CN103526101A - Metal cutting tool and preparation method thereof - Google Patents
Metal cutting tool and preparation method thereof Download PDFInfo
- Publication number
- CN103526101A CN103526101A CN201310448131.1A CN201310448131A CN103526101A CN 103526101 A CN103526101 A CN 103526101A CN 201310448131 A CN201310448131 A CN 201310448131A CN 103526101 A CN103526101 A CN 103526101A
- Authority
- CN
- China
- Prior art keywords
- cutting tool
- metal cutting
- parts
- alloys
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a metal cutting tool. The metal cutting tool comprises the components as follows: 24-36 parts of molybdenum alloys, 20-30 parts of iron-nickel alloys, 15-25 parts of titanium-niobium alloys, 3-5 parts of sodium sulfide, 3-6 parts of silicon sulfide and 1-2 parts of water glass. The metal cutting tool and a preparation method thereof have the benefits that the metal cutting tool is high in hardness and resistant to high temperatures, experiments prove that the hardness of the metal cutting tool is 1.5-2 times of that of an existing cutting tool sold in the market, the temperature tolerance can be improved by 20%-30%, and the service life is longer.
Description
Technical field
The present invention relates to alloy product field, be specifically related to a kind of metal cutting tool and preparation method thereof.
Background technology
Cutting tool is for the instrument of machining in machinofacture.Most cutters are that machine is used, but also have hand to use.The cutter using in machinofacture is substantially all for cutting metal material.So, high to the hardness requirement of cutter.Meanwhile, in cutting metal or other mechanically resistant material processes, because friction can produce high heat, greatly reduce the work-ing life of cutting tool.
Summary of the invention
Object of the present invention is exactly for above-mentioned defect of the prior art, provides a kind of hardness higher, and high heat-proof metal cutting tool.
To achieve these goals, technical scheme provided by the invention is: a kind of metal cutting tool, the material of described metal cutting tool includes the following component according to weight part meter: copper molybdenum alloy 24-36 part, iron-nickel alloy 20-30 part, titanium niobium alloy 15-25 part, sodium sulphite 3-5 part, silicon sulfide 3-6 part, water glass 1-2 part.
Further, above-mentioned a kind of metal cutting tool, the material of described metal cutting tool includes the following component according to weight part meter: 30 parts of copper molybdenum alloys, 25 parts of iron-nickel alloys, 20 parts of titanium niobium alloys, 4 parts, sodium sulphite, 5 parts of silicon sulfides, 1.5 parts of water glass.
Second object of the present invention has been to provide the preparation method of above-mentioned a kind of metal cutting tool, is after described three kinds of alloy moltens, to add all the other components again, pours in cutter mould after cooling and makes.
Beneficial effect of the present invention is: a kind of metal cutting tool provided by the invention and preparation method thereof, and hardness is high, high temperature resistant, experimental results show that, its hardness is 1.5-2 times of existing commercially available cutting tool product, and tolerable temperature can improve 20%-30%, and longer service life is of a specified duration.
Embodiment
embodiment 1:
, the material of described metal cutting tool includes following component: 24 tons of copper molybdenum alloys, 20 tons of iron-nickel alloys, 15 tons of titanium niobium alloys, 3 tons, sodium sulphite, 3 tons of silicon sulfides, 1 ton of water glass.The preparation method of above-mentioned a kind of metal cutting tool, is after described three kinds of alloy moltens, to add all the other components again, pours in cutter mould after cooling and makes.
embodiment 2:
, the material of described metal cutting tool includes following component: 36 tons of copper molybdenum alloys, 30 tons of iron-nickel alloys, 25 tons of titanium niobium alloys, 5 tons, sodium sulphite, 6 tons of silicon sulfides, 2 tons of water glass.The preparation method of above-mentioned a kind of metal cutting tool, is after described three kinds of alloy moltens, to add all the other components again, pours in cutter mould after cooling and makes.
embodiment 3:
, the material of described metal cutting tool includes following component: 30 tons of copper molybdenum alloys, 25 tons of iron-nickel alloys, 20 tons of titanium niobium alloys, 4 tons, sodium sulphite, 5 tons of silicon sulfides, 1.5 tons of water glass.The preparation method of above-mentioned a kind of metal cutting tool, is after described three kinds of alloy moltens, to add all the other components again, pours in cutter mould after cooling and makes.
Finally it should be noted that: the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although the present invention is had been described in detail with reference to previous embodiment, for a person skilled in the art, its technical scheme that still can record aforementioned each embodiment is modified, or part technical characterictic is wherein equal to replacement.Within the spirit and principles in the present invention all, any modification of doing, be equal to replacement, improvement etc., within all should being included in protection scope of the present invention.
Claims (3)
1. a metal cutting tool, is characterized in that, the material of described metal cutting tool includes the following component according to weight part meter: copper molybdenum alloy 24-36 part, iron-nickel alloy 20-30 part, titanium niobium alloy 15-25 part, sodium sulphite 3-5 part, silicon sulfide 3-6 part, water glass 1-2 part.
2. a kind of metal cutting tool according to claim 1, is characterized in that, the material of described metal cutting tool includes the following component according to weight part meter: 30 parts of copper molybdenum alloys, 25 parts of iron-nickel alloys, 20 parts of titanium niobium alloys, 4 parts, sodium sulphite, 5 parts of silicon sulfides, 1.5 parts of water glass.
3. according to the preparation method of the arbitrary described a kind of metal cutting tool of claim 1 or 2, it is characterized in that, is after described three kinds of alloy moltens, to add all the other components again, pours in cutter mould after cooling and makes.