CN103468165A - 一种光纤光缆用热熔胶 - Google Patents

一种光纤光缆用热熔胶 Download PDF

Info

Publication number
CN103468165A
CN103468165A CN2013103495783A CN201310349578A CN103468165A CN 103468165 A CN103468165 A CN 103468165A CN 2013103495783 A CN2013103495783 A CN 2013103495783A CN 201310349578 A CN201310349578 A CN 201310349578A CN 103468165 A CN103468165 A CN 103468165A
Authority
CN
China
Prior art keywords
hot melt
melt adhesive
optical fiber
kneader
preheated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013103495783A
Other languages
English (en)
Inventor
张洪滨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU HONGAN PRECISION MACHINERY Co Ltd
Original Assignee
BENGBU HONGAN PRECISION MACHINERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU HONGAN PRECISION MACHINERY Co Ltd filed Critical BENGBU HONGAN PRECISION MACHINERY Co Ltd
Priority to CN2013103495783A priority Critical patent/CN103468165A/zh
Publication of CN103468165A publication Critical patent/CN103468165A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种光纤光缆用热熔胶，其是由下述重量份的原料制得:A料：纳米氮化铝粉 4-8、热塑性弹性体SBS4-8、纳米陶土1-2、氧化聚乙烯蜡3-5，硬酯酸钙0.1-0.2、硬酯酸锌0.1-0.2、抗氧剂TBM-6 0.3-0.5、环氧棉子油酸丁酯1-2、钛酸酯偶联剂TMC-TTS 0.3-0.4；B料:萜烯树脂T-120 10-12,美国杜邦560EVA 45-50,玫瑰精油2-4，柠檬酸三丁酯0.2-0.4,氧化聚乙烯蜡1-2,硅烷偶联剂A-172 1-2，抗氧剂10101-2。

Description

一种光纤光缆用热熔胶
技术领域
本发明涉及热熔胶领域，确切地说是一种光纤光缆用热熔胶。
背景技术
热熔胶粘合是利用热熔胶机通过热力把热熔胶熔解，熔胶后的胶成为一种液体，通过热熔胶机的热熔胶管和热熔胶枪，送到被粘合物表面，热熔胶冷却后即完成了粘合。
发明内容
本发明的目的在于提供一种光纤光缆用热熔胶。
上述目的通过以下方案实现：
     一种光纤光缆用热熔胶，其特征在于：其是由下述重量份的原料制得:
A料：纳米氮化铝粉  4-8、热塑性弹性体SBS 4-8、纳米陶土1-2、氧化聚乙烯蜡3-5，硬酯酸钙0.1-0.2、硬酯酸锌0.1-0.2、抗氧剂TBM-6  0.3-0.5、环氧棉子油酸丁酯1-2、钛酸酯偶联剂TMC-TTS  0.3-0.4；
B料:萜烯树脂 T-120  10-12, 美国杜邦560 EVA  45-50,玫瑰精油2-4，柠檬酸三丁酯 0.2-0.4,氧化聚乙烯蜡1-2,硅烷偶联剂A-172  1-2，抗氧剂1010 1-2。
    所述的一种光纤光缆用热熔胶，其特征在于：
制备方法包括以下步骤：
（1）捏合机预加热至壁温190-210℃，按重量份加入纳米陶土、抗氧剂TBM-6  、环氧棉子油酸丁酯，捏合20-30分钟，再加入A料剩余各原料，于180-190℃捏合20-30min，取出冷却即得A料；
（2）捏合机预加热至壁温190-210℃，然后按重量份加入B料各原料，捏合30-40min，取出冷却即得B料；
（3）捏合机预加热至壁温180-200℃，加入A料和B料，捏合30-40min，取出冷却即得。
本发明的有益效果为：本发明热熔胶采用新配方组合,不仅提高了热熔胶的耐寒性,同时增加了热熔胶接着强度,可以完全满足光纤光缆产业对热熔胶性能的要求。
具体实施方式
 一种光纤光缆用热熔胶，其是由下述重量份（kg)的原料制得:
 A料：纳米氮化铝粉  7、热塑性弹性体SBS  6、纳米陶土2、氧化聚乙烯蜡3，硬酯酸钙0.2、硬酯酸锌0.2、抗氧剂TBM-6  0.5、环氧棉子油酸丁酯2、钛酸酯偶联剂TMC-TTS  0.4；
B料:萜烯树脂 T-120  12, 美国杜邦560 EVA  50,玫瑰精油2，柠檬酸三丁酯 0.4,氧化聚乙烯蜡1,硅烷偶联剂A-172  2，抗氧剂1010 2。
    所述的一种光纤光缆用热熔胶，
制备方法包括以下步骤：
（1）捏合机预加热至壁温190℃，按重量份加入纳米陶土、抗氧剂TBM-6  、环氧棉子油酸丁酯，捏合30分钟，再加入A料剩余各原料，于190℃捏合20-30min，取出冷却即得A料；
（2）捏合机预加热至壁温190℃，然后按重量份加入B料各原料，捏合30min，取出冷却即得B料；
（3）捏合机预加热至壁温200℃，加入A料和B料，捏合40min，取出冷却即得。
本实施例的粘结剂的表观粘度为5100MPa.s，剥离强度52N/2.5cm，初粘力达到5号钢球，开放时间37s，24小时热稳定性状稳定。

Claims (2)

1.一种光纤光缆用热熔胶，其特征在于：其是由下述重量份的原料制得:
A料：纳米氮化铝粉  4-8、热塑性弹性体SBS 4-8、纳米陶土1-2、氧化聚乙烯蜡3-5，硬酯酸钙0.1-0.2、硬酯酸锌0.1-0.2、抗氧剂TBM-6  0.3-0.5、环氧棉子油酸丁酯1-2、钛酸酯偶联剂TMC-TTS  0.3-0.4；
B料:萜烯树脂 T-120  10-12, 美国杜邦560 EVA  45-50,玫瑰精油2-4，柠檬酸三丁酯 0.2-0.4,氧化聚乙烯蜡1-2,硅烷偶联剂A-172  1-2，抗氧剂1010 1-2。
2.根据权利要求1所述的一种光纤光缆用热熔胶，其特征在于：
制备方法包括以下步骤：
（1）捏合机预加热至壁温190-210℃，按重量份加入纳米陶土、抗氧剂TBM-6  、环氧棉子油酸丁酯，捏合20-30分钟，再加入A料剩余各原料，于180-190℃捏合20-30min，取出冷却即得A料；
（2）捏合机预加热至壁温190-210℃，然后按重量份加入B料各原料，捏合30-40min，取出冷却即得B料；
（3）捏合机预加热至壁温180-200℃，加入A料和B料，捏合30-40min，取出冷却即得。
CN2013103495783A 2013-08-13 2013-08-13 一种光纤光缆用热熔胶 Pending CN103468165A (zh)