CN103431529B - High-temperature water paste print bra mould cup and manufacturing method thereof - Google Patents
High-temperature water paste print bra mould cup and manufacturing method thereof Download PDFInfo
- Publication number
- CN103431529B CN103431529B CN201310358838.3A CN201310358838A CN103431529B CN 103431529 B CN103431529 B CN 103431529B CN 201310358838 A CN201310358838 A CN 201310358838A CN 103431529 B CN103431529 B CN 103431529B
- Authority
- CN
- China
- Prior art keywords
- cut
- temperature water
- parts
- water slurry
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a high-temperature water paste print bra mould cup which comprises a shell fabric, a base fabric and filler filled between the shell fabric and the base fabric, wherein a water paste print is formed on the surface of the shell fabric. The invention further provides a method for manufacturing the high-temperature water paste print bra mould cup. The method comprises the steps: (1) making cut pieces; (2) preparing for printing; (3) conducting water paste printing; and (4) positioning and mould pressing. The high-temperature water paste print bra mould cup is simple, unified and attractive in appearance and relatively low in manufacturing cost, and a flower-shaped pattern can be designed in any position of the surface of the cup.
Description
Technical field
The present invention relates to a kind of brassiere mold cup and preparation method thereof, particularly relate to a kind of surface and there is brassiere mold cup of water slurry stamp and preparation method thereof.
Background technology
If the outward appearance of current brassiere wants to show the style characteristic in some flower faces, calico can only be adopted to make brassiere face cloth or calico is directly used in the face of surface when brassiere of mould cup.But calico generally adopts the hot transfer printing of calico paper or view picture printing and dyeing, and when view picture is printed, cost is lower.If but designer wants to design a flower pattern at certain local location of mould cup, then with just not too convenient when calico paper or printing and dyeing, and be enable completing, also can be very large for loss, cost is very high.Therefore the product substantially can't see on the market at present in a light face brassiere surface local print flower pattern or special stamp.
Summary of the invention
In order to overcome the defect of prior art, first object of the present invention is to provide the high-temperature water paste print bra mould cup that a kind of surface has water slurry stamp, this brassiere mold cup tailored appearance, designer by design design in the optional position in cup face, can reduce the stamp cost of manufacture of brassiere mold cup.
For achieving the above object, the invention provides a kind of high-temperature water paste print bra mould cup, comprising face cloth, base fabric and being filled in the filler in the middle of described cloth and base fabric, it is characterized in that: the surface of described cloth has water slurry stamp.
Wherein, described cloth is mercerising fabric, is preferably bright and beautiful polyurethane fabric.
Described filler can be sponge or 3D upright cotton, face cloth, base fabric and polyurethane sponge or 3D upright cotton fitted by glue spraying after hot repressing be bonded together.3D upright cotton is Whole fiber material, and gas permeability is better, also health environment-friendly more, and 3D upright cotton cut after leftover pieces can collect after again make and set up cotton, spillage of material is less, product also recyclable recycling, more economically environmental protection after consumer dresses.
Preferably, described cloth passes through together with ultrasonic heat bonding with the edge of described base fabric.By ultrasonic heat bonding, what eliminate face cloth and base fabric makes operation, also makes brassiere mold cup product appearance more succinct and unified.
Second object of the present invention is to provide a kind of method making above-mentioned high-temperature water paste print bra mould cup, it is characterized in that, comprises the following steps:
(1) cut-parts are made: first the face cloth of solid color, base fabric and sponge or 3D upright cotton are fitted, then be cut into the cut-parts of mold pressing;
(2) printing prepares: design stamp pattern, makes printing screen plate, prepare high temperature water slurry;
(3) water slurry printing: high temperature water slurry is printed in described cut-parts by printing screen plate;
(4) mold pressing is located: the described cut-parts with water slurry stamp are carried out positioning module pressure on hot pressing die.
Further, also comprise step (5) ultrasonic to cut: the cut-parts after mold pressing being shaped adopt ultrasonic mould to carry out ultrasonic and cut.
Wherein, described cloth is bright and beautiful polyurethane fabric.Brocade polyurethane fabric has mercerising surface, and its fusion points is lower and adhesive fastness is stronger, after mould cup is hot-forming with sponge or 3D upright cotton bond more firm, after its surperficial making water slurry stamp, design is more clear, attractive in appearance, and not fugitive color.
Preferably, described high temperature water slurry is the water slurry of high temperature resistant more than 200 DEG C.Owing to locating the hot pressing temperature of mold pressing usually at about 190 DEG C, in order to avoid high temperature is to the harmful effect of water slurry stamp, the high temperature resistant temperature of high temperature water slurry is greater than hot pressing temperature.
Wherein, the detailed process of described step (4) location mold pressing is: on hot pressing die, be fixedly installed pilot pin, in cut-parts, accomplish fluently location according to the position of pilot pin and put marking point, then to the pilot pin on position mould, cut-parts are put on mould, carries out positioning module pressure.
Compared to prior art, the present invention has the following advantages: brassiere mold cup product appearance is succinct, unified, attractive in appearance; The cost of brassiere mold cup has greatly been saved compared with common heat transfer printing; Breach the limitation that prior art is difficult to carry out local stamp, to the performance space that designer is very large, can by the optional position of design design in cup face.
figure of description
Fig. 1 is the technological process block-diagram that the present invention makes the method for high-temperature water paste print bra mould cup.
Detailed description of the invention
Below in conjunction with accompanying drawing, the preferred embodiment of the present invention is described in detail.
A kind of high-temperature water paste print bra mould cup provided by the invention, the face cloth comprised, base fabric and the filler be filled in the middle of described cloth and base fabric, the surface of described cloth has water slurry stamp.
Wherein, face cloth and base fabric are bright and beautiful polyurethane fabric.Described filler can be sponge or 3D upright cotton, adopts 3D upright cotton in the present embodiment.Face cloth, base fabric 3D upright cotton are bonded together by hot repressing after glue spraying laminating.Described cloth passes through together with ultrasonic heat bonding with the edge of described base fabric.By ultrasonic heat bonding, what eliminate face cloth and base fabric makes operation, also makes brassiere mold cup product appearance more succinct and unified.
Refer to Fig. 1, high-temperature water paste print bra mould cup of the present invention is prepared by following steps:
(1) cut-parts are made: first the face cloth of solid color, base fabric and 3D upright cotton are fitted by glue spraying, then be cut into the cut-parts of mold pressing;
(2) printing prepares: design stamp pattern, first makes the film according to stamp pattern, then make printing screen plate by the film, prepare the high temperature water slurry of high temperature resistant more than 200 DEG C simultaneously;
(3) water slurry printing: high temperature water slurry is printed in described cut-parts by printing screen plate;
(4) mold pressing is located: on hot pressing die, be fixedly installed pilot pin, in cut-parts, accomplish fluently location according to the position of pilot pin and put marking point, then to the pilot pin on position mould, the described cut-parts with water slurry stamp are carried out positioning module pressure on hot pressing die, and after compression molding, cloth, base fabric and 3D upright cotton are bonding becomes to be integrated;
(5) ultrasonic cuts: the cut-parts after mold pressing being shaped adopt ultrasonic mould to carry out ultrasonic and cut.
Described cloth is bright and beautiful polyurethane fabric.Brocade polyurethane fabric has mercerising surface, and its fusion points is lower and adhesive fastness is stronger, after mould cup is hot-forming with sponge or 3D upright cotton bond more firm, after its surperficial making water slurry stamp, design is more clear, attractive in appearance, and not fugitive color.
Above-described embodiment is only for illustrating technical conceive of the present invention and feature; its object is to person skilled in the art can be understood content of the present invention and implement according to this; can not limit the scope of the invention with this; all equivalences done according to Spirit Essence of the present invention change or modify, and all should be encompassed within protection scope of the present invention.
Claims (2)
1. a high-temperature water paste print bra mould cup, comprise face cloth, base fabric and be filled in the filler in the middle of described cloth and base fabric, it is characterized in that: described cloth is bright and beautiful polyurethane fabric, the surface of described cloth has water slurry stamp, described filler is sponge or 3D upright cotton, and described cloth passes through together with ultrasonic heat bonding with the edge of described base fabric; Described high-temperature water paste print bra mould cup adopts following steps to make:
(1) cut-parts are made: first the face cloth of solid color, base fabric and sponge or 3D upright cotton are fitted, then be cut into the cut-parts of mold pressing;
(2) printing prepares: design stamp pattern, makes printing screen plate, prepare high temperature water slurry;
(3) water slurry printing: high temperature water slurry is printed in described cut-parts by printing screen plate;
(4) mold pressing is located: the described cut-parts with water slurry stamp are carried out positioning module pressure on hot pressing die;
(5) ultrasonic cuts: the cut-parts after mold pressing being shaped adopt ultrasonic mould to carry out ultrasonic and cut;
Wherein, described high temperature water slurry is the water slurry of high temperature resistant more than 200 DEG C.
2. high-temperature water paste print bra mould cup according to claim 1, it is characterized in that: the detailed process of described step (4) location mold pressing is: on hot pressing die, be fixedly installed pilot pin, in cut-parts, accomplish fluently location according to the position of pilot pin and put marking point, then to the pilot pin on position mould, cut-parts are put on mould, carries out positioning module pressure.