CN103554641A - Rubber material for oil seal of automatic transmission - Google Patents
Rubber material for oil seal of automatic transmission Download PDFInfo
- Publication number
- CN103554641A CN103554641A CN201310522537.XA CN201310522537A CN103554641A CN 103554641 A CN103554641 A CN 103554641A CN 201310522537 A CN201310522537 A CN 201310522537A CN 103554641 A CN103554641 A CN 103554641A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber material
- automatic transmission
- rubber
- oil seal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of rubber technology, and particularly relates to a rubber material for an oil seal of an automatic transmission. The rubber material comprises the following raw materials in parts by weight: 100 parts of rubber raw material AEM, 1-2 parts of stearic acid, 1-2 parts of anti-aging agent 445, 5-10 parts of plasticizer TP-759, 3-4 parts of accelerant, 1-2 parts of vulcanizing agent Diak1-1, 5-15 parts of gaseous white carbon black, 70-85 parts of fast extruding furnace black, 1-2 parts of VAM (Vinyl Acetate Monomer) and 0.3-0.6 part of 18D. The rubber material has the beneficial effects that the rubber material has excellent mechanical strength, high rigidity, good heat resistance and aging-resistance properties, and excellent compression and permanent deformation resistance properties; the oil resistance property and wear resistance property can be enhanced; the rubber material has a large high and low temperature resistance range, so that the oil seal product of the automatic transmission can be used for a long time under the environment of -40 DEG C to 160 DEG C and the service life of the oil seal of the automatic transmission can be greatly prolonged.
Description
Technical field
The present invention relates to a kind of rubber technology field, relate in particular to a kind of automatic gear-box oil sealing elastomeric material.
Background technology
Along with automobile demand amount growth and the raising of automatic transmission entrucking ratio, the demand rapid growth of automatic transmission.Therefore, automatic gear-box piston ring is as the core packing technique of automatic transmission, and its demand also must keep rapid growth.
At present, the piston packing of domestic automatic transmission mainly relies on import, and product, from the NOKDeng company of German KACO, U.S. Federal-Mogul or Japan, but brings a high price.And because automatic gear-box piston ring is very high to the requirement of its material, as needs have good physical strength, rigidity, heat aging property, incompressible tension set performance, winter hardiness, oil resistance and wear resisting property etc., it is blank that domestic production substantially also belongs to.Therefore the exploitation of automatic gear-box piston packing loop material is extremely urgent.
Summary of the invention
The present invention is directed to above-mentioned the deficiencies in the prior art, a kind of automatic gear-box oil sealing elastomeric material is provided.This elastomeric material is functional, long service life.
The technical scheme that the present invention solves the problems of the technologies described above is as follows: a kind of automatic gear-box oil sealing elastomeric material, is comprised of the raw material of following weight:
On the basis of technique scheme, the raw material being preferably by following weight forms: the rubber raw materials AEM of 100 parts, the stearic acid of 1.5 parts, the softening agent TP-759 of 445,7 parts, the anti-aging agent of 1.5 parts, the vulkacit D OTG of 3.5 parts, the vulcanizing agent Diak1# of 1.5 parts, the gas-phase silica of 10 parts, the fast extrusion carbon black of 75 parts, the VAM of 1 part, the 18D of 0.4 part.
Elastomeric material of the present invention makes by ordinary method.
The AEM rubber raw materials that the present invention uses, when guaranteeing low temperature, selects oil resistance to improve and the higher trade mark of mooney viscosity, and sizing material has higher physical strength and good processing characteristics like this.
The present invention adopts rate accelerating material(RAM) TP-759, fabulous improvement the resistance to low temperature of material.
The present invention is added with gas-phase silica, can obviously improve automatic transmission fluid and be enclosed in the tear resistance in to-and-fro movement.
The present invention adopts amine curing agents sulfuration, incompressible tension set excellent property.
Elastomeric material of the present invention has excellent physical strength, higher rigidity, good heat aging property and good incompressible tension set performance, improve oil resistance and wear resisting property, filled up the blank of elastomeric material for domestic wheel box oil sealing, good high low temperature resistance range, can make automatic transmission fluid envelope product meet life-time service under-40 ℃~160 ℃ environment, the work-ing life of greatly having improved automatic gear-box oil sealing.
Embodiment
Below principle of the present invention and feature are described, example, only for explaining the present invention, is not intended to limit scope of the present invention.
Example 1
A kind of automatic gear-box oil sealing elastomeric material, raw material by following weight forms: the rubber raw materials AEM of 100 parts, the stearic acid of 1.5 parts, the softening agent TP-759 of 445,7 parts, the anti-aging agent of 1.5 parts, the vulkacit D OTG of 3.5 parts, the vulcanizing agent Diak 1# of 1.5 parts, the gas-phase silica of 8 parts, the fast extrusion carbon black of 75 parts, the processing aid VAM of 1 part, the 18D of 0.4 part.
Wherein processing aid VAM is inner pattern releasing agent applicable Vanfre VAM, and 18D is inner pattern releasing agent applicable Armeen 18D.
Example 2
A kind of automatic gear-box oil sealing elastomeric material, raw material by following weight forms: the rubber raw materials AEM of 100 parts, the stearic acid of 1 part, the softening agent TP-759 of 445,5 parts, the anti-aging agent of 1 part, the vulkacit D OTG of 3 parts, the vulcanizing agent Diak 1# of 2 parts, the gas-phase silica of 5 parts, the fast extrusion carbon black of 70 parts, the processing aid VAM of 1 part, the 18D of 0.4 part.
Wherein processing aid VAM is inner pattern releasing agent applicable Vanfre VAM, and 18D is inner pattern releasing agent applicable Armeen 18D.
Example 3
A kind of automatic gear-box oil sealing elastomeric material, raw material by following weight forms: the rubber raw materials AEM of 100 parts, the stearic acid of 2 parts, the softening agent TP-759 of 445,10 parts, the anti-aging agent of 1.5 parts, the vulkacit D OTG of 4 parts, the vulcanizing agent Diak 1# of 2 parts, the gas-phase silica of 10 parts, the fast extrusion carbon black of 75 parts, the processing aid VAM of 2 parts, the 18D of 0.3 part.
Wherein processing aid VAM is inner pattern releasing agent applicable Vanfre VAM, and 18D is inner pattern releasing agent applicable Armeen 18D.
Example 4
A kind of automatic gear-box oil sealing elastomeric material, raw material by following weight forms: the rubber raw materials AEM of 100 parts, the stearic acid of 1.5 parts, the softening agent TP-759 of 445,8 parts, the anti-aging agent of 1.5 parts, the vulkacit D OTG of 4 parts, the vulcanizing agent Diak 1# of 1 part, the gas-phase silica of 6 parts, the fast extrusion carbon black of 75 parts, the processing aid VAM of 2 parts, the 18D of 0.5 part.
Wherein processing aid VAM is inner pattern releasing agent applicable Vanfre VAM, and 18D is inner pattern releasing agent applicable Armeen 18D.
Test data
Hardness: according to the pocket sclerometer penetration hardness of GB/T531 rubber determination of test method.
Tensile strength, tensile yield: according to the mensuration (eqv ISO37) of GB/T528 vulcanized rubber and thermoplastic elastomer tensile stress-strain performance.
Tear strength: according to the mensuration of GB/T529 vulcanized rubber and thermoplastic elastomer tear strength (eqv ISO34).
Hot air aging: according to GB/T3512 vulcanized rubber or the accelerated deterioration of thermoplastic elastomer warm air and oven test.
Compression set: according to the mensuration (eqv ISO815) of GB/T7759 vulcanized rubber, thermoplastic elastomer normal temperature, high temperature and low temperature lower compression tension set
The liquid of resistance to ATF: according to the GB/T1690 vulcanized rubber experimental technique of resistance to liquid (neq ISO1817)
TR10 value: according to the mensuration temperature retraction method of GB/T7758 vulcanized rubber cold property (TR test)
The performance detection data of table 1 elastomeric material of the present invention
By table 1, can find out, the performance of elastomeric material of the present invention is obviously better than standard value.
The present invention can summarize with other the specific form without prejudice to spirit of the present invention or principal character.Therefore, no matter from which point, above-mentioned embodiment of the present invention all can only think explanation of the present invention can not limit the present invention, claims have been pointed out scope of the present invention, and scope of the present invention is not pointed out in above-mentioned explanation, therefore,, in the implication suitable with claims of the present invention and any change in scope, all should think to be included in the scope of claims.
Claims (2)
2. automatic gear-box oil sealing elastomeric material according to claim 1, it is characterized in that, by the raw material of following weight, formed: the rubber raw materials AEM of 100 parts, the stearic acid of 1.5 parts, the anti-aging agent 445 of 1.5 parts, the softening agent TP-759 of 7 parts, the vulkacit D OTG of 3.5 parts, the vulcanizing agent Diak1# of 1.5 parts, the gas-phase silica of 10 parts, the fast extrusion carbon black of 75 parts, the VAM of 1 part, the 18D of 0.4 part.