CN103465577A

CN103465577A - Wear-resistant film and production method thereof

Info

Publication number: CN103465577A
Application number: CN2013104342732A
Authority: CN
Inventors: 刘荣
Original assignee: SUZHOU HANXIN PLASTIC Co Ltd
Current assignee: SUZHOU HANXIN PLASTIC Co Ltd
Priority date: 2013-09-23
Filing date: 2013-09-23
Publication date: 2013-12-25

Abstract

The invention relates to a wear-resistant film. The film comprises three parts, namely an outer layer, a middle layer and an inner layer, wherein the outer layer accounts for 40% by weight, the middle layer accounts for 20% by weight, and the inner layer accounts for 40% by weight. The invention further provides a method for producing the film. The method comprises the steps of (1) mixing materials; (2) proportioning the materials; (3) carrying out film blowing. The film provided by the invention has the characteristics of high surface flatness, easiness in being subjected to corona, easiness in cladding and wear resistance, and continuous production can be realized through a film blowing machine by combining dispensing equipment.

Description

A kind of wear-resistance thin film and production method thereof

Technical field

The present invention relates to the film production manufacture field, specifically a kind of wear-resistance thin film and production method thereof.

Background technology

Blown film (BlowMembrane) is a kind of plastic working method, refers to the plastic pellet heating and melting is blown out to a kind of plastic processing of film again.If the film blown out with virgin material, color and luster is even, and clean, finished product stretches.If the plastic pellet made from the waste plastics reclaimed usually will add pigment when making film, the film of making may be just painted irregular, crisp and easily broken, and price is also lower.Blown film material by professional inflation film manufacturing machine production is applicable to various high-grade blister-packs.This film is due to its good barrier property, fresh-keeping, damp proof, frost protection, and oxygen barrier, oil resistant, can be widely used in the weight packing.As various fresh fruits, meat product, pickles, fresh milk, liquid beverage, medical supplies etc.If non-professional inflation film manufacturing machine or inflation film manufacturing machine do not make on sound lines in process, the coating materials of making so may be also substandard products.Most of PE are for the blown film film processed, and general low density PE (LDPE) or linearity are hanged down close PE(LLDPE) all available.The HDPE film-grade is generally used for the place that requires superior draftability and fabulous barrier properties.For example, the HDPE film is usually used in commodity bag, groceries bag and food Package.The PE processing film is generally by common blown film processing or the flat processing method of squeezing.

Due to the scope difference of film application, the characteristic of requirement has very large difference, also there is no a kind of easy volume production, high, the easy corona of surface smoothness, easy compound, wear-resisting film at present.

Summary of the invention

The present invention is above technical problem just, and a kind of easy volume production, high, the easy corona of surface smoothness, easy compound, wear-resisting film are provided.

The present invention is achieved through the following technical solutions:

A kind of wear-resistance thin film, comprise skin, middle level, internal layer three parts, the each several part proportion of composing is (percentage by weight): outer 40%, middle level 20%, internal layer 40%, its ectomesoderm is comprised of LDPE2420H, LLDPE920NT, PPO polyphenylene oxide, each component ratio for (percentage by weight): LDPE2420H accounts for 55%～60%, LLDPE920NT accounts for 25%～40%, PPO polyphenylene oxide 5%～20%; Middle level is comprised of LDPE2420H, LLDPE920NT, and each component ratio is for (percentage by weight): LDPE2420H accounts for 30%～40%, LLDPE920NT accounts for 60%～70%; Internal layer is comprised of LDPE2426H, MDPE5401, LLDPE218W, LLDPE920NT, each component ratio for (percentage by weight): LDPE2426H accounts for 20%～30%, MDPE5401 accounts for 20%～30%, LLDPE218W accounts for 20%～30%, LLDPE920NT accounts for 20%～30%.

A kind of production method of wear-resistance thin film comprises the following steps:

Step 1, batch mixing, stir each raw material to scale and make former mixed materials for later use by the percentage by weight of skin, middle level, each component of internal layer;

Step 2, batching, the former mixed material by the percentage by weight of skin, middle level, internal layer prepared by step 1 is prepared burden;

Step 3, blown film, adopt the inflation film manufacturing machine blow molding of being furnished with Automatic batching equipment to produce the film needed.

Film provided by the invention has high, the easy corona of surface smoothness, easy compound, wear-resisting characteristics, and can, in conjunction with dispensing equipment, by inflation film manufacturing machine, realize producing continuously.

The specific embodiment

Below in conjunction with specific embodiment, the present invention will be further described.

Embodiment 1

At first, by weight percentage by 60% LDPE2420H, 30% LLDPE920NT, 10% PPO polyphenylene oxide stirs and makes outer former mixed material, by weight percentage by 35% LDPE2420H, 65% LLDPE920NT stirs and makes the former mixed material in middle level, by weight percentage by 25% LDPE2426H, 25% MDPE5401, 25% LLDPE218W, 25% LLDPE920NT stirs and makes the former mixed material of internal layer, by weight percentage then by the former mixed material of skin, the former mixed material in middle level, the former mixed material of internal layer is by outer 40%, middle level 20%, internal layer 40% is prepared burden, after having prepared burden, can adopt the inflation film manufacturing machine blow molding of being furnished with Automatic batching equipment to produce the film needed.

Embodiment 2

At first, by weight percentage by 55% LDPE2420H, 25% LLDPE920NT, 20% PPO polyphenylene oxide stirs and makes outer former mixed material, by weight percentage by 30% LDPE2420H, 70% LLDPE920NT stirs and makes the former mixed material in middle level, by weight percentage by 20% LDPE2426H, 30% MDPE5401, 20% LLDPE218W, 30% LLDPE920NT stirs and makes the former mixed material of internal layer, by weight percentage then by the former mixed material of skin, the former mixed material in middle level, the former mixed material of internal layer is by outer 40%, middle level 20%, internal layer 40% is prepared burden, after having prepared burden, can adopt the inflation film manufacturing machine blow molding of being furnished with Automatic batching equipment to produce the film needed.

Embodiment 3

At first, by weight percentage by 58% LDPE2420H, 26% LLDPE920NT, 16% PPO polyphenylene oxide stirs and makes outer former mixed material, by weight percentage by 40% LDPE2420H, 60% LLDPE920NT stirs and makes the former mixed material in middle level, by weight percentage by 30% LDPE2426H, 20% MDPE5401, 30% LLDPE218W, 20% LLDPE920NT stirs and makes the former mixed material of internal layer, by weight percentage then by the former mixed material of skin, the former mixed material in middle level, the former mixed material of internal layer is by outer 40%, middle level 20%, internal layer 40% is prepared burden, after having prepared burden, can adopt the inflation film manufacturing machine blow molding of being furnished with Automatic batching equipment to produce the film needed.

Through test of many times, prove, it is the most obvious that PPO polyphenylene oxide improves the wearability effect.And, along with the increase of addition, its anti-wear performance also shows a rising trend.

Claims

1. a wear-resistance thin film, comprise skin, middle level, internal layer three parts, the each several part proportion of composing is (percentage by weight): outer 40%, middle level 20%, internal layer 40%, its ectomesoderm is comprised of LDPE2420H, LLDPE920NT, PPO polyphenylene oxide, each component ratio for (percentage by weight): LDPE2420H accounts for 55%～60%, LLDPE920NT accounts for 25%～40%, PPO polyphenylene oxide 5%～20%; Middle level is comprised of LDPE2420H, LLDPE920NT, and each component ratio is for (percentage by weight): LDPE2420H accounts for 30%～40%, LLDPE920NT accounts for 60%～70%; Internal layer is comprised of LDPE2426H, MDPE5401, LLDPE218W, LLDPE920NT, each component ratio for (percentage by weight): LDPE2426H accounts for 20%～30%, MDPE5401 accounts for 20%～30%, LLDPE218W accounts for 20%～30%, LLDPE920NT accounts for 20%～30%.

2. a kind of film according to claim 1, is characterized in that outer each component ratio is that LDPE2420H accounts for 60%, LLDPE920NT accounts for 30%, PPO polyphenylene oxide 10%; Each component ratio of middle level is that LDPE2420H accounts for 35%, LLDPE920NT accounts for 65%; Each component ratio of internal layer is that LDPE2426H accounts for 25%, MDPE5401 accounts for 25%, LLDPE218W accounts for 25%, LLDPE920NT accounts for 25%.

3. a kind of film according to claim 1, is characterized in that outer each component ratio is that LDPE2420H accounts for 55%, LLDPE920NT accounts for 25%, PPO polyphenylene oxide 20%; Each component ratio of middle level is that LDPE2420H accounts for 30%, LLDPE920NT accounts for 70%; Each component ratio of internal layer is that LDPE2426H accounts for 20%, MDPE5401 accounts for 30%, LLDPE218W accounts for 20%, LLDPE920NT accounts for 30%.

4. a kind of film according to claim 1, is characterized in that outer each component ratio is that LDPE2420H accounts for 58%, LLDPE920NT accounts for 26%, PPO polyphenylene oxide 16%; Each component ratio of middle level is that LDPE2420H accounts for 40%, LLDPE920NT accounts for 60%; Each component ratio of internal layer is that LDPE2426H accounts for 30%, MDPE5401 accounts for 20%, LLDPE218W accounts for 30%, LLDPE920NT accounts for 20%.

5. the production method of a film comprises the following steps: