CN1033949A - The dehydrogenation catalyst particles of stratiform - Google Patents
The dehydrogenation catalyst particles of stratiform Download PDFInfo
- Publication number
- CN1033949A CN1033949A CN87108352A CN87108352A CN1033949A CN 1033949 A CN1033949 A CN 1033949A CN 87108352 A CN87108352 A CN 87108352A CN 87108352 A CN87108352 A CN 87108352A CN 1033949 A CN1033949 A CN 1033949A
- Authority
- CN
- China
- Prior art keywords
- catalyst
- component
- platinum
- carrier
- catalyst granules
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of novel hydrocarbon conversion catalyst system, this system comprises a kind of catalyst granules, its composition contains a platinum group metal component, a kind of promoter metal component that is selected from tin, germanium, rhenium and composition thereof, the halogen component that alkali metal that choosing adds or alkaline-earth metal or its component of mixture and choosing add is loaded on the solid refractory oxides carrier of 850 microns of nominal equivalent diameters at least.This novel catalyst system is useful especially as the dehydrogenation of hydrocarbons catalyst.Also introduced this Preparation of catalysts method.
Description
The present invention relates to a kind of novel catalyst granules with layer structure and has the conversion of hydro carbons down, particularly relates to the dehydrogenation of dehydrogenatable hydrocarbons.The present invention also relates to a kind of novel lamellar catalyst granules and manufacture method thereof.
The dehydrogenation of hydro carbons is an important commercial run, need a large amount of dehydrogenation hydro carbons, these products such as washing agent, high-knock rating gasoline, medical product, plastics, synthetic rubber and other products well-known to those skilled in the art because make various chemical products.An example of the method is that dehydrogenation of isobutane is made isobutene, and isobutene polymerization again obtains tackifier, can be used for buffer and antioxygen compound that binding agent, engine oil viscosity index (VI) compound and plastics are used.
Having known has many kinds of catalyst, they contain a kind of composition of platinum family and one of be selected from tin, germanium, the rhenium group or its mixture help catalytic metal component.For example United States Patent (USP) 3,632, and 503,3,755,481 and 3,878,131 disclose and comprise platinum-group component and tin and germanium component and be loaded in catalyst on the porous carrier.Yet, when the germanium component evenly distributes, obtained best result in whole carrier material according to these reference introductions.And say nothing in this material and do not talk the skin that most of catalytic metal component is confined to catalyst granules and have what advantage.In fact above-mentioned material is pointed out, catalyst preferably should reduce under substantially anhydrous situation before the hydrocarbon conversion being used for, and it is in order to guarantee that metal component carefully is distributed in the carrier material equably that material also further points out to design this step.
United States Patent (USP) 3,682,838 and 3,761,531 disclose the catalyst that comprises platinum-group component and a kind of IV A family metal component.With the same in the material of front, point out that also catalyst preferably will pass through reduction step before using.Also further pointing out to design reduction step in these materials is to want guarantee fund's metal particles will be evenly distributed in the whole catalyst.
United States Patent (USP) 3,558,477,3,562,147,3,584,060 and 3,649,566 all disclose and have comprised a platinum-group component and the catalyst of rhenium component on heat-resisting oxide carrier.Yet, as before material in, these materials also point out to obtain best result when platinum-group component and rhenium component are evenly distributed in the surface of whole catalyst and the hole.
United States Patent (USP) 3,897, a kind of method of producing the novel metal catalyst is disclosed in 368, used noble metal is a platinum, and platinum is optionally to be deposited on the outer surface of catalyst, it only is that platinum is immersed in outer field advantage and the special surface activating agent for the noble metal dipping is used on the outer surface that yet this material has been set forth.And we find now uncannily, as on the outer surface that the overwhelming majority of a kind of metal component of selecting in a kind of platinum group metal and tin, germanium, the rhenium group all is attached to catalyst carrier the time, just can obtain, in method of dehydrogenating, show the catalyst that improves function.
The carbon monoxide-olefin polymeric and the manufacture method thereof that the purpose of this invention is to provide a kind of improvement, resultant another purpose is the dehydrogenation of conversion, particularly hydro carbons for hydro carbons, and an improved method is provided.
Therefore a main aspect of the present invention is a kind of catalyst granules, it comprises by a kind of platinum group metal component with catalytically effective amount, promoter metal component by a kind of or its mixture of selecting in tin, germanium, the rhenium group, and select alkali metal or the alkaline earth metal component that adds, combine with the refractory oxides carrier of solid.The nominal equivalent diameter of carrier is at least 850 microns, platinum group metal component and help catalytic metal component to be immersed on the surface of refractory oxides carrier with special method wherein, make the mean concentration of these components in outside 100 micron layers of catalyst, be at least two times of each component respective concentration in catalyst granules core 200 micron diameters.
Another aspect of the present invention is the method for a kind of catalyst system of preparation, this catalyst system comprises a kind of catalyst granules, this particle comprises a kind of platinum group metal component, promoter metal component by a kind of or its mixture of selecting in tin, germanium, the rhenium group, and select alkali metal or the alkaline earth metal component that adds, combine with solid refractory oxides carrier.The nominal equivalent diameter of carrier is at least 850 microns, platinum group metal component and help catalytic metal component to be immersed on the surface of refractory oxides carrier with special method wherein, make the mean concentration of these components in outside 100 micron layers of catalyst, be at least two times of respective concentration of each component in catalyst granules core 200 micron diameters.
Another aspect of the present invention is a kind of method of the hydrocarbon conversion, and the method is included under the hydrocarbon conversion condition, makes transformable hydrocarbon have the laminated metal structure and comprise each step that the catalyst system and catalyzing of catalyst granules contacts with described above.In the best application scenario, but transformable hydrocarbon is the hydrocarbon of dehydrogenation, and used conversion condition is a dehydrogenation condition of producing corresponding dehydrogenated hydrocarbon.
In a word the present invention is a kind of catalyst of improvement, its manufacture method and neon gown plum green pepper ā
Principal character of the present invention is a kind of platinum group metal component, preferably also has a kind of promoter metal component that is selected from tin, germanium, rhenium group or its mixture, and surface impregnation is on catalyst carrier material.The nominal equivalent diameter of this carrier is 850 microns at least, and whole basically platinum-group component and promoter metal component be all on the skin of catalyst carrier, maximum 400 microns dark.In other words, notable feature of the present invention is platinum-group component, preferably also has promoter metal component, all surface impregnation is in the particle of solid carrier, its impregnation method makes in outside 100 micron layers of carrier, and the mean concentration of these components is at least interior these components of carrier core 200 micron diameters twice of concentration separately.Be to be understood that " outside " this speech, its definition is the outermost layer of catalyst granules; " layer " is meant the basic one deck uniformly of thickness; " nominal equivalent diameter " be meant for non-garden shape particle, be the minimum diameter of its particle, promptly along the smallest particles thickness of the line measurement by the particle center.
When the mean concentration of a kind of metal component in outside 100 micron layers of catalyst is at least two times of the mean concentration of this metal component in catalyst core 200 micron diameters, just think that this metal component is a surface impregnation.Except platinum group metal component and help catalytic metal component, beyond the surface impregnation, another aspect of the present invention also comprises, when carrying out surface impregnation, whole basically platinum-group component and promoter metal component all catalyst carrier the darkest 400 microns with interior skin in." whole basically " refer to has 75% surface impregnation component at least.This characteristic of catalyst is described out platinum group metal component, also can comprise the catalytic metal component that helps of surface impregnation, has concentration gradient on the catalyst carrier surface to inside.As has been noted in the skin of 100 microns of carrier surfaces, platinum-group component or also can comprise the concentration of the cocatalyst component of surface impregnation is the twice of platinum-group component or cocatalyst component concentration in catalyst core 200 micron diameters at least.The metal concentration of surface impregnation reduces gradually along the direction to carrier center.Platinum group metal or also can comprise the catalytic metal component that helps of surface impregnation, the nominal equivalent diameter of carrier and the actual fabrication method of catalyst are depended in the variation of the actual concentrations gradient in catalyst carrier.Therefore, platinum group metal component or also can comprise the distribution of the promoter metal component of surface impregnation, best definition is for being surface impregnation, and basically all carrier the darkest 400 microns with interior skin in, and " whole basically " refer to and have 75% component at least.
As previously mentioned, the nominal equivalent diameter of carrier material is 850 microns at least, for catalyst carrier material with such diameter, surface impregnation the skin of 75% component be about 100 microns.When the equivalent diameter of catalyst carrier surpassed more than 2000 microns, the skin of surface impregnation 75% component is the darkest to be 400 microns.
Although also imperfectly understand, can think the component of surface impregnation all is confined in 400 microns dark shells of catalyst carrier outer surface basically that its catalytic site is just easier to be approaching, makes hydrocarbon reactants and product have shorter diffusion path.Owing to shortened diffusion path, reactant and the product time of staying in catalyst granules shortens, thereby the undesirable side effect that produces owing to secondary reaction is reduced.Increased selectivity like this to desired product.For example: become in the reaction of monoolefine at dehydrating alkanes, shorten diffusion path length and just make the desired monoolefine that obtains, leaving before the catalyst granules, because of being adsorbed onto on the catalytic site once more, reducing and continue the chance that dehydrogenation generates unwanted skeletal isomerization thing, cracking product and aromatic hydrocarbons.
Another feature of the present invention is to have promoter metal component in catalyst system.This component can be selected from tin, germanium, rhenium group and composition thereof.As has pointed out the front:, the promoter metal component of catalytically effective amount is in kind carried out surface impregnation preferably as platinum-group component.Carried out after the surface impregnation in promoter metal component, may be basically all in 400 microns dark skins of catalyst carrier particle.According to the weight of final composition, be that benchmark calculates with the element generally, catalyst contains 0.01~10%(weight) promoter metal component, and preferably contain 0.1~5%(weight of having an appointment) promoter metal component.
When promoter metal component of the present invention was the germanium component, all germanium components may all exist with the oxidation state that is higher than metal element in catalyst.This component may be present in the composition with compound form, for example with oxide, sulfide, halide, oxychloride, aluminate etc., perhaps to exist with carrier material or with the form of other component combination in the composition.The better consumption of germanium component should be enough to make and contain in last catalyst composition by the about 0.01~10%(weight of element) germanium, best result derives from about 0.1~5%(weight) germanium.
Another kind also is that better promoter metal component is the tin component.This component can be with metal element, also can be to exist, or to exist with physics or chemically combined form with other component in porous carrier materials and/or the catalyst composition with forms such as compound such as oxide, sulfide, halide, oxychlorides.The consumption of tin component is to be enough to make contain in the last catalyst composition by the about 0.01~10%(weight of element preferably) tin, and best consumption is about 0.1~5%(weight).
Another selectable cocatalyst component is the rhenium component.This component can also can be with compound with metal element, exists as the form of oxide, sulfide, halide etc., or exists with physics or chemically combined form with other component in porous carrier materials and/or the catalyst composition.Best rhenium amounts of components should be enough to make and contain in last composition by the about 0.01~5%(weight of element) rhenium.
As for the optimum content of various promoter metal component in the catalyst, have been found that rhenium component, germanium component and tin components contents are provided with the ratio relation with platinum-group component content, be a good method.Like this, select the amount of rhenium component usually, make that the platinum group metal contained is about 0.05: 1~about 2.75: 1 to the atomic ratio of rhenium in composition, best scope is about 0.25: 1~about 2: 1.Equally, select the tin components contents to make the composition that obtains contain the atomic ratio of platinum group metal to tin usually, about 0.1: 1~about 5: 1, best scope was about 0.5: 1~about 3: 1.Usually select the amount of germanium component, make that the germanium that contains is about 0.25: 1~about 5: 1 to the atomic ratio of platinum group metal in composition.
Platinum group metal and promoter metal component, can be suitable for obtaining the platinum group metal surface impregnation with any, and the method for promoter metal component surface impregnation, be attached in the catalyst composition of the present invention, to promoter metal, its dipping method should make the promoter metal component of whole basically surface impregnations all in the darkest 400 microns skin of catalyst carrier particle.
The component of platinum family and the dipping method preferably that promoter metal component also can be arranged are that the soluble and decomposable complex compound solution with platinum-group component and required promoter metal component hangs down acid dip.In general, the selection of solvent for use is the ability according to the used decomposable complex compound of its dissolving in this step dipping, and this solvent is to hang down acidity, the preferably aqueous solution.Low acidity refers to that dipping solution is generally 2 equivalents or below 2 equivalents.The most handy HCl solution, also can be with nitric acid and so on.
In preparation during catalyst of the present invention, more operable typical water-soluble, decomposable platinum family compound has: chloroplatinic acid, ammonium chloroplatinate, bromoplatinic acid, platinous chloride, platinum tetrachloride hydrate, dichloro carbonyl platinous chloride, dinitro diaminourea platinum, palladium bichloride, palladium bichloride dihydrate, palladium nitrate or the like.As the source of platinum, chloroplatinic acid is best.
Operable germanium compound has: germanium oxide, tetraethoxy germanium, four propoxyl group germanium, germanium tetrachloride, bifluoride germanium, tetrafluoride germanium, two iodate germanium, a germanium sulfide and similar compounds.A kind of good especially dipping solution is that the germanium metal by new life is dissolved in the oxychlorination germanium that produces in the chlorine water.Inferior good dipping solution is to be dissolved in the absolute ethyl alcohol by germanium tetrachloride.
The operable suitable pink salt or the water soluble compound of tin have: the pentahydrate of stannous bromide, stannous chloride, stannic chloride, stannic chloride, stannic chloride tetrahydrate, stannic chloride trihydrate, stannic chloride diamines, three chloro-stannic bromides, stannic chromate, stannous fluoride, tin fluoride, stannic iodide, STANNOUS SULPHATE CRYSTALLINE, tartaric acid tin and similar compound.The use of the chloride of tin such as stannic chloride and stannous chloride is good especially.
The compound of the rhenium that the typical case is available has: ammonium perrhenate, perrhenic acid sodium, potassium perrhenate and similar salt.In addition, also can use halid solution of rhenium such as chlorination rhenium; And best dipping solution is the aqueous solution of perrhenic acid.
Platinum-group component and promoter metal component can combine with carrier with any order.Can follow one or more promoter metal component of surface impregnation more earlier in carrier upper surface dipping platinum-group component.Also can be earlier in carrier upper surface dipping promoter metal component, dipping is gone up platinum-group component again.Also can consider to make platinum-group component and promoter metal component while surface impregnation to the solid refractory oxides carrier of nominal equivalent diameter more than 850 microns.
As previously mentioned, the present invention includes to use and contain the alkaline components that choosing adds or the carbon monoxide-olefin polymeric of alkaline earth metal component or its mixture.More particularly, this component is selected from the compound of one group of alkali metal-caesium, rubidium, potassium, sodium, lithium and the compound of a group of alkaline-earth metal-calcium, strontium, barium, magnesium and beryllium.In catalyst composition, this component can be with metastable compound such as oxide and sulfide exists or exist with the form with one or more other component combinations in the composition, or to exist in conjunction with the form as metal aluminate with alumina supporting material.Also can explain as following, because the composition of alkali metal containing and alkaline earth metal component,, usually will in air atmosphere, calcine being used to transform before the hydro carbons.So this component is a metal oxide being used for the most probable state of dehydrogenation.No matter what the accurate form that exists in composition of this component is, its preferably consumption be to make composition contain to have an appointment 0.01 to about 10%(weight) alkali metal or alkaline-earth metal, preferably contain 0.05~5%(weight of having an appointment).Alkali metal or alkaline-earth metal but must not be to be evenly distributed in the catalyst granules preferably.When the compound of this component lithium, potassium, caesium or its mixture, usually obtain best result.
Any method that can know with present technique field personnel alkali metal or alkaline earth metal component, combines with the carrier mass of porous, as with infusion process, coprecipitation, physical mixed and ion-exchange or the like.Yet the best way is the dipping of carrier material; This can or carry out later on before calcining, also can be before other components are added in carrier material, in the process or carry out afterwards.After platinum-group component and promoter metal component interpolation, add this component again and usually obtain best result; Because it can neutralize acid used in the dipping process in conjunction with said components.In general, the dip operation of carrier material, equally also be to contact with suitable, the decomposable compound or the salting liquid of required alkali metal or alkaline-earth metal, suitable compound comprises: halide, sulfate, nitrate, acetate, carbonate and similar compounds.For example: with after carrier combines, can obtain fabulous result with lithium nitrate or potassium nitrate aqueous solution dipping immediately in platinum-group component.
Catalyst composition of the present invention also can comprise halogen component.Halogen component can be fluorine, chlorine, bromine or iodine, or their mixture.Chlorine and bromine are best halogen components.Generally, halogen component is to exist with the state with porous carrier materials and basic component combination.Although be not absolutely necessary, had better be dispersed in the catalyst composition well for halogen component of the present invention.The content of halogen component is counted 0.2 of last catalyst composition~about 15%(weight with amount of element).
Can be attached to halogen component in the catalyst composition in any suitable manner; Can in carrier material preparation, carry out, also can be before, in the process or carry out afterwards in conjunction with other catalyst components.For example: may contain halogen in order to the alumina sol that generates desired alumina supporter material, a part of halogen component is provided in last catalyst composition so at least.When being attached on the carrier material, also can add halogen component or part halogen component, for example: when the platinum-impregnated component, use chloroplatinic acid to other catalytic components.Equally, catalyst is contacted with halogen or halogen-containing compound, the solution that contains halogen, suspension or dispersant, also can be added to halogen or part halogen in the catalyst composition, this can make other catalytic components with carrier material in conjunction with before or after carry out.Suitable halogen contained compound comprises, halogen-containing acid, for example: hydrochloric acid.In the follow-up catalyst regeneration stage catalyst is contacted with the compound, solution, suspension or the dispersant that contain halogen, also can add halogen or part halogen.
Catalyst of the present invention also can contain the sulphur component.General sulphur components contents is counted about 0.01 of last catalyst composition by element and is arrived 2%(weight).The sulphur component can be attached in the catalyst composition in any suitable manner, and the compound of the most handy sulphur or sulfur-bearing as hydrogen sulfide or low-molecular-weight mercaptan, contacts with catalyst composition under the condition that hydrogen exists.Hydrogen is about 100 to the mol ratio of sulphur, and temperature preferably is incorporated into the sulphur component from about 10 ℃ to about 540 ℃ under anhydrous condition.
Catalyst also can contain other annexing ingredient or its mixture, and they are separately or as catalyst aid, collaborative activity of such catalysts, selectivity and the stability improved.This catalyst aid preferably but must not be evenly distributed in the catalyst granules.Some catalyst aid of knowing comprises: antimony, arsenic, bismuth, cadmium, chromium, cobalt, copper, gallium, gold, indium, iron, manganese, nickel, scandium, silver, tantalum, thallium, titanium, tungsten, uranium, zinc and zirconium.Best component is from thallium, gallium and indium component.These annexing ingredients can be added to wherein in carrier material preparation or after the preparation in any suitable manner, and they also can be before adding other catalyst components, simultaneously or afterwards, are added in the catalyst composition in any suitable manner.
Best catalyst of the present invention is nonacid." non-acid " refers to herein, and catalyst has very low skeletal isomerization activity, promptly tests under dehydrogenation condition, and catalyst is lower than the 10%(mole to the amount that butene-1 is converted into isobutene), and preferably be lower than the 1%(mole).If necessary, improve the amount of basic component in the scope that present patent application requires, or use the steam treated catalyst, to remove some halogen component, can reduce the acidity of catalyst, it is nonacid making catalyst.
Catalyst component with the carrier material of porous in conjunction with after, generally will the catalyst composition that obtains about 100 °-Yue 320 ℃ down dry about 1-24 hours or longer, and then calcine about 10 hours of about 0.5-or longer down at about 320 °-600 ℃.Be used for before the hydroconversion process at last, burnt catalyst composition generally also will reduce.Restoring operation is in reducing environment, preferably in the hydrogen of doing, individual hour of about 0.5-10 or longer under about 100 °-Yue 650 ℃, the selection of temperature and time, whole basically platinum-group component that should be enough to reduce is the metal element state.
The oxide carrier material that solid is heat-resisting, the sorptive material of porous preferably, and have about 5-500m
2The high surface of/g.For the condition of using in hydroconversion process, this porous material should be heat-resisting relatively, and the catalyst carrier material that is generally used in the hydroconversion process also plans to comprise within the scope of the invention.For example: (1) activated carbon, coke or charcoal; (2) silica or silica gel, carborundum, clay and silicate, comprising synthetic preparation with naturally occurring, can be with also can be: activated clay, china clay, diatomite, bleaching earth, kaolin etc. without acid treatment, for example; (3) pottery, porcelain, broken refractory brick, alum clay; (4) heat-resisting inorganic oxide such as aluminium oxide, titanium dioxide, zirconium dioxide, chromium oxide, beryllium oxide, vanadium oxide, cerium oxide, hafnium oxide, zinc oxide, magnesia, boron oxide, thorium oxide, silica-alumina, silica-magnesia, chromium oxide-aluminium oxide, aluminium oxide-boron oxide, silica-zirconia or the like; (5) alumino-silicate of crystalline zeolite shape as the faujasite and/or the modenite of natural existence or synthetic preparation, can be Hydrogen, or metal cation have been gone up in exchange; (6) spinelle is as MgAl
2O
4, FeAl
2O
4, ZnAl
2O
4, CaAl
2O
4And other similar compounds, they have formula M O-Al
2O
3, M is the metal of divalence; (7) combination of one or more materials in above-mentioned each group.The best carrier material of this catalyst is an aluminium oxide, particularly γ or η aluminium oxide.
The nominal equivalent diameter of soild oxide carrier of the present invention as noted is at least about 850 microns.The nominal equivalent diameter refers to particle and be not less than 850 micron thickness on its narrowest diameter.Like this, be minimum about 850 microns of spherical its diameter as fruit granule, if columniform (situation about extruding in this way), the diameter of its circular cross-section is at least about 850 microns, and at least also about 850 microns of the length of cylinder.Equally, if the grain shape side of being that extrudes or rectangular, then its any one limit and height all can not be less than about 850 microns.Before surface analysis cross no matter the equivalent diameter of carrier how, platinum group metal and cocatalyst component, surface impregnation is believed that diffusion path can reduce, and can be improved desired product selectivity in the darkest 400 microns skin.It seems logically to be, the nominal equivalent diameter of carrier granular is reduced to be lower than 850 microns, can shorten diffusion path again.Yet the pressure drop that causes by catalyst bed of dwindling of particle diameter increases, and has increased relevant problem.Like this, the catalytic component of the dipping of all surfaces basically, be limited in the darkest 400 microns skin, limiting catalyst particle nominal equivalent diameter is at least about 850 microns simultaneously, preferably 1500 microns, then can when reducing diffusion path, keep the industrial available beds pressure drop and the device of catalyst.
Can by synthetic or naturally occurring original material, prepare good alumina supporting material with any suitable method, carrier can be the shape of any needs, and as spherical, sheet, pie, the shape extruded etc., the best shape of aluminium oxide is spherical.Importantly, the size of particle should make its nominal diameter at least about 850 microns, and certainly the about 1600 microns particle of nominal diameter is better.
Make the method for alumina balls, be metallic aluminium to be dissolved in the suitable acid become alumina sol, again the mixture of the colloidal sol that obtains and gelling agent such as urea is dripped in the oil bath, to generate the spheric granules of oxidation aluminium glue, comprise aging, dry and calcining by known method again, can be easy to convert it into desired γ or η alumina supporting material.Making the method for aluminium oxide cylinder, is the suitable gelatinizing agent that makes alumina powder and water and q.s, as nitric acid, mixes mutually, obtains extruded material group.Make material group extrude and be cut into the extrudate particle again by the mould of a suitable size.Also can make the alumina support of other shapes with usual way.After the alumina particle moulding, generally also want dry and calcining.Alumina support carries out intermediate treatment possibly in preparation process, comprises that water or Ammonia wash, and these processing all are well known in the art.
As noted, catalyst particularly suitable of the present invention is made hydrocarbon conversion catalyst, and the hydrocarbon that transform is contacted with catalyst under the hydrocarbon conversion condition.Conversion condition comprises: temperature is from about 200 °-1000 ℃, and pressure was from about 200 hours of the atmospheric pressure-about 0.1-of Yue 25 gauge pressures (101-2634KPa) liquid hourly space velocity (LHSV)
-1
According to one embodiment of present invention, but make the hydro carbons of dehydrogenation contact with catalyst composition of the present invention in keeping the dehydrogenation zone of dehydrogenation condition, the carrying out of this contact can be in fixed bde catalyst system, movable bed catalyst system, fluid bed system etc. or with single stage operation.Fixed bed system preferably.The hydrocarbon feed air-flow gives heat to required reaction temperature in the fixed bed system, feeds the dehydrogenation zone that fixed bde catalyst is housed again.Dehydrogenation zone itself also can comprise one or more reaction zones that separate, and there is heater the centre, to guarantee to enter the reaction temperature that each reaction zone can be kept to be needed.Hydrocarbon can be upper reaches, dirty or Radial Flow mode with the contact of catalyst bed.Plant-scale reactor preferably makes the hydro carbons radial flow cross catalyst bed, and hydro carbons can mix phase with liquid phase, vapour-liquid, vapour phase contact with catalyst, and vapour phase preferably.
But but the hydro carbons of dehydrogenation comprises the hydro carbons of carbon number from 2-30 or higher dehydrogenation, and alkane, alkylaromatic hydrocarbon, cycloalkane and alkene are arranged.Can be that carbon number is 2-30 or higher normal alkane with one group of hydro carbons of this catalyst dehydrogenation.This catalyst is specially adapted to carbon number is corresponding monoolefine or is carbon number that 3-15 or higher dehydrogenation of mono-olefins are corresponding alkadienes from 2-15 or higher dehydrating alkanes.
Dehydrogenation condition is: temperature is from about 400~900 ℃, and (1~1013KPA), liquid hourly space velocity (LHSV) (LHSV) was from about 0.1~100 hour from about 0.01~10 atmospheric pressure for pressure
-1Normal alkane is generally reached same conversion, and molecular weight is lower, and is temperature required higher.The pressure of dehydrogenation, it is low as far as possible maintained by the restriction of equipment, to help chemical balance.
Usually the logistics that flows out of dehydrogenation zone contains the product of unconverted dehydrogenatable hydrocarbons, hydrogen and dehydrogenation reaction.The normal cooling of this effluent circulation is also passed through a hydrogen Disengagement zone, to tell the vapour phase of Fu Qing from the liquid phase of rich hydrocarbon, the liquid phase of rich hydrocarbon will further be separated usually, and method can use suitable selectivity adsorbent, selective solvent, one or more selective reaction or design by means of suitable fractionation.Reclaim unconverted dehydrogenatable hydrocarbons, but and can be recycled to dehydrogenation zone.The product that obtains dehydrogenation reaction is as final products or as the intermediate products of other compound.
Before entering dehydrogenation zone, by in the middle of the dehydrogenation zone or after passing through, but the hydro carbons of dehydrogenation all can mix mutually with diluent.Diluent can be hydrogen, steam, methane, ethane, carbon dioxide, nitrogen, argon gas or similar gas or their mixture.Hydrogen is best diluent.When generally making diluent with hydrogen, its consumption should be enough to guarantee, hydrogen is to the mol ratio of hydrocarbon about 0.1: 1 to about 40: 1, and mol ratio is can get best result by about 10: 1 o'clock in about 1: 1.General diluent hydrogen stream by dehydrogenation zone is in the isolated recycle hydrogen in Hydrogen Separation district by the dehydrogenation zone effluent.
The water or the material that can generate water under dehydrogenation condition can be added in the dehydrogenation zone by continuously or intermittently as alcohol, aldehyde, ether or ketone, and its dosage calculates by the water of a great deal of, are about 1~20000PPM(weight of reinforced hydrocarbon stream).Contain 6~30 or during more carbon atom dehydrogenations making, add about 1~10000PPM(weight) water, obtain best result.
For in industrial successful use, dehydrogenation should have three characteristics, i.e. high activity, high selectivity and good stable.Activity is that catalyst is specified under the reaction condition at one group, and reactant is converted into measuring of product, promptly in given temperature, pressure, time of contact, as adding diluent such as hydrogen, also has the concentration of diluent.The activity of dehydrogenation is to measure for alkane amount in the raw material percentage that alkane transforms or disappears.Selectivity is that catalyst is converted into desirable product to reactant, with respect to measuring of the ability of reactant inversion quantity.Selection of catalysts is to measure the total mole number that transforms with respect to alkane, measures the amount of alkene in the product, represents with mole percent.Stability is activity and selectivity parameter, the measuring of the speed that changes with line duration, and the speed little expression catalyst of healing is more stable.
Because the dehydrogenation of hydro carbons is the endothermic reaction, and conversion ratio is subjected to Equilibrium limit, institute thinks that obtaining high conversion wishes to operate under high temperature and low hydrogen dividing potential drop.Under this harsh condition, be difficult to keep high activity and selectivity for a long time, because undesirable side reaction has increased as aromatisation, cracking, isomerization and coking.Therefore, a kind of its activity of acquisition, selectivity, the stable novel hydrocarbon dehydrogenation that all is improved are useful.
The embodiment that introduces below is to further specify Catalyst And Method of the present invention.The example that example is just enumerated for explanation, and should not think the present invention in other restriction of explaining widely, given as appended claim.
Fig. 1 and Fig. 2 have explained through diagrams and have been different from catalyst A of the present invention and accord with the behavior of catalyst B of the present invention in the dehydrating alkanes method.Fig. 1 is expressed as normal alkane conversion ratio (percentage by weight) function of online hourage in the test.Fig. 2 is the selectivity that generates positive alkene with the catalyst that weight percent is represented, as the functional arrangement of normal alkane conversion ratio (percetage by weight).
Fig. 3,4 and 5 expressions are corresponding to the catalyst in example 2,4 and 5, the radially gradient of platinum group metal and promoter metal.The expression of Metal Distribution is with the ratio of special metal concentration to alumina concentration, to being figure from the micron number of particle surface distance.The distribution of metal is definite with SEM (SEM).It should be noted that and do not represent actual metal concentration among the figure, just along catalyst granules metal relative concentration radially.
Embodiment 1
In order to show superiority of the present invention, prepared first kind and be different from comparative catalyst of the present invention.Earlier prepared the ball-aluminium oxide carrier with the oil drop method of knowing, again tin component precursor and alumina hydrosol fusion, this hydrosol of gelling and the tin component is combined with carrier again.The tin component is evenly distributed in the whole catalyst granules in this example, contains about 1500 microns of the ball-aluminium oxide carrier diameter of tin component.Again with containing H
2PtCl
6+ LiNo
3With 3.4% HNO
3The aqueous solution flood the carrier of stanniferous.Dipping rear catalyst in 150 ℃ of stoves dry 2 hours is again about 540 ℃ of calcinings 2.5 hours.Use about 2 hours of hydrogen reducing catalyst down at 500 ℃ then.This catalyst is catalyst A, contains 0.38% the platinum of having an appointment, about 0.5% tin and about 0.6% lithium, and they all are evenly distributed on whole catalyst particles intragranular.
Embodiment 2
Made second kind of catalyst according to the present invention in this example, made H
2Ptcl
6+ SnCl
2And the 1%HCl combination, preparation Pt(II)-the Sn(II) complex solution, and with the about 1500 microns 250cc ball-aluminium oxide carrier of its dipping diameter.Behind the dipping, catalyst is in stove, and drying is two hours under about 150 ℃, and calcines about 2.5 hours down at about 540 ℃.Thereafter, use LiNO
3The aqueous solution comes impregnated catalyst.In stove, under about 150 ℃, made catalyst dry 2 hours, and under about 540 ℃, calcined again 2.5 hours again.Burnt catalyst reduced about 2 hours down at 500 ℃ with hydrogen again.This catalyst by manufacturing of the present invention is called catalyst B.The last composition of catalyst B, 0.38% the platinum of having an appointment, 0.4% tin and about 0.6% lithium.
Embodiment 3
In this example,, come evaluate catalysts A, B with its performance as the normal alkane dehydrogenation.Test is to carry out in the pilot plant of device and product separator that responds.Raw material feeds reaction zone, and contacts with catalyst therein.Then, separate the also effluent in analytical reactions district.Raw material is being returned-is being changed on the basis, contains the 11.8%(weight of having an appointment) positive C
10Alkane, 26.7%(weight) positive C
11Alkane, 34% (weight) Nao 12Alkane and 27.5%(weight) positive C
13Alkane.Reaction zone maintains about 20Psig(138KPa gauge pressure) pressure.The reinforced speed that feeds reaction zone is enough to obtain about 70 hours
-1Liquid hourly space velocity (LHSV).Diluent hydrogen adds the speed of reaction zone, should be enough to make hydrogen that the molar ratio of hydrocarbon is about 4: 1.Raw material is heated to about 495 ℃ earlier before with the catalyst contact, the water content in the reaction zone maintains about 2000ppm(weight).
Fig. 1 and 2 has provided the result of these tests, Fig. 1 has described the function of normal alkane conversion ratio (percentage by weight) as online hourage with figure, the definition of normal alkane conversion ratio is an actual weight of having carried out the component of certain reaction in the fresh feed, divided by the gross weight of raw material.By among Fig. 1 as can be seen, catalyst A and B, practical manifestation goes out essentially identical normal alkane conversion ratio.Fig. 2 has described total positive alkene (TNO) selectivity (percentage by weight) with figure, as the function of normal alkane conversion ratio (percentage by weight).The definition of total positive olefine selective percentage is the weight that is converted into the raw material components of required positive olefin product, divided by the total amount of the raw material components that has carried out certain reaction.Observe the data of Fig. 2 and can find out catalyst B of the present invention, compare, show the selectivity of the higher desired positive alkene of generation with being different from catalyst A of the present invention.Can think that catalyst of the present invention shows higher selectivity, be the direct result of surface impregnation platinum and tin, also because whole platinum and tin component basically, all in the darkest 400 microns skin of catalyst granules.Can think that also this qualification that catalyst metal components is distributed promptly can reduce the diffusion path of reactant and product, the pressure by reaction zone falls simultaneously, industrial also be feasible.
Embodiment 4
According to United States Patent (USP) 3,584, method 060(Rausch) has prepared this routine catalyst.This catalyst is different from catalyst of the present invention.For preparing this catalyst, prepare the about 1500 microns ball-aluminium oxide carrier of diameter with the oil drop method of knowing.Again a spot of stannic chloride is dissolved in the nitric acid preparation dipping solution.In this solution, add a spot of 3.26%(weight again) the perrhenic acid solution and the 2.543%(weight of rhenium) platinum acid chloride solution of platinum.Adding water again makes solution weight reach 100 grams.Make this solution with above-mentioned ball-aluminium oxide carrier combination.Impregnated ball, 150 ℃ dry two hours down, the dry ball of crossing is containing 10%(weight again) in the air of steam, 540 ℃ of calcinings two hours, more only in air, 540 ℃ of calcining half an hour.
This dipping and make the catalyst composition that step obtains contains following catalytically-active metals: 0.388%(weight) platinum, 0.423%(weight) rhenium and 0.366%(weight) tin.This catalyst is called catalyst C.
Embodiment 5
Here according to United States Patent (USP) 3,878, method 131(Hayes) has prepared a kind of catalyst.It is not a catalyst of the present invention.Prepare the about 1500 microns ball-aluminium oxide carrier of diameter with the oil drop method of knowing.The preparation of dipping solution is that a spot of stannous chloride is dissolved in the hydrochloric acid, again the solution of dilute with water gained.Again the solution of germanium tetrachloride in ethanol is added in the above-mentioned solution, and then adds the small amounts of chlorine platinic acid.Resulting dipping solution and above-mentioned catalyst carrier combine.Impregnated carrier 150 ℃ dry two hours down, the impregnated carrier of doing is containing 10%(weight again) in the air of steam 540 ℃ of calcinings two hours, under similarity condition, do not add steam calcination two hours again.
The catalytically-active metals amount that contains in the catalyst composition that assay determination obtains is: 0.389%(weight) platinum, 0.263%(weight) tin, 0.245%(weight) germanium, this catalyst is called catalyst D.
Embodiment 6
Use SEM (SEM) in this example, estimated the catalyst C and the D of catalyst B of the present invention and prior art.The purpose of this analysis is to determine that above-mentioned every kind of catalyst is along the radially relative distribution of impregnating metal of catalyst granules.Before continuing discussion, should point out that the SEM data do not provide the metal actual amount of catalyst particles intragranular any point, only provide relative distribution situation with respect to the metal of aluminium oxide.In other words, each the possibility of result of analyzing can not be asked the integration of distribution curve not since zero point, can cause constructional mistake like that, because entire curve can be moved or move down.Therefore, these curves only are used as Metal Distribution relatively.
As by Fig. 3,4 and 5 see, observe platinum distribution along catalyst in catalyst B, C and D and show that the distribution of platinum is actually in the skin of catalyst granules in catalyst B of the present invention.The amount of platinum ((Pt K value/AlK value) * 1000 values) is 11 to 12 at particle surface, and is dropping to 3 from 100 microns places, catalyst carrier surface.So the feature platinum surface impregnation of catalyst B, because the concentration of platinum is more than two times of 200 microns core platinum of catalyst carrier relative concentration in 100 microns top layer.This is opposite with prior art catalyst C, the latter sees as Fig. 4, all constant along the value of catalyst granules whole radially ((Pt K value/AlK value) * 1000) is 10, and constant to prior art catalyst D as seen from Figure 5 along this value of catalyst granules be 12.Therefore these two kinds of catalyst can be described as the even dipping of platinum.
How the loyal color rice huller prostitute small cup of diving of beech is imitated the amount ((Sn K value/AlK value) * 1000 values) that S appreciates visible tin in the present invention, begins greater than 40, and is dropping to almost nil from 100 microns places, catalyst granules surface.As tin component among the prior art catalyst C that Fig. 4 saw also is surface impregnation, but the preceding platinum of having pointed out is not surface impregnation, so it is different from catalyst of the present invention.At last, as shown in Figure 5 among the prior art catalyst D tin component distribute and be even dipping.
Claims (8)
1, a kind of catalyst granules, this particle contains the platinum group metal component of catalytically effective amount, with be selected from tin, germanium, the promoter metal part of rhenium or its mixture, and combine with solid refractory oxides carrier, the nominal equivalent diameter that it is characterized in that said solid carrier is at least 850 microns, platinum group metal component and promoter metal component are surface impregnations, and the platinum-group component of surface impregnation and promoter metal component, mean concentration in outside 100 micron layers of catalyst granules is the twice of each respective components concentration in catalyst granules core 200 micron diameters at least.
2,, be combined with the alkali metal or the alkaline-earth metal composition of catalytically effective amount according to the catalyst granules of claim 1.
3,, it is characterized in that alkaline components is the lithium component according to the catalyst granules of claim 2.
4,, be combined with the halogen component of catalytically effective amount according to the catalyst granules of claim 1.
5,, it is characterized in that halogen component is the chlorine component according to the catalyst granules of claim 4.
6, according to any catalyst granules of claim 1 to 5, wherein the nominal equivalent diameter of solid carrier is 1500 microns.
7, a kind of hydroconversion process, the method is included under the hydrocarbon conversion condition, the contacted step of catalyst system that transformable hydrocarbon is formed with any catalyst granules of claim 1 to 6.
8, according to the hydroconversion process of claim 7, it is characterized in that, but transformable hydrocarbon is the hydrocarbon of dehydrogenation, and the hydrocarbon conversion condition is a dehydrogenation condition.