CN103523873A - Active quanta water generator filter material - Google Patents
Active quanta water generator filter material Download PDFInfo
- Publication number
- CN103523873A CN103523873A CN201310447584.2A CN201310447584A CN103523873A CN 103523873 A CN103523873 A CN 103523873A CN 201310447584 A CN201310447584 A CN 201310447584A CN 103523873 A CN103523873 A CN 103523873A
- Authority
- CN
- China
- Prior art keywords
- medical stone
- tourmalinite
- musyushi
- water
- marine alga
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of filter materials, and particularly relates to an active quanta water generator filter material. The filter material comprises the components in percentage by weight as follows: 20%-60% of tourmaline, 2%-6% of medical stone, 2%-6% of muyu stone, 10%-30% of activated carbon and 10%-30% of seaweed mud; the rated weight percentage of the tourmaline is 50%, the medical stone is 5%, the muyu stone is 5%, the activated carbon is 25%, and the seaweed mud is 25%; and the weight ratio of the tourmaline, the medical stone, the muyu stone, the activated carbon and the seaweed mud is 10: 1: 1: 5: 5. The filter material is high in adsorption capacity, good in filter effect, healthy and safe, can promote life vitality, and can be absorbed rapidly after entering a body; after the filter material enters a cell, the nutrition physiological function of water approaches that of water in a human cell; and the filter material has the effects of relieving metabolic diseases and promoting growth.
Description
Technical field
The invention belongs to filtrate technical field, be specifically related to a kind of active quantum water generator filtrate.
Background technology
In the aftertreatment technology of pure water preparation and secondary filter, filtrate is the part of most critical, the power of filtrate adsorptive power is directly connected to the effect of water filtration, and market does not have a kind of filtrate can accomplish after waste water, tap water filter, to become a kind of active quantum water now, because active quantum water does not produce feeling of repletion after drinking, promote vitality, enter in body and can absorb very soon, in infiltration cell, make the nutritional-physiological function of water approach the water in human body cell, the effect of alleviating in addition metabolic trouble and promoting to grow.
Summary of the invention
In order to overcome above shortcomings part in prior art, the object of the present invention is to provide a kind of high adsorption capacity, good filtration effect, healthy and safe, can control a kind of active quantum water generator filtrate of disease.
In order to reach above-mentioned object, the present invention adopts following concrete technical scheme:
Active quantum water generator filtrate, comprises tourmalinite, medical stone, MUSYUSHI, gac, marine alga mud, and the weight percent of each component is tourmalinite 20%~60%, medical stone 2%~6%, MUSYUSHI 2%~6%, gac 10%~30%, marine alga mud 10%~30%.
Further, described tourmalinite, medical stone, MUSYUSHI, gac, marine alga mud volume weight percent are tourmalinite 50%, medical stone 5%, MUSYUSHI 5%, gac 25%, marine alga mud 25%; Part by weight between described tourmalinite, medical stone, MUSYUSHI, gac, marine alga mud is 10:1:1:5:5.
The production technique of active quantum water generator filtrate, comprises the steps,
1,10 parts of tourmalinite, 1 part of medical stone and 1 part of MUSYUSHI are cleaned with clear water after and be immersed in clear water several days;
2,5 parts of marine alga mud and 5 parts of gacs are mixing cured, and high-temperature firing becomes Ceramic Balls;
3, Ceramic Balls in step (2) is poured in the water that soaks tourmalinite, medical stone and MUSYUSHI in step (1), fully stir compound;
4, after tourmalinite, medical stone, MUSYUSHI and Ceramic Balls being rinsed with high purity water, vacuum hydro-extraction is dried;
5, put in proportion filter flask moulding.
Compared with prior art, the present invention has following outstanding advantages and effect:
High adsorption capacity, good filtration effect, healthy and safe, promote vitality, enter in body and can absorb very soon, infiltrate in cell, make the nutritional-physiological function of water approach the water in human body cell, the effect of alleviating in addition metabolic trouble and promoting to grow.
Embodiment
Active quantum water generator filtrate, comprises tourmalinite, medical stone, MUSYUSHI, gac, marine alga mud, and the weight percent of each component is tourmalinite 20%~60%, medical stone 2%~6%, MUSYUSHI 2%~6%, gac 10%~30%, marine alga mud 10%~30%.
Further, described tourmalinite, medical stone, MUSYUSHI, gac, marine alga mud volume weight percent are tourmalinite 50%, medical stone 5%, MUSYUSHI 5%, gac 25%, marine alga mud 25%; Part by weight between described tourmalinite, medical stone, MUSYUSHI, gac, marine alga mud is 10:1:1:5:5.
The production technique of active quantum water generator filtrate, comprises the steps,
1,10 parts of tourmalinite, 1 part of medical stone and 1 part of MUSYUSHI are cleaned with clear water after and be immersed in clear water several days;
2,5 parts of marine alga mud and 5 parts of gacs are mixing cured, and high-temperature firing becomes Ceramic Balls;
3, Ceramic Balls in step (2) is poured in the water that soaks tourmalinite, medical stone and MUSYUSHI in step (1), fully stir compound;
4, after tourmalinite, medical stone, MUSYUSHI and Ceramic Balls being rinsed with high purity water, vacuum hydro-extraction is dried;
5, put in proportion filter flask moulding.
Following is material effects and contact in filtrate:
Tourmalinite: tourmalinite is born chargedly has electric field also to have magnetic field, can brine electrolysis and make its subset, and the pH value that can affect water transforms to weakly alkaline subset aqueous nature.Make normal water have 13-15 molecular macromolecular mass water of moisture at 140-150 hertz of each water clusters, entering 100 hertz has the molecular small-micelle water of 5-7 moisture with interior each water clusters.And then the pH value (7.2) of change water.
Medical stone and MUSYUSHI: there is catalytic effect, make tourmalinite better effects if, make water become weakly alkaline subset mineral element water.Can remove organism, the toxin of curing the disease, heterochromatic peculiar smell and heavy metal etc., retain organic mineral substance, the characteristics such as activation.
Gac: be a kind of black powdery, the amorphous carbon with porous of granular or ball shape, main component is carbon, also containing a small amount of oxygen, hydrogen, sulphur, nitrogen, chlorine.There is larger surface-area (500~10002/ grams), have very strong absorption property, can be in its Adsorption on Surface gas, liquid or colloidal solids; Earthy Taste mainly for tourmalinite, medical stone, MUSYUSHI surface is removed.
Marine alga mud: be a kind of carrier of filtrate moulding, without any pollution, there is again the feature that adsorptivity is strong, have certain decontamination purification function.
Finally it should be noted that: above embodiment is only unrestricted in order to technical scheme of the present invention to be described, although the present invention is had been described in detail with reference to preferred embodiment, those of ordinary skill in the art is to be understood that, can modify or be equal to replacement technical scheme of the present invention, and not departing from the spirit and scope of technical solution of the present invention, it all should be encompassed in the middle of claim scope of the present invention.
Claims (3)
1. active quantum water generator filtrate, is characterized in that: comprise tourmalinite, medical stone, MUSYUSHI, gac, marine alga mud, the weight percent of each component is tourmalinite 20%~60%, medical stone 2%~6%, MUSYUSHI 2%~6%, gac 10%~30%, marine alga mud 10%~30%.
2. according to described in the active quantum water generator of claim 1 filtrate, it is characterized in that: described tourmalinite, medical stone, MUSYUSHI, gac, marine alga mud volume weight percent are tourmalinite 50%, medical stone 5%, MUSYUSHI 5%, gac 25%, marine alga mud 25%; Part by weight between described tourmalinite, medical stone, MUSYUSHI, gac, marine alga mud is 10:1:1:5:5.
3. the production technique of the active quantum water generator of claim 1 filtrate, is characterized in that: comprises the steps,
1,10 parts of tourmalinite, 1 part of medical stone and 1 part of MUSYUSHI are cleaned with clear water after and be immersed in clear water several days;
2,5 parts of marine alga mud and 5 parts of gacs are mixing cured, and high-temperature firing becomes Ceramic Balls;
3, Ceramic Balls in step (2) is poured in the water that soaks tourmalinite, medical stone and MUSYUSHI in step (1), fully stir compound;
4, after tourmalinite, medical stone, MUSYUSHI and Ceramic Balls being rinsed with high purity water, vacuum hydro-extraction is dried;
5, put in proportion filter flask moulding.