A kind of modification low-viscosity rubber asphalt and preparation method thereof
Technical field:
The present invention relates to pavement construction material technical field, relate in particular to a kind of rubber modified bitumen and preparation method thereof.
Background technology:
Economy develops rapidly in recent years, newly-built a large amount of motorway, and consequent junked tire gets more and more, and junked tire is stacked and occupied a large amount of spaces and have glue stink, becomes the important component part of current noxious waste pollution.Rubber asphalt is a kind of modifying asphalt agglutinate of efficient, energy-saving and environmental protection, but the research application through decades finds, in use there are some drawbacks in traditional rubber pitch, its construction workability and storage stability poor, and in construction process, environmental pollution is more serious.Reaction forming agent and viscosity modifier composite modified rubber asphalt are a kind of novel rubber asphalts, add in Sasobit and Poly Propylene Wax to rubber asphalt through series reaction, after high speed shear, fully stir and breed the modified rubber asphalt cement formed after a hour.Research is thought, rubber modified bitumen has ageing resistance and anti-fatigue performance, the effect that prolonging service life of pavement, delayed reflex crack, reduction noise etc. are outstanding, and preparation technology's simple and flexible, construction workability is good, and hot storage stability is good, be applicable to various types of bituminous coat project, its popularization is imperative, has responded National Sustainable Development Strategies, is the another direction of current Modified Bitumen Pavement development.
Summary of the invention:
The object of the present invention is to provide a kind of modification low-viscosity rubber asphalt and preparation method thereof, rubber modified bitumen material is the type material of energy-conserving and environment-protective, production technique of the present invention is simple, economic value added is high, its indices all meets the technological standard of rubber asphalt, softening temperature >=58 DEG C, 40<25 DEG C of penetration degree <80, recovery of elasticity >=55 ﹪, 2.0Pa.s < kinematic viscosity < 4.0Pa.s.
Object of the present invention is achieved through the following technical solutions:
A kind of modification low-viscosity rubber asphalt, be made up of matrix pitch, using rubber powder of waste tire, Sha Suobi Depew asphalt modifier and Poly Propylene Wax, the weight percent of each component is: matrix pitch 65-74 ﹪, using rubber powder of waste tire 18-26 ﹪, Sha Suobi Depew asphalt modification agent content is the 3-8 ﹪ of matrix pitch weight, and Poly Propylene Wax content is the 2-8 ﹪ of matrix pitch weight.
Preferred as technique scheme, described matrix pitch is that Korea S import 70# heavily hands over matrix pitch.
Preferred as technique scheme, described using rubber powder of waste tire is 40-80 order oblique radial-ply tyre rubber powder.
Preferred as technique scheme, described Poly Propylene Wax fusing point is 120 DEG C-160 DEG C.
A kind of modification low-viscosity rubber asphalt preparation method of the present invention slowly adds using rubber powder of waste tire when being and matrix pitch being heated to 160 DEG C in matrix pitch intensification tank, adopt device for quickly elevating temperature, in 5 minutes, mixture temperature is risen to 185 DEG C, high speed shear adds the Sha Suobi Depew asphalt modifier that measures after half an hour and Poly Propylene Wax breeds one hour, namely obtains modification low-viscosity rubber asphalt.
Accompanying drawing illustrates:
Below in conjunction with accompanying drawing, the present invention is described further:
Fig. 1 is production technological process of the present invention.
Embodiment:
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment only for explaining the present invention, does not form limiting the scope of the present invention.
Embodiment 1: in matrix pitch intensification tank by weight percent be 69% Korea S import 70# slowly add the 40-80 order oblique radial-ply tyre rubber powder that weight percent is 23% when heavily handing over matrix pitch to be heated to 160 DEG C, adopt device for quickly elevating temperature, in 5 minutes, mixture temperature is risen to 185 DEG C, the Poly Propylene Wax of high speed shear adds matrix pitch weight 5% Sasobit (Sha Suobi Depew) asphalt modifier and matrix pitch weight 6.6% after half an hour breeds one hour, namely obtains modification low-viscosity rubber asphalt.
Embodiment 2: in matrix pitch intensification tank by weight percent be 72% Korea S import 70# slowly add the 40-80 order oblique radial-ply tyre rubber powder that weight percent is 23% when heavily handing over matrix pitch to be heated to 160 DEG C, adopt device for quickly elevating temperature, in 5 minutes, mixture temperature is risen to 185 DEG C, the Poly Propylene Wax of high speed shear adds matrix pitch weight 4% Sasobit (Sha Suobi Depew) asphalt modifier and matrix pitch weight 3% after half an hour breeds one hour, namely obtains modification low-viscosity rubber asphalt.
Embodiment 3: in matrix pitch intensification tank by weight percent be 73% Korea S import 70# slowly add the 40-80 order oblique radial-ply tyre rubber powder that weight percent is 23% when heavily handing over matrix pitch to be heated to 160 DEG C, adopt device for quickly elevating temperature, in 5 minutes, mixture temperature is risen to 185 DEG C, the Poly Propylene Wax of high speed shear adds matrix pitch weight 3% Sasobit (Sha Suobi Depew) asphalt modifier and matrix pitch weight 2.5% after half an hour breeds one hour, namely obtains modification low-viscosity rubber asphalt.Index is in table 1.
Table 1
Formulating of recipe |
25 DEG C of penetration degrees |
Softening temperature |
Recovery of elasticity |
177 DEG C of viscosity |
|
(0.1mm) |
(℃) |
(%) |
(pa.s) |
69%70# matrix+23% rubber powder |
54 |
63 |
75 |
1.6 |
72%70# matrix+23% rubber powder |
50 |
68 |
83 |
2.3 |
73%70# matrix+23% rubber powder |
49 |
72 |
84 |
2.8 |
Adopt the modified rubber asphalt mixture of asphalt content 5.4%, make high-temperature rutting test, low-temperature bending test, indirect tensile test on frozen-thaw and residual stability test-results respectively as table 2.
Table 2
According to the every experimental result in table, illustrate that the properties of modified rubber asphalt mixture all can meet technical requirements.