CN103554791A - High-pressure-resistant fluorine rubber tube - Google Patents
High-pressure-resistant fluorine rubber tube Download PDFInfo
- Publication number
- CN103554791A CN103554791A CN201310457849.7A CN201310457849A CN103554791A CN 103554791 A CN103554791 A CN 103554791A CN 201310457849 A CN201310457849 A CN 201310457849A CN 103554791 A CN103554791 A CN 103554791A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber tube
- fluorine rubber
- fluorine
- pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a high-pressure-resistant fluorine rubber tube comprising the components of: 135 parts of fluorine rubber, 7 parts of toluene diisocyanate, 18 parts of magnesium oxide, 4 parts of calcium hydroxide, 1 part of fluorine wax, 6 parts of carbon black, 2 parts of silicone, and 12 parts of toluene diisocyanate. The rubber tube also comprises 8 parts of diisopropylbenzene peroxide, and 4 parts of polyvinyl alcohol. The rubber tube has the advantages that: the high-pressure-resistant fluorine rubber tube has high pressure resistance, and the application effect of fluorine rubber tube can be greatly improved. With the formula provided by the invention, enterprise production resource can be greatly saved, and enterprise production cost can be reduced.
Description
Technical field
The present invention relates to a kind of Chemicals, especially a kind of high pressure resistant fluorine rubber-pipe.
Background technology
Other rubber phase ratios of viton, viton has the characteristic of good high temperature resistant, oil resistant and the medicine of resistance to number of chemical corrosion, along with fluorine sebific duct, the expansion of fluorine adhesive tape range of application, therefore the environment for use of viton and working conditions, also in continuous change, require also in continuous raising the withstand voltage properties of fluorine sebific duct, fluorine adhesive tape.
Summary of the invention
The technical problem to be solved in the present invention is to provide a kind of high pressure resistant fluorine rubber-pipe.
For solving the problems of the technologies described above, high pressure resistant fluorine rubber-pipe of the present invention, is characterized in that: comprise following component, 135 parts of viton, 7 parts of toluene di-iso-cyanide esters, 18 parts, magnesium oxide, 4 parts, calcium hydroxide, 1 part, fluorine wax, 6 parts of carbon blacks, 2 parts of siloxanes, 12 parts of toluene di-iso-cyanide esters.
Described rubber hose also comprises 8 parts of dicumyl peroxides.
Described rubber hose also comprises 4 parts of polyvinyl alcohol.
Beneficial effect of the present invention is: a kind of withstand voltage fluorine rubber-pipe of the present invention is had to very strong resistance to pressure, can significantly improve the result of use of fluorine sebific duct.Adopt formula of the present invention can greatly save the resources of production of enterprise, reduce the production cost of enterprise.
Embodiment
Embodiment 1
High pressure resistant fluorine rubber-pipe of the present invention, is characterized in that: comprise following component, 135 parts of viton, 7 parts of toluene di-iso-cyanide esters, 18 parts, magnesium oxide, 4 parts, calcium hydroxide, 1 part, fluorine wax, 6 parts of carbon blacks, 2 parts of siloxanes, 12 parts of toluene di-iso-cyanide esters.
Embodiment 2
High pressure resistant fluorine rubber-pipe of the present invention, is characterized in that: comprise following component, 135 parts of viton, 7 parts of toluene di-iso-cyanide esters, 18 parts, magnesium oxide, 4 parts, calcium hydroxide, 1 part, fluorine wax, 6 parts of carbon blacks, 2 parts of siloxanes, 12 parts of toluene di-iso-cyanide esters, 8 parts of dicumyl peroxides.
Embodiment 3
High pressure resistant fluorine rubber-pipe of the present invention, is characterized in that: comprise following component, 135 parts of viton, 7 parts of toluene di-iso-cyanide esters, 18 parts, magnesium oxide, 4 parts, calcium hydroxide, 1 part, fluorine wax, 6 parts of carbon blacks, 2 parts of siloxanes, 12 parts of toluene di-iso-cyanide esters, 8 parts of dicumyl peroxides, 4 parts of polyvinyl alcohol.
The above, be only to preferred embodiment of the present invention, not the present invention done to other forms of restriction, and any those skilled in the art may utilize the technology contents of above-mentioned announcement to be changed or be modified as the equivalent embodiment of equal variation.Every the present invention program's content that do not depart from,, all drops in protection scope of the present invention any simple modification made for any of the above embodiments, equivalent variations and remodeling according to technical spirit of the present invention.
Claims (3)
1. a high pressure resistant fluorine rubber-pipe, is characterized in that: comprise following component, 135 parts of viton, 7 parts of toluene di-iso-cyanide esters, 18 parts, magnesium oxide, 4 parts, calcium hydroxide, 1 part, fluorine wax, 6 parts of carbon blacks, 2 parts of siloxanes, 12 parts of toluene di-iso-cyanide esters.
2. according to high pressure resistant fluorine rubber-pipe claimed in claim 1, it is characterized in that: described rubber hose also comprises 8 parts of dicumyl peroxides.
3. according to high pressure resistant fluorine rubber-pipe claimed in claim 2, it is characterized in that: described rubber hose also comprises 4 parts of polyvinyl alcohol.