CN103482966A - Ceramic comb - Google Patents
Ceramic comb Download PDFInfo
- Publication number
- CN103482966A CN103482966A CN201310452855.3A CN201310452855A CN103482966A CN 103482966 A CN103482966 A CN 103482966A CN 201310452855 A CN201310452855 A CN 201310452855A CN 103482966 A CN103482966 A CN 103482966A
- Authority
- CN
- China
- Prior art keywords
- parts
- comb
- ceramic
- oxide
- broach
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a ceramic comb and belongs to the technical field of ceramic production. The comb comprises a comb body and comb teeth, which are integrated, wherein the comb body and the comb teeth are both made of ceramics and integrally formed with a high-temperature firing method. The ceramic comb has the advantages of high strength, smoothness for combing and high possibility of cleaning; meanwhile, a one-step forming method is adopted, so that the manufacturing process is simplified, the difficulty is lowered, the rejection rate is reduced, and the cost is saved.
Description
Technical field
The present invention relates to a kind of ceramic comb, belong to the ceramic production technology field.
Background technology
Comb, claim again comb, and claim again comb ancient times, is the instrument that arranges hair, and shape is usually flat, and with a lot of teeth.Some comb is with handle, and some does not have.Now comb of a great variety as: mahogany comb, sandalwood comb, horn comb etc.Comb is more than 300 kind of the five large series such as minute utility comb, technique comb, Tourist's comb, high-grade elaboration comb, health-care comb on kind.
A kind of important indicator of passing judgment on comb performance quality is that its combing is smooth, a lot of horn combs on the market at present, goat's horn combs out to be sold, these combs are exactly to flaunt smooth, rare banner, but along with expanding economy, farm is more and more less, there is no so much ox and sheep at all, more need not talk and utilize the angle of ox and sheep to make comb.In addition, the most traditional the most general another material of making comb again is exactly timber, is all to adopt timber to make comb miscellaneous since ancient times.The timber comb is light portable; it is rotten that but timber easily goes mouldy; work-ing life is short; not easy to clean; and appeal now to protect forest resources; the value of every trees is far longer than it and is cut down the value when timber, so develop a kind of novel material, makes comb, is very abreast of the times requirement.
201210506755.X disclose a kind of ceramic comb, this comb is comprised of comb body and broach, by the once shaped of high-temperature firing method, but the pottery that this patent adopts is general brittle ceramic, not to ceramic modified,, due to ceramic fragility, in the comb use procedure, easily fracture, the work-ing life of comb is short.Therefore develop a kind of ceramic comb that adopts special ceramics to make, extend the work-ing life of comb, reduce the difficulty in the production process, it is very significant reducing scrap rate.
It is raw material that barium carbonate, cupric oxide, cobalt oxide, zinc oxide, boron, calcite, kaolin, aluminum oxide, quartz, saltpetre, soda ash, antimonous oxide are take in the present invention, develop a kind of ceramic comb, this comb has the advantage that intensity is high, combing is smooth, easy to clean; Simultaneously, adopt once moulding method, reduced the making processes of product, difficulty reduces, and has reduced scrap rate, has saved cost.
Summary of the invention
The purpose of this invention is to provide a kind of ceramic comb, this pottery comb is comprised of all-in-one-piece comb body processed and broach, it is characterized in that: comb body and broach are made by stupalith, and are integrated by the once shaped of high-temperature firing method; The present invention has advantages of that intensity is high, combing is smooth, easy to clean; Simultaneously, adopt once moulding method, reduced the making processes of product, difficulty reduces, and has reduced scrap rate, has saved cost.
In order to address the above problem, the technical solution adopted in the present invention is:
A kind of comb body of ceramic comb and broach adopt special ceramic material to make, and the component of following weight part, consist of:
3 ~ 8 parts of barium carbonates, 0.01 ~ 0.03 part of cupric oxide, 0.005 ~ 0.01 part of cobalt oxide, 5 ~ 10 parts, zinc oxide, 1 ~ 5 part of boric acid, 20 ~ 35 parts, calcite, 5 ~ 10 parts of kaolin, 3 ~ 8 parts, aluminum oxide, 35 ~ 55 parts, quartz, 3 ~ 8 parts, saltpetre, 3 ~ 8 parts of soda ash, 0.5 ~ 2.0 part of antimonous oxide.
A kind of preparation method of ceramic comb, comprise the steps:
Take 3 ~ 8 parts of barium carbonates, 0.01 ~ 0.03 part of cupric oxide, 0.005 ~ 0.01 part of cobalt oxide, 5 ~ 10 parts, zinc oxide, 1 ~ 5 part of boric acid, 20 ~ 35 parts, calcite, 5 ~ 10 parts of kaolin, 3 ~ 8 parts, aluminum oxide, 35 ~ 55 parts, quartz, 3 ~ 8 parts, saltpetre, 3 ~ 8 parts of soda ash, 0.5 ~ 2.0 part of antimonous oxide, mixing and stirring, the high temperature melt of 1500 ~ 1550 ℃ 1.5 ~ 2.0 hours, liquid mould molding by melting, be drying to obtain ceramic comb.
The present invention with respect to the beneficial effect of prior art is:
Ceramic comb of the present invention is comprised of all-in-one-piece comb body processed and broach, it is characterized in that: comb body and broach are made by stupalith, and are integrated by the once shaped of high-temperature firing method; The present invention has advantages of that intensity is high, combing is smooth, easy to clean; Simultaneously, adopt once moulding method, reduced the making processes of product, difficulty reduces, and has reduced scrap rate, has saved cost.
Embodiment
Below by embodiment, the present invention is described in further details, these embodiment only are used for illustrating the present invention, do not limit the scope of the invention.
Embodiment 1
A kind of comb body of ceramic comb and broach adopt special ceramic material to make, and the component of following weight part, consist of:
3 parts of barium carbonates, 0.01 part of cupric oxide, 0.005 part of cobalt oxide, 5 parts, zinc oxide, 1 part of boric acid, 20 parts, calcite, 5 parts of kaolin, 3 parts, aluminum oxide, 35 parts, quartz, 3 parts, saltpetre, 3 parts of soda ash, 0.5 part of antimonous oxide.
A kind of preparation method of ceramic comb comprises the steps:
Take 3 parts of barium carbonates, 0.01 part of cupric oxide, 0.005 part of cobalt oxide, 5 parts, zinc oxide, 1 part of boric acid, 20 parts, calcite, 5 parts of kaolin, 3 parts, aluminum oxide, 35 parts, quartz, 3 parts, saltpetre, 3 parts of soda ash, 0.5 part of antimonous oxide, mixing and stirring, the high temperature melt of 1500 ℃ 2 hours, liquid mould molding by melting, be drying to obtain ceramic comb.
Embodiment 2
A kind of comb body of ceramic comb and broach adopt special ceramic material to make, and the component of following weight part, consist of:
8 parts of barium carbonates, 0.03 part of cupric oxide, 0.01 part of cobalt oxide, 10 parts, zinc oxide, 5 parts of boric acid, 35 parts, calcite, 10 parts of kaolin, 8 parts, aluminum oxide, 55 parts, quartz, 8 parts, saltpetre, 8 parts of soda ash, 2.0 parts of antimonous oxides.
A kind of preparation method of ceramic comb comprises the steps:
Take 8 parts of barium carbonates, 0.03 part of cupric oxide, 0.01 part of cobalt oxide, 10 parts, zinc oxide, 5 parts of boric acid, 35 parts, calcite, 10 parts of kaolin, 8 parts, aluminum oxide, 55 parts, quartz, 8 parts, saltpetre, 8 parts of soda ash, 2.0 parts of antimonous oxides, mixing and stirring, the high temperature melt of 1510 ℃ 2 hours, liquid mould molding by melting, be drying to obtain ceramic comb.
Embodiment 3
A kind of comb body of ceramic comb and broach adopt special ceramic material to make, and the component of following weight part, consist of:
5 parts of barium carbonates, 0.02 part of cupric oxide, 0.007 part of cobalt oxide, 8 parts, zinc oxide, 3 parts of boric acid, 30 parts, calcite, 8 parts of kaolin, 5 parts, aluminum oxide, 45 parts, quartz, 5 parts, saltpetre, 5 parts of soda ash, 1.0 parts of antimonous oxides.
A kind of preparation method of ceramic comb comprises the steps:
Take 5 parts of barium carbonates, 0.02 part of cupric oxide, 0.007 part of cobalt oxide, 8 parts, zinc oxide, 3 parts of boric acid, 30 parts, calcite, 8 parts of kaolin, 5 parts, aluminum oxide, 45 parts, quartz, 5 parts, saltpetre, 5 parts of soda ash, 1.0 parts of antimonous oxides, mixing and stirring, the high temperature melt of 1520 ℃ 2 hours, liquid mould molding by melting, be drying to obtain ceramic comb.
Embodiment 4
A kind of comb body of ceramic comb and broach adopt special ceramic material to make, and the component of following weight part, consist of:
3 parts of barium carbonates, 0.01 part of cupric oxide, 0.01 part of cobalt oxide, 10 parts, zinc oxide, 5 parts of boric acid, 35 parts, calcite, 5 parts of kaolin, 8 parts, aluminum oxide, 35 parts, quartz, 3 parts, saltpetre, 8 parts of soda ash, 0.5 part of antimonous oxide.
A kind of preparation method of ceramic comb comprises the steps:
Take 3 parts of barium carbonates, 0.01 part of cupric oxide, 0.01 part of cobalt oxide, 10 parts, zinc oxide, 5 parts of boric acid, 35 parts, calcite, 5 parts of kaolin, 8 parts, aluminum oxide, 35 parts, quartz, 3 parts, saltpetre, 8 parts of soda ash, 0.5 part of antimonous oxide, mixing and stirring, the high temperature melt of 1530 ℃ 2 hours, liquid mould molding by melting, be drying to obtain ceramic comb.
Embodiment 5
A kind of comb body of ceramic comb and broach adopt special ceramic material to make, and the component of following weight part, consist of:
8 parts of barium carbonates, 0.03 part of cupric oxide, 0.005 part of cobalt oxide, 5 parts, zinc oxide, 1 part of boric acid, 20 parts, calcite, 10 parts of kaolin, 3 parts, aluminum oxide, 55 parts, quartz, 8 parts, saltpetre, 8 parts of soda ash, 2.0 parts of antimonous oxides.
A kind of preparation method of ceramic comb comprises the steps:
Take 8 parts of barium carbonates, 0.03 part of cupric oxide, 0.005 part of cobalt oxide, 5 parts, zinc oxide, 1 part of boric acid, 20 parts, calcite, 10 parts of kaolin, 3 parts, aluminum oxide, 55 parts, quartz, 8 parts, saltpetre, 8 parts of soda ash, 2.0 parts of antimonous oxides, mixing and stirring, the high temperature melt of 1540 ℃ 2 hours, liquid mould molding by melting, be drying to obtain ceramic comb.
Claims (4)
1. a ceramic comb is characterized in that: comb body and broach adopt special ceramic material to make, and the component of following weight part, consist of:
3 ~ 8 parts of barium carbonates, 0.01 ~ 0.03 part of cupric oxide, 0.005 ~ 0.01 part of cobalt oxide, 5 ~ 10 parts, zinc oxide, 1 ~ 5 part of boric acid, 20 ~ 35 parts, calcite, 5 ~ 10 parts of kaolin, 3 ~ 8 parts, aluminum oxide, 35 ~ 55 parts, quartz, 3 ~ 8 parts, saltpetre, 3 ~ 8 parts of soda ash, 0.5 ~ 2.0 part of antimonous oxide.
2. a kind of ceramic comb according to claim 1, is characterized in that: comb body and broach employing special ceramic material
Make, the component of its weight part forms: 5 parts of barium carbonates, 0.02 part of cupric oxide, 0.008 part of cobalt oxide, 4 parts, zinc oxide, 4 parts of boric acid, 30 parts, calcite, 7 parts of kaolin, 4 parts, aluminum oxide, 40 parts, quartz, 5 parts, saltpetre, 5 parts of soda ash, 1.8 parts of antimonous oxides.
3. the preparation method of a ceramic comb, it is characterized in that: comb body and broach are integrated by the once shaped of high-temperature firing method.
4. the preparation method of a kind of ceramic comb according to claim 3 is characterized in that: by above-mentioned each component mixing and stirring, the high temperature melt of 1500 ~ 1550 ℃ 1.5 ~ 2.0 hours, the liquid mould molding by melting, be drying to obtain ceramic comb.