CN103553372A - Method for producing lime by using waste Nan'an marble powder - Google Patents
Method for producing lime by using waste Nan'an marble powder Download PDFInfo
- Publication number
- CN103553372A CN103553372A CN201310515841.1A CN201310515841A CN103553372A CN 103553372 A CN103553372 A CN 103553372A CN 201310515841 A CN201310515841 A CN 201310515841A CN 103553372 A CN103553372 A CN 103553372A
- Authority
- CN
- China
- Prior art keywords
- lime
- marble
- marble flour
- discarded
- flour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for producing lime by using waste Nan'an marble powder. The method comprises the steps of collecting waste marble powder in the stone industry in a classified mode; piling, drying and homogenizing the marble powder in a classified mode in a piling shed; shaping applicable marble powder directly or by granulating, and then feeding the marble powder into an industrial kiln for calcination, wherein marbles are decomposed in the kiln through calcination to generate high-quality burnt lime with small particle size, high porosity and high activity, and the lime is further used for producing lime derivative products. The method is characterized in that a wet powdery material is adopted and is subjected to light burning and fast burning to prepare active lime, so that the method is favorable for reducing the consumption of natural limestone mine resources. According to the method disclosed by the invention, waste marble powder generated by the stone industry is used for producing lime and downstream derivative products of the lime, so that the problem of pollution caused by the discharge of waste stone powder in the stone industry can be effectively solved, the waste stone powder can be digested and saved, the sustainable development of the stone industry is promoted, and the method is of great significance of improving environmental protection and economic benefit.
Description
Technical field
The invention belongs to resources circulation comprehensive utilization and metallurgical building materials field of Environment Protection, be specifically related to a kind of method of utilizing the discarded marble flour of Nanan to produce lime.
Background technology
Quickened lime is a kind of high-quality soft burnt lime, has that particle is little, void content is high, volume density is little, specific surface area is large, an active high and CO
2the remaining feature such as few.Lime is a kind of important starting material in industrial production, be widely used in the fields such as environmental protection, chemical industry, building materials, metallurgy, particularly in the smelting process of iron and steel, used in a large number, on increasing substantially the quality of steel, having important impact, is a kind of requisite smelting auxiliary material in Iron And Steel Industry.
Marble flour is the cutting powder that stone slab source mill produces when cutting saw marble material, and in working angles, its crystal under saw blade extruding of the stone material in marble saw kerf is damaged, and forms the powder that fineness is little, surface-area is huge.Can produce more than 200 ten thousand tons of discarded marble flours our province Nanan head town year, the accumulation of stone flour not only land occupation but also contaminate environment, cause direct impact to the Sustainable development of stone material industry.By Nanan's marble flour is carried out to physical and chemical experiment analysis: chemical composition and the Wingdale of marble flour are basically identical, only difference to some extent on crystalline structure, Wingdale belongs to microcrystal or undefined structure, and marble crystallization degree is high, crystal is fine and close, and reactive behavior is little.According to its chemical constitution and physical properties, research and develop a kind of novel process and technology of utilizing discarded marble flour to produce quickened lime, make the utilization that obtains dissolving of a large amount of discarded marble flours, significant to realizing the comprehensive utilization of solid waste.
Summary of the invention
Activity of Lime is the important indicator of weighing lime calcining quality, and its product price and use range thereof are had to considerable influence.The object of the present invention is to provide a kind of method of utilizing the discarded marble flour of Nanan to produce quickened lime, make the utilization that obtains dissolving of discarded marble flour, realize the Sustainable development of Ornamental Stone Industry.
For achieving the above object, the present invention adopts following technical scheme:
A kind of method of utilizing the discarded marble flour of Nanan to produce lime, by the discarded wet-milling shape marble flour categorised collection of Ornamental Stone Industry, in heap canopy, classify and store up, after drying, homogenizing, by marble flour directly or after granulation formation, feed Industrial Stoves calcining, marble is CaO and CO through calcining and decomposing in kiln
2, the lime generating after decomposing is discharged after supercooler is cooling, deposits in airtight lime reservoir.
Described marble flour fineness is 0.02 ~ 0.1mm.
Described disposal be by dissimilar marble flour through categorised collection, oven dry, homogenizing, guarantee that the calcium carbonate content in marble flour is 90%.
Described granulation formation is in marble flour, to add admixture, adopts mechanical pelleting, and marble flour is a granulated into piece, forms spherical, block material, and fragmentation Control is at 20 ~ 150mm;
Described admixture comprises lime, gypsum, sulfonated lignin.
It is calciner that described Industrial Stoves adopt suspension kiln, shaft furnace or rotary kiln, and calcining temperature is controlled at 900 ~ 1150 ℃.
The reaction the present invention relates to is as follows:
CaCO
3→CaO+CO
2
Remarkable advantage of the present invention is:
(1) utilize first the discarded marble flour of Nanan as raw material production lime.Mass-producing comprehensive utilization to the discarded marble flour of Nanan, solves the pollution problem that stone flour discharges, and guarantees that the Sustainable development of stone material industry is significant, and will produce huge ecological benefits and economic benefit.
(2) the present invention is according to the feature of the discarded marble flour of Nanan, by techniques such as categorised collection, oven dry, homogenizing, granulations, suit measures to local conditions to utilize original state powder raw material to carry out quickened lime calcining, production technology and equipments can guarantee the quality technology requirement of marble flour active lime calcination, the quickened lime making is a kind of high-quality soft burnt lime, have that particle is little, void content is high, active high, avoid the step of ordinary method crushed stone lime stone simultaneously, reached useless, the energy-saving and cost-reducing object of profit.
(3) be conducive to reduce the exploitation in natural limestone mine, reduce the consumption of limestone mine resource, and alleviate the environmental problems such as vegetation deterioration that cause thus.
Accompanying drawing explanation
Fig. 1 is process flow sheet of the present invention.
Embodiment
A kind of step of utilizing the discarded marble flour of Nanan to produce lime is:
By the discarded wet-milling shape marble flour categorised collection of Ornamental Stone Industry, at heap, classify in canopy and store up, after drying, homogenizing, by marble flour directly or after granulation formation, feed Industrial Stoves and calcine, marble is CaO and CO through calcining and decomposing in kiln
2, the lime generating after decomposing is discharged after supercooler is cooling, deposits in airtight lime reservoir.
embodiment 1
By the discarded wet-milling shape marble flour categorised collection of Ornamental Stone Industry, in heap canopy, disposal is stored up in classification, mechanical drying, and homogenizing in homogenizing storehouse, guarantees that the calcium carbonate content in marble flour is 90%.To be dried marble flour and directly send into suspension kiln calcining, calcining temperature is 900 ℃, and marble is CaO and CO through calcining and decomposing in kiln
2, the lime generating after decomposing is discharged after supercooler is cooling, deposits in airtight lime reservoir.Described discarded marble powdery fineness of materials is 0.02 ~ 0.1mm.
embodiment 2
By the discarded wet-milling shape marble flour categorised collection of Ornamental Stone Industry, in heap canopy, classify and store up, mechanical drying, homogenizing in homogenizing storehouse, guarantees that the calcium carbonate content in marble flour is 90%.In marble flour, add lime, adopt mechanical pelleting, marble flour is a granulated into piece, form block material, lumpiness is 20mm.Granulation formation material is sent into shaft furnace calcining, and calcining temperature is 1000 ℃, and marble is CaO and CO through calcining and decomposing in kiln
2, the lime generating after decomposing is discharged after supercooler is cooling, deposits in airtight lime reservoir.Described discarded marble powdery fineness of materials is 0.02 ~ 0.1mm.
embodiment 3
By the discarded wet-milling shape marble flour categorised collection of Ornamental Stone Industry, in heap canopy, classify and store up, mechanical drying, homogenizing in homogenizing storehouse, guarantees that the calcium carbonate content in marble flour is 90%.In marble flour after homogenizing, add gypsum, adopt mechanical pelleting, marble flour is a granulated into piece, form block material, lumpiness is 150mm.Granulation formation material is sent into calcined by rotary kiln, and calcining temperature is 1150 ℃, and marble is CaO and CO through calcining and decomposing in kiln
2, the lime generating after decomposing is discharged after supercooler is cooling, deposits in airtight lime reservoir.Described discarded marble powdery fineness of materials is 0.02 ~ 0.1mm.
The foregoing is only better case study on implementation of the present invention, all equalizations of doing according to the present patent application the scope of the claims change and modify, and all should belong to covering scope of the present invention.
Claims (6)
1. the method for utilizing the discarded marble flour of Nanan to produce lime, it is characterized in that: by the discarded wet-milling shape marble flour categorised collection of Ornamental Stone Industry, in heap canopy, classify and store up, after drying, homogenizing, by marble flour directly or after granulation formation, feed Industrial Stoves calcining, marble is CaO and CO through calcining and decomposing in kiln
2, the lime generating after decomposing is discharged after supercooler is cooling, deposits in airtight lime reservoir.
2. the method for utilizing the discarded marble flour of Nanan to produce lime according to claim 1, is characterized in that: described discarded marble flour fineness is 0.02 ~ 0.1mm.
3. the method for utilizing the discarded marble flour of Nanan to produce lime according to claim 1, is characterized in that: the marble flour in the different places of production, through categorised collection, oven dry, homogenizing, guarantees that the calcium carbonate content in marble flour is 90%.
4. the method for utilizing the discarded marble flour of Nanan to produce lime according to claim 1, is characterized in that: utilize machinery or artificial drying method that marble flour is dried to water ratio 1 ~ 10%.
5. the Nanan that utilizes according to claim 1 discards the method that marble flour is produced lime, it is characterized in that: described granulation formation is in marble flour, to add admixture, adopts mechanical pelleting, and marble flour is a granulated into piece, form spherical, block material, granularity is controlled at 20 ~ 150mm;
Described admixture comprises lime, gypsum, sulfonated lignin.
6. the method for utilizing the discarded marble flour of Nanan to produce lime according to claim 1, is characterized in that: it is calciner that described Industrial Stoves adopt suspension kiln, shaft furnace or rotary kiln, and calcining temperature is controlled at 900 ~ 1150 ℃.