as while there will not be periodic annealing after titanium band annealing sheet material Internal and external cycle microstructure and property homogeneity is poor; Utilising efficiency and the economical efficiency in production line, annealing furnace and workshop have been promoted; And can promote the efficiency of production titanium-steel-titanium composition board.
Embodiment 4:
The Horizontal Continuous Furnace that the present embodiment atmosphere exchange system is applicable, comprises inlet seal 1, preheating section 2, and heating zone 3, cooling section 4, exit seal 5, is arranged in the gas ventilator 6 on cooling section and is arranged in the gas-circulating system 7 in heating zone.
When Horizontal Continuous Furnace is produced steel band, in stove, adopting hydrogen nitrogen (hydrogen volume is than 80%) gas mixture is protective atmosphere, when needs change production titanium band into, it is creep mode that continuous annealing furnace operational mode is set, reduce continuous annealing furnace furnace temperature, when each district's furnace temperature of annealing furnace is down to 800 ℃, the main airing system of the gas ventilator 6 being equipped with by continuous annealing furnace passes into fast nitrogen in stove, air cushion airing system 8 also makes steel band keep overhang by nitrogen-blow simultaneously, progressively complete the displacement to furnace atmosphere, use again high-purity (volume fraction 99.99%) argon purge, the main airing system of the gas ventilator 6 being equipped with by continuous annealing furnace passes into fast argon gas in stove, air cushion airing system 8 also makes steel band keep overhang by winding-up argon gas simultaneously, progressively protective atmosphere in stove is replaced into needed argon gas, in replacement process, by gas-circulating system 7, strengthening furnace atmosphere circulates, complete the displacement to furnace atmosphere, thereby meet the continuous annealing protective atmosphere needs of titanium band.After furnace atmosphere displacement complete (argon content reaches 99%), heat up, and connect steel band and titanium band by processing apparatus before continuous annealing furnace entrance, annealing product is replaced by titanium band, adjustment annealing furnace is normal operation mode, carries out the annealing of titanium band in continuous annealing furnace;
When Horizontal Continuous Furnace is produced titanium band, in stove, adopting argon gas is protective atmosphere, when needs production line changes production steel band into, it is creep mode that continuous annealing furnace operational mode is set, reduce continuous annealing furnace furnace temperature, the main airing system of the gas ventilator 6 being equipped with by continuous annealing furnace passes into fast nitrogen in stove, air cushion airing system 8 also makes steel band keep overhang by nitrogen-blow simultaneously, utilize nitrogen purging progressively the argon shield atmosphere in stove to be replaced into nitrogen, when rising to 800 ℃, each district's furnace temperature of annealing furnace passes into hydrogen, the main airing system of the gas ventilator 6 being equipped with by continuous annealing furnace passes into fast hydrogen in stove, air cushion airing system 8 also makes steel band keep overhang by winding-up hydrogen simultaneously, progressively protective atmosphere in stove is replaced into needed hydrogen nitrogen (hydrogen volume is than 80%) gas mixture, in replacement process, by gas-circulating system 7, strengthening furnace atmosphere circulates, complete the displacement to furnace atmosphere, thereby meet the continuous annealing protective atmosphere needs of steel band.After furnace atmosphere displacement complete (hydrogen volume is than 80%), heat up, and connect titanium band and steel band by processing apparatus before continuous annealing furnace entrance, annealing product is replaced by steel band, adjustment annealing furnace is normal operation mode, carries out the annealing of steel band in continuous annealing furnace.
Thereby realizing and replacing flexibly protective atmosphere in stove according to need of production is hydrogen nitrogen mixture or argon gas atmosphere, reach the object of the annealing that meets steel band annealing and titanium band; And can to titanium band and steel band, carry out after continuous annealing respectively, produce titanium-steel-titanium composition board.The function that realization is rolled and anneals titanium band and steel band on a continuous annealing line, need not be for carrying out the annealing of titanium band and producing special newly-built annealing furnace.And the quality problems such as while there will not be periodic annealing after titanium band annealing sheet material Internal and external cycle microstructure and property homogeneity is poor; Utilising efficiency and the economical efficiency in production line, annealing furnace and workshop have been promoted; And can promote the efficiency of production titanium-steel-titanium composition board.
It is as follows that the system of Application Example 1-4 is carried out the embodiment of atmosphere method of replacing:
Embodiment 5:
An atmosphere method of replacing, furnace annealing product is stainless-steel roll, protective atmosphere is perhydro atmosphere, it is creep mode that continuous annealing furnace operational mode is set, and reduces after continuous annealing furnace furnace temperature, passes into nitrogen purging annealing furnace with displacement furnace atmosphere; Pass into again argon gas atmosphere, furnace atmosphere is replaced again; Furnace atmosphere displacement after (argon content reaches 99%), heats up completely, and to change annealing product be titanium band, and adjustment annealing furnace is normal operation mode, carries out the annealing of titanium band in continuous annealing furnace.
Embodiment 6:
An atmosphere method of replacing, furnace annealing product is titanium volume, protective atmosphere is argon gas atmosphere, it is creep mode that continuous annealing furnace operational mode is set, and reduces after continuous annealing furnace furnace temperature, passes into nitrogen purging annealing furnace with displacement furnace atmosphere; Pass into again hydrogen atmosphere, furnace atmosphere is replaced again; After furnace atmosphere hydrogen content reaches 90%, heat up, and to change annealing product be Stainless Steel Band, adjustment annealing furnace is normal operation mode, carries out the annealing of Stainless Steel Band in continuous annealing furnace.
Claims (5)
1. the atmosphere method of replacing of a continuous annealing furnace, it is characterized in that: the protective atmosphere exchange system being equipped with by continuous annealing furnace body, in continuous annealing furnace, by Stainless Steel Band annealing pattern, when titanium band annealing pattern is changed mutually, completing protective atmosphere replaces, according to technique, need to be protective atmosphere in needed stove by the protective atmosphere Rapid replacement in stove, thereby complete the adjustment of protective atmosphere in stove; Described protective atmosphere exchange system is connected with outer protection gas airing system; Mainly comprise the steps:
A: it is creep mode that continuous annealing furnace operational mode is set, furnace annealing product is stainless-steel roll or titanium volume;
B: pass into nitrogen purging annealing furnace with displacement furnace atmosphere after reducing furnace temperature;
C: according to annealing product protective atmosphere needs, pass into the protective atmosphere needing, furnace atmosphere is replaced;
D: after furnace atmosphere is replaced, heats up, and change annealing product, adjustment annealing furnace is normal operation mode, anneals in continuous annealing furnace;
Described continuous annealing furnace be when Stainless Steel Band anneal after changing annealing product, and for preventing Stainless Steel Band heat-tinting, the interior employing of stove hydrogen nitrogen mixture is protective atmosphere, and hydrogen volume is than 75% ~ 100%; When titanium band is annealed, hydrogen nitrogen mixture in continuous annealing furnace need be purged totally, guarantee that argon gas atmosphere is protective atmosphere, purity of argon is greater than 99%.
2. the atmosphere method of replacing of continuous annealing furnace according to claim 1, is characterized in that: described atmosphere method of replacing specifically comprises the steps:
When continuous annealing furnace is produced steel band, in stove, adopting hydrogen nitrogen mixture is protective atmosphere; When this continuous annealing furnace need to be for the production of titanium band, it is creep mode that continuous annealing furnace operational mode is set, and reduces continuous annealing furnace furnace temperature; When each district's furnace temperature of annealing furnace is down to 800 ℃, utilize protective atmosphere exchange system to carry out nitrogen purging, progressively the hydrogen nitrogen mixture protective atmosphere in stove is replaced into nitrogen, with protective atmosphere exchange system, carry out again the high-purity argon gas purging of volume fraction 99.99%, progressively protective atmosphere in stove is replaced into needed argon gas, thereby meets the continuous annealing protective atmosphere needs of titanium band; After furnace atmosphere displacement completely, after argon content reaches 99%, in continuous annealing furnace, heat up, and connect steel band and titanium band by processing apparatus before continuous annealing furnace entrance, annealing product is replaced by titanium band; Adjustment annealing furnace is normal operation mode, carries out the annealing of titanium band in continuous annealing furnace;
When continuous annealing furnace is produced titanium band, in stove, adopting argon gas is protective atmosphere; When production line changes into, produce steel band and this continuous annealing furnace need to be for the production of steel band time, it is creep mode that continuous annealing furnace operational mode is set, and reduces continuous annealing furnace furnace temperature; Utilize protective atmosphere exchange system to carry out nitrogen purging, progressively the argon shield atmosphere in stove is replaced into nitrogen; When each district's furnace temperature of annealing furnace rises to 800 ℃, utilize protective atmosphere exchange system to pass into hydrogen, progressively protective atmosphere in stove is replaced into needed hydrogen nitrogen mixture, thereby meet the continuous annealing protective atmosphere needs of steel band; After furnace atmosphere displacement completely, hydrogen volume, than after 75% ~ 100%, heats up in continuous annealing furnace, and by processing apparatus connection titanium band and steel band before continuous annealing furnace entrance, annealing product is replaced by steel band; Adjustment annealing furnace is normal operation mode, carries out the annealing of steel band in continuous annealing furnace.
3. the atmosphere method of replacing of continuous annealing furnace according to claim 1 and 2, is characterized in that: protective atmosphere exchange system divides two subsystems, is respectively main airing system and time airing system; Main airing system passes into fast protective atmosphere in atmosphere displacement in the stage in stove, inferior airing system in production phase regulating stove internal pressure to guarantee furnace pressure state.
4. the atmosphere method of replacing of continuous annealing furnace according to claim 3, is characterized in that: protective atmosphere exchange system is configured in heating zone or the cooling section of continuous annealing furnace, or is configured in the transition section between heating zone and cooling section; The protective atmosphere recycle system is configured in heating zone or the cooling section of continuous annealing furnace, or is configured in the transition section between heating zone and cooling section.
5. according to the atmosphere method of replacing of the continuous annealing furnace described in claim 1 or 2 or 4, it is characterized in that: heating zone is retort furnace; When heating zone is retort furnace, described protective atmosphere exchange system and the protective atmosphere recycle system are not all arranged on heating zone.