CN103357778A - Pan and manufacturing method thereof - Google Patents
Pan and manufacturing method thereof Download PDFInfo
- Publication number
- CN103357778A CN103357778A CN2012101033268A CN201210103326A CN103357778A CN 103357778 A CN103357778 A CN 103357778A CN 2012101033268 A CN2012101033268 A CN 2012101033268A CN 201210103326 A CN201210103326 A CN 201210103326A CN 103357778 A CN103357778 A CN 103357778A
- Authority
- CN
- China
- Prior art keywords
- pot
- pan
- thickness
- edge
- limit
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a pan which comprises a pan bottom and a pan edge, wherein a pan brim is arranged at the top of the pan edge; the thickness of the pan bottom and the thickness of the pan brim are greater than that of the pan edge; and the thicknesses of the pan bottom, the pan brim and the pan edge are between 0.5mm and 6mm. The thickness of the pan bottom of the pan with the structure is greater, so that the pan bottom can be heated uniformly and does not deform easily, and the probability of pan pasting is low; the pan edge of the pan is thinner, so that the weight of a whole pan body is lighter; and the thickness of the pan brim of the pan is greater, so that the pan is better in strength, and the overall usability of the pan is better. The invention further discloses a manufacturing method of the pan. By implementing the steps sequentially, a formed product is more reasonable in thickness distribution and the usability is improved correspondingly.
Description
Technical field
The present invention relates to cook equipment manufacturing technology field, particularly a kind of pot.The invention still further relates to a kind of manufacture method for the production of this kind pot.
Background technology
Pot is as the requisite cooking apparatus of a kind of daily life, and it has brought many facilities for daily life, and along with the in recent years continuous growth of living standard and user's user demand, people also have higher requirement to the serviceability of pot.
Composite steel pot in the market mostly is greatly the uniform thickness product, and the product thickness after its moulding is generally at 2 millimeters～5 millimeters.Have this pot that waits thick structure, although can satisfy basic culinary art needs, thickness is 2 millimeters pot, because its material is thinner, is out of shape using to produce in consisting of easily, and is prone to the phenomenon of being burned when cooking; And thickness is greater than 3 millimeters pot, and himself weight is larger, brings inconvenience when mentioning pot for the user in cooking process.
Therefore, how to optimize the product thickness after pot moulding, so that its serviceability is more preferably the important technological problems that those skilled in the art need to solve at present.
Summary of the invention
For solving the problems of the technologies described above, the invention provides a kind of pot, product thickness and serviceability thereof after its moulding are better.Another object of the present invention provides a kind of manufacture method for the production of above-mentioned pot.
For solving the problems of the technologies described above, the invention provides a kind of pot, comprise the bottom of a pan and pot limit, the top on described pot limit has the pot edge, the thickness in the described the bottom of a pan and the thickness of described pot edge are all greater than the thickness on described pot limit, and the thickness on the described the bottom of a pan, described pot edge and described pot limit is all between 0.5 millimeter～6 millimeters.
Preferably, the described the bottom of a pan is specially by one or more thes bottom of a pan of making in steel plate, aluminium sheet, copper coin, iron plate, titanium plate or other metallic plates;
Described pot limit is specially by one or more pot limits of making in steel plate, aluminium sheet, copper coin, iron plate, titanium plate or other metallic plates;
Described pot edge is specially by one or more pot edges of making in steel plate, aluminium sheet, copper coin, iron plate, titanium plate or other metallic plates.
The present invention also provides a kind of pot manufacture method, comprises step:
Get the raw materials ready, the removing surface of some metal blanks is clean, and at its surface coating one deck lubricating oil;
Compressing, each metal blank is stacked on the mould, and make punch and the die matched moulds of described mould by extruder, with the multiple layer metal plate is pressed into thickness between 0.5 millimeter～6 millimeters the pot, and after the moulding the pot the bottom of a pan thickness and pot edge thickness all greater than its pot limit thickness
Preferably, described metal blank is specially one or more in steel plate, aluminium sheet, copper coin, iron plate, titanium plate or other metallic plates.
Relative above-mentioned background technology, pot provided by the present invention, comprise the bottom of a pan and pot limit, the top on described pot limit has the pot edge, the thickness in the described the bottom of a pan and the thickness of described pot edge are all greater than the thickness on described pot limit, and the thickness on the described the bottom of a pan, described pot edge and described pot limit is all between 0.5 millimeter～6 millimeters.Pot with this kind structure, the thickness at its place, the bottom of a pan is larger, can guarantee that being heated evenly of place, the bottom of a pan is not yielding, the difficult phenomenon of being burned, and place, its pot limit is thinner, so that the weight of whole pot body is less, simultaneously, the thickness at its place, pot edge is larger, makes its abrasion resistance properties better, thereby so that the whole serviceability of described pot is better.
Description of drawings
Fig. 1 for a kind of implementation side of the present invention provide the pot the structure cutaway view;
The flow chart of manufacture method of the pot that Fig. 2 provides for a kind of specific embodiment of the present invention.
The specific embodiment
Core of the present invention provides a kind of pot, and product thickness and serviceability thereof after its moulding are better; A kind of manufacture method for above-mentioned pot is provided simultaneously.
In order to make those skilled in the art person understand better the present invention program, the present invention is described in further detail below in conjunction with the drawings and specific embodiments.
Please refer to Fig. 1, Fig. 1 for a kind of implementation side of the present invention provide the pot the structure cutaway view.
In the specific embodiment, pot provided by the present invention comprises the bottom of a pan 11 and pot limit 12, and the top on pot limit 12 has pot edge 13, the thickness of the thickness in the bottom of a pan 11 and pot edge 13 is all greater than the thickness on pot limit 12, and the thickness on the bottom of a pan 11, pot edge 13 and pot limit 12 is all between 0.5 millimeter～6 millimeters.Pot with this kind structure, the thickness at its 11 places, the bottom of a pan is larger, can guarantee that being heated evenly of 11 places, the bottom of a pan is not yielding, the difficult phenomenon of being burned, and 12 places, its pot limit are thinner, so that the weight of whole pot body is less, simultaneously, the thickness at its 13 places, pot edge is larger, makes its abrasion resistance properties better, thereby so that the whole serviceability of described pot is better.
Further, the bottom of a pan 11 is specially by one or more thes bottom of a pan of making in steel plate, aluminium sheet, copper coin, iron plate, titanium plate or other metallic plates; Pot limit 12 is specially by one or more pot limits of making in steel plate, aluminium sheet, copper coin, iron plate, titanium plate or other metallic plates; Pot edge 13 is specially by one or more pot edges of making in steel plate, aluminium sheet, copper coin, iron plate, titanium plate or other metallic plates.
In the specific embodiment, the manufacture method of pot provided by the present invention comprises:
Step 101: get the raw materials ready;
The removing surface of some metal blanks is clean, and at its surface coating one deck lubricating oil, so that the smooth enforcement of follow-up compressing technique.
Step 102: compressing;
Each metal blank is stacked on the mould, and make punch and the die matched moulds of described mould by extruder, with the multiple layer metal plate is pressed into thickness between 0.5 millimeter～6 millimeters the pot, and after the moulding the pot the bottom of a pan thickness and pot edge thickness all greater than its pot limit thickness.So that the distribution of the product thickness after its moulding is more reasonable, the corresponding raising of serviceability.
In summary, the pot that provides among the present invention comprises the bottom of a pan and pot limit, and the top on described pot limit has the pot edge, the thickness in the described the bottom of a pan and the thickness of described pot edge are all greater than the thickness on described pot limit, and the thickness on the described the bottom of a pan, described pot edge and described pot limit is all between 0.5 millimeter～6 millimeters.Pot with this kind structure, the thickness at its place, the bottom of a pan is larger, can guarantee that being heated evenly of place, the bottom of a pan is not yielding, the difficult phenomenon of being burned, and place, its pot limit is thinner, so that the weight of whole pot body is less, simultaneously, the thickness at its place, pot edge is larger, makes its abrasion resistance properties better, thereby so that the whole serviceability of described pot is better.
In addition, the manufacture method for above-mentioned pot provided by the invention, by the successively enforcement of each step, so that the distribution of the product thickness after the moulding is more reasonable, the corresponding raising of serviceability.
More than pot provided by the present invention and manufacture method thereof are described in detail.Used specific case herein principle of the present invention and embodiment are set forth, the explanation of above embodiment just is used for helping to understand method of the present invention and core concept thereof.Should be pointed out that for those skilled in the art, under the prerequisite that does not break away from the principle of the invention, can also carry out some improvement and modification to the present invention, these improvement and modification also fall in the protection domain of claim of the present invention.
Claims (4)
1. pot, comprise the bottom of a pan and pot limit, the top on described pot limit has the pot edge, it is characterized in that: the thickness in the described the bottom of a pan and the thickness of described pot edge are all greater than the thickness on described pot limit, and the thickness on the described the bottom of a pan, described pot edge and described pot limit is all between 0.5 millimeter～6 millimeters.
2. as claimed in claim 1 pot, it is characterized in that: the described the bottom of a pan is specially by one or more thes bottom of a pan of making in steel plate, aluminium sheet, copper coin, iron plate, titanium plate or other metallic plates;
Described pot limit is specially by one or more pot limits of making in steel plate, aluminium sheet, copper coin, iron plate, titanium plate or other metallic plates;
Described pot edge is specially by one or more pot edges of making in steel plate, aluminium sheet, copper coin, iron plate, titanium plate or other metallic plates.
3. the manufacture method of a pot is characterized in that, comprises step:
Get the raw materials ready, the removing surface of some metal blanks is clean, and at its surface coating one deck lubricating oil;
Compressing, each metal blank is stacked on the mould, and make punch and the die matched moulds of described mould by extruder, with the multiple layer metal plate is pressed into thickness between 0.5 millimeter～6 millimeters the pot, and after the moulding the pot the bottom of a pan thickness and pot edge thickness all greater than its pot limit thickness.
4. the manufacture method of pot as claimed in claim 3, it is characterized in that: described metal blank is specially one or more in steel plate, aluminium sheet, copper coin, iron plate, titanium plate or other metallic plates.