CN103333485A - High impact resistance nanometer composite material - Google Patents
High impact resistance nanometer composite material Download PDFInfo
- Publication number
- CN103333485A CN103333485A CN 201310178397 CN201310178397A CN103333485A CN 103333485 A CN103333485 A CN 103333485A CN 201310178397 CN201310178397 CN 201310178397 CN 201310178397 A CN201310178397 A CN 201310178397A CN 103333485 A CN103333485 A CN 103333485A
- Authority
- CN
- China
- Prior art keywords
- composite material
- impact resistance
- high impact
- high resistance
- nano composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a high impact resistance nanometer composite material, which is prepared from the following raw materials, by weight: 20-45% of a polyamide resin, 10-15% of a toughening agent, 15-30% of nanometer powder, 0.1-0.5% of an antifoaming agent, 0.2-1% of a lubricant, 0.5-2% of a solvent, and the balance of deionized water. The high impact resistance nanometer composite material has the following advantages that: the high impact resistance nanometer composite material prepared from various raw materials has a high impact resistance effect, friction wear can be reduced or avoided with the lubricant so as to enhance impact resistance, the toughening agent and the antifoaming agent are combined so as to effectively enhance a viscosity of the nanometer composite material, an application range is wide, and enterprise requirements are met.
Description
Technical field
The present invention relates to a kind of matrix material, relate in particular to a kind of high resistance nano composite material.
Background technology
Polyamide resin is the broad-spectrum industrial chemicals of a kind of excellent property, have that tough and tensile, flexibility, bonding force are strong, wear-resisting, characteristic such as oil resistant, water-fast, antienzyme bacterium, the common method that improves material impact intensity is to increase toughner in prescription, general toughner is elastomerics or the rubber of high score subclass, be spherical under the microcosmic, in the extrusion of sheet material, these toughner are stretched along extruding direction, finally present flat pattern, unnotched impact strength is higher in the vertical to cause sheet material, and transversely unnotched impact strength is lower.
Therefore, for addressing the above problem, the spy provides a kind of new technical scheme to satisfy the demands.
Summary of the invention
The purpose of this invention is to provide a kind of high resistance nano composite material.
The technical solution used in the present invention is:
A kind of high resistance nano composite material, made by following raw materials by weight percent and proportioning thereof:
Polyamide resin 20-45%;
Toughner 10-15%;
Nano-powder 15-30%;
Defoamer 0.1-0.5%;
Lubricant 0.2-1%;
Solvent 0.5-2%;
Surplus is deionized water.
Further, described toughner is paracril, polyvinyl butyral acetal or Vinyl Acetate Copolymer.
Further, described defoamer is silicone oil or mineral oil.
Further, described nano-powder is nano titanium oxide.
Further, described solvent is dehydrated alcohol or methyl alcohol.
Advantage of the present invention is: the height resistance property nano composite material of being made by each raw material has the high effect of resisting, lubricant can reduce or avoid frictional wear, strengthened resistance, toughner and defoamer combine, can effectively strengthen the viscosity of nano composite material, applied widely, meet requirement of enterprise.
Embodiment
In order to deepen the understanding of the present invention, the invention will be further described below in conjunction with embodiment, and this embodiment only is used for explaining the present invention, does not constitute the restriction to protection domain of the present invention.
Embodiment 1
A kind of high resistance nano composite material is made by following raw materials by weight percent and proportioning thereof: polyamide resin 20%; Paracril 15%; Nano titanium oxide 30%; Silicone oil 0.5%; Lubricant 1%; Dehydrated alcohol 2%; Surplus is deionized water.
Embodiment 2
A kind of high resistance nano composite material is made by following raw materials by weight percent and proportioning thereof: polyamide resin 32%; Polyvinyl butyral acetal 12%; Nano titanium oxide 20%; Mineral oil 0.25%; Lubricant 0.8%; Methyl alcohol 1.2%; Surplus is deionized water.
Embodiment 3
A kind of high resistance nano composite material is made by following raw materials by weight percent and proportioning thereof: polyamide resin 45%; Vinyl Acetate Copolymer 10%; Nano titanium oxide 15%; Mineral oil 0.1%; Lubricant 0.2%; Dehydrated alcohol 0.5%; Surplus is deionized water.
Advantage of the present invention is: the height resistance property nano composite material of being made by each raw material has the high effect of resisting, lubricant can reduce or avoid frictional wear, strengthened resistance, toughner and defoamer combine, can effectively strengthen the viscosity of nano composite material, applied widely, meet requirement of enterprise.
Claims (5)
1. one kind high resistance nano composite material is characterized in that: made by following raw materials by weight percent and proportioning thereof:
Polyamide resin 20-45%;
Toughner 10-15%;
Nano-powder 15-30%;
Defoamer 0.1-0.5%;
Lubricant 0.2-1%;
Solvent 0.5-2%;
Surplus is deionized water.
2. a kind of high resistance nano composite material according to claim 1, it is characterized in that: described toughner is paracril, polyvinyl butyral acetal or Vinyl Acetate Copolymer.
3. a kind of high resistance nano composite material according to claim 1, it is characterized in that: described defoamer is silicone oil or mineral oil.
4. a kind of high resistance nano composite material according to claim 1, it is characterized in that: described nano-powder is nano titanium oxide.
5. a kind of high resistance nano composite material according to claim 1, it is characterized in that: described solvent is dehydrated alcohol or methyl alcohol.