CN1035228C - Paper shoe-pad and its producing technology - Google Patents
Paper shoe-pad and its producing technology Download PDFInfo
- Publication number
- CN1035228C CN1035228C CN93115952A CN93115952A CN1035228C CN 1035228 C CN1035228 C CN 1035228C CN 93115952 A CN93115952 A CN 93115952A CN 93115952 A CN93115952 A CN 93115952A CN 1035228 C CN1035228 C CN 1035228C
- Authority
- CN
- China
- Prior art keywords
- weight
- solution
- percentage
- cardboard
- time
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a pair of paper shoe pads and a producing technology thereof. The pair of shoe pads is made of cotton pulp paper boards with the compactness of 0.4 to 0.5 g/cc, is soaked twice in the aqueous solution of high molecular compounds in order to have the functions of water prevention, abrasion resistance and deformation resistance, and can also be soaked in medicine solution in order to have the functions of moisturizing skins, slushing and relieving itching. The pair of paper shoe pads can treat and prevent dermatophytosis.
Description
The present invention relates to a kind of production technology of paper shoe-pad.
The shoe-pad that present people wear is generally made of cotton.This fabric shoe-pad is because the cost height, so generally all be to use repeatedly after washing, so it just exists the shortcoming that wears trouble, and this in addition fabric shoe-pad is blocked up as making, and dress is uncomfortable, and if thin excessively, then play pleat easily.Existing industrial paperboard is because its gas permeability and tension, fracture resistance are relatively poor, so be not suitable for making shoe-pad.
The production technology that the purpose of this invention is to provide a kind of paper shoe-pad, characteristics such as its cost is low, can disposablely use, and has wear-resisting, absorbing sweat simultaneously, does not play pleat, indeformable, and is not rancid, and removing dampness to relieve itching is arranged, suppress conk, functions such as skin care.
The object of the present invention is achieved like this: a kind of paper shoe-pad, it is characterized in that this shoe-pad is that the employing tightness is a 0.4-0.5 gram/cubic centimetre, through waterproof, anti-deformation, the cotton pulp cardboard that wear-resistant immersion is handled is made, its production technology is as follows: adopt 100% cotton pulp to make the cardboard that tightness is a 0.4-0.5 gram/cubic centimetre, the preparation percentage by weight is the melamine resin aqueous solution (pH value is 4.5-5.5) of 2.5-3.0%, the cardboard of making is flooded in above-mentioned solution, the impregnating resin amount is 5-8%, after oven dry or the air dry, in 100 ℃ of-120 ℃ of environment, wore out 10 minutes, the preparation percentage by weight is 1799 polyvinyl alcohol water solutions of 2.5-3%, above-mentioned cardboard through flooding is for the first time carried out the dipping second time in this solution, pickup is the 3-5% of weight, then oven dry or air dry.
The cardboard that the present invention adopts has characteristics such as low tightness, high-hydroscopicity, highly-breathable, loose, softness, after (waterproof, anti-deformation) floods for the first time, the paper fiber surface has one deck resin molding, institute so that it possessed moisture-proof, indeformable, do not play performances such as pleat, folding, tensile strength also is improved, after flooding for the second time, make it have wear-resisting characteristics, therefore can wear indeformable more than 15 days, phozy, not wear and tear with the shoe-pad of this paperboard, and comfortable and easy to wear.If will pass through drug-treated again through the cardboard behind the above-mentioned double-steeping, not only can have not rancid characteristics, can also possess skin care, prevent and treat functions such as the ringworm of the foot.
The employed melamine resin aqueous solution can be with the urea-formaldehyde resin aqueous solution of 0.5-1% or with the PAE resin aqueous solution replacement of 5-6% in the above-mentioned production technology, and 1799 polyvinyl alcohol water solutions can be used the polyacrylamide solution of 1-3%, perhaps use the polyvinyl acetate aqueous solution of 0.2-1%, perhaps use the 0.5-2% CMC aqueous solution, perhaps use the aqueous gelatin solution of 0.5-2%, perhaps styrene-butadiene latex or the butadiene acrylonitrile rubber whey solution with 1-3% substitutes (above percentage all is weight percentage).
The invention will be further described below in conjunction with embodiment.
Embodiment 1
Adopt 100% bleached cotton starch make quantitative 250 the gram/square metre, tightness is the cardboard of 0.4 gram/cubic centimetre, in being 2.5% the melamine resin aqueous solution (pH value is 4.5), percentage by weight carries out the dipping first time, pickup is 5%, after drying, wears out 10 minutes in 100 ℃ of environment, in being 3% polyvinyl alcohol water solution, percentage by weight carries out the dipping second time then, pickup is 5%, after the oven dry, cuts according to the standard footwear sizes and to make shoe-pad.
Embodiment 2
Adopt 100% bleached cotton starch make quantitative 270 the gram/square metre, tightness is the cardboard of 0.5 gram/cubic centimetre, in being 3.0% the melamine resin aqueous solution (pH value is 5.5), percentage by weight carries out the dipping first time, pickup is 8%, behind 60 ℃ of environment, dry, in 120 ℃ of environment, wore out 10 minutes, in being 2.5% polyvinyl alcohol water solution, percentage by weight carries out the dipping second time then, pickup is 3%, after drying, carries out drug-treated, promptly at glycerine 1%, flood for the third time in the aqueous solution of formalin 0.5%, pickup is glycerine 0.6%, dries behind the formalin 0.4%, makes shoe-pad by the standard footwear sizes.Has skin care, not rancid characteristics through the shoe-pad of impregnation process for the third time.
Embodiment 3
Adopt 100% bleached cotton starch make quantitative 260 the gram/square metre, tightness is the cardboard of 0.41 gram/cubic centimetre, in being 2.8% the melamine resin aqueous solution (pH value is 5), percentage by weight carries out the dipping first time, pickup is 7%, after the oven dry, in 100 ℃ of environment, wore out 10 minutes, in being 2.8% polyvinyl alcohol water solution, percentage by weight carries out the dipping second time then, pickup is 4%, after drying, carry out the drug-treated first time, promptly at glycerine 1.5%, flood for the third time in the aqueous solution of formalin 1%, pickup is a glycerine 0.9%, formalin 0.6%, carry out the drug-treated second time after making shoe-pad by the standard footwear sizes, at first cloves 20-30 is restrained, Asian puccoon 25-35 gram, bletilla striata 25-35 gram, corter pseudolaricis 30-40 gram, thank with skin 30-40 gram adding 2000-2500 ml water and boiled 15-20 minute, filter and take out soup, shoe-pad is put into soup flood, every pair of pickup is the 13-18 milliliter, dry in the shade after the taking-up.After the process drug-treated second time, shoe-pad has the inhibition conk, and the function of removing dampness to relieve itching can be prevented the generation of tinea pedis disease, and can play therapeutic action to tinea pedis disease.
Embodiment 4
Adopt 100% bleached cotton starch make quantitative 250 the gram/square metre, tightness is the cardboard of 0.4 gram/cubic centimetre, in being 0.5% urea-formaldehyde resin aqueous solution (pH value is 4.5), percentage by weight carries out the dipping first time, pickup is 5%, after drying, wears out 10 minutes in 100 ℃ of environment, in being 3% polyvinyl alcohol water solution, percentage by weight carries out the dipping second time then, pickup is 5%, after the oven dry, cuts according to the standard footwear sizes and to make shoe-pad.
Embodiment 5
Adopt 100% bleached cotton starch make quantitative 270 the gram/square metre, tightness is the cardboard of 0.5 gram/cubic centimetre, in being 3.0% the melamine resin aqueous solution (pH value is 5.5), percentage by weight carries out the dipping first time, pickup is 8%, behind 60 ℃ of environment, dry, in 120 ℃ of environment, wore out 10 minutes, in being 3% polyacrylamide solution, percentage by weight carries out the dipping second time then, pickup is 3%, after drying, carries out drug-treated, promptly at glycerine 1%, flood for the third time in the aqueous solution of formalin 0.5%, pickup is glycerine 0.6%, dries behind the formalin 0.4%, makes shoe-pad by the standard footwear sizes.Has skin care, not rancid characteristics through the shoe-pad of impregnation process for the third time.
Embodiment 6
Adopt 100% bleached cotton starch make quantitative 260 the gram/square metre, tightness is the cardboard of 0.41 gram/cubic centimetre, in being 5% PAE resin aqueous solution (pH value is 5), percentage by weight carries out the dipping first time, pickup is 7%, after the oven dry, in 100 ℃ of environment, wore out 10 minutes, in being 2% butadiene acrylonitrile rubber whey solution, percentage by weight carries out the dipping second time then, pickup is 4%, after drying, carry out the drug-treated first time, promptly at glycerine 1.5%, flood for the third time in the aqueous solution of formalin 1%, pickup is a glycerine 0.9%, formalin 0.6%, carry out the drug-treated second time after making shoe-pad by the standard footwear sizes, at first cloves 20-30 is restrained, Asian puccoon 25-35 gram, bletilla striata 25-35 gram, corter pseudolaricis 30-40 gram, thank with skin 30-40 gram adding 2000-2500 ml water and boiled 15-20 minute, filter and take out soup, shoe-pad is put into soup flood, every pair of pickup is the 13-18 milliliter, dry in the shade after the taking-up.After the process drug-treated second time, shoe-pad has the inhibition conk, and the function of removing dampness to relieve itching can be prevented the generation of tinea pedis disease, and can play therapeutic action to tinea pedis disease.
Claims (7)
1, a kind of production technology of paper shoe-pad, it is characterized in that at first preparing percentage by weight is 2.5-3.0, pH value is the melamine resin aqueous solution of 4.5-5.5, with tightness is that 100% cotton pulp cardboard of 0.4-0.5 gram/cubic centimetre floods in above-mentioned solution, impregnating resin amount 5-8%, after the drying, in 100-120 ℃ of environment, wore out 10 minutes, preparing percentage by weight again is 1799 polyvinyl alcohol water solutions of 2.5-3, above-mentioned cardboard through flooding is for the first time carried out the dipping second time in this solution, pickup is the 3-5% of weight, then oven dry or air dry.
2, a kind of production technology of paper shoe-pad, it is characterized in that at first preparing the PAE resin aqueous solution that urea-formaldehyde resin aqueous solution that percentage by weight is 0.5-1 or percentage by weight are 5-6, with tightness is that 0.4-0.5 gram/cube li 100% a cotton pulp cardboard of adopting floods in above-mentioned solution, impregnating resin amount 5-8%, after the drying, in 100-120 ℃ of environment, wore out 10 minutes, preparing percentage by weight again is 1799 polyvinyl alcohol water solutions of 2.5-3, above-mentioned cardboard through flooding is for the first time carried out the dipping second time in this solution, pickup is the 3-5% of weight, then oven dry or air dry.
3, a kind of production technology of paper shoe-pad, it is characterized in that at first preparing percentage by weight is 2.5-3.0, pH value is the melamine resin aqueous solution of 4.5-5.5, with tightness is that 100% cotton pulp cardboard of 0.4-0.5 gram/cubic centimetre floods in above-mentioned solution, impregnating resin amount 5-8%, after the drying, in 100-120 ℃ of environment, wore out 10 minutes, prepare the polyacrylamide solution that percentage by weight is 1-3 again, above-mentioned cardboard through flooding is for the first time carried out the dipping second time in this solution, pickup is the 3-5% of weight, then oven dry or air dry.
4, a kind of production technology of paper shoe-pad, it is characterized in that at first preparing percentage by weight is 2.5-3.0, pH value is the melamine resin aqueous solution of 4.5-5.5, with tightness is that 100% cotton pulp cardboard of 0.4-0.5 gram/cubic centimetre floods in above-mentioned solution, impregnating resin amount 5-8%, after the drying, in 100-120 ℃ of environment, wore out 10 minutes, preparing percentage by weight again is the polyvinyl acetate aqueous solution of 0.2-1, above-mentioned cardboard through flooding is for the first time carried out the dipping second time in this solution, pickup is the 3-5% of weight, then oven dry or air dry.
5, a kind of production technology of paper shoe-pad, it is characterized in that at first preparing percentage by weight is 2.5-3.0, pH value is the melamine resin aqueous solution of 4.5-5.5, with tightness is that 100% cotton pulp cardboard of 0.4-0.5 gram/cubic centimetre floods in above-mentioned solution, impregnating resin amount 5-8%, after the drying, in 100-120 ℃ of environment, wore out 10 minutes, preparing percentage by weight again is the CMC aqueous solution of 0.5-2, above-mentioned cardboard through flooding is for the first time carried out the dipping second time in this solution, pickup is the 3-5% of weight, then oven dry or air dry.
6, a kind of production technology of paper shoe-pad, it is characterized in that at first preparing percentage by weight is that 2.5-3.0, pH value are the melamine resin aqueous solution of 4.5-5.5, with tightness is that 100% cotton pulp cardboard of 0.4-0.5 gram/cubic centimetre floods in above-mentioned solution, impregnating resin amount 5-8%, after the drying, in 100-120 ℃ of environment, wore out 10 minutes, prepare the aqueous gelatin solution that percentage by weight is 0.5-2 again, above-mentioned cardboard through flooding is for the first time carried out the dipping second time in this solution, pickup is the 3-5% of weight, then oven dry or air dry.
7, a kind of production technology of paper shoe-pad, it is characterized in that at first preparing percentage by weight is 2.5-3.0, pH value is the melamine resin aqueous solution of 4.5-5.5, with tightness is that 100% cotton pulp cardboard of 0.4-0.5 gram/cubic centimetre floods in above-mentioned solution, impregnating resin amount 5-8%, after the drying, in 100-120 ℃ of environment, wore out 10 minutes, prepare styrene-butadiene latex or butadiene acrylonitrile rubber whey solution that percentage by weight is 1-3 again, above-mentioned cardboard through flooding is for the first time carried out the dipping second time in this solution, pickup is the 3-5% of weight, then oven dry or air dry.