CN103465335A

CN103465335A - Manufacturing method of novel rosewood carving chair

Info

Publication number: CN103465335A
Application number: CN2013104165367A
Authority: CN
Inventors: 颜仁明
Original assignee: CHANGZHOU FUDA REDWOOD FURNITURE FACTORY
Current assignee: CHANGZHOU FUDA REDWOOD FURNITURE FACTORY
Priority date: 2013-09-13
Filing date: 2013-09-13
Publication date: 2013-12-25

Abstract

The invention discloses a manufacturing method of a novel rosewood carving chair. The manufacturing method includes a), manufacturing a front layer and a back layer of the back of a chair, b), manufacturing a carving layer of the back of the chair, c), assembling the back of the chair, d) manufacturing other parts, e), assembling a carving chair, f), scrapping finish and g), waxing. The manufacturing method of the novel rosewood carving chair is reasonable in process arrangement, convenient to implement, can be used for independently manufacturing rosewood carving portion, can effectively reduce wear and tear of rosewood materials, simplify the manufacturing process and is beneficial to production of medium and small workshops.

Description

A kind of preparation method of Novel red wood carving chair

Technical field

The present invention relates to a kind of preparation method of redwood carving chair, relate in particular to a kind of preparation method with redwood carving chair of unique carving structure, belong to the mahogany furniture technical field.

background technology

Mahogany furniture starts from the Ming Dynasty, the simple and unadorned symmetry of its outward appearance body, and natural wood color and texture are pleasant.Redwood mainly adopt the Chinoiserie manufacture engraving, Tenon, inlay, the traditional handicraft such as curve, in its moulding and technique significantly national characteristic be to the most attractive part of many collectors, a lot of people claim that mahogany furniture is humane furniture, artistical furniture.Chinese-style chair is generally that pure solid wood is made, and the high-grade Chinese-style chair that deeply is subject to the successful personage of various circles of society to hold in both hands love is not stinted especially, to take the contour Duanmu's material of redwood be raw material, continue to use China traditional joinery and its construction and raw lacquer technology, and in conjunction with the modern crafts gimmick, work with great care and form through 100 multiple working procedures, not only stabilized structure, durable in use, and elegant attractive in appearance, be rich in classic wingceltis rhythm.

Carved pattern on the existing redwood carving chair chair back all adopts material all in one piece carving technique, its complicated process of preparation, and loss is large, and cost is high, and therefore, the price of redwood carving chair is all more expensive, is difficult to come into the family of ordinary populace; Simultaneously, owing to adopting material all in one piece carving technique, there are limitation in kind and the structure of carved pattern, and are unsuitable for being produced in batches, have limited the development of redwood carving technique.

Summary of the invention

For the demand, the invention provides a kind of preparation method of Novel red wood carving chair, this preparation method's procedure arrangement is reasonable, be easy to implement, unique distinction is that the redwood carved pattern can carry out independent preparation, effectively reduce the loss of redwood material, simplify production technology, be applicable to being produced in batches.

The present invention is a kind of preparation method of Novel red wood carving chair, and this preparation method comprises the steps: a) to prepare the forward and backward layer of the chair back, b) prepares chair back carving layer, and c) the assembling chair back, d) prepare remaining part, e) assembling carving chair, and f) scraped finish, g) wax.

In a preferred embodiment of the present invention,, in described step a), the forward and backward layer of the chair back adopts framework design, and front layer thickness is 18mm, and rear layer thickness is 22mm, and width is 35mm.

In a preferred embodiment of the present invention, be symmetrical arranged some sunk structures on described forward and backward layer faying face, specification is about 25mm*15mm*8mm.

In a preferred embodiment of the present invention, in described step b), chair back carving layer comprise the carved pattern at middle part and along it peripheral connecting block structure, the specification of connecting block structure is 25mm*15mm*16mm.

In a preferred embodiment of the present invention, in described step c), before assembling, need to smear the redwood viscose glue on the faying face of forward and backward; During assembling, the connecting block structure in the carving layer coordinates with the sunk structure on forward and backward layer, and fit system is interference fit; After assembling, need apply the external force of 100-120N, the application of force time is about 4-5 hour.

In a preferred embodiment of the present invention, in described step f), this operation comprises scraper scraped finish and sand papering, and sand papering need be carried out repeatedly, and the granularity of sand paper is successively decreased from big to small, until the surface roughness of blank reaches the 6.4um left and right.

In a preferred embodiment of the present invention, in described step g), at first, use pure cotton cloth that natural beeswax is evenly spread upon to each parts surface; Then, the application of force is swiping repeatedly, and the external force size is about 40N, and the swiping time is about 15 minutes; Finally, using granularity is that 1000 purpose sand paper are polished, the floating wax on removing component surface; The above-mentioned process of waxing need operate more than 4 times repeatedly.

The present invention has disclosed a kind of preparation method of Novel red wood carving chair, and this preparation method's procedure arrangement is reasonable, is easy to implement, its redwood carving part can be carried out independent preparation, effectively reduce the loss of redwood material, simplified production technology, be conducive to middle individual workship and organize production.

The accompanying drawing explanation

Below in conjunction with the drawings and specific embodiments, the present invention is further detailed explanation:

Fig. 1 is the preparation method's of embodiment of the present invention Novel red wood carving chair process figure.

The specific embodiment

Below in conjunction with accompanying drawing, preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that, protection scope of the present invention is made to more explicit defining.

Fig. 1 is the preparation method's of embodiment of the present invention Novel red wood carving chair process figure; This preparation method comprises the steps: a) to prepare the forward and backward layer of the chair back, b) prepares chair back carving layer, and c) the assembling chair back, d) prepare remaining part, e) assembling carving chair, and f) scraped finish, g) wax.

Embodiment

The preparation method's of the Novel red wood carving chair that the present invention mentions concrete preparation process is as follows:

A) prepare the forward and backward layer of the chair back, the forward and backward layer of the chair back adopts framework design, and front layer thickness is 18mm, and rear layer thickness is 22mm, and width is 35mm; Be symmetrical arranged some sunk structures on the faying face of anterior layer and rear layer, profile is rectangle, and specification is about 25mm*15mm*8mm; The preparation technology of this sunk structure comprises: line, chiseling and polishing etc., the quantity of above-mentioned sunk structure and position are arranged according to the kind of carved pattern, generally, the total quantity on upper and lower two frameworks is no less than 3, much not 6 of the total quantitys on left and right two frameworks;

B) prepare chair back carving layer, this carving layer comprises the carved pattern at middle part and the peripheral connecting block structure along it, forward and backward upper sunk structure arranged of the quantity of connecting block structure and specification and the chair back coordinates, and the specification of this connecting block structure is 25mm*15mm*16mm;

C) the assembling chair back, the chair back is comprised of anterior layer, carving layer and rear layer; Before assembling, need to smear the redwood viscose glue on the faying face of forward and backward, during assembling, connecting block structure in the carving layer coordinates with the sunk structure on forward and backward layer, and fit system is interference fit, after assembling, need apply the external force of 100-120N, the application of force time is about 4-5 hour, bonding after, the gap between forward and backward layer is no more than 0.1mm;

D) prepare remaining part, this operation comprises the independent preparation of the parts such as seat board, chair leg and handrail, and this technology is known technology, at this, no longer describes;

E) assembling carving chair, each parts of carving chair all adopt joinery and its construction to be connected;

F) scraped finish, this operation comprises scraper scraped finish and sand papering, and wherein, sand papering need be carried out repeatedly, and the granularity of sand paper is successively decreased from big to small, until the surface roughness of blank reaches the 6.4um left and right;

G) wax, wax material is selected natural beeswax, and the process of waxing is as follows: at first, use pure cotton cloth that beeswax is evenly spread upon to each parts surface; Then, the application of force is swiping repeatedly, and the external force size is about 40N, and the swiping time is about 15 minutes; Finally, using granularity is that 1000 purpose sand paper are polished, the floating wax on removing component surface; The above-mentioned process of waxing need operate more than 4 times repeatedly, makes every effort to redwood chair surface and presents moist, simple and unsophisticated makings.

The present invention has disclosed a kind of preparation method of Novel red wood carving chair, be characterized in: this preparation method's procedure arrangement is reasonable, be easy to implement, its redwood carving part can be carried out independent preparation, effectively reduce the loss of redwood material, simplified production technology, be conducive to middle individual workship and organize production.

The above; it is only the specific embodiment of the present invention; but protection scope of the present invention is not limited to this; any those of ordinary skill in the art are in the disclosed technical scope of the present invention; the variation that can expect without creative work or replacement, within all should being encompassed in protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.

Claims

1. the preparation method of a Novel red wood carving chair, this preparation method comprises the steps: a) to prepare the forward and backward layer of the chair back, b) prepares chair back carving layer, and c) the assembling chair back, d) prepare remaining part, e) assembling carving chair, f) scraped finish, g) wax.

2. the preparation method of Novel red wood carving chair according to claim 1, is characterized in that, in described step a), the forward and backward layer of the chair back adopts framework design, and front layer thickness is 18mm, and rear layer thickness is 22mm, and width is 35mm.

3. the preparation method of Novel red wood carving chair according to claim 2, is characterized in that, on described forward and backward layer faying face, is symmetrical arranged some sunk structures, and specification is about 25mm*15mm*8mm.

4. the preparation method of Novel red wood carving chair according to claim 1, it is characterized in that, in described step b), chair back carving layer comprise the carved pattern at middle part and along it peripheral connecting block structure, the specification of connecting block structure is 25mm*15mm*16mm.

5. the preparation method of Novel red wood carving chair according to claim 1, is characterized in that, in described step c), before assembling, needs to smear the redwood viscose glue on the faying face of forward and backward; During assembling, the connecting block structure in the carving layer coordinates with the sunk structure on forward and backward layer, and fit system is interference fit; After assembling, need apply the external force of 100-120N, the application of force time is about 4-5 hour.

6. the preparation method of Novel red wood carving chair according to claim 1, it is characterized in that, in described step f), this operation comprises scraper scraped finish and sand papering, sand papering need be carried out repeatedly, the granularity of sand paper is successively decreased from big to small, until the surface roughness of blank reaches the 6.4um left and right.

7. the preparation method of Novel red wood carving chair according to claim 1, is characterized in that, in described step g), at first, uses pure cotton cloth that natural beeswax is evenly spread upon to each parts surface; Then, the application of force is swiping repeatedly, and the external force size is about 40N, and the swiping time is about 15 minutes; Finally, using granularity is that 1000 purpose sand paper are polished, the floating wax on removing component surface; The above-mentioned process of waxing need operate more than 4 times repeatedly.