CN103480389B - There is the Catalysts and its preparation method of hydrogenation catalyst effect and application and method for hydrotreating hydrocarbon oil - Google Patents

There is the Catalysts and its preparation method of hydrogenation catalyst effect and application and method for hydrotreating hydrocarbon oil Download PDF

Info

Publication number
CN103480389B
CN103480389B CN201210191945.7A CN201210191945A CN103480389B CN 103480389 B CN103480389 B CN 103480389B CN 201210191945 A CN201210191945 A CN 201210191945A CN 103480389 B CN103480389 B CN 103480389B
Authority
CN
China
Prior art keywords
catalyst
metallic element
carrier
lithium
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210191945.7A
Other languages
Chinese (zh)
Other versions
CN103480389A (en
Inventor
马军建
杨清河
曾双亲
聂红
李大东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sinopec Research Institute of Petroleum Processing
China Petroleum and Chemical Corp
Original Assignee
Sinopec Research Institute of Petroleum Processing
China Petroleum and Chemical Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sinopec Research Institute of Petroleum Processing, China Petroleum and Chemical Corp filed Critical Sinopec Research Institute of Petroleum Processing
Priority to CN201210191945.7A priority Critical patent/CN103480389B/en
Publication of CN103480389A publication Critical patent/CN103480389A/en
Application granted granted Critical
Publication of CN103480389B publication Critical patent/CN103480389B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention provides a kind of Catalysts and its preparation method and the application with hydrogenation catalyst effect, this catalyst contains carrier and load at least one group VIII metallic element on the carrier and at least one group vib metallic element, described group VIII metallic element and group vib metallic element are non-uniform Distribution along this catalyst radial section separately, wherein, along this catalyst radial section

Description

There is the Catalysts and its preparation method of hydrogenation catalyst effect and application and method for hydrotreating hydrocarbon oil
Technical field
The present invention relates to a kind of Catalysts and its preparation method and the application with hydrogenation catalyst effect, the invention still further relates to a kind of method for hydrotreating hydrocarbon oil.
Background technology
Outside sulphur removal, nitrogen, also containing the metal impurities such as a large amount of Ni, V, Fe, Ca and asphalitine and colloid in heavy oil.In the hydroprocessing processes of this type of feedstock oil, these impurity can be adsorbed in catalyst surface covering activated centre or be deposited in catalyst duct and block duct, thus cause the inactivation of catalyst.Therefore, for the appearance metal ability of the catalyst of heavy-oil hydrogenation processing procedure and coking resistivity, the direct life cycle etc. to catalyst is had an impact.
US4760045 discloses a kind of heavy oil hydrogenating treatment catalyst, this catalyst contains the active metal component with hydrogenation catalyst effect that porous refractory oxides carrier and load at least one are on this carrier selected from periodic table of elements VB race, group vib and group VIII, wherein, along catalyst cross section, the distribution of the concentration of described metal component meets Cr l<Cr 2and R 1>R 2, wherein, R 1and R 2represent the distance r from kernel of section to respective point respectively 1and r 2with the ratio of the distance from kernel of section to outer surface, Cr 1and Cr 2represent the concentration of the described metal component of described respective point respectively.
CN101376106B discloses a kind of heavy oil hydrogenating treatment catalyst, the at least one that this catalyst contains carrier and effective dose is selected from the metal component that group VIII and at least one are selected from group vib, wherein, the concentration of described group VIII metal component is non-uniform Distribution along catalyst radial section, wherein, the concentration of outer surface metal component is 0.1-0.85 with the ratio of the concentration of central metal component; The concentration of described group vib metal component is evenly distributed along catalyst radial section, and wherein, the concentration of outer surface metal component is 0.90-1.5 with the ratio of the concentration of central metal component.Carrier in this catalyst is aluminium oxide.
CN101462080A discloses a kind of preparation method of catalyst with non-uniform distribution of active metal component, comprise at least one adopting the method for dipping to introduce effective dose on carrier and be selected from the metal component that group VIII and at least one are selected from group vib, wherein, described dipping comprises the steps: that (1) order will be selected from nitric acid, phosphoric acid, oxalic acid, citric acid, tartaric acid, pimelic acid, one or more acid in adipic acid contain the compound of the metal component of group vib with being selected from least one, at least one is mixed into solution containing the compound of metal component of group VIII and water, wherein, the ratio of the compound molal quantity sum of the molal quantity of described acid and the metal component containing group vib and the metal component containing group VIII is 0.1-0.92, the consumption of described water makes the amount of final solution by volume be 0.85 η-1.1 η, η is the water absorption rate of carrier, (2) under room temperature with the mixed solution impregnated carrier that step (1) is prepared, dip time is 1-5 hour, (3) carrier after step (2) being flooded in being greater than 60 DEG C to 160 DEG C dry 2-10 hour, and at 400-600 DEG C of roasting 2-5 hour.
Practical application shows, above-mentioned heavy oil hydrogenating treatment catalyst has good stability in use in the hydroprocessing processes of heavy oil.
But heavily become bad along with oil property becomes, refinery has to process crude oil more inferior, therefore in the urgent need to having more high catalytic activity, better catalytic stability and the hydrogenation catalyst in longer service life.
Summary of the invention
The object of the present invention is to provide a kind of Catalysts and its preparation method with hydrogenation catalyst effect, catalyst according to the invention demonstrates higher catalytic activity, better catalytic stability and longer service life in the hydrotreatment of hydrocarbon ils (particularly heavy hydrocarbon oil).
The present inventor finds in research process, with by containing at least one hydrated alumina, carrier prepared by the raw material of at least one lithium-containing compound and at least one cellulose ether, the compound of group VIII metallic element and on this carrier compound loaded containing group vib metallic element will be contained, and (namely group VIII metallic element and group vib metallic element are distributed in " yolk " type, the active metal concentrations at catalyst center place is higher than the active metal concentrations of catalyst external surface), the catalyst formed thus demonstrates higher catalytic activity in the hydrogenation reaction of hydrocarbon ils (particularly heavy hydrocarbon oil).This completes the present invention.
A first aspect of the present invention provides a kind of catalyst with hydrogenation catalyst effect, this catalyst contains carrier and load at least one group VIII metallic element on the carrier and at least one group vib metallic element, described group VIII metallic element and group vib metallic element are non-uniform Distribution along this catalyst radial section separately, wherein, along this catalyst radial section
for group VIII metallic element is in the mean concentration of the outer surface of described catalyst;
for group VIII metallic element is in the mean concentration of the center of described catalyst;
be the mean concentration of group vib metallic element at the outer surface of described catalyst;
be the mean concentration of group vib metallic element in the center of described catalyst;
Described carrier is hydrated alumina forming matter, is made up of the raw material containing at least one hydrated alumina, at least one lithium-containing compound and at least one cellulose ether.
A second aspect of the present invention provides a kind of method preparing the catalyst with hydrogenation catalyst effect, the method is included in supported on carriers at least one group VIII metallic element and at least one group vib metallic element, load is on the carrier substantially in a salt form separately for described group VIII metallic element and group vib metallic element, wherein, described carrier is hydrated alumina forming matter, by containing at least one hydrated alumina, formed body prepared by the raw material of at least one lithium-containing compound and at least one cellulose ether, and described formed body is carried out drying at higher than 180 DEG C and not higher than the temperature of 300 DEG C and makes.
A third aspect of the present invention provides the catalyst with hydrogenation catalyst effect prepared by method of the present invention.
A fourth aspect of the present invention provides the application of catalyst according to the invention in hydrocarbon oil hydrogenation process.
A fifth aspect of the present invention provides a kind of method for hydrotreating hydrocarbon oil, and the method comprises under hydroprocessing conditions, by hydrocarbon ils and catalyst exposure of the present invention.
Catalyst according to the invention demonstrates higher catalytic activity in the HDM reaction of hydrocarbon ils (particularly heavy hydrocarbon oil).Further, use in the hydrocarbon oil hydrogenation demetalization process of catalyst of the present invention, metal trends towards the center being deposited on catalyst, and thus catalyst according to the invention has higher appearance metal ability, and then has higher stability and longer service life.
According to the preparation method with the catalyst of hydrogenation catalyst effect of the present invention, to prepare formed body by the raw material containing at least one hydrated alumina, at least one lithium-containing compound and at least one cellulose ether, and described formed body is carried out drying at higher than 180 DEG C and not higher than the temperature of 300 DEG C and the article shaped made as carrier, adopt the conventional method of this area can prepare the catalyst of active component (that is, group VIII metallic element and group vib metallic element) distribution in " yolk " type.That is, method is simple according to of the present invention.
Detailed description of the invention
A first aspect of the present invention provides a kind of catalyst with hydrogenation catalyst effect, and this catalyst contains carrier and load at least one group VIII metallic element on the carrier and at least one group vib metallic element.Term " at least one " refers to one or more.
Catalyst according to the invention is using group VIII metallic element and group vib metallic element as the active component with hydrogenation catalyst effect.
Catalyst according to the invention, the content of described group VIII metallic element and group vib metallic element can carry out suitable selection according to the embody rule occasion of catalyst.Such as, when catalyst according to the invention is used for the hydrotreatment of hydrocarbon ils (particularly heavy hydrocarbon oil), with the total amount of described catalyst for benchmark, the content of described carrier can be 70-95 % by weight, is preferably 75-93 % by weight; With oxide basis, the content of described group VIII metallic element can be 1-8 % by weight, is preferably 1.5-5 % by weight; With oxide basis, the content of described group vib metallic element can be 3-22 % by weight, is preferably 5-20 % by weight.
Catalyst according to the invention, the various elements with hydrogenation catalyst effect that described group VIII metallic element and described group vib metallic element can be commonly used for this area.Preferably, described group VIII metallic element is cobalt and/or nickel, and described group vib metallic element is molybdenum and/or tungsten.
Catalyst according to the invention, basic (that is, mainly or in fact) load is on the carrier in a salt form separately for described group VIII metallic element and described group vib metallic element.That is, described group VIII metallic element preferably with the form load of the salt containing group VIII metallic element on the carrier, and described group vib metallic element preferably with the form load of the salt containing group vib metallic element on the carrier.Also namely, preferably basic (that is, mainly or in fact) with the form load of non-oxidized substance on the carrier separately for described group VIII metallic element and described group vib metallic element.
Catalyst according to the invention, described group VIII metallic element and group vib metallic element are non-uniform Distribution along the radial section of catalyst, wherein, along this catalyst radial section,
for group VIII metallic element is in the mean concentration of the outer surface of described catalyst;
for group VIII metallic element is in the mean concentration of the center of described catalyst;
be the mean concentration of group vib metallic element at the outer surface of described catalyst;
be the mean concentration of group vib metallic element in the center of described catalyst.
Preferably, along this catalyst radial section,
More preferably, along this catalyst radial section,
In the present invention, adopt SEM and energy disperse spectroscopy (that is, SEM-EDX) to measure the distribution of metallic element along catalyst radial section, calculate metallic element at the ratio of the mean concentration of catalyst granules outer surface with the mean concentration of center.Wherein, the mean concentration of outer surface is the mean value of outer surface 20 numerical point counting rates; Mean value (the note: the counting rate along the radial every bit of carrier in SEM-EDX characterization result is mutually corresponding with this tenor of 20 the numerical point counting rates in some place centered by the mean concentration of center, the size of counting rate reflects this tenor height, but does not represent the real content of this metal).
Catalyst according to the invention, described carrier is hydrated alumina forming matter, is made up of the raw material containing at least one hydrated alumina, at least one lithium-containing compound and at least one cellulose ether.
Catalyst according to the invention, described raw material contains at least one hydrated alumina, at least one lithium-containing compound and at least one cellulose ether, but not containing peptizing agent (such as: Alumina gel, nitric acid, citric acid, oxalic acid, acetic acid, formic acid, malonic acid, hydrochloric acid and trichloroacetic acid).
Catalyst according to the invention, the composition of described raw material can carry out suitable selection according to the application scenario of catalyst.Usually, with the total amount of described raw material for benchmark, the total content of described cellulose ether can be 0.5-12 % by weight, is preferably 1-10 % by weight, is more preferably 2-8 % by weight; With Li 2the total content of the described lithium-containing compound of O meter can be 0.5-10 % by weight, is preferably 0.5-8 % by weight, is more preferably 0.5-5 % by weight; With Al 2o 3the total content of the described hydrated alumina of meter can be 78-98 % by weight, is preferably 82-98 % by weight, is more preferably 87-97 % by weight.In the present invention, when calculating the total amount of described raw material, lithium-containing compound is with Li 2o counts, and hydrated alumina is with Al 2o 3meter, and do not comprise the water introduced in described material forming process.
In the present invention, described cellulose ether refers to the ether system derivative formed after the hydrogen atom at least part of hydroxyl in cellulosic molecule is replaced by one or more alkyl, and wherein, multiple described alkyl can be identical, also can be different.Described alkyl is selected from the alkyl of replacement and unsubstituted alkyl.Described unsubstituted alkyl is preferably alkyl (such as: C 1-C 5alkyl).In the present invention, C 1-C 5the instantiation of alkyl comprise C 1-C 5straight chained alkyl and C 3-C 5branched alkyl, can for but be not limited to: methyl, ethyl, n-pro-pyl, isopropyl, normal-butyl, isobutyl group, the tert-butyl group, n-pentyl, isopentyl and tertiary pentyl.The alkyl of described replacement can be such as by the alkyl of hydroxyl or carboxyl substituted (such as: C 1-C 5the alkyl be optionally substituted by a hydroxyl group, C 1-C 5by the alkyl of carboxyl substituted), its instantiation can include but not limited to: methylol, ethoxy, hydroxypropyl, hydroxyl butyl, carboxymethyl, carboxyethyl and carboxylic propyl group.
The present invention is not particularly limited for the substituent quantity of the hydrogen atom in the kind of described cellulose ether and the hydroxyl in substituted cellulose molecule, can be common various cellulose ethers.Particularly, described cellulose ether can be selected from but be not limited to: methylcellulose, ethyl cellulose, hydroxyethylcellulose, HEMC, hydroxypropyl cellulose, hydroxypropyl methylcellulose, carboxymethyl cellulose, carboxyethyl cellulose and carboxymethyl hydroxyethyl cellulose.Preferably, described cellulose ether is selected from methylcellulose, HEMC and hydroxypropyl methylcellulose.
According to the present invention, the compound containing lithium atom in the various molecular structures that described lithium-containing compound can be commonly used for this area.Such as, described lithium-containing compound can be selected from lithium salts and the organic acid lithium salts of inorganic acid, is preferably selected from water-soluble lithium salts and the water-soluble lithium salts of organic acid of inorganic acid.Particularly, described lithium-containing compound can be selected from lithium nitrate, lithium sulfate, lithium chloride, lithium oxalate and lithium acetate.Preferably, described lithium-containing compound is selected from lithium nitrate, lithium oxalate and lithium acetate.
In the present invention, the kind of described hydrated alumina is not particularly limited, and can be that the routine of this area is selected.Preferably, described hydrated alumina is selected from boehmite, gibbsite, unformed hydrated alumina and boehmite.More preferably, described hydrated alumina is boehmite.
According to the present invention, described raw material can also can improve the various extrusion aids of the processing characteristics of described raw material containing at least one.The content of described extrusion aid can be the routine selection of this area.Preferably, with the total amount of described raw material for benchmark, the total content of described extrusion aid can be 0.1-8 % by weight, is preferably 0.5-5 % by weight.The present invention is not particularly limited for the kind of described extrusion aid, can be that the routine of this area is selected.Preferably, described extrusion aid is starch (that is, described raw material is also containing starch).As the starch in the various sources that the starch of extrusion aid can be commonly used for this area, such as: by vegetable seeds through pulverizing the powder obtained, as sesbania powder.
Catalyst according to the invention, described carrier can prepare formed body by the raw material containing at least one hydrated alumina, at least one lithium-containing compound and at least one cellulose ether, and described formed body is carried out drying prepares.The various methods that this area can be adopted conventional, to prepare described formed body, are not particularly limited.Such as: directly by least one hydrated alumina, at least one cellulose ether and at least one lithium-containing compound mixed-forming, thus described formed body can be obtained; Also can first by least one hydrated alumina and at least one cellulose ether mixed-forming, obtained preform, then load at least one lithium-containing compound on this preform, thus obtain described formed body.
One of the present invention preferred embodiment in, the method being prepared described formed body by described raw material comprises: at least one hydrated alumina, at least one lithium-containing compound and at least one cellulose ether are mixed with water, obtain the first mixture, and by shaping for described first mixture.
In another preferred embodiment of the present invention, the method being prepared described formed body by described raw material comprises: at least one hydrated alumina and at least one cellulose ether are mixed with water, obtain the second mixture, and described second mixture is successively carried out shaping and dehydration, obtain preform, load at least one lithium-containing compound on described preform.
In this embodiment, on described preform, the mode of load at least one lithium-containing compound can be the routine selection of this area, such as: can by described preform is contacted with the solution containing at least one lithium-containing compound, thus by described lithium-containing compound load on described preform.The mode contacted with described solution by described preform can be selected for the routine of this area, such as: by flooding or spraying, described preform can be contacted with the solution containing at least one lithium-containing compound, thus by described lithium-containing compound load on described preform.Adopt dipping mode by described lithium-containing compound load on described preform time, described dipping can be saturated dipping, also can flood for supersaturation.The solvent of the described solution containing at least one lithium-containing compound can be the routine selection of this area, is preferably water.The concentration of the described solution containing at least one lithium-containing compound is not particularly limited, with enable the amount of the lithium-containing compound of load on described preform meet the demands (such as previously described content) be as the criterion.
In this embodiment, the condition of described dehydration is not particularly limited, and can be that the routine of this area is selected, be as the criterion can remove water.Usually, described dehydration can be carried out lower than at the temperature of 350 DEG C more than 60 DEG C, preferably carries out at higher than 180 DEG C and not higher than the temperature of 300 DEG C, more preferably carries out at the temperature of 200-260 DEG C.The time of described dehydration can carry out suitable selection according to the temperature of dehydration, is not particularly limited.Usually, the time of described dehydration can be 1-48 hour, is preferably 2-24 hour, is more preferably 2-12 hour.
Catalyst according to the invention, the consumption for the preparation of the water of described first mixture or described second mixture is not particularly limited, as long as the consumption of water can guarantee various component to mix.
Catalyst according to the invention, described shaping mode is not particularly limited, and can adopt the various molding modes that this area is conventional, such as: extrusion, spraying, round as a ball, compressing tablet or their combination.One of the present invention preferred embodiment in, come shaping by the mode of extrusion.
Catalyst according to the invention, described carrier can have various shape according to concrete instructions for use, such as: spherical, bar shaped, annular, cloverleaf pattern, honeycombed or butterfly.
Catalyst according to the invention, the formed body prepared by the raw material containing at least one hydrated alumina, at least one lithium-containing compound and at least one cellulose ether is carried out dry condition to be not particularly limited, can be the routine selection of this area, be as the criterion with the volatile component that can remove on described formed body.Such as: the temperature of described drying can be more than 60 DEG C and lower than 350 DEG C.Preferably, described drying be greater than 180 DEG C and not higher than the temperature of 300 DEG C under carry out.More preferably, the temperature of described drying is 200-260 DEG C.The time of described drying can carry out suitable selection according to the temperature of drying, meets instructions for use be as the criterion can make volatile matter content in the article shaped that finally obtains.Usually, the time of described drying can be 1-48 hour, is preferably 2-24 hour, is more preferably 2-12 hour.
Catalyst according to the invention, described carrier has good intensity and absorbent properties.
Particularly, described carrier radial crushing strength loss late (that is, δ value) is after steeping less than 10%, can be even less than 5%.
In the present invention, δ value is used for the strength retention of evaluation carrier, is defined by following formula:
&delta; = Q 1 - Q 2 Q 1 &times; 100 % ,
Wherein, Q 1for the radial crushing strength of the carrier without water soaking, in N/mm,
Q 2for through water soaking 30 minutes and in the radial crushing strength of the carrier of 120 DEG C of dryings after 4 hours, in N/mm.
Catalyst according to the invention, Q 1can be more than 12N/mm, be even more than 15N/mm.Generally, Q 1for 15-30N/mm(is as 15-25N/mm).
In the present invention, described radial crushing strength according to " Petrochemical Engineering Analysis method " (Science Press, nineteen ninety the first edition, the volumes such as Yang Cuiding) in the RIPP 25-90 that records the method that specifies measure.
Catalyst according to the invention, the water absorption rate of described carrier is 0.4-1.5, is generally 0.6-1(as 0.6-0.8).
In the present invention, described water absorption rate refers to that the dry excessive deionized water of carrier soaks the ratio of the weight of the weight change value of 30 minutes front and back and the carrier of described drying.Concrete method of testing is: by carrier to be measured 120 DEG C of dryings 4 hours, then sieves with 40 object standard screens, takes 20g oversize and (be designated as w as testing sample 1), testing sample 50g deionized water is soaked 30 minutes, after filtration, solid phase is drained 5 minutes, the weight then weighing the solid phase drained (is designated as w 2), with following formulae discovery water absorption rate:
Catalyst according to the invention, described catalyst can also can improve the component of the catalytic performance of catalyst containing at least one, such as: P elements.The present invention is not particularly limited for the described content that can improve the component of the catalytic performance of catalyst, can be that the routine of this area is selected.Preferably, with the total amount of catalyst for benchmark, with oxide basis, the described content that can improve the component of the catalytic performance of catalyst is 0.1-10 % by weight.More preferably, with the total amount of catalyst for benchmark, with oxide basis, the described content that can improve the component of the catalytic performance of catalyst is 0.5-5 % by weight.
Catalyst according to the invention can adopt this area to be usually used in preparing the method preparation of active component distribution in " yolk " type.The present inventor finds in research process, formed body is prepared by the raw material containing at least one hydrated alumina, at least one lithium-containing compound and at least one cellulose ether at the carrier of the active component for load with hydrogenation catalyst effect, and when described formed body being carried out drying at higher than 180 DEG C and not higher than the temperature of 300 DEG C and makes, adopt conventional method by described active constituent loading on this carrier, the catalyst that active component distributes in " yolk type " can be obtained.
Thus, a second aspect of the present invention provides a kind of preparation method with the catalyst of hydrogenation catalyst effect, the method is included in supported on carriers at least one group VIII metallic element and at least one group vib metallic element, load is on the carrier substantially in a salt form for described group VIII metallic element and group vib metallic element, wherein, described carrier is hydrated alumina forming matter, by containing at least one hydrated alumina, formed body prepared by the raw material of at least one lithium-containing compound and at least one cellulose ether, and described formed body is carried out drying at higher than 180 DEG C and not higher than the temperature of 300 DEG C and makes.
According to method of the present invention, described group VIII metallic element and group vib metallic element load capacity on the carrier, to make in the catalyst of final preparation, the content of group VIII metallic element and group vib metallic element can meet concrete instructions for use and be as the criterion.Such as, when catalyst according to the invention is used for carrying out hydrotreatment to hydrocarbon ils (particularly heavy hydrocarbon oil), described group vib metallic element and group VIII metallic element load capacity on the carrier make, with the total amount of the catalyst finally prepared for benchmark, the content of described carrier can be 70-95 % by weight, is preferably 75-93 % by weight; With oxide basis, the content of described group VIII metallic element can be 1-8 % by weight, is preferably 1.5-5 % by weight; The content of described group vib metallic element can be 3-22 % by weight, is preferably 5-20 % by weight.
According to method of the present invention, described group VIII metallic element is preferably cobalt and/or nickel, and described group vib metallic element is preferably molybdenum and/or tungsten.
According to method of the present invention, basic (that is, mainly or in fact) load is on the carrier in a salt form separately for described group VIII metallic element and described group vib metallic element.Also namely, basic (that is, mainly or in fact) with the form load of non-oxidized substance on the carrier separately for described group VIII metallic element and described group vib metallic element.
The various modes that this area can be adopted conventional by described group VIII metallic element and described group vib metallic element substantially with the form load of salt (that is, substantially with non-oxidized substance) on the carrier, such as: dipping.Described dipping can be saturated dipping, also can be excessive dipping.According to method of the present invention, can on the carrier by group VIII metallic element and the load of group vib metallic element simultaneously, also can gradation by described group VIII metallic element and the load of described group vib metallic element on the carrier.
In one embodiment of the invention, by described group VIII metallic element and described group vib metallic element substantially with salt (namely, basic with non-oxidized substance) form load mode on the carrier comprise: with containing at least one containing the salt of group VIII metallic element and at least one containing the compound of group vib metallic element aqueous impregnation described in carrier, and carry out drying by flooding the carrier obtained.
In another embodiment of the invention, by described group VIII metallic element and described group vib metallic element substantially with salt (namely, basic with non-oxidized substance) form load mode on the carrier comprise: with containing at least one containing the salt of group VIII metallic element aqueous impregnation described in carrier, and carry out drying by flooding the carrier obtained, there is the carrier of the described salt containing group VIII metallic element with the aqueous impregnation load of the compound containing group vib metallic element containing at least one, and carry out drying by flooding the carrier obtained.
In another embodiment of the present invention, by described group VIII metallic element and described group vib metallic element substantially with salt (namely, basic with non-oxidized substance) form load mode on the carrier comprise: with containing at least one containing the compound of group vib metallic element aqueous impregnation described in carrier, and carry out drying by flooding the carrier obtained, there is the carrier of the described compound containing group vib metallic element with the aqueous impregnation load of the salt containing group VIII metallic element containing at least one, and carry out drying by flooding the carrier obtained.
According to the present invention, the various water soluble salts containing group VIII metallic element that the described salt containing group VIII metallic element can be commonly used for this area, such as: the described salt containing group VIII metallic element can be selected from the water-soluble group VIII slaine of inorganic acid, the water-soluble group VIII slaine of organic acid and the water-insoluble compound containing group VIII metallic element and contact with sour (as phosphoric acid) and/or alkali (as ammoniacal liquor) water soluble salt formed in water.
Particularly, the described salt containing group VIII metallic element can be selected from but be not limited to: the water soluble salt that cobalt nitrate, cobalt acetate, basic cobaltous carbonate contact with acid (as phosphoric acid) and/or alkali (as ammoniacal liquor) and formed in water, cobalt chloride, aqueous cobalt complex compound, nickel nitrate, nickel acetate, basic nickel carbonate contact with acid (as phosphoric acid) and/or alkali (as ammoniacal liquor) water soluble salt, nickel chloride and the water-soluble nickel complex that are formed in water.Described aqueous cobalt complex compound can be such as Cobalt Edetate; Described water-soluble nickel complex can be such as citric acid nickel.Preferably, the described salt containing group VIII metallic element is selected from cobalt nitrate, basic cobaltous carbonate and in water, contact the water soluble salt, the basic nickel carbonate that are formed with acid (as phosphoric acid) and/or alkali (as ammoniacal liquor) contact with sour (as phosphoric acid) and/or alkali (as ammoniacal liquor) water soluble salt and nickel nitrate that are formed in water.
According to the present invention, the described kind containing the compound of group vib metallic element is not particularly limited, can be the conventional water soluble compound containing group vib metallic element of this area, such as can be selected from the water-soluble group vib slaine of inorganic acid, the water-soluble group vib slaine of organic acid, containing group vib metallic element heteropoly acid, in water, contact with acid (as phosphoric acid) or alkali the water soluble compound formed containing the heteropolyacid salt of group vib metallic element and the oxide of group vib metal.
Particularly, the described compound containing group vib metallic element can be selected from the water soluble salt of molybdic acid, the water soluble salt of para-molybdic acid, ammonium tungstate, ammonium metatungstate, ammonium paratungstate, ethyl ammonium metatungstate, phosphotungstic acid, phosphomolybdic acid, phosphotungstic acid nickel, phosphotungstic acid cobalt, silico-tungstic acid nickel, silico-tungstic acid cobalt, phosphomolybdic acid nickel, phosphomolybdic acid cobalt, P-Mo-Wo acid nickel, P-Mo-Wo acid cobalt, silicomolybdic acid nickel, silicomolybdic acid cobalt, silicon molybdenum nickel tungstate, silicon molybdenum cobaltous tungstate and molybdenum oxide in water, contact the water soluble compound formed with phosphoric acid.In the present invention, the water soluble salt of described molybdic acid comprises water-soluble metal salt and the ammonium molybdate of molybdic acid; The water soluble compound of described para-molybdic acid comprises water-soluble metal salt and the ammonium paramolybdate of para-molybdic acid.Preferably, the described salt containing group vib metallic element is selected from ammonium molybdate, ammonium paramolybdate, ammonium metatungstate, ammonium tungstate and molybdenum oxide in water, contacts the water soluble compound formed with phosphoric acid.
According to method of the present invention, concentration for the described aqueous solution is also not particularly limited, as long as can make in the catalyst of final preparation, the content of group VIII metallic element and group vib metallic element meets instructions for use (such as previously described requirement).
According to method of the present invention, under the condition can commonly used in this area, carry out drying by flooding the carrier obtained.Usually, the condition of described drying comprises: temperature can be 100-200 DEG C, is preferably 120-150 DEG C; Time can be 1-15 hour, is preferably 3-10 hour.
According to method of the present invention, described carrier prepares formed body by the raw material containing at least one hydrated alumina, at least one lithium-containing compound and at least one cellulose ether, and described formed body is carried out drying at higher than 180 DEG C and not higher than the temperature of 300 DEG C and makes.Preferably, the temperature of described drying is 200-260 DEG C.
According to method of the present invention, the time of described drying can carry out suitable selection as the case may be, is as the criterion with the volatile ingredient that can remove on carrier.Such as, the time of described drying can be 1-48 hour, is preferably 2-24 hour, is more preferably 2-12 hour.
According to method of the present invention, described raw material contains at least one hydrated alumina, at least one lithium-containing compound and at least one cellulose ether, but not containing peptizing agent (such as: Alumina gel, nitric acid, citric acid, oxalic acid, acetic acid, formic acid, malonic acid, hydrochloric acid and trichloroacetic acid).
According to method of the present invention, the composition of described raw material can carry out suitable selection according to the application scenario of catalyst.Usually, with the total amount of described raw material for benchmark, the total content of described cellulose ether can be 0.5-12 % by weight, is preferably 1-10 % by weight, is more preferably 2-8 % by weight; With Li 2the total content of the described lithium-containing compound of O meter can be 0.5-10 % by weight, is preferably 0.5-8 % by weight, is more preferably 0.5-5 % by weight; With Al 2o 3the total content of the described hydrated alumina of meter can be 78-98 % by weight, is preferably 82-98 % by weight, is more preferably 87-97 % by weight.
According to method of the present invention, the kind of described cellulose ether, described lithium-containing compound and described hydrated alumina is described in detail above, does not repeat them here.
According to method of the present invention, described raw material can also contain at least one extrusion aid.The content of described extrusion aid can be the routine selection of this area.Preferably, with the total amount of described raw material for benchmark, the total content of described extrusion aid can be 0.1-8 % by weight, is preferably 0.5-5 % by weight.The present invention is not particularly limited for the kind of described extrusion aid, can be that the routine of this area is selected.Preferably, described extrusion aid is starch (that is, described raw material is also containing starch).As the starch in the various sources that the starch of extrusion aid can be commonly used for this area, such as: by vegetable seeds through pulverizing the powder obtained, as sesbania powder.
Method according to the present invention is by preparing formed body by by the raw material containing at least one hydrated alumina, at least one lithium-containing compound and at least one cellulose ether, and the article shaped of described formed body being carried out drying and preparing carrys out Kaolinite Preparation of Catalyst as carrier.The various methods that this area can be adopted conventional, to prepare described formed body, are not particularly limited.Such as: directly by least one hydrated alumina, at least one cellulose ether and at least one lithium-containing compound mixed-forming, thus described formed body can be obtained; Also can first by least one hydrated alumina and at least one cellulose ether mixed-forming, obtained preform, then load at least one lithium-containing compound on this preform, thus obtain described formed body.
One of the present invention preferred embodiment in, the method being prepared described formed body by described raw material comprises: at least one hydrated alumina, at least one lithium-containing compound and at least one cellulose ether are mixed with water, obtain the first mixture, and by shaping for described first mixture.
In another preferred embodiment of the present invention, the method being prepared described formed body by described raw material comprises: at least one hydrated alumina and at least one cellulose ether are mixed with water, obtain the second mixture, and described second mixture is successively carried out shaping and dehydration, obtain preform, at described preform load at least one lithium-containing compound.
In this embodiment, the various methods that this area can be adopted conventional by described lithium-containing compound load on described preform, such as: described preform can be contacted with the solution containing at least one lithium-containing compound, thus by described lithium-containing compound load on the carrier.The mode contacted with the solution containing at least one lithium-containing compound by described preform can be selected for the routine of this area, such as: by flooding or spraying, described preform can be contacted with the solution containing at least one lithium-containing compound, thus by described lithium-containing compound load on described preform.Adopt dipping mode by described lithium-containing compound load on described preform time, described dipping can be saturated dipping, also can flood for supersaturation.The solvent of the described solution containing at least one lithium-containing compound can be the routine selection of this area, is preferably water.The concentration of the described solution containing at least one lithium-containing compound is not particularly limited, with enable the amount of the lithium-containing compound of load on described preform meet the demands (such as previously described content) be as the criterion.
In this embodiment, the condition of described dehydration is not particularly limited, and can be that the routine of this area is selected, be as the criterion can remove water.Usually, described dehydration is carried out at higher than 180 DEG C and not higher than the temperature of 300 DEG C, preferably carries out at the temperature of 200-260 DEG C.The time of described dehydration can carry out suitable selection according to the temperature of dehydration, is not particularly limited.Usually, the time of described dehydration can be 1-48 hour, is preferably 2-24 hour, is more preferably 2-12 hour.
According to method of the present invention, the consumption for the preparation of the water of described first mixture or described second mixture is not particularly limited, as long as the consumption of water can guarantee various component to mix.
According to method of the present invention, described shaping method is not particularly limited, and can adopt the various molding modes that this area is conventional, such as: extrusion, spraying, round as a ball, compressing tablet or their combination.One of the present invention preferred embodiment in, come shaping by the mode of extrusion.
According to method of the present invention, described carrier can have various shape according to concrete instructions for use, such as: spherical, bar shaped, annular, cloverleaf pattern, honeycombed or butterfly.
According to method of the present invention, can also comprise and introduce the component that at least one can improve the catalytic performance of the catalyst of final preparation on described carrier, such as: P elements.By before group VIII metallic element described in load and group vib metallic element, described component can be introduced on described carrier; Also can while group VIII metallic element described in load and group vib metallic element, by described component load on the carrier.The described introduction volume can improving the component of the performance of catalyst can be selected for the routine of this area.Usually, the described introduction volume can improving the component of the performance of catalyst makes in the catalyst of final preparation, and with oxide basis, the content of described component is 0.1-10 % by weight, is preferably 0.5-5 % by weight.
In prepared according to the methods of the invention catalyst, there is group vib metallic element and the distribution in " yolk " type of group VIII metallic element of hydrogenation catalyst effect, in the hydrotreatment of hydrocarbon ils (particularly heavy hydrocarbon oil), show higher activity.
Thus, a third aspect of the present invention provides a kind of catalyst prepared by method of the present invention.
Prepared according to the methods of the invention catalyst, described group VIII metallic element and group vib metallic element are non-uniform Distribution along the radial section of catalyst, wherein, along this catalyst radial section,
for group VIII metallic element is in the mean concentration of the outer surface of described catalyst;
for group VIII metallic element is in the mean concentration of the center of described catalyst;
be the mean concentration of group vib metallic element at the outer surface of described catalyst;
be the mean concentration of group vib metallic element in the center of described catalyst.
Preferably, along this catalyst radial section,
More preferably, along this catalyst radial section,
Catalyst according to the invention demonstrates higher catalytic activity, better stability and longer service life in the hydrotreatment of hydrocarbon ils (particularly heavy hydrocarbon oil).
Thus, a fourth aspect of the present invention provides the application of a kind of catalyst according to the invention in hydrocarbon oil hydrogenation process.
A fifth aspect of the present invention provides a kind of method for hydrotreating hydrocarbon oil, and the method comprises under hydroprocessing conditions, by hydrocarbon ils and catalyst exposure of the present invention.
In the present invention, described hydrocarbon ils can for the various hydrocarbon raw material carrying out hydrotreatment that needs, and being preferably variously needs the heavier hydrocarbon feeds of carrying out HDM process.Particularly, described hydrocarbon ils can be crude oil, reduced crude and decompression residuum.
Method for hydrotreating hydrocarbon oil according to the present invention is by by hydrocarbon ils and catalyst exposure provided by the invention, and with higher efficiency, hydrotreatment is carried out to hydrocarbon ils, all the other conditions for hydrotreatment are not particularly limited, can according to pending hydrocarbon oil properties, the Conventional wisdom according to this area carries out suitable selection.Such as, when described hydrocarbon ils is heavy hydrocarbon oil, described hydroprocessing condition comprises: temperature can be 300-450 DEG C, is preferably 330-400 DEG C; Hydrogen dividing potential drop can be 5-20MPa, is preferably 6-18MPa; The volume space velocity of hydrocarbon ils can be 0.1-3.0 hour -1, be preferably 0.15-2 hour -1; Hydrogen to oil volume ratio can be 200-2500, is preferably 300-2000.
According to method for hydrotreating hydrocarbon oil of the present invention, described catalyst before the use, can carry out presulfurization under the normal condition of this area.The condition of presulfurization can be such as in presence of hydrogen, at the temperature of 140-370 DEG C, carry out presulfurization with sulphur, hydrogen sulfide or sulfur-bearing raw material, and described presulfurization can be carried out outside reactor also can be In-situ sulphiding in reactor.
The present invention is described in detail below in conjunction with embodiment and comparative example.
In following examples and comparative example, the method specified in RIPP 25-90 is adopted to measure the radial crushing strength of carrier.
In following examples and comparative example, following methods is adopted to measure the δ value of carrier: to adopt the method mensuration that specifies in RIPP 25-90 (to be designated as Q without the radial crushing strength of the carrier of water soaking 1); Carrier is placed in 50g deionized water, soaks 30 minutes, then filter, by the solid that obtains at the temperature of 120 DEG C dry 4 hours, the radial crushing strength measuring dry solid according to the method specified in RIPP 25-90 (was designated as Q 2), adopt following formulae discovery δ value,
&delta; = Q 1 - Q 2 Q 1 &times; 100 % .
In following examples and comparative example, following methods is adopted to measure the water absorption rate of carrier: by carrier to be measured 120 DEG C of dryings 4 hours, then to sieve with 40 object standard screens, take 20g oversize and (be designated as w as testing sample 1), testing sample 50g deionized water is soaked 30 minutes, after filtration, solid phase is drained 5 minutes, the weight then weighing the solid phase drained (is designated as w 2), with following formulae discovery water absorption rate:
In following examples and comparative example, contents on dry basis is by measuring testing sample 600 DEG C of roastings 4 hours.
In following examples and comparative example, measure forming of catalyst by x-ray fluorescent spectrometry (that is, XRF).
In following examples and comparative example, adopt SEM and energy disperse spectroscopy (namely, SEM-EDX) measure the distribution of metallic element along catalyst radial section, calculate metallic element at the ratio of the mean concentration of catalyst granules outer surface with the mean concentration of center.Wherein, the mean concentration of outer surface is the mean value of outer surface 20 numerical point counting rates; Mean value (the note: the counting rate along the radial every bit of carrier in SEM-EDX characterization result is mutually corresponding with this tenor of 20 the numerical point counting rates in some place centered by the mean concentration of center, the size of counting rate reflects this tenor height, but does not represent the real content of this metal).
Embodiment 1-10 is for illustration of Catalysts and its preparation method of the present invention and application.
Embodiment 1
(1) with stirring 5.0g LiNO 3be dissolved in 95mL deionized water, obtain containing the lithium aqueous solution.By 100.0g boehmite powder (purchased from Sinopec catalyst Chang Ling branch company, contents on dry basis is 69.5 % by weight), 4.0g methylcellulose (purchased from Zhejiang Hai Shen Chemical Co., Ltd.), 3.0g sesbania powder and above-mentioned containing lithium aqueous solution even.The mixture obtained is sent in extruder and extrudes, obtain wet bar.The wet bar extruded is placed in baking oven, 200 DEG C of dryings 6 hours, thus obtains carrier.Measure the radial crushing strength of the carrier obtained, water absorption rate and δ value, result is listed in Table 1.
(2) 4.71g basic nickel carbonate (NiO content is 51 % by weight), 12.0g molybdenum oxide and 1.12g phosphoric acid are dissolved in the water, are mixed with 60mL solution; The carrier (diameter is 1.1mm, and particle length is 2-5mm, and contents on dry basis is 71.0 % by weight) the solution impregnation 20.0g step (1) obtained prepared, dip time is 4 hours.After filtration, by the solid product that obtains in 120 DEG C of dryings 4 hours, obtain catalyst B 1 of the present invention, its composition illustrates in table 2.
Comparative example 1
(1) with stirring 5.0g LiNO 3be dissolved in 95mL deionized water, obtain containing the lithium aqueous solution.100.0g boehmite powder (purchased from Sinopec catalyst Chang Ling branch company, contents on dry basis is 69.5 % by weight), 2.5mL red fuming nitric acid (RFNA), 3.0g sesbania powder and the above-mentioned lithium-containing solution of 95mL are mixed.The mixture obtained is sent in extruder and extrudes, obtain wet bar.The wet bar extruded is placed in baking oven, and 200 DEG C of dryings 6 hours, then 600 DEG C of roastings 4 hours, thus obtain carrier, measure its radial crushing strength, water absorption rate and δ value, result is listed in Table 1.
(2) 4.71g basic nickel carbonate (with embodiment 1), 12.0g molybdenum oxide and 1.12g phosphoric acid are dissolved in the water, are mixed with 60mL solution.The carrier (diameter is 1.1mm, and particle length is 2-5mm) the solution impregnation 14.40g step (1) obtained prepared, dip time is 4 hours.By the solid product that obtains in 120 DEG C of dryings 4 hours, obtain catalyst A 1, its composition is listed in table 2.
Comparative example 2
(1) method identical with comparative example 1 is adopted to prepare carrier, unlike, do not carry out roasting at 600 DEG C, thus obtain carrier.Measure the radial crushing strength of the carrier obtained, water absorption rate and δ value, result is listed in Table 1.
(2) the method Kaolinite Preparation of Catalyst identical with comparative example 1 is adopted, unlike, carrier is carrier prepared by comparative example 2 step (1), and in dipping process, the phenomenon of dissolving and structure collapses appears in carrier, and the catalyst A 2 obtained cannot use as preformed catalyst.
Comparative example 3
Adopt the method Kaolinite Preparation of Catalyst identical with embodiment 1, unlike, in step (1), the wet bar extruded is placed in baking oven, 175 DEG C of dryings 12 hours, thus obtain carrier, the catalyst obtained is designated as A3, and its composition is listed in table 2.
Comparative example 4
Adopt the method Kaolinite Preparation of Catalyst identical with embodiment 1, unlike, in step (1), the wet bar extruded is placed in baking oven, 200 DEG C of dryings 6 hours, then 500 DEG C of roastings 3 hours, thus obtaining carrier, the catalyst obtained is designated as A4, and its composition is listed in table 2.
Comparative example 5
Adopt the method Kaolinite Preparation of Catalyst identical with embodiment 1, unlike, in step (2), the solid product obtained after 4 hours, then 500 DEG C of roastings 3 hours, thus is obtained catalyst in 120 DEG C of dryings, the catalyst obtained is designated as A5, and its composition is listed in table 2.
Embodiment 2
(1) in the retort of a 2L with and the mode of flowing adds aluminum sulfate solution that 2000mL concentration is 48g/L and sodium aluminate solution that (alumina content is for 200g/L, causticity coefficient is 1.58) carry out precipitation reaction, reaction temperature is 50 DEG C, and pH value is 6.0, and reaction time is 15 minutes; The slurries vacuum filter obtained is filtered, to be filtered complete after, on filter cake supplement add 20L deionized water (temperature is 40 ± 5 DEG C) flush cake about 60 minutes.Filter cake after washing is joined 1.5L deionized water for stirring and becomes slurries, slurries are carried out drying with being pumped into spray dryer, control the outlet temperature of spray dryer within the scope of 100-110 DEG C, the dry materials time is 2 minutes, obtain hydrated alumina, wherein, alumina content is 63 % by weight, is defined as amorphous state through XRD analysis.
(2) with stirring 3.0g LiNO 3be dissolved in 95mL deionized water and obtain containing the lithium aqueous solution.Unformed hydrated alumina 50.0g boehmite (purchased from Sinopec catalyst Chang Ling branch company, contents on dry basis is 69.5 % by weight), 50.0g step (1) prepared, 2.0g methylcellulose (purchased from Zhejiang Hai Shen Chemical Co., Ltd.), 3.0g HEMC (purchased from Shanghai Hui Guang Fine Chemical Co., Ltd) and the above-mentioned lithium aqueous solution that contains stir.The mixture obtained is sent in extruder and extrudes, obtain wet bar.The wet bar obtained is placed in baking oven, 220 DEG C of dryings 6 hours, thus obtains carrier.Measure the radial crushing strength of the carrier obtained, water absorption rate and δ value, result is listed in Table 1.
(3) 1.18g basic nickel carbonate (NiO content is 51 % by weight), 3.00g molybdenum oxide and 0.28g phosphoric acid are dissolved in the water, are mixed with 60mL nickel-molybdenum-phosphorus solution.The carrier (diameter is 1.1mm, and particle length is 2-5mm, and contents on dry basis is 71.3 % by weight) the solution impregnation 20.0g step (2) obtained prepared, dip time is 4 hours.After filtration, by the solid that obtains in 120 DEG C of dryings 4 hours, obtain catalyst B 2 of the present invention, its composition is listed in table 2.
Embodiment 3
(1) with at the temperature being stirred in 60 DEG C, 9.8g lithium oxalate is dissolved in 95mL deionized water, prepares containing the lithium aqueous solution.By 60.0g boehmite (purchased from Sinopec catalyst Chang Ling branch company, contents on dry basis is 69.5 % by weight), 40.0g gibbsite (purchased from Pingguo Aluminium Industry Co., Guangxi, contents on dry basis is 64.5 % by weight), 1.0g methylcellulose (purchased from Zhejiang Hai Shen Chemical Co., Ltd.), 2.0g hydroxypropyl methylcellulose (purchased from Zhejiang Hai Shen Chemical Co., Ltd.), 3.0g sesbania powder and above-mentionedly to stir containing the lithium aqueous solution.The mixture obtained is sent in extruder and extrudes, obtain wet bar.The wet bar obtained is placed in baking oven, 200 DEG C of dryings 12 hours, thus obtains carrier.Measure the radial crushing strength of the carrier obtained, water absorption rate and δ value, result is listed in Table 1.
(2) 0.34g basic cobaltous carbonate (CoO content is 70 % by weight), 1.2g molybdenum oxide and 0.11g phosphoric acid are dissolved in the water, are mixed with 60mL nickel-molybdenum-phosphorus solution.The carrier (diameter is 1.1mm, and particle length is 2-5mm, and contents on dry basis is 69.7 % by weight) the solution impregnation 20.0g step (1) obtained prepared, dip time is 1 hour.After filtration, by the solid that obtains in 120 DEG C of dryings 4 hours, obtain catalyst B 3 of the present invention, its composition is listed in table 2.
Embodiment 4
(1) with stirring, 2.0g lithium acetate being dissolved in 90mL deionized water, preparing containing the lithium aqueous solution.100.0g boehmite SB powder (purchased from Sasol company, contents on dry basis is 75.0 % by weight), 3.0g HEMC (purchased from Shanghai Hui Guang Fine Chemical Co., Ltd) and the above-mentioned lithium aqueous solution that contains are stirred.The mixture obtained is sent in extruder and extrudes, obtain wet bar.The wet bar obtained is placed in baking oven, 300 DEG C of dryings 2 hours, thus obtains carrier.Measure the radial crushing strength of the carrier obtained, water absorption rate and δ value, result is listed in Table 1.
(2) by 2.71g nickel nitrate (Ni (NO 3) 26H 2and 4.11g ammonium metatungstate ((NH O) 4) 6w 7o 244H 2o) be dissolved in the water, be mixed with 18.0mL nickel tungsten solution.The carrier (diameter is 1.1mm, and particle length is 2-5mm, contents on dry basis 68.5 % by weight) the solution impregnation 20.0g step (1) obtained prepared, dip time is 1 hour.After filtration, by the solid product that obtains in 120 DEG C of dryings 4 hours, obtain catalyst B 4 of the present invention, its composition is listed in table 2.
Comparative example 6
Adopt the method Kaolinite Preparation of Catalyst identical with embodiment 4, unlike, in step (1), the wet bar obtained is placed in baking oven, 330 DEG C of dryings 2 hours, thus obtains carrier, and then obtain catalyst A 6, its composition is listed in table 2.
Embodiment 5
(1) by 100.0g boehmite SB powder (purchased from Sasol company, contents on dry basis is 75.0 % by weight), 3.0g HEMC (purchased from Shanghai Hui Guang Fine Chemical Co., Ltd), 2.0g hydroxypropyl methylcellulose (purchased from Shanghai Hui Guang Fine Chemical Co., Ltd), 3.0g sesbania powder, 6.0gLiNO 3mix with 90mL water.The mixture obtained is sent in extruder and extrudes, obtain wet bar.The wet bar obtained is placed in baking oven, 250 DEG C of dryings 4 hours, thus obtains carrier.Measure the radial crushing strength of the carrier obtained, water absorption rate and δ value, result is listed in Table 1.
(2) 0.78g basic nickel carbonate (NiO content is 51 % by weight), 2.0g molybdenum oxide and 0.19g phosphoric acid are dissolved in the water, are mixed with 60mL nickel-molybdenum-phosphorus solution.The carrier (diameter is 1.1mm, and particle length is 2-5mm, and contents on dry basis is 77.3 % by weight) the solution impregnation 18.1g step (1) obtained prepared, dip time is 4 hours.After filtration, by the solid that obtains in 130 DEG C of dryings 6 hours, obtain catalyst B 5 of the present invention, its composition is listed in table 2.
Embodiment 6
(1) at the temperature of 50 DEG C, with stirring 8.0g LiNO 3be dissolved in 90mL deionized water, prepare containing the lithium aqueous solution.By 100.0g boehmite (purchased from Yantai, Shandong Heng Hui Chemical Co., Ltd., contents on dry basis is 71.0 % by weight), 5.0g hydroxypropyl methylcellulose (purchased from Shanghai Hui Guang Fine Chemical Co., Ltd), 3.0g sesbania powder and above-mentioned containing lithium aqueous solution even.The mixture obtained is sent in extruder and extrudes, obtain wet bar.The wet bar obtained is placed in baking oven, 190 DEG C of dryings 4 hours, thus obtains carrier.Measure the radial crushing strength of the carrier obtained, water absorption rate and δ value, result is listed in Table 1.
(2) 1.76g basic nickel carbonate (NiO content is 51 % by weight), 4.50g molybdenum oxide and 0.42g phosphoric acid are dissolved in the water, are mixed with 60mL nickel-molybdenum-phosphorus solution.The carrier (diameter is 1.1mm, and particle length is 2-5mm, and contents on dry basis is 67.7 % by weight) the solution impregnation 20.0g step (1) obtained obtained, dip time is 4 hours.After filtration, by the solid product that obtains in 150 DEG C of dryings 3 hours, obtain catalyst B 6 of the present invention, its composition is listed in table 2.
Embodiment 7
(1) method identical with embodiment 2 is adopted to prepare carrier, unlike, the content of methylcellulose is 4.0g.The radial crushing strength of the carrier obtained, water absorption rate and δ value are listed in Table 1.
(2) adopting the method Kaolinite Preparation of Catalyst identical with embodiment 2, is that (diameter is 1.1mm to the carrier prepared of 19.8g embodiment 7 step (1) unlike, carrier, particle length is 2-5mm, contents on dry basis is 72.2 % by weight), obtain catalyst B 7 of the present invention, its composition is listed in table 2.
Embodiment 8
(1) 100.0g boehmite powder (purchased from Sinopec catalyst Chang Ling branch company, contents on dry basis is 69.5 % by weight), 4.0g methylcellulose (purchased from Zhejiang Hai Shen Chemical Co., Ltd.) and 3.0g sesbania powder are mixed.The mixture obtained is sent in extruder and extrudes, obtain wet bar.The wet bar extruded is placed in baking oven, 185 DEG C of dryings 6 hours.
At the temperature of 50 DEG C, with stirring 8.0g LiNO 3be dissolved in 90mL deionized water, prepare containing the lithium aqueous solution.Take 50.0g shaping and drying bar, put into above-mentioned containing the lithium aqueous solution, soak after 4 hours and filter, 200 DEG C of dryings 6 hours, thus obtain carrier.Measure the radial crushing strength of the carrier obtained, water absorption rate and δ value, result is listed in Table 1.
(2) adopting the method Kaolinite Preparation of Catalyst identical with embodiment 1, is that (diameter is 1.1mm to the carrier prepared of 20.0g embodiment 8 step (1) unlike, carrier, particle length is 2-5mm, contents on dry basis is 70.5 % by weight), obtain catalyst B 8 of the present invention, its composition is listed in table 2.
Embodiment 9
(1) method identical with embodiment 4 step (1) is adopted to prepare carrier, unlike, the wet bar obtained is placed in baking oven, 260 DEG C of dryings 2 hours, thus obtains carrier.Measure the radial crushing strength of the carrier obtained, water absorption rate and δ value, result is listed in Table 1.
(2) the method Kaolinite Preparation of Catalyst identical with embodiment 4 step (2) is adopted, unlike, carrier is that (diameter is 1.1mm to the carrier prepared of embodiment 9 step (1), particle length is 2-5mm, contents on dry basis is 79.4 % by weight), obtain catalyst B 9 of the present invention, its composition is listed in table 2.
Embodiment 10
(1) method identical with embodiment 6 step (1) is adopted to prepare carrier, unlike, the wet bar obtained is placed in baking oven, 200 DEG C of dryings 4 hours, thus obtains carrier.Measure the radial crushing strength of the carrier obtained, water absorption rate and δ value, result is listed in Table 1.
(2) the method Kaolinite Preparation of Catalyst identical with embodiment 6 step (2) is adopted, unlike, carrier is that (diameter is 1.1mm to the carrier prepared of embodiment 10 step (1), particle length is 2-5mm, contents on dry basis is 76.5 % by weight), obtain catalyst B 10 of the present invention, its composition is listed in table 2.
Table 1
Numbering Crushing strength (N/mm) Water absorption rate δ value (%)
Embodiment 1 24.5 0.66 2.9
Comparative example 1 26.1 0.88 2.1
Comparative example 2 19.1 0.67 64.0
Comparative example 3 24.2 0.64 3.0
Comparative example 4 25.1 0.82 2.3
Comparative example 5 24.5 0.66 2.9
Embodiment 2 21.2 0.78 3.2
Embodiment 3 20.8 0.71 2.1
Embodiment 4 22.3 0.74 2.5
Comparative example 6 22.5 0.77 3.2
Embodiment 5 23.5 0.75 3.5
Embodiment 6 24.3 0.64 3.1
Embodiment 7 25.5 0.65 3.1
Embodiment 8 21.5 0.67 3.4
Embodiment 9 24.6 0.70 1.9
Embodiment 10 25.1 0.65 2.2
The result display of table 1, the carrier in catalyst according to the invention has good strength retention, even if crushing strength still higher after soaking in water.
Table 2
Embodiment 11-20 is for illustration of catalyst of the present invention and application thereof and method for hydrotreating hydrocarbon oil.
Embodiment 11-20
In sand, subtract slag evaluate catalyst prepared by embodiment 1-10 respectively as feedstock oil, feedstock oil character is listed in table 3.Evaluate and carry out in the autoclave device being equipped with magnetic agitation.
Reaction condition comprises: agent oil quality ratio is 0.05, and reaction temperature is 380 DEG C, and reaction initial pressure is 8MPa, reacts sample analysis after 6 hours.Nickel in the oil adopting plasma emission spectrum (AES/ICP) method assaying reaction to generate, the content of vanadium.By the total demetallization per of following formulae discovery, result is listed in table 4.
Adopt SEM-EDX to characterize the distribution of vanadium on catalyst radial section that reacted catalyst deposits, and calculate the ratio (V of the mean concentration of the center of the mean concentration of vanadium on the outer surface of catalyst and catalyst outer surface/ V center), result is listed in table 4.
Comparative example 7-11
Adopt the performance of the catalyst prepared in the method evaluation comparative example 1 identical with embodiment 11-20 and comparative example 3-6, result is listed in table 4.
Table 3
Density (20 DEG C)/gcm -3 1.04
Carbon residue/wt% 25.68
Sulfur content/wt% 7.23
Nickel content/wppm 73.9
Content of vanadium/wppm 183.4
Table 4
Embodiment is numbered Catalyst is numbered Total metal removal rate/% V Outer surface/V Center
Embodiment 11 B1 76 0.55
Comparative example 7 A1 63 1.33
Comparative example 8 A3 71 1.06
Comparative example 9 A4 65 1.25
Comparative example 10 A5 74 1.14
Embodiment 12 B2 89 0.55
Embodiment 13 B3 69 0.75
Embodiment 14 B4 84 0.60
Comparative example 11 A6 68 1.05
Embodiment 15 B5 82 0.45
Embodiment 16 B6 90 0.50
Embodiment 17 B7 85 0.56
Embodiment 18 B8 77 0.59
Embodiment 19 B9 87 0.55
Embodiment 20 B10 91 0.45
The result of table 4 shows, it is active that catalyst according to the invention has higher HDM.And, when catalyst according to the invention is used for the HDM reaction of heavy hydrocarbon oil, the metal removed trends towards depositing in the center of catalyst, make catalyst according to the invention have higher appearance metal ability, thus catalyst according to the invention has better stability and longer service life.

Claims (36)

1. one kind has the catalyst of hydrogenation catalyst effect, this catalyst contains carrier and load at least one group VIII metallic element on the carrier and at least one group vib metallic element, described group VIII metallic element and group vib metallic element are non-uniform Distribution along this catalyst radial section separately, wherein, along this catalyst radial section
for group VIII metallic element is in the mean concentration of the outer surface of described catalyst;
for group VIII metallic element is in the mean concentration of the center of described catalyst;
be the mean concentration of group vib metallic element at the outer surface of described catalyst;
be the mean concentration of group vib metallic element in the center of described catalyst;
Described carrier is hydrated alumina forming matter, is made up of a kind of raw material, described raw material by least one hydrated alumina, at least one lithium-containing compound, at least one cellulose ether and containing or at least one extrusion aid that do not contain form.
2. catalyst according to claim 1, wherein, along this catalyst radial section,
3. catalyst according to claim 1, wherein, with the total amount of catalyst for benchmark, the content of described carrier is 70-95 % by weight, with oxide basis, the content of described group VIII metallic element is 1-8 % by weight, and the content of described group vib metallic element is 3-22 % by weight.
4. catalyst according to claim 1, wherein, described carrier prepares formed body by described raw material, and described formed body is carried out drying make.
5. catalyst according to claim 4, wherein, the temperature of described drying is higher than 180 DEG C and not higher than 300 DEG C.
6. catalyst according to claim 5, wherein, the temperature of described drying is 200-260 DEG C.
7. the catalyst according to claim 1 or 4, wherein, with the total amount of described raw material for benchmark, the total content of described cellulose ether is 0.5-12 % by weight, with Li 2the total content of the described lithium-containing compound of O meter is 0.5-10 % by weight, with Al 2o 3the total content of the described hydrated alumina of meter is 78-98 % by weight.
8. catalyst according to claim 7, wherein, with the total amount of described raw material for benchmark, the total content of described cellulose ether is 2-8 % by weight, with Li 2the total content of the described lithium-containing compound of O meter is 0.5-5 % by weight, with Al 2o 3the total content of the described hydrated alumina of meter is 87-97 % by weight.
9. the catalyst according to claim 1 or 4, wherein, described cellulose ether is selected from methylcellulose, HEMC and hydroxypropyl methylcellulose.
10. the catalyst according to claim 1 or 4, wherein, described lithium-containing compound is selected from lithium nitrate, lithium sulfate, lithium chloride, lithium oxalate and lithium acetate;
Described hydrated alumina is selected from boehmite, gibbsite, unformed hydrated alumina and boehmite.
11. according to the catalyst in claim 1,3 and 4 described in any one, and wherein, the water absorption rate of described carrier is 0.4-1.5, δ value is less than 10%, Q 1for more than 12N/mm,
Wherein, &delta; = Q 1 - Q 2 Q 1 &times; 100 % ,
Q 1for the radial crushing strength of the carrier without water soaking, in N/mm,
Q 2for through water soaking 30 minutes and in the radial crushing strength of the carrier of 120 DEG C of dryings after 4 hours, in N/mm.
12. catalyst according to claim 11, wherein, the water absorption rate of described carrier is 0.6-1, δ value is less than 5%, Q 1for 15-30N/mm.
13. according to the catalyst in claim 1-3 described in any one, and wherein, described group VIII metallic element is cobalt and/or nickel, and described group vib metal is molybdenum and/or tungsten.
14. catalyst according to claim 1, wherein, with the total amount of described raw material for benchmark, the content of described extrusion aid is 0.1-8 % by weight.
15. catalyst according to claim 14, wherein, with the total amount of described raw material for benchmark, the content of described extrusion aid is 0.5-5 % by weight.
16. according to the catalyst in claim 1,14 and 15 described in any one, and wherein, described extrusion aid is starch.
17. according to the catalyst in claim 1,14 and 15 described in any one, and wherein, described extrusion aid is sesbania powder.
18. 1 kinds of methods preparing the catalyst with hydrogenation catalyst effect, the method is included in supported on carriers at least one group VIII metallic element and at least one group vib metallic element, load is on the carrier substantially in a salt form separately for described group VIII metallic element and group vib metallic element, it is characterized in that, described carrier is hydrated alumina forming matter, formed body is prepared by a kind of raw material, and described formed body is carried out drying at higher than 180 DEG C and not higher than the temperature of 300 DEG C and makes, described raw material is by least one hydrated alumina, at least one lithium-containing compound, at least one cellulose ether and at least one extrusion aid composition containing or do not contain.
19. methods according to claim 18, wherein, the mode being prepared formed body by described raw material comprises:
At least one hydrated alumina, at least one lithium-containing compound and at least one cellulose ether are mixed with water, obtains the first mixture, and by shaping for described first mixture; Or
At least one hydrated alumina and at least one cellulose ether are mixed with water, obtains the second mixture, and described second mixture is successively carried out shaping and dehydration, obtain preform, load at least one lithium-containing compound on described preform.
20. methods according to claim 18 or 19, wherein, the temperature of described drying is 200-260 DEG C.
21. methods according to claim 18 or 19, wherein, with the total amount of described raw material for benchmark, the total content of described cellulose ether is 0.5-12 % by weight, with Li 2the total content of the described lithium-containing compound of O meter is 0.5-10 % by weight, with Al 2o 3the total content of the described hydrated alumina of meter is 78-98 % by weight.
22. methods according to claim 21, wherein, with the total amount of described raw material for benchmark, the total content of described cellulose ether is 2-8 % by weight, with Li 2the total content of the described lithium-containing compound of O meter is 0.5-5 % by weight, with Al 2o 3the total content of the described hydrated alumina of meter is 87-97 % by weight.
23. methods according to claim 18 or 19, wherein, described cellulose ether is selected from methylcellulose, HEMC and hydroxypropyl methylcellulose.
24. methods according to claim 18 or 19, wherein, described lithium-containing compound is selected from lithium nitrate, lithium sulfate, lithium chloride, lithium oxalate and lithium acetate;
Described hydrated alumina is selected from boehmite, gibbsite, unformed hydrated alumina and boehmite.
25. methods according to claim 18, wherein, described group vib metallic element and group VIII metallic element load capacity on the carrier make, with the total amount of the catalyst finally prepared for benchmark, the content of described carrier is 70-95 % by weight, with oxide basis, the content of described group VIII metallic element is 1-8 % by weight, and the content of described group vib metallic element is 3-22 % by weight.
26. methods according to claim 18 or 25, wherein, by being immersed in supported on carriers at least one group VIII metallic element and at least one group vib metallic element.
27. methods according to claim 26, wherein, the method also comprises carries out drying by flooding the carrier obtained, and the condition of described drying comprises: temperature is 100-200 DEG C, and the time is 1-15 hour.
28. methods according to claim 18 or 25, wherein, described group VIII metallic element is cobalt and/or nickel, and described group vib metallic element is molybdenum and/or tungsten.
29. methods according to claim 18, wherein, with the total amount of described raw material for benchmark, the content of described extrusion aid is 0.1-8 % by weight.
30. methods according to claim 29, wherein, with the total amount of described raw material for benchmark, the content of described extrusion aid is 0.5-5 % by weight.
31. according to the method in claim 18,29 and 30 described in any one, and wherein, described extrusion aid is starch.
32. according to the method in claim 18,29 and 30 described in any one, and wherein, described extrusion aid is sesbania powder.
33. catalyst with hydrogenation catalyst effect prepared by the method in claim 18-32 described in any one.
The application of catalyst in hydrocarbon oil hydrogenation process in 34. claim 1-17 and claim 33 described in any one.
35. 1 kinds of method for hydrotreating hydrocarbon oil, the method comprises under hydroprocessing conditions, by the catalyst exposure in hydrocarbon ils and claim 1-17 and claim 33 described in any one.
36. methods according to claim 35, wherein, described hydrocarbon ils is one or more in crude oil, reduced crude and decompression residuum.
CN201210191945.7A 2012-06-11 2012-06-11 There is the Catalysts and its preparation method of hydrogenation catalyst effect and application and method for hydrotreating hydrocarbon oil Active CN103480389B (en)