CN103540046A - Thermoplastic elastomer composition for crane cable sheath - Google Patents
Thermoplastic elastomer composition for crane cable sheath Download PDFInfo
- Publication number
- CN103540046A CN103540046A CN201210240069.2A CN201210240069A CN103540046A CN 103540046 A CN103540046 A CN 103540046A CN 201210240069 A CN201210240069 A CN 201210240069A CN 103540046 A CN103540046 A CN 103540046A
- Authority
- CN
- China
- Prior art keywords
- cable sheath
- polyvinyl chloride
- thermoplastic elastomer
- parts
- crane cable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a crane cable, particularly a composition for a crane cable sheath. The thermoplastic elastomer for a crane cable sheath comprises the following components in parts by weight: 30-35 parts of PVC (polyvinyl chloride) resin, 8-10 parts of light calcium carbonate, 28-30 parts of TOTM (trioctyl trimellitate), 2-3 parts of DOS (dioctyl sebacate), 1-1.5 parts of epoxy soybean oil, 2-2.5 parts of environment-friendly calcium zinc stabilizer and 0.2-0.5 part of low-molecular polyethylene wax. The components are subjected to extrusion molding to obtain the cable sheath. The composition saves the cost, simplifies the technique, enhances the production efficiency, and satisfies the operational requirements of the customers.
Description
Technical field
The present invention relates to crane cable, relate in particular to crane cable sheath composition.
Background technology
Lifting machine requires cable to have certain tensile strength with cable, flexibility, fatigue resistance, weathering resistance, in conventional crane cable, often use neoprene rubber or chlorinatedpolyethylene rubber as the sheath of cable, rubber must have its advantage in crane cable use procedure, but also Shortcomings, neoprene or chlorinatedpolyethylene rubber must adopt large-scale Banbury mixer in mixed glue, in extrusion, must adopt continuous high temperature steam vulcanization line, the equipment of Zhe Dui company and industrial scale have proposed harsh requirement, too far behind to catch up especially to the general cable producer that does not possess this throughput.
Summary of the invention
The present invention is intended to address the aforementioned drawbacks, and a kind of crane cable sheath composition for thermoplastic elastomer is provided.The present invention provides cost savings, and has simplified technique, has improved production efficiency, has met client's service requirements.
For addressing the above problem, a kind of crane cable sheath of the present invention composition for thermoplastic elastomer, it comprises following parts by weight:
Polyvinyl chloride resin: 30~35,
Light calcium carbonate 1250 orders: 8~10,
TOTM:28~30,
DOS:2~3,
Epoxy soybean oil 1~1.5,
Environment-friendly calcium zinc stabilizer 2~2.5,
Low-molecular polyethylene wax, molecular weight 2500-4000,0.2~0.5;
Wherein polyvinyl chloride resin is the mixture that comprises PVC2500 type and PVC1300 type weight ratio 4:1.
Described crane cable sheath composition for thermoplastic elastomer, it comprises following parts by weight:
Polyvinyl chloride resin: 32~34,
Light calcium carbonate 1250 orders: 9~10,
TOTM:29.5~30,
DOS:2.5~3,
Epoxy soybean oil 1~1.5,
Environment-friendly calcium zinc stabilizer 2~2.5,
Low-molecular polyethylene wax, molecular weight 2500-4000,0.2~0.5;
Wherein polyvinyl chloride resin is the mixture that comprises PVC2500 type and PVC1300 type weight ratio 4:1.
Described crane cable sheath composition for thermoplastic elastomer, it comprises following parts by weight:
Polyvinyl chloride resin: 33.5,
Light calcium carbonate 1250 orders: 10,
TOTM:?30,
DOS:2.8,
Epoxy soybean oil 1.3,
Environment-friendly calcium zinc stabilizer 2.4,
Low-molecular polyethylene wax, molecular weight 2500-4000,0.4;
Wherein polyvinyl chloride resin is the mixture that comprises PVC2500 type and PVC1300 type weight ratio 4:1.
Adopting described crane cable sheath with composition for thermoplastic elastomer, to prepare the method for cable sheath, is described each component to be dropped into extruding machine extrusion molding form described cable sheath.
The invention has the beneficial effects as follows: adopted thermoplastic elastomer as crane cable sheath, reached client's service requirements.Simplified technique, reduced cost, solve some companies and there is no endless vulcanization production line, can not produce the equipment barrier of crane cable, through on probation, in 1 year, in process, there are not any quality problems, reached in the past and lifting machine use Plastic-sheathed Cable sheath identical work-ing life yet, obtained client's consistent favorable comment and approval.
Embodiment
A sheath composition for thermoplastic elastomer, it comprises following parts by weight:
Polyvinyl chloride resin: 30~35,
Light calcium carbonate 1250 orders: 8~10,
TOTM:28~30,
DOS:2~3,
Epoxy soybean oil 1~1.5,
Environment-friendly calcium zinc stabilizer 2~2.5,
Low-molecular polyethylene wax, molecular weight 2500-4000,0.2~0.5;
Wherein polyvinyl chloride resin is the mixture that comprises PVC2500 type and PVC1300 type weight ratio 4:1.
Described crane cable sheath composition for thermoplastic elastomer, preferred, it comprises following parts by weight:
Polyvinyl chloride resin: 32~34,
Light calcium carbonate 1250 orders: 9~10,
TOTM:29.5~30,
DOS:2.5~3,
Epoxy soybean oil 1~1.5,
Environment-friendly calcium zinc stabilizer 2~2.5,
Low-molecular polyethylene wax, molecular weight 2500-4000,0.2~0.5;
Wherein polyvinyl chloride resin is the mixture that comprises PVC2500 type and PVC1300 type weight ratio 4:1.
Described crane cable sheath composition for thermoplastic elastomer, best, it comprises following parts by weight:
Polyvinyl chloride resin: 33.5,
Light calcium carbonate 1250 orders: 10,
TOTM:?30,
DOS:2.8,
Epoxy soybean oil 1.3,
Environment-friendly calcium zinc stabilizer 2.4,
Low-molecular polyethylene wax, molecular weight 2500-4000,0.4;
Wherein polyvinyl chloride resin is the mixture that comprises PVC2500 type and PVC1300 type weight ratio 4:1.
Softening temperature (ASMTD3954) 105-120 ℃ that described low molecular polyethylene is cured; Viscosity (ASMTD326) 200-300cps/140, molecular weight (GPC) 2500-4000; Density (ASMTD1505) 0.94.
Adopt described crane cable sheath with composition for thermoplastic elastomer, to prepare the method for cable sheath, described each component is dropped into extruding machine extrusion molding and form described cable sheath.
Compare with the sheath of traditional chloroprene rubber, sheath performance of the present invention is more outstanding:
Table: the performance perameter synopsis of two kinds of sheaths
Claims (4)
1. a crane cable sheath composition for thermoplastic elastomer, is characterized in that, it comprises following parts by weight:
Polyvinyl chloride resin: 30~35,
Light calcium carbonate 1250 orders: 8~10,
TOTM:28~30,
DOS:2~3,
Epoxy soybean oil 1~1.5,
Environment-friendly calcium zinc stabilizer 2~2.5,
Low-molecular polyethylene wax, molecular weight 2500-4000,0.2~0.5;
Wherein polyvinyl chloride resin is the mixture that comprises PVC2500 type and PVC1300 type weight ratio 4:1.
2. crane cable sheath composition for thermoplastic elastomer according to claim 1, is characterized in that, it comprises following parts by weight:
Polyvinyl chloride resin: 32~34,
Light calcium carbonate 1250 orders: 9~10,
TOTM:29.5~30,
DOS:2.5~3,
Epoxy soybean oil 1~1.5,
Environment-friendly calcium zinc stabilizer 2~2.5,
Low-molecular polyethylene wax, molecular weight 2500-4000,0.2~0.5;
Wherein polyvinyl chloride resin is the mixture that comprises PVC2500 type and PVC1300 type weight ratio 4:1.
3. crane cable sheath composition for thermoplastic elastomer according to claim 1, is characterized in that, it comprises following parts by weight:
Polyvinyl chloride resin: 33.5,
Light calcium carbonate 1250 orders: 10,
TOTM:?30,
DOS:2.8,
Epoxy soybean oil 1.3,
Environment-friendly calcium zinc stabilizer 2.4,
Low-molecular polyethylene wax, molecular weight 2500-4000,0.4;
Wherein polyvinyl chloride resin is the mixture that comprises PVC2500 type and PVC1300 type weight ratio 4:1.
4. the crane cable sheath of employing as described in claim 1-3 prepared a method for cable sheath with composition for thermoplastic elastomer, it is characterized in that, described each component dropped into extruding machine extrusion molding and form described cable sheath.