CN103333432A - Pvc processing adhesive - Google Patents
Pvc processing adhesive Download PDFInfo
- Publication number
- CN103333432A CN103333432A CN2013102806200A CN201310280620A CN103333432A CN 103333432 A CN103333432 A CN 103333432A CN 2013102806200 A CN2013102806200 A CN 2013102806200A CN 201310280620 A CN201310280620 A CN 201310280620A CN 103333432 A CN103333432 A CN 103333432A
- Authority
- CN
- China
- Prior art keywords
- pvc
- tackiness agent
- pvc processing
- adhesive
- stearic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a PVC processing adhesive, which is characterized in that: it comprises the following raw materials by mass: 30%-40% of ultrafine light calcium carbonate, 16%-19% of ACR resin PVC processing modifier LS-01, 10%-15% of stearic acid 1801, 10%-20% of high density polyethylene semi-refined paraffin wax, 10%-20% of waste fly ash, 8%-15% of a DN-302 coupling agent, and 4%-6% of epoxy soybean oil, and the materials are subjected to high-temperature stirring and cooling, thus obtaining the PVC processing adhesive. The PVC processing adhesive provided in the invention is an energy-saving filler, can replace filler in PVC wood-plastic sheet, PVC pipe, plastic-steel profile and rubber production, has high filling content in PVC and low cost. And the product made of the adhesive has the characteristics of strong flexibility, increased hardness, long service cycle, and recyclability, etc.
Description
Technical field
The present invention relates to a kind of PVC of being applied to Wood plastic boards, pvc pipe material, plastic-steel section bar, and the tackiness agent in field such as rubber industry, particularly a kind of PVC processing tackiness agent.
Background technology
At present, owing to the forest scarcity, can only regard rubbish later with the product use that timber is made, cause environmental pollution, the measured product of matter also can only be with 5～6 years, and of long duration, process is exposed to the weather, easy deformation, rotten.The PVC industry has obtained development at full speed, therefore, need to solve PVC Wood plastic boards, pvc pipe material, plastic-steel section bar, and rubber industry in replace stopping composition, make the PVC processing tackiness agent that has stronger snappiness behind the production, can increase product hardness.
Summary of the invention
The present invention has overcome the defective of above-mentioned existence, and purpose is for realizing the low-carbon environment-friendly of building industry, meet the requirement of cycles, economized recycling, the PVC processing tackiness agent of a kind of PVC of making Wood plastic boards, pvc pipe material, plastic-steel section bar and rubber industry being provided.
PVC processing tackiness agent content Description of the present invention:
PVC processing tackiness agent of the present invention, it is characterized in that: the per-cent by quality adopts following raw material: superfine light calcium carbonate 30%～40%, ACR resin PVC modifier LS-01 16%～19%, stearic acid 1,801 10%～15%, high density polyethylene(HDPE) SEMI-REFINED PARAFFIN WAX 10%～20%, rejected fly ash 10%～20%, DN-302 coupling agent 8%～15%, epoxy soybean oil 4%～6%, pass through high-temperature stirring, cool off, make PVC processing tackiness agent.
PVC processing tackiness agent of the present invention is a kind of energy-saving stopping composition, in PVC Wood plastic boards, pvc pipe material, plastic-steel section bar and rubber industry production, replace stopping composition, have the loading level height that combines with PVC, cost product low, after making and have characteristics such as stronger snappiness, the hardness that can increase product, life cycle length, recycling capable of circulation.
Embodiment
PVC of the present invention processing tackiness agent is achieved in that to do below by embodiment to specify.
Make PVC processing tackiness agent, per-cent by quality adopts following raw material: superfine light calcium carbonate 30%～40%, ACR resin PVC modifier LS-01 16%～19%, stearic acid 1,801 10%～15%, high density polyethylene(HDPE) SEMI-REFINED PARAFFIN WAX 10%～20%, rejected fly ash 10%～20%, DN-302 coupling agent 8%～15%, epoxy soybean oil 4%～6%, pass through high-temperature stirring, cool off, make PVC processing tackiness agent.
Production PVC processing of the present invention tackiness agent, the raw material that adopts is:
The superfine light calcium carbonate that Hebei Xu Shi calcium industry company limited produces;
The PVC modifier LS-01 that Shandong Rui Feng macromolecular material limited-liability company produces;
The stearic acid 1801 (MADE IN MAL AYSIA STEARIC ACID 1801) that Malaysia makes;
The SEMI-REFINED PARAFFIN WAX that PetroChina Company Ltd.'s Daqing Petrochemical Company is produced;
The flyash that the normal prosperous company limited in Shenyang produces;
The DN-302 coupling agent that the peaceful coupling agent of Nanjing product company limited produces;
The epoxy soybean oil that Dandong City additives for plastics factory produces.
Embodiment
Produce 100 ㎏ PVC processing tackiness agent, get raw material: superfine light calcium carbonate 32 ㎏, ACR resin PVC modifier LS-01 18 ㎏, stearic acid 1,801 12 ㎏, high density polyethylene(HDPE) SEMI-REFINED PARAFFIN WAX 15 ㎏, rejected fly ash 10 ㎏, DN-302 coupling agent 9 ㎏ and epoxy soybean oil 4 ㎏.
Above-mentioned various raw material mixed configuration are poured in homogenizer or the high speed mixer, homogenizer or high speed mixer are made up of high temperature batch mixing and low temperature batch mixing two portions, raw material under 115 ℃ of temperature through high temperature batch mixing, stirring, then by the high temperature section blowing to low temperature batch mixing section, blowing is in mixing tank for coating colors after high speed rotating is cooled to 70 ℃ of temperature, treats that material loading is pushed to extrude unit; Make the PVC processing tackiness agent that can be used for producing PVC Wood plastic boards, pvc pipe material, plastic-steel section bar and rubber industry at forcing machine.
PVC processing tackiness agent of the present invention; have the loading level height, save cost, the long characteristics of product life cycle easy to use, that make of PVC processing tackiness agent; meet global low-carbon emission, conserve forests, improve the theory of production environment; be a kind of structure material of environment-friendly type, can be widely used in PVC Wood plastic boards, pvc pipe material, plastic-steel section bar and rubber industry.
Claims (2)
1. a PVC processes tackiness agent, it is characterized in that: the per-cent by quality adopts following raw material: superfine light calcium carbonate 30%～40%, ACR resin PVC modifier LS-01 16%～19%, stearic acid 1,801 10%～15%, high density polyethylene(HDPE) SEMI-REFINED PARAFFIN WAX 10%～20%, rejected fly ash 10%～20%, DN-302 coupling agent 8%～15%, epoxy soybean oil 4%～6%, pass through high-temperature stirring, cool off, make PVC processing tackiness agent.
2. PVC according to claim 1 processes tackiness agent, it is characterized in that: produce 100 ㎏ PVC processing tackiness agent, get raw material: superfine light calcium carbonate 32 ㎏, ACR resin PVC modifier LS-01 18 ㎏, stearic acid 1,801 12 ㎏, high density polyethylene(HDPE) SEMI-REFINED PARAFFIN WAX 15 ㎏, rejected fly ash 10 ㎏, DN-302 coupling agent 9 ㎏ and epoxy soybean oil 4 ㎏.