CN103341488B - A kind of processing method of 1/8th hard slim pure copper strips of state - Google Patents
A kind of processing method of 1/8th hard slim pure copper strips of state Download PDFInfo
- Publication number
- CN103341488B CN103341488B CN201310212008.XA CN201310212008A CN103341488B CN 103341488 B CN103341488 B CN 103341488B CN 201310212008 A CN201310212008 A CN 201310212008A CN 103341488 B CN103341488 B CN 103341488B
- Authority
- CN
- China
- Prior art keywords
- copper strips
- pure copper
- rolling
- state
- hard
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The processing method that the invention discloses a kind of 1/8th hard slim pure copper strips of state, wherein by selecting pure copper strips raw material and being rolling to the finished product thickness size of required 1/8th hard state pure copper strips obtained, first carry out it again making annealing treatment and obtaining the semi-finished product copper strips of soft state, the most above-mentioned semi-finished product copper strips is carried out and hightension rolling, just can obtain hard state (H/8) the relatively thin pure copper strips of required 1/8th at rolling time control controlling rolling tension force.The production procedure of this processing method is short, and processing cost is low, and the production efficiency of product is high, and the performance of the slim pure copper strips product of acquisition has good stability.
Description
Technical field
The processing method that the present invention relates to a kind of pure copper strips, the processing method particularly relating to the pure copper strips of a kind of 1/8th hard states and thinner thickness.
Background technology
In the market,
H/2
State (1/2nd hard states),
H/4
State (1/4th hard states) and
H
State (the hardest state) copper strips is relatively conventional, and the production method of above-mentioned copper strips is the most ripe.The method producing above-mentioned copper strips in traditional mode of production mainly has two kinds, and one is accurately to be controlled by working modulus, and another kind of method is then by partial annealing technology controlling and process, obtains the band of different conditions.But require for Special use
H/8
The pure copper strips of state (1/8th hard states) thinner thickness, according to first method, because working modulus and drafts are less, is difficulty with production and processing；And according to second method, because Vickers hardness area requirement is less, wayward, therefore, copper strips production method of the prior art is all difficult to meet its production requirement.
Summary of the invention
It is an object of the invention to provide the processing method of a kind of 1/8th hard slim pure copper strips of state to obtain 1/8th hard state pure copper strips of thinner thickness.
For reaching above-mentioned purpose, the technical solution used in the present invention is:
The processing method of a kind of 1/8th hard slim pure copper strips of state, described processing method comprises the steps:
(
1
) raw material preparation, select pure copper strips raw material, and described pure copper strips raw material is rolling to the finished product thickness size of 1/8th hard state pure copper strips of required acquisition；
(
2
) annealing, the described pure copper strips rolled being put in annealing furnace and makes annealing treatment, annealing temperature controls
260
DEG C～
350
DEG C, the heating-up time controls
2h
~
6h
, and be incubated
3h
~
8h
, the temperature come out of the stove after insulation is
60
DEG C～
70
DEG C, it is thus achieved that soft state semi-finished product copper strips；
(
3
) cleaning treatment, the surface of described semi-finished product copper strips is carried out；
(
4
) hightension rolling, the described semi-finished product copper strips after cleaning is carried out hightension rolling, during rolling, tension force controls
1300N
~
1900N
Between, i.e. obtain described 1/8th hard state pure copper strips after rolling.
Preferably, described step (
1
In), the trade mark of described pure copper strips raw material is
TU0
、
TU1
、
TU2
、
T2
In one.
Preferably, described step (
1
In), the thickness of the described pure copper strips after rolling is
0.08mm
~
0.2mm
。
Preferably, described step (
4
In), rolling speed controls
40m/min
~
60m/min
。
Utilization due to technique scheme, the present invention compared with prior art has the advantage that the processing method of the hard slim pure copper strips of state of one 1/8th of the present invention, wherein by selecting pure copper strips raw material and being rolling to the finished product thickness size of required 1/8th hard state pure copper strips obtained, first carry out it again making annealing treatment and obtaining the semi-finished product copper strips of soft state, the most above-mentioned semi-finished product copper strips is carried out and hightension rolling, rolling time control controlling rolling tension force just can obtain the hard state of required 1/8th (
H/8
) relatively thin pure copper strips.The production procedure of this processing method is short, and processing cost is low, and the production efficiency of product is high, and the performance of the slim pure copper strips product of acquisition has good stability.
Detailed description of the invention
Below in conjunction with specific embodiment, technical scheme is further elaborated.
Specific embodiment
1
The selection trade mark is
TU2
Pure copper strips as raw material, and be rolling to thickness through four-high reversing mill and be
0.15mm
, width be
380mm
Copper strips, then the pure copper strips after rolling is put in bell type annealing furnace and makes annealing treatment, annealing temperature is
260
DEG C, the heating-up time
2h
And be incubated
3h
, tapping temperature is
60
DEG C, it is thus achieved that soft state (
M
State) semi-finished product copper strips.Forwarding to this semi-finished product copper strips be carried out on cleaning machine row again, use hightension rolling, winding tension is
1400N
, speed is
60m/min
.During rolling, need to observe the flatness situation of copper strip surface, adjust winding tension in time, prevent from causing deformation of strip because winding tension is excessive.The copper strips product of rolling is obtained after rolling.
Specific embodiment
2
With embodiment in this embodiment
1
Difference be, during rolling, the tension force of rolling is
1800N
, after rolling, obtain the copper strips product of rolling.
Above-mentioned two embodiment is produced the copper strips product obtained and carries out performance detection, according to
GB/T228.1
With
GB/T4340.1
Standard test.Respectively to the soft state semi-finished product copper strips after annealing, specific embodiment
1
The first group of copper strips product obtained and specific embodiment
2
The second group of copper strips product obtained take head, in, tail three part detection sample, measure each group of detection tensile strength of sample and Vickers hardness respectively, measurement result is as shown in the table:
As can be seen from the above table, through embodiment
1
, embodiment
2
The hardness of the copper strips product obtained is satisfied by
HV60
~
70
, tensile strength meets
240MPa
~
270 MPa
, reach 1/8th hard states (
H/8
) the correlated performance requirement of pure copper strips.
To sum up, the processing method of the hard slim pure copper strips of state of one 1/8th of the present invention, the performance wherein utilizing intermetallic composite coating to harden, solve working modulus and be difficult to problem uppity with partial annealing, it is thus achieved that the hard state of 1/8th of stable performance (
H/8
) relatively thin pure copper strips.The production procedure of this processing method is short, and processing cost is low, and the production efficiency of product is high, and the performance of the slim pure copper strips product simultaneously obtained has good stability.
Above-described embodiment is only for technology design and the feature of the explanation present invention; its object is to allow person skilled in the art will appreciate that present disclosure and to be carried out; can not limit the scope of the invention with this; all equivalence changes made according to spirit of the invention or modification, all should contain within the scope of the present invention.
Claims (1)
1. the processing method of the hard slim pure copper strips of state, it is characterised in that: described processing method comprises the steps:
(1) raw material prepares, select pure copper strips raw material, and described pure copper strips raw material is rolling to the finished product thickness size of 1/8th hard state pure copper strips of required acquisition, wherein, the trade mark of described pure copper strips raw material is the one in TU0, TU1, TU2, T2, and the thickness of the described pure copper strips after rolling is 0.08mm～0.2mm；
(2) annealing, puts into the described pure copper strips rolled in annealing furnace and makes annealing treatment, and annealing temperature controls at 260 DEG C～350 DEG C, heating-up time controls at 2h～6h, and it being incubated 3h～8h, the temperature come out of the stove after insulation is 60 DEG C～70 DEG C, it is thus achieved that soft state semi-finished product copper strips；
(3) cleaning treatment, is carried out the surface of described semi-finished product copper strips；
(4) hightension rolling, carries out hightension rolling to the described semi-finished product copper strips after cleaning, and during rolling, tension force controls between 1300N～1900N, and rolling speed controls i.e. to obtain described 1/8th hard state pure copper strips after 40m/min～60m/min, rolling.