CN103508747A - High-purification-rate high-strength honeycomb ceramic and preparation method thereof - Google Patents
High-purification-rate high-strength honeycomb ceramic and preparation method thereof Download PDFInfo
- Publication number
- CN103508747A CN103508747A CN201210200523.1A CN201210200523A CN103508747A CN 103508747 A CN103508747 A CN 103508747A CN 201210200523 A CN201210200523 A CN 201210200523A CN 103508747 A CN103508747 A CN 103508747A
- Authority
- CN
- China
- Prior art keywords
- parts
- titanium dioxide
- stearic acid
- purification rate
- honey comb
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses high-purification-rate high-strength honeycomb ceramic. The ceramic is composed of the components of, by weight: 30-50 parts of cordierite, 20-40 parts of alumina, 2-8 parts of yttrium oxide, 2-10 parts of titanium dioxide, 10-20 parts of clay, 10-25 parts of talc powder, 2-8parts of stearic acid, and 10-26 parts of deionized water. Compared with prior art, the high-purification-rate high-strength honeycomb ceramic is prepared with rare earth metal, titanium dioxide, and the like with a special ratio, such that cost is low, and purification rate is high. Also, the ceramic has the advantages of high strength, high-temperature resistance, and long service life. The ceramic can be used under a temperature of 1500-1700 DEG C. The preparation process is simple, and sintering temperature is reduced, such that energy-saving and consumption-reducing purposed can be achieved.
Description
Technical field
The invention belongs to ceramic field, relate in particular to a kind of high purification rate, high strength ceramic honey comb and preparation method thereof.
Background technology
The raising to automobile exhaust emission standard with various countries that increases considerably along with car owning amount, treating vehicle exhaust more and more comes into one's own, the three-element catalytic technology that the ceramic honey comb of wherein take is carrier is considered to effective and the most feasible improvement technology at present, and it can change hydrocarbon polymer harmful in tail gas, oxynitride and carbon monoxide into nontoxic carbonic acid gas, nitrogen G&W simultaneously.For this reason, people are deepening constantly the research of three-element catalytic technology, to improve the cost of processing efficiency and reduction catalyzer.
At present topmost automobile catalyst factory also all adopts the formula of precious metal system in the world.At these, take in the catalyzer that precious metal is active component, the content of precious metal is all higher, and general bullion content can reach every liter more than 1.0 grams.Because the resource of precious metal is in the world very limited, expensive, therefore, adopt the technology of precious metal in large-scale application, to be subject to certain restriction.
Because the fracture toughness property of cordierite honeycomb ceramic is lower, thus its bending strength and wear resisting property poor; Therefore to ask for something fastness to rubbing and physical strength compare Gao field, just can not only adopt traditional trichroite is material preparation.
Summary of the invention
The present invention is just in order to overcome above-mentioned deficiency, and technical problem to be solved is to provide a kind of high purification rate, high strength ceramic honey comb.
The technical problem that the present invention also will solve is to provide the preparation method of above-mentioned high purification rate, high strength ceramic honey comb.
For solving the problems of the technologies described above, the technical solution adopted in the present invention is as follows:
Purification rate, a high strength ceramic honey comb, it is comprised of the component of following parts by weight:
30~50 parts of trichroites
20~40 parts, aluminum oxide
2~8 parts of yttrium oxides
2~10 parts of titanium dioxide
Clay 10-20 part
Talcum powder 10-25 part
Stearic acid 2-8 part
Deionized water 10-26 part.
Wherein, as screening formulation, it is comprised of the component of following parts by weight:
40 parts of trichroites
30 parts, aluminum oxide
5 parts of yttrium oxides
6 parts of titanium dioxide
15 parts of clays
18 parts of talcum powder
5 parts of stearic acid
18 parts of deionized waters.
The method of preparing above-mentioned high purification rate, high strength ceramic honey comb, it comprises the steps:
1, press formula ratio, get after trichroite, aluminum oxide, yttrium oxide, titanium dioxide, clay, talcum powder batching carry out ball milling, batch mixing, to be crushed to 300~400 orders standby;
2, the stearic acid of formula ratio, deionized water are added in raw material standby in step 1, mix latter old 24 hours and obtain pug;
3, pug is put into vacuum pugmill and carried out after mud refining, then put into single-lead-screw extruding briquetting machine moulding;
4, the hygrometric state honeycomb ceramic body of extrusion molding is put into stove dryness finalization and become dry body;
5, honeycomb ceramic body dry body is put into calcining furnace, at 1300~1400 ℃ of temperature, be incubated 2~3 hours;
6, cooling coming out of the stove.
Beneficial effect: high purification rate of the present invention, high strength ceramic honey comb are compared compared with prior art, adopt the raw materials such as the rare earth metal of special proportioning and titanium dioxide to make, not only cheap, and there is higher purification rate, also have advantages of that intensity is high, high temperature resistant, long service life simultaneously, can at 1500~1700 ℃ of temperature, use, its preparation technology is simple, firing temperature declines, and can reach energy-saving and cost-reducing object.
Embodiment
Embodiment 1:
Purification rate, a high strength ceramic honey comb, it is comprised of the component of following parts by weight:
40 parts of trichroites
30 parts, aluminum oxide
5 parts of yttrium oxides
6 parts of titanium dioxide
15 parts of clays
18 parts of talcum powder
5 parts of stearic acid
18 parts of deionized waters.
The method of preparing above-mentioned high purification rate, high strength ceramic honey comb, it comprises the steps:
1, press formula ratio, get after trichroite, aluminum oxide, yttrium oxide, titanium dioxide, clay, talcum powder batching carry out ball milling, batch mixing, to be crushed to 300~400 orders standby;
2, the stearic acid of formula ratio, deionized water are added in raw material standby in step 1, mix latter old 24 hours and obtain pug;
3, pug is put into vacuum pugmill and carried out after mud refining, then put into single-lead-screw extruding briquetting machine moulding;
4, the hygrometric state honeycomb ceramic body of extrusion molding is put into stove dryness finalization and become dry body;
5, honeycomb ceramic body dry body is put into calcining furnace, at 1300~1400 ℃ of temperature, be incubated 2~3 hours;
6, cooling coming out of the stove.
Embodiment 2:
Purification rate, a high strength ceramic honey comb, it is comprised of the component of following parts by weight:
30 parts of trichroites
20 parts, aluminum oxide
2 parts of yttrium oxides
2 parts of titanium dioxide
10 parts of clays
10 parts of talcum powder
2 parts of stearic acid
10 parts of deionized waters.
The method of preparing above-mentioned high purification rate, high strength ceramic honey comb, it comprises the steps:
1, press formula ratio, get after trichroite, aluminum oxide, yttrium oxide, titanium dioxide, clay, talcum powder batching carry out ball milling, batch mixing, to be crushed to 300~400 orders standby;
2, the stearic acid of formula ratio, deionized water are added in raw material standby in step 1, mix latter old 24 hours and obtain pug;
3, pug is put into vacuum pugmill and carried out after mud refining, then put into single-lead-screw extruding briquetting machine moulding;
4, the hygrometric state honeycomb ceramic body of extrusion molding is put into stove dryness finalization and become dry body;
5, honeycomb ceramic body dry body is put into calcining furnace, at 1300~1400 ℃ of temperature, be incubated 2~3 hours;
6, cooling coming out of the stove.
Embodiment 3:
Purification rate, a high strength ceramic honey comb, it is comprised of the component of following parts by weight:
50 parts of trichroites
40 parts, aluminum oxide
8 parts of yttrium oxides
10 parts of titanium dioxide
20 parts of clays
25 parts of talcum powder
8 parts of stearic acid
26 parts of deionized waters.
The method of preparing above-mentioned high purification rate, high strength ceramic honey comb, it comprises the steps:
1, press formula ratio, get after trichroite, aluminum oxide, yttrium oxide, titanium dioxide, clay, talcum powder batching carry out ball milling, batch mixing, to be crushed to 300~400 orders standby;
2, the stearic acid of formula ratio, deionized water are added in raw material standby in step 1, mix latter old 24 hours and obtain pug;
3, pug is put into vacuum pugmill and carried out after mud refining, then put into single-lead-screw extruding briquetting machine moulding;
4, the hygrometric state honeycomb ceramic body of extrusion molding is put into stove dryness finalization and become dry body;
5, honeycomb ceramic body dry body is put into calcining furnace, at 1300~1400 ℃ of temperature, be incubated 2~3 hours;
6, cooling coming out of the stove.
Claims (3)
1. high purification rate, a high strength ceramic honey comb, is characterized in that its being comprised of following parts by weight:
30~50 parts of trichroites
20~40 parts, aluminum oxide
2~8 parts of yttrium oxides
2~10 parts of titanium dioxide
Clay 10-20 part
Talcum powder 10-25 part
Stearic acid 2-8 part
Deionized water 10-26 part.
2. high purification rate according to claim 1, high strength ceramic honey comb, is characterized in that it is comprised of following parts by weight:
40 parts of trichroites
30 parts, aluminum oxide
5 parts of yttrium oxides
6 parts of titanium dioxide
15 parts of clays
18 parts of talcum powder
5 parts of stearic acid
18 parts of deionized waters.
3. a method of preparing high purification rate described in claim 1, high strength ceramic honey comb, is characterized in that it comprises the steps:
(1) press formula ratio, get after trichroite, aluminum oxide, yttrium oxide, titanium dioxide, clay, talcum powder batching carry out ball milling, batch mixing, to be crushed to 300~400 orders standby;
(2) stearic acid of formula ratio, deionized water are added in raw material standby in step (1), mix latter old 24 hours and obtain pug;
(3) pug is put into vacuum pugmill and carried out after mud refining, then put into single-lead-screw extruding briquetting machine moulding;
(4) the hygrometric state honeycomb ceramic body of extrusion molding is put into stove dryness finalization and become dry body;
(5) honeycomb ceramic body dry body is put into calcining furnace, at 1300~1400 ℃ of temperature, be incubated 2~3 hours;
(6) cooling coming out of the stove.