CN1035520A - Based on the resin for making lens of urethane, contain the manufacture method of plastic lens and this kind lens of this kind resin - Google Patents
Based on the resin for making lens of urethane, contain the manufacture method of plastic lens and this kind lens of this kind resin Download PDFInfo
- Publication number
- CN1035520A CN1035520A CN89100865A CN89100865A CN1035520A CN 1035520 A CN1035520 A CN 1035520A CN 89100865 A CN89100865 A CN 89100865A CN 89100865 A CN89100865 A CN 89100865A CN 1035520 A CN1035520 A CN 1035520A
- Authority
- CN
- China
- Prior art keywords
- lens
- urethane
- compound
- sulfur
- keyed jointing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Having disclosed the resin for making lens based on poly-propylhomoserin, is to be reacted and made by one or more sulfur-bearing polyisocyanate compounds and one or more sulfur-bearing polyvalent alcohols, and the lens based on urethane that contain these resins.It is extensive based on the manufacturing of the lens of urethane also to disclose a kind of preparation, is included in before the cast polyreaction, inner pattern releasing agent applicable is added in the mixture of above-mentioned polyisocyanates and polyvalent alcohol.
Description
The present invention relates to a kind of resin for making lens, based on the lens and the method for making this lens of urethane based on urethane.In recent years, plastic lens has been widely used in optical element, as the lens of glasses and photographic camera.Plastic lens is compared with the inorganics lens, it in light weight, more non-friable, and dyeing easily.
One of the resin that is widely used in this kind lens at present is the radical polymerization product of Diethylene Glycol diene propyl carbonate (hereinafter abbreviating DAC as) for example.The extremely excellent shock resistance of this resin tool, in light weight, have good dyestuff affinity and machinability, comprise cutting and polishing performance.
Yet, plant the specific refractory power low (n of the made lens of resin thus than inorganics lens
D=1.50), the latter's n
D=1.52.In order to obtain the optical property with the glass lens equivalence, just must increase center thickness, peripheral thickness and the curvature of lens, the result makes that whole lens are too thick and nonconforming.Therefore, be badly in need of providing the more resin of high refractive index of tool.
Other can provide the resin of high refractive index plastic lens to also have resin based on urethane, this is to get by isocyanate compound and oxy-compound such as Diethylene Glycol reaction (to be disclosed in Japanese Patent Laid-Open 136601/1982, USP 4443588), and get (Japanese Patent Laid-Open164615/1983) for the bisphenol-A reaction with halogen-containing oxy-compound such as tetrabromo, and get (Japanese Patent Laid-Open 194401/1985 and 217229/1985 with the reaction of the oxy-compound of sulfur-bearing, USP 4680369,4780522), get with the multi-thioalcohol compound reaction in addition (Japanese Patent Laid-Open 199016/1985 and 267316/1987, USP 4689387).
But, though by the specific refractory power of the made lens of these resins than with made higher of DAC, but still be not inconsistent ideal.In addition, owing to the dispersion of refractive index coefficient that makes and contain a plurality of halogen atoms or aromatic ring in the molecule, make the lens that make like this in preparation during these resins for improving specific refractory power is bigger, weathering resistance is good and than great.
When molded lens based on urethane, owing between urethanes and mould good adhesion is arranged, making usually, the polymeric lens are difficult to deviate from from mould.For improving release property, the present inventor once proposed to use the method (Japanese Patent Laid-Open 267316/1987) of external release agent in the past, used the method (Japanese Patent Laid-Open 236818/1987) of polyolefin resin mould in addition.
But above method is not still closed requirement for improving based on the release property of lens in cast poymerization of urethane.
When using external release agent, be used to handle mould inner surface medicament some ooze the surface that moves to polymerizable lens and inner, produce problems such as the inhomogeneous and muddiness of lens surface.When mould was repeatedly used, each molded cycle all needed to handle with releasing agent.Handling the productivity that lens are produced like this and descend, is extremely uneconomic in industrial production.
When using the polyolefine mould, this resin mold can be out of shape at high temperature, causes the profile of moulded lens seriously irregular.Can not be applied to require the very occasion of pinpoint accuracy of molded surface tool so found resin die.
Use inner pattern releasing agent applicable to improve an example of molded article release property, in DAC, add butyl phosphate exactly.But this inner pattern releasing agent applicable has detrimentally affect (S.Mima, " Polymer Digest, 3,39(1984) "), therefore use still not yet in effect for the outward appearance of moulded piece.
The present invention is by means of a kind of resin based on urethane that improves character than prior art tool is provided, and provide the method for producing this resin, thereby overcome problem and the shortcoming in the prior art, and a kind of lens that have the character that is better than the prior art lens and contain this resin are provided, and a kind of method of producing these lens is provided.
The purpose of this invention is to provide a kind of water white resin based on urethane, this resin has high refractive index and low dispersion of refractive index coefficient, and is applicable to the lens of producing in light weight, excellent weathering resistance and shock resistance.
Purpose of the present invention also comprises provides a kind of lens based on urethane, these lens have height accurate surface profile and extremely excellent optical property, and the method for producing these lens is provided, do not comprise in this method that the used mould inner surface of system lens is carried out the special demoulding to be handled.
Other purposes of the present invention and advantage will partly propose in the aftermentioned explanation, and part can be recognized from this specification sheets, or recognized from enforcement of the present invention.Objects and advantages of the present invention will be by these modes and combination, and particularly the content by appended claims realizes and reaches.
Be the purpose of the present invention that reaches these purposes and describe in detail and implement as this paper, the present invention includes a kind of production method that is used to make lens based on the resin of urethane, this method comprises reacts one or more sulfur-bearing polyisocyanate compounds and one or more sulfur-bearing polyol compounds, and the lens that contain this kind resin.
The present invention also provides a kind of production method of the lens based on urethane, this method comprises a kind of inner pattern releasing agent applicable is joined in the mixture of one or more sulfur-bearing polyisocyanate compounds and one or more sulfur-bearing polyol compounds, then this mixture is carried out cast poymerization making a kind of lens, and the lens that provide a kind of method thus to produce.
Resin based on urethane of the present invention is a water white transparency, has high refractive index and low dispersion of refractive index coefficient, is specially adapted to produce lens.
The excellent weathering resistance of lens tool based on urethane of the present invention, in light weight and have an excellent shock resistance.The excellent optical property of this lens tool, surface topography is very accurate.
The preferred embodiments of the invention are described in detail in detail below.
The compound that is used as the sulfur-bearing polyisocyanates in the method for the invention for example has: the sulfur-bearing aliphatic polyisocyanate, as two isocyanic acid sulfo-diethyl esters, two isocyanic acid sulfo-dipropyls, two isocyanic acid sulfo-s, two own fat, the dimethyl sulfone vulcabond, two isocyanic acid dithio dimethyl esters, two isocyanic acid dithio diethyl esters, two isocyanic acid dithio dipropyl esters; The aromatic polyisocyanate of sulfur compound keyed jointing, as diphenyl sulfide-2,4 '-vulcabond, diphenyl sulfide-4,4 '-vulcabond, 3,3 '-dimethoxy-4 ', 4 '-two isocyanato-dibenzyl sulfides, two (4-isocyanato-aminomethyl phenyl) sulfide, 3,3 '-two isocyanic acids-4,4 '-p-methoxy-phenyl THIOGLYCOL ester; The aromatic polyisocyanate that contains the disulphide keyed jointing, as phenylbenzene disulphide-4,4 '-vulcabond, 2,2 '-dimethyl diphenyl disulphide-5,5 '-vulcabond, 3,3 '-dimethyl diphenyl disulphide-5,5 '-vulcabond, 3,3 '-dimethyl diphenyl disulphide-6,6 '-vulcabond, 4,4 '-dimethoxy phenylbenzene disulphide-5,5 '-vulcabond, 3,3 '-dimethoxy phenylbenzene disulphide-4,4 '-vulcabond, 4,4 '-dimethoxy phenylbenzene disulphide-3,3 '-vulcabond; The aromatic polyisocyanate that contains the sulfone keyed jointing, as sulfobenzide-4,4 '-vulcabond, sulfobenzide-3,3 '-vulcabond, benzidine sulfone-4,4 '-vulcabond, diphenylmethyl sulfone-4,4 '-vulcabond, 4-methyldiphenyl sulfone-2,4 '-vulcabond, 4,4 '-dimethoxy sulfobenzide-3,3 '-vulcabond, 3,3 '-dimethoxy-4 ', 4 '-two isocyanato-dibenzyl sulfones, 4,4 '-dimethyl diphenyl sulfone-3,3 '-vulcabond, 4,4 '-di-t-butyl sulfobenzide-3,3 '-vulcabond, 4,4 '-p-methoxy-phenyl-ethylene two sulfones-3,3 '-vulcabond, 4,4 '-dichloro-sulfobenzide-3,3 '-vulcabond; The aromatic polyisocyanate that contains the sulphonate keyed jointing, as 4-methyl-3-isocyanato-phenyl sulphonyl-4 '-the isocyanato-phenol ester, 4-methoxyl group-3-isocyanato-phenyl sulphonyl-4 '-the isocyanato-phenol ester; The aromatic polyisocyanate that contains the sulphonamide keyed jointing, as 4-methyl-3-isocyanato-phenyl-N-sulfonanilide-3 '-methyl-4 '-isocyanic ester, two benzene sulfonyls-1,2-ethylene diamine-4,4 '-vulcabond, 4,4 '-anisole sulphonyl-1,2-ethylene diamine-3,3 '-vulcabond, 4-methyl-3-isocyanato-phenyl-N-sulfonanilide-4-methyl-3 '-isocyanic ester; Sulfur heterocyclic compound, as 2,5-two isocyanic acid thiophene esters, 2,5-two isocyanic acids-1,4-dithiane ester.
The derivative that is applicable to above-mentioned isocyanic ester of the present invention for example comprises: halogenated compound such as chlorinated isocyanuric acid esters and bromination isocyanic ester, and the biuret reaction product, with the adduct of TriMethylolPropane(TMP), dimerisation products and trimerization product.
Preferred polyisocyanate compound should be liquid, and very low in the vapour pressure of room temperature.The advantage of the aliphatic polyisocyanate of sulfur-bearing be they be heated and light action inhibited from yellowing.These polyisocyanate compounds can use separately, perhaps are used in combination.
The polyol compound that is applicable to the inventive method for example comprises the aliphatic polyol with diphenyl sulfide skeleton, for example two (4-(hydroxy ethoxy) phenyl) sulfide, two (4-(2-propoxyl) phenyl) sulfide, two (4-(2,3-two propoxyls) sulfide phenyl), two (4-(4-hydroxyl cyclohexyloxy) phenyl) sulfide, two (2-methyl-4-(hydroxy ethoxy)-6-butyl phenyls) sulfide; The oxyethane of above-mentioned polyvalent alcohol and/or propylene oxide adduct add resultant and on average are no more than 3 moles in every mole of this hydroxyl groups; The aliphatic polyol that contains the sulfide keyed jointing, for example two (2-hydroxyethyl) sulfide, 1, two (the 2-hydroxyethyl sulfydryl) ethane of 2-, 1,4-dithiane-2,5-glycol, two (2, the 3-dihydroxypropyl) sulfide, four (4-hydroxyl-2-thia butyl) methane, 1, two (the 2-hydroxyethylthio ethyl) hexanaphthenes of 3-; The aliphatic polyol that contains the disulphide keyed jointing is as two (2-hydroxyethyl) disulphide and two (2, the 3-dihydroxypropyl) disulphide; The polyvalent alcohol that contains phenolic hydroxyl group and sulphur, for example two (4-hydroxyphenyl) sulfones (trade mark is called bisphenol S), tetrabromo be for bisphenol S, the tetramethyl-bisphenol S, 4,4 '-thiobis (the 6-tertiary butyl-3-methylphenol).
Be applicable to that halide derivative of the present invention for example comprises the sulfur-bearing polyvalent alcohol of chlorating sulfur-bearing polyvalent alcohol and bromination, these also can use.These sulfur-bearing polyvalent alcohols can use separately, or are combined into the mixture use.
The usage quantity of sulfur-bearing polyisocyanate compound and sulfur-bearing polyol compound is that every mole of hydroxyl uses about 0.5-3.0 mole isocyanate functional group, and preferably every mole of hydroxyl uses about 0.5-1.5 mole isocyanate functional group.
Plastic lens of the present invention contains urethane resin of the present invention, connects and contain in this resin by isocyanate group and hydroxyl deutero-ammonia ester bond.In this resin and lens,, certainly contain allophanate except that containing this ammonia ester bond connects, urea, biuret and other keyed jointings specifically depend on desired character.
For example, when its ammonia ester bond being connect and further reaction and when increasing cross-linking density, can obtain useful result usually of isocyanate group.In such cases, this reaction is to react being higher than 100 ℃ of temperature in the presence of excessive polyisocyanate component.Other mode by means of using small amount of amine compound or similar substance simultaneously, can also be introduced urea and/or biuret keyed jointing.When except that using this polyvalent alcohol, also using polyisocyanates reactive behavior compound, must consider discoloration problem.
Can add different additives, chain propagation agent for example, linking agent, fast light stablizer, UV light absorber, oxidation inhibitor, oil-soluble colourant and stopping composition are to reach required special properties.
When needed, can also use the used known catalysts of preparation urethane, so that speed of reaction is adjusted to desired scope.
Lenticular resins of the present invention and lens can be made by the cast poymerization method usually.The sulfur-bearing polyisocyanate compound is mixed with the polyvalent alcohol of sulfur-bearing.If needed, the mixture degassing with gained is poured into then in the mould, and carries out polymerization.
By of the present invention based on the made lens of the resin of urethane through after the physical or chemical treatment, for example surface finish, antistatic treatment, hard coat, anti-reaction coat, after dyeing and dim light are handled, can possess following character: anti-reflective, surface hardness, abrasion resistance, chemical-resistant, antifog property and profile style characteristic.
The inventor has found that, before carrying out cast poymerization, adds inner pattern releasing agent applicable in the mixture of polyisocyanates and polyvalent alcohol, can make the easier demoulding of lens after the polymerization, and stripping result is better.
In the present invention, the inner pattern releasing agent applicable that is suitable for for example has: fluorine-containing nonionogenic tenside, siliceous nonionogenic tenside, alkyl quaternary ammonium salts, acid phosphoric acid ester, whiteruss, wax class, higher fatty acid and soap class thereof, high-grade aliphatic ester, higher fatty alcohol, bisamide, the ethylene oxide adduct of polysiloxane and aliphatic amine.
The selection of the inner pattern releasing agent applicable that is suitable for is according to monomeric combination, polymeric reaction condition, economic condition and operation difficulty or ease.These releasing agents can use separately, or use two or more mixture.
Being applicable to that fluorine-containing nonionogenic tenside of the present invention and siliceous nonionogenic tenside for example comprise contains perfluoroalkyl or polydimethylsiloxane base or phosphate-based compound in the molecule.The fluorine-containing nonionogenic tenside that is suitable for for example comprises Unidain
TM: DS-401 and DS-403 (Daikin Kogyo Co., Ltd product); Also has F-Top
TM: EF-122A, EF-126 and EF-301(Shin-Akita Chemical Co., Ltd. product).The trial product Q2-120A that a kind of suitable siliceous nonionogenic tenside example is Dow Chemical Co..
Be applicable to that alkyl quaternary ammonium salts of the present invention for example comprises cats product, quaternary ammonium alkyl halogenide for example, phosphoric acid ester and sulfuric ester, as trimethylammonium cetyl chloride ammonium, the trimethylammonium octadecyl ammonium chloride, dimethyl ethyl cetyl chloride ammonium, triethyl dodecyl chlorination ammonium, tri-n-octyl methyl ammonium chloride, diethyl cyclohexyl dodecyl chlorination ammonium.
Be applicable to that acid phosphoric acid ester of the present invention for example comprises the acid phosphoric acid ester of sec.-propyl, the di-isopropyl acid phosphoric acid ester, butyl acid phosphate, the dibutyl acid phosphoric acid ester, octyl group acid phosphoric acid ester, dioctyl acid phosphoric acid ester, the isodecyl acid phosphoric acid ester, the diiso decyl acid phosphoric acid ester, tridecyl alcohol acid phosphoric acid ester, two (tridecyl alcohol acidity) phosphoric acid ester.
Be applicable to that higher fatty acid metallic soap of the present invention for example comprises zinc soap, calcium soap, magnesium soap, nickel soap and the Copoloid of stearic acid, oleic acid, sad, lauric acid, docosoic and ricinoleate acid, Zinic stearas for example, zinc oleate, zinc palmitate, zinc laurate, calcium stearate, calcium oleate, calcium palmitate, calcium laurate, Magnesium Stearate, magnesium oleate, Magnesium monolaurate, magnesium palmitate, nickel stearate, oleic acid nickel, palmitinic acid nickel, lauric acid nickel, copper stearate, cupric oleate, lauric acid copper, copper palmitate.
Be applicable to that high-grade aliphatic ester of the present invention for example comprises that acid wherein for example has stearic acid by the ester of higher fatty acid with alcohol reaction gained, oleic acid is sad, lauric acid, ricinoleate acid, alcohol wherein for example has ethylene glycol, propylene glycol, butyleneglycol, neopentyl glycol, hexylene glycol.
These inner pattern releasing agent applicables can be used singly or in combination.Total consumption of releasing agent is counted about 1-5000ppm by the summation of this polyisocyanates and polyvalent alcohol.When consumption is less than 0.1ppm, demoulding ability variation.When consumption during greater than 10000ppm, molded lens generation blushing.When consumption is too much, because in polymerization process, institute's moulded lens causes the profile accuracy variation of lens surface too early from mould surface.
Though the polymeric temperature and time can be had nothing in common with each other because of the type of monomer and additive such as releasing agent, polyreaction is normally at-20 ℃ to about 200 ℃ of about 0.5-72 of temperature range hours approximately, better be to about 150 ℃, preferably from about 50 ℃-120 ℃ from room temperature.
Polymeric lens can be annealed when needed.
By the resulting lens based on urethane of the present invention, its molded surface has very high profile accuracy and has excellent optical property, and tool is in light weight, and shock resistance is extremely excellent, and is applicable to the lens of making glasses and photographic camera.
Example
By following example and comparison example the present invention is illustrated, these examples are only as the usefulness of giving an example for the present invention.About the property detection of gained lens, measure its specific refractory power, Abbe number, weathering resistance, release property and outward appearance by following method with resin.
Specific refractory power and Abbe number:
With the Pulfrich refractometer in 20 ℃ of mensuration.
Weathering resistance:
Resin for making lens is placed the climatic test instrument that is equipped with the daylight carbon arc lamp.After 200 hours lens are taken out, with the lens before it and the test with resin form and aspect relatively.Evaluation result is no change (zero), slight flavescence (△), flavescence (*).
Release property:
After polyreaction is finished, a tetrafluoroethylene wedge is squeezed into the interface of lens and glass molds.The gained result is divided into following two classes.
Zero-very easy demoulding.
*-some or whole can not the demoulding.
Outward appearance:
Detect by an unaided eye and estimate.
Example 1A
The mixture of preparation 15.0 gram (0.04 mole) four (4-hydroxyl-2-thia butyl) methane and 13.8 gram (0.08 mole) two isocyanic acid sulfo-diethyl esters, and in the mould that constitutes by a glass molds and pad of impouring.With 48 hours mould is heated to 120 ℃ at a slow speed from room temperature then, finishes polyreaction.The gained lens are water white transparency, and have excellent weathering resistance.The refractive index n of these lens
20 DBe 1.59, Abbe number ν
20Be 45, density d
20Be 1.36.
Example 2A-13A and comparison example 1A-3A
Composition shown in the application table 1 prepares lens by the described same steps as of example 1A.
Gathered the physical testing result in the table 1.
Example 1B
Preparation 13.8 gram (0.08 mole) two isocyanic acid sulfo-diethyl esters, 15.0 gram (0.04 mole) four (4-hydroxyl-2-thia butyl) methane and 0.003 gram Unidain
TMDS-401(inner pattern releasing agent applicable, Daikin Kogyo Co., Ltd. product), and in the mould that constitutes by a glass molds and pad of impouring, and mould gradually is heated to 120 ℃ from room temperature with 24 hours, finish polyreaction.After polymerization was finished, lens were easy to deviate from from mould.Prepared lens are water white transparency, refractive index n
20 DBe 1.59, Abbe number ν
20Be 45, density d
20Be 1.36.
Example 2B-17B
Composition shown in the application table 2 is pressed the described same steps as of example 1B and is made lens.The physical properties test result is summarized in table 2.
Comparison example 1B-8B
The same steps as described by example 1B prepares lens, and difference is that mould therefor uses by following condition, and the composition shown in the application table 3.Gained the results are summarized in table 3.
Mould is handled a hurdle following condition also is shown in the table 3.
(1) is untreated ... use glass molds, do not carry out any releasing agent and handle.
(2) external release agent is handled ... with external release agent YSR-6209
TM(Toshiba Silicon Co. product) applies and carries on the back and overlay on the glass mold internal surface.
(3) recirculation is used ... the glass molds that the process external release agent is handled reuses without any further processing after a polymerization is used.
(4) polypropylene molds ... make polypropylene molds with injection moulding, be used for the instead of glass mould, and without any surface treatment.
Claims (27)
1, a kind of resin based on urethane comprises one or more sulfur-bearing polyisocyanate compounds and one or more sulfur-bearing polyol compounds reacted forming.
2, a kind of lens based on urethane are comprising a kind of resin based on urethane by claim 1.
3, a kind of method of producing based on the lens of urethane comprises a kind of inner pattern releasing agent applicable is joined in the mixture that is made of one or more sulfur-bearing polyisocyanate compounds and one or more sulfur-bearing polyol compounds, carries out cast poymerization then.
4, a kind of lens based on urethane, these lens are to be made by the method for claim 3.
5, the resin based on urethane of claim 1, sulfur-bearing polyisocyanate compound wherein is to be selected from: sulfur-bearing aliphatic polyisocyanate compound, the aromatic polyisocyanate compound that contains the sulfide keyed jointing, the aromatic polyisocyanate compound that contains the disulphide keyed jointing, the aromatic polyisocyanate compound that contains the sulfone keyed jointing, the aromatic polyisocyanate compound that contains the sulphonate keyed jointing contains the aromatic polyisocyanate compound and the sulfur heterocyclic compound of sulphonamide keyed jointing.
6, based on the lens of urethane, comprising the resin based on urethane of claim 5.
7, the method for claim 3, sulfur-bearing polyisocyanate compound wherein is to be selected from: sulfur-bearing aliphatic polyisocyanate compound, the aromatic polyisocyanate compound that contains the sulfide keyed jointing, the aromatic polyisocyanate compound that contains the disulphide keyed jointing, the aromatic polyisocyanate compound that contains the sulfone keyed jointing, the aromatic polyisocyanate compound that contains the sulphonate keyed jointing contains the aromatic polyisocyanate compound and the sulfur heterocyclic compound of sulphonamide keyed jointing.
8, based on the lens of urethane, these lens are to make by the method for claim 7.
9, the resin based on urethane of claim 1, sulfur-bearing polyol compound wherein is to be selected from: the aliphatic polyol compound with diphenyl sulfide skeleton, the aliphatic polyol compound of sulfur compound keyed jointing contains the aliphatic polyol compound of disulphide keyed jointing and the polyol compound that contains phenol hydroxyl and sulphur.
10, based on the lens of urethane, this lens package contains right and requires 9 the resin based on urethane.
11, the method for claim 3, sulfur-bearing polyol compound wherein is to be selected from: the aliphatic polyol compound with diphenyl sulfide skeleton, the aliphatic polyol compound of sulfur compound keyed jointing contains the aliphatic polyol compound of disulphide keyed jointing and the polyol compound that contains phenol hydroxyl and sulphur.
12, based on the lens of urethane, these lens are to make by the method for claim 11.
13, the resin based on urethane of claim 1, wherein this polyisocyanate compound is the every mole of about 0.5-3.0 mole of hydroxyl isocyanate functional group to the molar ratio of this polyol compound.
14, based on the lens of urethane, this lens package contains right and requires 13 the resin based on urethane.
15, the method for claim 3, wherein this polyisocyanate compound is the every mole of about 0.5-3.0 mole of hydroxyl isocyanate functional group to the molar ratio of this polyol compound.
16, based on the lens of urethane, these lens are to make by the method for claim 15.
17, the method for claim 3, inner pattern releasing agent applicable wherein are a kind of fluorine-containing nonionogenic tensides.
18, the method for claim 3, inner pattern releasing agent applicable wherein are a kind of siliceous nonionogenic tensides.
19, the method for claim 3, inner pattern releasing agent applicable wherein are a kind of alkyl quaternary ammonium saltss.
20, the method for claim 3, inner pattern releasing agent applicable wherein are a kind of acid phosphoric acid esters.
21, based on the lens of urethane, these lens are to make by the method for claim 17.
22, based on the lens of urethane, these lens are to make by the method for claim 18.
23, based on the lens of urethane, these lens are to make by the method for claim 19.
24, based on the lens of urethane, these lens are to make by the method for claim 20.
25, the method for claim 3, the consumption of inner pattern releasing agent applicable is wherein counted about 0.1-10000ppm by this polyisocyanate compound and this polyol compound summation.
26, based on the lens of urethane, these lens are to make by the method for claim 25.
27, the method for claim 3, the reaction of wherein cast poymerization be from approximately-20 ℃ carry out to about 200 ℃ temperature range.