CN103387770A - Preparation method of nanometer transparent iron oxide red color paste for both water and oil - Google Patents
Preparation method of nanometer transparent iron oxide red color paste for both water and oil Download PDFInfo
- Publication number
- CN103387770A CN103387770A CN2013102679027A CN201310267902A CN103387770A CN 103387770 A CN103387770 A CN 103387770A CN 2013102679027 A CN2013102679027 A CN 2013102679027A CN 201310267902 A CN201310267902 A CN 201310267902A CN 103387770 A CN103387770 A CN 103387770A
- Authority
- CN
- China
- Prior art keywords
- iron oxide
- water
- mill base
- agent
- nanometer transparent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Material name | Example 1 | Example 2 | Example 3 |
Deionized water | 23.5 | 23.5 | 15.3 |
Sterilant | 0.2 | 0.2 | 0.2 |
PEG-200 | 5 | 5 | 5 |
Titanate coupling agent CT-115A | 1.5 | 1.5 | 1.5 |
Dispersion resin EFKA-1502 | 25 | - | - |
Dispersion resin EFKA-1503 | - | 24 | 25 |
EFKA4540 | 10 | - | - |
EFKA4560 | - | 10 | - |
TEGO752W | - | - | 12 |
Transparent iron oxide red | 35 | 35 | 40 |
AMP-95 | 0.4 | 0.4 | 0.5 |
BYK-024 | 0.2 | 0.2 | 0.3 |
Gas phase SiO 2 | 0.2 | 0.2 | 0.2 |
Emulsion or resinous type | Compatibility test | ΔE |
Benzene emulsion | Qualified | 0.26 |
Pure-acrylic emulsion | Qualified | 0.30 |
Acrylate and vinyl acetate emulsion | Qualified | 0.36 |
Uncle's acrylic emulsion | Qualified | 0.25 |
Aqueous polyurethane emulsion | Qualified | 0.38 |
Aqueous alkide resin | Qualified | 0.4 |
The oiliness acrylic resin | Qualified | 0.45 |
Long oil alkyd | Qualified | 0.32 |
The oiliness urethane resin | Qualified | 0.45 |
Claims (7)