CN103362227B - A kind of integrated many materials warming plate - Google Patents
A kind of integrated many materials warming plate Download PDFInfo
- Publication number
- CN103362227B CN103362227B CN201310266109.5A CN201310266109A CN103362227B CN 103362227 B CN103362227 B CN 103362227B CN 201310266109 A CN201310266109 A CN 201310266109A CN 103362227 B CN103362227 B CN 103362227B
- Authority
- CN
- China
- Prior art keywords
- parts
- plate
- aluminium foil
- glass magnesium
- many materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A kind of integrated many materials warming plate, it is combined by aluminium foil, glass magnesium plate, closed perlite insulation layer and cement board and forms.The present invention also has fire-proof function while insulation, uses safer, and greatly increases application life, can reach more than 25 years, easier for installation, and cost of manufacture is low, good looking appearance, can make shades of colour.
Description
Technical field
The present invention relates to building material field, specifically relate to a kind of integrated many materials warming plate.
Background technology
The material such as warming plate many employings EPS plate, ASPS plate of current skin is made, though this material can play the effect of insulation, but due to its all dead lipid materials, burning-point is low, can not play fireproofing function, fire spreading can be accelerated when building breaking out of fire, safety factor is not high, and this kind of materials'use life-span is not high, slag-off phenomenon of generally fading after exterior wall arranges 3-5, its construction technology relative complex made, cost is high.
Summary of the invention
The object of the invention is to the deficiency overcoming above-mentioned technology, provide one can fireproof warming plate, and long service life, cost of manufacture is cheap.
For achieving the above object, the technical solution used in the present invention is: a kind of integrated many materials warming plate, and it is combined by aluminium foil, glass magnesium plate, closed perlite insulation layer and cement board and forms.Described glass magnesium plate is made up of the raw material of following weight portion: 80 ~ 120 parts, magnesia, French chalk 40 ~ 60 parts, 20 ~ 40 parts, sawdust, perlite 3 ~ 5 parts.Described closed perlite is made up of the raw material of following weight portion: bead 120 ~ 180 parts, hydrophober 2.1 ~ 2.6 parts, water glass 90 ~ 110 parts, silicon phosphate 6 ~ 10 parts, calcium bicarbonate 22 ~ 26 parts, 95 ~ 105 parts, water, polypropylene 0.4 ~ 0.6 part, hydroxypropyl methylcellulose 1.2 ~ 1.8 parts.Described cement board is made up of the raw material of following weight portion: 425# cement 400 ~ 500 parts, great Sha 500 ~ 600 parts, rubber powder 8 ~ 12 parts, cellulose 2 ~ 4 parts.
Described glass magnesium plate and cement board all add layer of non-woven fabric or grid cloth in the process made.
The technique that described many materials integrated heat-preservation hanging plate makes coats F-C paint or multi-color on the aluminium foil made, and then on aluminium foil, coat polyurethane sealing, aluminium foil is bonded on glass magnesium plate, under the pressure of 25MPa, aluminium foil, glass magnesium plate, closed perlite insulation layer and cement board to be forced together composition warming plate by press, and fuse through the temperature of 80 ~ 100 degrees Celsius, then the microwave drying passage that warming plate is delivered into 30 meters long by conveyer belt is carried out drying.
Described closed perlite insulation layer can replace with EPS plate and polyurethane foam material, and described aluminium foil can omit, and directly F-C paint or multi-color is coated on glass magnesium plate and can reaches required effect equally.
The raw material components of the better weight portion of glass magnesium plate of the present invention is: 100 parts, magnesia, French chalk 50 parts, 30 parts, sawdust, perlite 4 parts.
The raw material components of the better weight portion of closed perlite of the present invention is: bead 150 parts, hydrophober 2.4 parts, water glass 100 parts, silicon phosphate 8 parts, calcium bicarbonate 24 parts, 100 parts, water, polypropylene 0.5 part, hydroxypropyl methylcellulose 1.5 parts.
The raw material components of the better weight portion of cement board of the present invention is: 425# cement 450 parts, great Sha 550 parts, rubber powder 10 parts, cellulose 3 parts.
Beneficial effect of the present invention is: while insulation, also have fire-proof function, use safer, and greatly increase application life, can reach more than 25 years, easier for installation, and cost of manufacture is low, good looking appearance, can make shades of colour.
Detailed description of the invention
Below in conjunction with embodiment, the present invention will be further described.
Embodiment 1
A kind of integrated many materials warming plate, combined by aluminium foil, glass magnesium plate, closed perlite insulation layer and cement board and form, described glass magnesium plate is made up of the raw material of following weight portion: 80 parts, magnesia, French chalk 40 parts, 20 parts, sawdust, perlite 3 parts.Described closed perlite is made up of the raw material of following weight portion: bead 120 parts, hydrophober 2.1 parts, water glass 90 parts, silicon phosphate 6 parts, calcium bicarbonate 22 parts, 95 parts, water, polypropylene 0.4 part, hydroxypropyl methylcellulose 1.2 parts.Described cement board is made up of the raw material of following weight portion: 425# cement 400 parts, great Sha 500 parts, rubber powder 8 parts, cellulose 2 parts.
The manufacture craft of described glass magnesium plate is: get magnesium chloride and be dissolved in water, measure and be adjusted to 23 degree with Baume hydrometer, then add centesimal modifier; Get raw material by the formula of glass magnesium plate and stir dry powder, adding magnesium chloride solution above-mentioned in right amount, after being stirred to suitable thick dilution, doing plate.
The manufacture craft of described cement board takes after raw material mixes according to above-mentioned cement board raw material components, and add water and stir, being placed in mould of stirring treats that it solidifies.
The technique that described many materials integrated heat-preservation hanging plate makes coats F-C paint or multi-color on the aluminium foil made, and then on aluminium foil, coat polyurethane sealing, aluminium foil is bonded on glass magnesium plate, under the pressure of 25MPa, aluminium foil, glass magnesium plate, closed perlite insulation layer and cement board to be forced together composition warming plate by press, and fuse through the temperature of 80 ~ 100 degrees Celsius, then the microwave drying passage that warming plate is delivered into 30 meters long by conveyer belt is carried out drying.
Described closed perlite insulation layer can replace with EPS plate and polyurethane foam material, and described aluminium foil can omit, and directly F-C paint or multi-color is coated on glass magnesium plate and can reaches required effect equally.
Embodiment 2
A kind of integrated many materials warming plate, it is combined by aluminium foil, glass magnesium plate, closed perlite insulation layer and cement board and forms.Described glass magnesium plate is made up of the raw material of following weight portion: 120 parts, magnesia, French chalk 60 parts, 40 parts, sawdust, perlite 5 parts.Described closed perlite is made up of the raw material of following weight portion: bead 180 parts, hydrophober 2.6 parts, water glass 110 parts, silicon phosphate 10 parts, calcium bicarbonate 26 parts, 105 parts, water, polypropylene 0.6 part, hydroxypropyl methylcellulose 1.8 parts.Described cement board is made up of the raw material of following weight portion: 425# cement 500 parts, great Sha 600 parts, rubber powder 12 parts, cellulose 4 parts.
Manufacture craft is with embodiment 1.
Embodiment 3
A kind of integrated many materials warming plate, is combined by aluminium foil, glass magnesium plate, closed perlite insulation layer and cement board and forms.The raw material components of the weight portion of described glass magnesium plate is: 100 parts, magnesia, French chalk 50 parts, 30 parts, sawdust, perlite 4 parts.The raw material components of the weight portion of described closed perlite is: bead 150 parts, hydrophober 2.4 parts, water glass 100 parts, silicon phosphate 8 parts, calcium bicarbonate 24 parts, 100 parts, water, polypropylene 0.5 part, hydroxypropyl methylcellulose 1.5 parts.The raw material components of the weight portion of described cement board is: 425# cement 450 parts, great Sha 550 parts, rubber powder 10 parts, cellulose 3 parts.
Claims (4)
1. integration many materials warming plate, is characterized in that: it is combined by aluminium foil, glass magnesium plate, closed perlite insulation layer and cement board and forms; Described glass magnesium plate is made up of the raw material of following weight portion: 80 ~ 120 parts, magnesia, French chalk 40 ~ 60 parts, 20 ~ 40 parts, sawdust, perlite 3 ~ 5 parts; Described closed perlite insulation layer is made up of the raw material of following weight portion: bead 120 ~ 180 parts, hydrophober 2.1 ~ 2.6 parts, water glass 90 ~ 110 parts, silicon phosphate 6 ~ 10 parts, calcium bicarbonate 22 ~ 26 parts, 95 ~ 105 parts, water, polypropylene 0.4 ~ 0.6 part, hydroxypropyl methylcellulose 1.2 ~ 1.8 parts; Described cement board is made up of the raw material of following weight portion: 425# cement 400 ~ 500 parts, great Sha 500 ~ 600 parts, rubber powder 8 ~ 12 parts, cellulose 2 ~ 4 parts.
2. the integrated many materials warming plate of one according to claim 1, is characterized in that: described glass magnesium plate and cement board all add layer of non-woven fabric or grid cloth in the process made.
3. the integrated many materials warming plate of one according to claim 1, it is characterized in that: the technique that described many materials integrated heat-preservation hanging plate makes coats F-C paint or multi-color on the aluminium foil made, and then on aluminium foil, coat polyurethane sealing, aluminium foil is bonded on glass magnesium plate, by press under the pressure of 25MPa by aluminium foil, glass magnesium plate, closed perlite insulation layer and cement board force together composition warming plate, and fuse through the temperature of 80 ~ 100 degrees Celsius, then the microwave drying passage that warming plate is delivered into 30 meters long by conveyer belt is carried out drying.
4. the integrated many materials warming plate of one according to claim 1, is characterized in that: described closed perlite insulation layer EPS plate and polyurethane foam material replace, and described aluminium foil omits, and directly F-C paint or multi-color is coated on glass magnesium plate.