CN103507191B - A kind of curtain coating batches middle permeation waterproof humidity-permeant TPU membrane - Google Patents

A kind of curtain coating batches middle permeation waterproof humidity-permeant TPU membrane Download PDF

Info

Publication number
CN103507191B
CN103507191B CN201210226476.8A CN201210226476A CN103507191B CN 103507191 B CN103507191 B CN 103507191B CN 201210226476 A CN201210226476 A CN 201210226476A CN 103507191 B CN103507191 B CN 103507191B
Authority
CN
China
Prior art keywords
tpu
permeant
die head
waterproof humidity
tpu membrane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210226476.8A
Other languages
Chinese (zh)
Other versions
CN103507191A (en
Inventor
何建雄
王一良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Xionglin New Material Technology Co., Ltd.
Original Assignee
Dongguan Xionglin New Materials Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongguan Xionglin New Materials Technology Co Ltd filed Critical Dongguan Xionglin New Materials Technology Co Ltd
Priority to CN201210226476.8A priority Critical patent/CN103507191B/en
Publication of CN103507191A publication Critical patent/CN103507191A/en
Application granted granted Critical
Publication of CN103507191B publication Critical patent/CN103507191B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to saturating waterproof membrane production technical field in new TP U, particularly relate to a kind of novel curtain coating and batch middle permeation waterproof humidity-permeant TPU membrane.A kind of novel curtain coating of the present invention batches the product of middle permeation waterproof humidity-permeant TPU membrane, and it comprises selects, by adding new TPU pellet of filling a prescription after high-temperature fusion, to extrude---cool---shaping---batching from extruder die head.It comprises die head, and it also comprises the decorative pattern shaping wheel, shaping cooling wheel, the driving wheel that are arranged under extruder die head, also comprises rubber expanding wheel, rolling driving wheel, static elimination wheel, anti-skidding Teflon and wrap-up.The present invention fills a prescription uniqueness, novelty, to breach in other permeation waterproof humidity-permeant film must blowing, attached PE just fertile limitation, allow the more convenient operation of postorder, reduce the dual waste of polyethylene and thermoplastic polyurethane, cost-saving, improve the quality of products.

Description

A kind of curtain coating batches middle permeation waterproof humidity-permeant TPU membrane
Technical field
The invention belongs to TPU field of new, particularly relate to a kind of novel middle permeation waterproof humidity-permeant TPU membrane new product.
Background technology
TPU (thermoplastic polyurethane) is environmental protection macromolecule polymer, which overcome many defects of PVC and PU film, not only have most of characteristic of rubber and common plastics, but also have excellent comprehensive physical and chemical property, so the following material that is otherwise known as.In TPU, permeation waterproof humidity-permeant film adopts TPU pellet, and the film made by special process, it inherits the outstanding physical property of TPU, and range of application is very extensive.Owing to having avirulent advantage, meet environmental requirement, in TPU, permeation waterproof humidity-permeant film product is widely used in the fields such as high-grade clothing, footwear material, blowing bag, packaging and handicraft.
Summary of the invention
The object of this invention is to provide permeation waterproof humidity-permeant TPU membrane in one, this waterproof humidity-permeant film adopts TPU particle through extruder die head, the TPU melt of thickness between 0.01mm-0.10mm is attached to rapidly the cooling wheel surface of low temperature, melt is cooled fast and forms transparent or cloudy surface or coloured TPU film.This product not only maintains the original good characteristic of TPU, and adds new function, and waterproof, gas permeability are splendid.
Middle permeation waterproof humidity-permeant TPU membrane key property of the present invention shows:
1, film thickness: 0.01mm ~ 0.10mm;
2, with reference to GB/T4744-1984 standard, utilize YG812 type water tester, record film more than water pressure resistance 10000mmH25;
3, with reference to GB/T12704-91B standard, the method for executing is utilized to record between the moisture permeability 8500 ~ 10000g/m2*24hrs of film.
The production technology spy that described a kind of curtain coating batches middle permeation waterproof humidity-permeant TPU membrane is: the temperature first setting die head, and when after the temperature that extruder die head reaches set, die head is started working.Now, extruder by TPU pellet by die head heating, flow out-cooling-shaping-batch after melting.
Described process conditions are: die head temperature 80 ~ 250 DEG C; Curtain coating speed 2 ~ 300m/min; TPU casting temperature 80 ~ 250 DEG C; Thickness 0.01 ~ the 0.10mm of TPU membrane; Coiling speed 2 ~ 300m/min; Electric current 20 ~ 140A.
Distinguishing feature of the present invention is: the method adopting high temperature curtain coating, will form permeation waterproof humidity-permeant TPU film in individual layer, without the need to attached PE or other film after TPU melting.
Present invention process is unique, simple, breach permeation waterproof humidity-permeant film in other and must use blowing, attached PE just fertile limitation, allow the more convenient operation of postorder, reduce the dual waste of polyethylene and thermoplastic polyurethane, cost-saving, and product environment-protecting asepsis, waterproof, permeability are fabulous, wear-resisting, heat-resisting, be the optimal material making high-grade dress ornament, footwear, packaging, water sport items.
Detailed description of the invention.Described production curtain coating batches middle permeation waterproof humidity-permeant TPU membrane step:
First set the temperature of extruder die head, when after the temperature that extruder die head reaches set, die head is started working, by TPU pellet by extruder die head heating, flow out-cooling-shaping-batch after melting.
Described process conditions are: extruder die head temperature 80 ~ 250 DEG C; Curtain coating speed 2 ~ 300m/min; TPU casting temperature 80 ~ 250 DEG C; Thickness 0.01 ~ the 0.10mm of TPU membrane; Coiling speed 2 ~ 300m/min; Electric current 20 ~ 140A.
The each group of formula of raw material of described novel middle permeation waterproof humidity-permeant TPU membrane is: TPU pellet: 30 ~ 95Phr; Interior lubrication prescription: 0.1 ~ 60Phr; Outer lubrication prescription: 0.1 ~ 70Phr; Antioxidant: 0.01 ~ 10Phr; UV resistant agent: 0.01 ~ 10Phr.
Described interior lubrication prescription is SA, ethylidene benzoic acid glycerine alcohol ester, and its effect can increase thin smooth, brightness when estimating shaping.
Described outer lubrication prescription adipic acid pentaerythritol ester, its effect reduces film viscosity when take-up, to ensure that the top layer of film is bright and clean, smooth, convenient processing.

Claims (1)

1. in, a production method for permeation waterproof humidity-permeant TPU membrane, is characterized in that, the composition of raw materials of described middle permeation waterproof humidity-permeant TPU membrane is: TPU pellet: 30 ~ 95Phr; Interior lubrication prescription: 0.1 ~ 60Phr; Outer lubrication prescription: 0.1 ~ 70Phr; Antioxidant: 0.01 ~ 10Phr; UV resistant agent: 0.01 ~ 10Phr; Wherein said TPU pellet is TPUE, and described interior lubrication prescription is SA, ethylidene benzoic acid glycerine alcohol ester, and described outer lubrication prescription is adipic acid pentaerythritol ester;
The production method of described middle permeation waterproof humidity-permeant TPU membrane comprises the following steps: the temperature first setting extruder die head, after machine die head to be extruded reaches set temperature, extruder die head is started working, TPU pellet is by flowing out after extruder die head heating, melting, then cooling is---shaping---batches, obtain middle permeation waterproof humidity-permeant TPU membrane product, wherein working condition parameter is: extruder die head temperature 80 ~ 250 DEG C; Curtain coating speed 2 ~ 300m/min; TPU casting temperature 80 ~ 250 DEG C; Thickness 0.01 ~ the 0.10mm of TPU membrane; Coiling speed 2 ~ 300m/min; Electric current 20 ~ 140A.
CN201210226476.8A 2012-06-22 2012-06-22 A kind of curtain coating batches middle permeation waterproof humidity-permeant TPU membrane Active CN103507191B (en)