CN103555406B - Graphitic lubricant as well as preparation and usage methods thereof - Google Patents
Graphitic lubricant as well as preparation and usage methods thereof Download PDFInfo
- Publication number
- CN103555406B CN103555406B CN201310564334.7A CN201310564334A CN103555406B CN 103555406 B CN103555406 B CN 103555406B CN 201310564334 A CN201310564334 A CN 201310564334A CN 103555406 B CN103555406 B CN 103555406B
- Authority
- CN
- China
- Prior art keywords
- oildag
- preparation
- aircraft
- stir
- lubricant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a graphitic lubricant as well as preparation and usage methods thereof. According to the following technical scheme, the graphite lubricate comprises the compositions in percentage by weight: 78-90% of calcium-based lubricating grease, 6-18% of NO.20 aviation lubricant and 3-7% of colloidal graphite powder. The graphitic lubricant can play role in lubricating and being water-tolerant, strong in adhesivity and anti-wear when being applied to parts of a power generator friction clutch and the like, thus being convenient to use.
Description
Technical field
The present invention relates to a kind of lubricant, particularly relate to a kind of oildag and preparation method thereof and using method.
Background technology
In the use procedure of spare part, antithesis part needs to do swabbing, some existing calcium base graphited oils are utilized to carry out swabbing under normal circumstances, calcium base graphited oil many employings vegetable and animals oils calcium soap multiviscosisty mineral oil is also added with crystalline flake graphite and makes, but existing calcium base graphited oil have about 100 DEG C be just hydrolyzed, lubricating grease runs off and the shortcoming of poor adhesion, lubrication anti-wear effect is not good, have impact on the lubrication of component and effect of resistance to wearing.
Summary of the invention
The object of this invention is to provide a kind of oildag, be applied to the component such as generator power clutch, play lubrication, water-fast, adhesivity is strong and wear-resistant effect.
Technical scheme of the present invention is as follows:
A kind of oildag, described oildag comprises quicklime grease, No. 20 aircraft oils and oildag, wherein quicklime grease content (mass ratio) is 78 ~ 90%, No. 20 aircraft oil content (mass ratio) are 6 ~ 18%, and oildag content pulvis (mass ratio) is 3 ~ 7%.
Present invention also offers the preparation method of above-mentioned oildag, this preparation method comprises the steps: that taking regulation ratio quantity No. 20 aircraft oils puts into clean container, then take regulation ratio quantity colloidal graphite powder to add in described No. 20 aircraft oils, stir and be mixed with mixture; Regulation ratio quantity quicklime grease is preheated to 40 ~ 60 DEG C, then described mixture is poured in described quicklime grease, stir, described oildag; After naturally cooling to room temperature, be stored in airtight metal vessel.
Present invention also offers the using method of above-mentioned oildag, described using method comprises the steps: the piece surface that need apply lubricant with rubber industry solvent oil (SH0004) cleaning, and places 10min ~ 15min in atmosphere; The piece surface of lubricant need be applied again with acetone cleaning, and place 15min ~ 20min in atmosphere; Before coating, stir described oildag 5min ~ 10min to forming uniform batching; With brush or other instrument by thin for described oildag and be coated in the surface of part equably, the described oildag acetone residuing in non-coated surface is removed.
Beneficial effect of the present invention is as follows:
1, in oildag of the present invention, 78 ~ 90% quicklime grease are material of main part, play lubrication and water-fast effect in oildag.
2,6 ~ No. 18%20 aircraft oils that the present invention adds are thick oil, namely improve the adhesivity of oildag, and the oil film simultaneously formed in metallic surface improves protection function.
3,3 ~ 7% colloidal graphite powders of the present invention's interpolation, provide excellent heat resistance, overcome quicklime grease poor heat resistance, be just hydrolyzed at about 100 DEG C, lose denseness, lose the shortcoming of lubrication, improve the wear-resistant abrasive ability in metallic surface simultaneously.
4, oildag of the present invention has good water tolerance, oilness, shear stability, adhesivity, wear-resistant property, little to human body, environmental contamination, the features such as the easy construction of user.
Embodiment
A kind of oildag, wherein quicklime grease is 80g, and No. 20 aircraft oils are 15g, and graphite pulvis stopped by glue is 5g; Quicklime grease meets GB49l, No. 20 aircraft oils meet GB440, colloidal graphite powder is commercially available prod.Its preparation method is as follows: take 15g20 aircraft oil and put into clean container, then take 5g colloidal graphite powder and add in No. 20 aircraft oils, stir and be mixed with mixture; 80g quicklime grease is preheated to 50 DEG C, then said mixture is poured in quicklime grease, stir, after naturally cooling to room temperature, be stored in airtight metal vessel.
The using method of above-mentioned oildag, comprises the steps: the piece surface that need apply lubricant with rubber industry solvent oil (SH0004) cleaning, and places 15min in atmosphere; The piece surface of lubricant need be applied again with acetone cleaning, and place 15min in atmosphere; Before coating, stir oildag 10min and form uniform batching; With brush by thin for described oildag and be coated in the surface of part equably, the described oildag acetone residuing in non-coated surface is removed.
Claims (2)
1. the preparation method of an oildag, it is characterized in that, described oildag comprises quicklime grease, No. 20 aircraft oils and colloidal graphite powder, wherein quicklime grease content (mass ratio) is 78 ~ 90%, No. 20 aircraft oil content (mass ratio) are 6 ~ 18%, and colloidal graphite powder content (mass ratio) is 3 ~ 7%; The preparation method of described oildag comprises the steps: that taking regulation ratio quantity No. 20 aircraft oils puts into clean container, then take regulation ratio quantity colloidal graphite powder to add in described No. 20 aircraft oils, stir and be mixed with mixture; Regulation ratio quantity quicklime grease is preheated to 40 ~ 60 DEG C, then described mixture is poured in described quicklime grease, stir, described oildag; After naturally cooling to room temperature, be stored in airtight metal vessel.
2. a using method for oildag as claimed in claim 1, is characterized in that, described using method comprises the steps: the piece surface that need apply lubricant with the cleaning of rubber industry solvent oil, and places 10min ~ 15min in atmosphere; The piece surface of lubricant need be applied again with acetone cleaning, and place 15min ~ 20min in atmosphere; Before coating, stir described oildag 5min ~ 10min to forming uniform batching; With brush by thin for described oildag and be coated in the surface of part equably, the described oildag acetone residuing in non-coated surface is removed.