CN103554628A - Special material for tubular product produced by recovering and modifying waste cross-linked PE (Poly Ethylene) cable material as well as preparation method of special material - Google Patents
Special material for tubular product produced by recovering and modifying waste cross-linked PE (Poly Ethylene) cable material as well as preparation method of special material Download PDFInfo
- Publication number
- CN103554628A CN103554628A CN201310588088.9A CN201310588088A CN103554628A CN 103554628 A CN103554628 A CN 103554628A CN 201310588088 A CN201310588088 A CN 201310588088A CN 103554628 A CN103554628 A CN 103554628A
- Authority
- CN
- China
- Prior art keywords
- special material
- cable
- crosslinked
- sheet stock
- waste
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a special material for a tubular product produced by recovering and modifying a waste cross-linked PE (Poly Ethylene) cable material, and relates to regeneration of plastics. The special material is prepared from the following components in parts by weight: recovered cross-linked PE cable crushed sheet stocks, 30-50 parts of crushed sheet stocks of a PE hollow blow molding product, 5-20 parts of LDPE (Low-Density Polyethylene) blow molding feedback particles, 3-10 parts of POE (Polyolefin Elastomer), 0.1-0.3 part of calcium stearate and 0.2-1 part of PE wax. Compared with the prior art, the special material has the advantages that the mobility of the special material for the tubular product produced by recovering and modifying the waste cross-linked PE cable material, which is disclosed by the invention, is within a conventional HDPE (High-Density Polyethylene) tubular product material range, the tensile strength is greater than that of a novel material of the HDPE tubular product, and the breaking elongation further satisfies the demand. The general advantage of the special material disclosed by the invention is even superior to that of the new material.
Description
Technical field
The present invention relates to a kind of waste and old crosslinked PE CABLE MATERIALS and reclaim modification production special material for tube and preparation method thereof.
Background technology
Twisted polyethylene cable is because crosslinked, regeneration processing is very difficult, and crosslinked polyethylene is multiplex now carrys out thermal degradation oil refining, but pollutes very serious, Hou Bei is banned by country oil refining enterprise, and crosslinked polyethylene has been recycled into the hang-up that Plastics in China is recycled.
Crosslinked PE, because corsslinking molecular knot forms tridimensional network, is difficult to fragmentation and melting, and reclaims broken crosslinked PE because mobility is lower, is difficult to forming process again.
Summary of the invention
One of object of the present invention is just to provide a kind of waste and old crosslinked PE CABLE MATERIALS to reclaim modification and produces special material for tube, this waste and old crosslinked PE CABLE MATERIALS reclaims modification and produces special material for tube mobility within conventional H DPE tube material scope, tensile strength is higher than HDPE tubing virgin material, elongation at break also meets the requirements, and overall advantage is even higher than virgin material.
Technical scheme is: a kind of waste and old crosslinked PE CABLE MATERIALS reclaims modification and produces special material for tube, and this waste and old crosslinked PE CABLE MATERIALS reclaims modification production special material for tube and made by following composition:
The broken sheet stock of crosslinked PE cable reclaiming
The broken sheet stock 30-50 of PE Blow Molded Articles weight part
LDPE blown film feed back particle 5-20 weight part
POE 3-10 weight part
Calcium stearate 0.1-0.3 weight part
And PE wax 0.2-1 weight part.
Two of object of the present invention is to provide a kind of above-mentioned waste and old crosslinked PE CABLE MATERIALS to reclaim the preparation method that special material for tube is produced in modification.
Technical scheme is: a kind of method of preparing above-mentioned waste and old crosslinked PE CABLE MATERIALS recovery modification production special material for tube, comprises the following steps:
Step 1: the broken sheet stock of the crosslinked PE cable reclaiming and the broken sheet stock cleaning and dewatering of PE Blow Molded Articles is dry;
Step 2: get all the other raw materials and put into high mixer mix together with the broken sheet stock of crosslinked PE cable in step 1, the broken sheet stock of PE Blow Molded Articles.
Step 3: double-screw extruding pelletizing.
Step 4: by particle drying.
As preferably, the broken sheet stock size of described crosslinked PE cable is 4-7mm, and PE Blow Molded Articles fragmentation sheet stock size is 4-7mm.
As preferably, in described step 2, the high-speed mixer and mixing time is 3-5 minute.
As preferably, in described step 3, twin screw extruder engine speed 30HZ, Screw Extrusion temperature is 165-200 ℃.
Inventive principle and beneficial effect:
Crosslinked PE cable waste or used plastics, because crosslinked, it is netted that molecular structure is, melt-processed is very difficult, it is low that a lot of large-scale PE requirements for pipes of existing market are melted finger, we are by the crosslinked PE of low flow and the better Blow Molded Articles PE material of mobility hybrid process, improved the mobility of crosslinked polyethylene, reduced the mobility of Blow Molded Articles PE, modified plastics mobility after this combination of two kinds meets large pipe PE processing fluidity just, consider consistency and over-all properties, we increase by two ingredient compatibilitys by adding part LDPE and POE, improve toughness, add PE improves in formula lubricated simultaneously, with calcium stearate, cover outer lubricated, it is the inside and outside lubricated best effect that reaches.
Embodiment
Below in conjunction with specific embodiment, the present invention is further illustrated.
The waste and old crosslinked PE CABLE MATERIALS of embodiment 1 reclaims the preparation that special material for tube is produced in modification
Step 1: raw material is prepared, broken sheet stock 40 weight parts of the crosslinked PE cable reclaiming (being broken into big or small 4-7mm left and right) and broken sheet stock 40 weight parts of PE Blow Molded Articles (being broken for big or small 4-7mm left and right) cleaning and dewatering are dry.
Step 2: get LDPE blown film feed back particle 15 weight parts, POE 5 weight parts, calcium stearate 0.15 weight part and PE wax 0.15 weight part and put into high mixer together with crosslinked PE cable broken material in step 1, the broken sheet stock of PE Blow Molded Articles, mix 3-5 minute.
Step 3: double-screw extruding pelletizing, engine speed 30HZ, Screw Extrusion temperature is 165-200 ℃.
Step 4: by particle drying, packing.
Embodiment 2
Regeneration pipe material PP Pipe Compound and other tube material that embodiment 1 is produced carry out respectively Performance Detection, contrast as following table one:
Table one
Sequence number | Test item | Crosslinked PE feed back | HDPE tube material | Embodiment 1 | Detection method |
1 | MFR g/10min 5Kg | —— | 0.1-0.5 | 0.17 | GB/T 3682 |
2 | Tensile strength Mpa | 28 | 20 | 24 | GB/T 1040 |
3 | Yield strength MPa | 28 | 20 | 24 | GB/T 1040 |
4 | Elongation at break % | 340 | ≥200 | 287 | GB/T 1040 |
As can be seen from Table I, although crosslinked feed back performance is fine, mobility is very poor, 5 ㎏, 190 ℃, can not squeeze material, the life-span is difficult to processing, according to invention, produces crosslinked PE regenerating and modifying special material for tube, mobility is within conventional H DPE tube material scope, tensile strength is higher than HDPE tubing virgin material, and elongation at break also meets the requirements, and overall advantage is even higher than virgin material.
Claims (5)
1. waste and old crosslinked PE CABLE MATERIALS reclaims modification and produces a special material for tube, and this waste and old crosslinked PE CABLE MATERIALS reclaims modification production special material for tube and made by following composition:
The broken sheet stock 30-50 of the crosslinked PE cable weight part reclaiming
The broken sheet stock 30-50 of PE Blow Molded Articles weight part
LDPE blown film feed back particle 5-20 weight part
POE 3-10 weight part
Calcium stearate 0.1-0.3 weight part
And PE wax 0.2-1 weight part.
2. prepare waste and old crosslinked PE CABLE MATERIALS claimed in claim 1 and reclaim the method that special material for tube is produced in modification, comprise the following steps:
Step 1: the broken sheet stock of the crosslinked PE cable reclaiming and the broken sheet stock cleaning and dewatering of PE Blow Molded Articles is dry;
Step 2: get all the other raw materials and put into high mixer mix together with the broken sheet stock of crosslinked PE cable in step 1, the broken sheet stock of PE Blow Molded Articles;
Step 3: double-screw extruding pelletizing;
Step 4: by particle drying.
3. waste and old crosslinked PE CABLE MATERIALS according to claim 2 reclaims the method that special material for tube is produced in modification, it is characterized in that: the broken sheet stock size of described crosslinked PE cable is 4-7mm, and the broken sheet stock size of PE Blow Molded Articles is 4-7mm.
4. waste and old crosslinked PE CABLE MATERIALS according to claim 2 reclaims the method that special material for tube is produced in modification, it is characterized in that: in described step 2, the high-speed mixer and mixing time is 3-5 minute.
5. waste and old crosslinked PE CABLE MATERIALS according to claim 2 reclaims the method that special material for tube is produced in modification, it is characterized in that: in described step 3, and twin screw extruder engine speed 30HZ, Screw Extrusion temperature is 165-200 ℃.