CN103351722A - Green energy-saving light-emitting paint - Google Patents
Green energy-saving light-emitting paint Download PDFInfo
- Publication number
- CN103351722A CN103351722A CN 201310266480 CN201310266480A CN103351722A CN 103351722 A CN103351722 A CN 103351722A CN 201310266480 CN201310266480 CN 201310266480 CN 201310266480 A CN201310266480 A CN 201310266480A CN 103351722 A CN103351722 A CN 103351722A
- Authority
- CN
- China
- Prior art keywords
- parts
- solution
- green energy
- pigment
- saving light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a green energy-saving light-emitting paint which is composed of the following components in parts by weight: 100-150 parts of water, 0.8-1.2 parts of sodium hexametaphosphate solution, 10-13 parts of pearlescent pigment, 2-4 parts of luminous pigment, 10-13 parts of zinc oxide, 1.8-2.3 parts of tributyl phosphate, 30-50 parts of hydroxy cellulose solution, 10-12 parts of hydroxyethyl cellulose, 5-10 parts of rutile titanium white, 5 parts of color paste, 100-120 parts of sodium carboxymethyl cellulose solution, 50-60 parts of polyacrylamide solution, 40-60 parts of aluminum sulfate solution, 1-3 parts of terbium oxide catalyst, 5-10 parts of toughener, 5-15 parts of flame retardant, 50-60 parts of polybutene alcoholic solution and 50-60 parts of styrene-acrylic emulsion. The material has the advantages of high temperature resistance, low temperature resistance, abrasion resistance, long service life, environment friendliness and no harm to the human body.
Description
Technical field
The present invention relates to a kind of green energy conservation luminous paint.
Background technology
Noctilucence product in the domestic Coating Market, generally adopt the synthetic resin emulsion multi-colour spraying plastic paint, although this coating rich color, texture is stronger, but also exists the some shortcomings part, can't show illumination effect stiff unchanged, night such as the object plane after decorating, part material is poisonous or inflammable and explosive, do not have an environmental-protecting performance, production and workmen are had injury, and some noctilucence time is short and investment of production is large, high in cost of production, is difficult to the satisfying the market diversified demand.
Summary of the invention
Technical problem to be solved by this invention is: a kind of green energy conservation luminous paint is provided.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A kind of green energy conservation luminous paint, composition by following parts by weight forms: water 100-150 part, sodium hexametaphosphate solution 0.8-1.2 part, pearly pigment 10-13 part, luminous pigment 2-4 part, zinc oxide 10-13 part, tbp 1.8-2.3 part, hydroxylated cellulose solution 30-50 part, Natvosol 10-12 part, Rutile type Titanium Dioxide 5-10 part, 5 parts of mill bases, carboxymethylcellulose sodium solution 100-120 part, polyacrylamide solution 50-60 part, alum liquor 40-60 part, terbium sesquioxide catalyzer 1-3 part, toughner 5-10 part, fire retardant 5-15 part, polybutene alcoholic solution 50-60 part, benzene emulsion 50-60 part.
The invention has the beneficial effects as follows: high temperature resistant, the low temperature of this material energy, humidity, wear-resistant, long service life, environmental protection does not injure human body.
Embodiment
Embodiment 1
A kind of green energy conservation luminous paint, composition by following parts by weight forms: water 100-150 part, sodium hexametaphosphate solution 0.8-1.2 part, pearly pigment 10-13 part, luminous pigment 2-4 part, zinc oxide 10-13 part, tbp 1.8-2.3 part, hydroxylated cellulose solution 30-50 part, Natvosol 10-12 part, Rutile type Titanium Dioxide 5-10 part, 5 parts of mill bases, carboxymethylcellulose sodium solution 100-120 part, polyacrylamide solution 50-60 part, alum liquor 40-60 part, terbium sesquioxide catalyzer 1-3 part, toughner 5-10 part, fire retardant 5-15 part, polybutene alcoholic solution 50-60 part, benzene emulsion 50-60 part.
Claims (1)
1. green energy conservation luminous paint, composition by following parts by weight forms: water 100-150 part, sodium hexametaphosphate solution 0.8-1.2 part, pearly pigment 10-13 part, luminous pigment 2-4 part, zinc oxide 10-13 part, tbp 1.8-2.3 part, hydroxylated cellulose solution 30-50 part, Natvosol 10-12 part, Rutile type Titanium Dioxide 5-10 part, 5 parts of mill bases, carboxymethylcellulose sodium solution 100-120 part, polyacrylamide solution 50-60 part, alum liquor 40-60 part, terbium sesquioxide catalyzer 1-3 part, toughner 5-10 part, fire retardant 5-15 part, polybutene alcoholic solution 50-60 part, benzene emulsion 50-60 part.