CN103321092B - 涂布型远红外辐射保鲜包装纸板的制备方法 - Google Patents
涂布型远红外辐射保鲜包装纸板的制备方法 Download PDFInfo
- Publication number
- CN103321092B CN103321092B CN201310276544.6A CN201310276544A CN103321092B CN 103321092 B CN103321092 B CN 103321092B CN 201310276544 A CN201310276544 A CN 201310276544A CN 103321092 B CN103321092 B CN 103321092B
- Authority
- CN
- China
- Prior art keywords
- coating
- far
- far infrared
- infrared radiation
- fresh
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种涂布型远红外辐射保鲜包装纸板的制备方法,其特征是,包括以下工艺步骤:(1)涂料制备:将远红外陶瓷粉、粘合剂和分散剂按质量比1:9~11:7~8混合搅拌均匀,静置20~25分钟,得到远红外辐射涂料;(2)涂布:将远红外涂料均匀涂布在瓦楞纸里纸的表面,涂布量为850~950g/平方米,并控制涂布后的表面无直径大于1mm的颗粒状突起或空洞;(3)将涂布远红外涂料的瓦楞纸在85~90℃进行干燥,使得到的瓦楞纸的水份控制在11±3%。本发明与现有技术相比优点在于:工序简单、制造成本相对较低;制成包装容器用于包装水果、蔬菜,可以有效地维持细胞活性,保持果蔬新鲜。试验表明,相同条件下与普通包装纸箱对比,远红外包装纸箱保鲜效果良好,可将好果率提高20%~60%,具有很强的市场竞争优势。
Description
技术领域
本发明涉及一种用来制作果蔬保鲜用包装箱的材料,尤其是一种涂布型远红外辐射保鲜包装纸板的制备方法。
背景技术
纸和纸板作为传统包装材料,发展至今仍是现代包装材料的重要支柱之一。在中国,纸包装材料占包装材料总量的40%左右,从发展趋势看,纸包装的用量会越来越大。据中国包装网报道,尽管中国纸产品使用量增长势头迅猛,但市场上现有的产品结构与需求结构与之不相适应,主要表现为质量档次低,品种结构不合理。目前,中国纸及纸板产品品种较少,不及发达国家可生产纸种的一半。同时,产品技术含量较低,质量较差,包装纸箱传统的包装功能已不能完全满足消费者需求。
尽管瓦楞纸箱以重量轻、缓冲性能好、造型结构可塑性强、无公害等优势广泛应用于果蔬包装,但对于水果、蔬菜这种高水分含量的鲜活农产品,普通瓦楞纸箱仍存在不足之处。果蔬产品水分含量高,用瓦楞纸箱包装其水分易于蒸发、散失,造成果蔬萎蔫、失重、品质下降。在运输过程中,如何保持果蔬的新鲜,一直是一个未能得到圆满解决的技术难题。
为了使水果蔬菜在贮运过程中保持新鲜,目前采用的技术手段主要包括:将保鲜剂喷洒在果蔬上,或将保鲜剂加水稀释成保鲜液,将果蔬浸渍一段时间,晾干后再进行包装;也可采用保鲜包装箱,例如将聚乙烯膜作为保鲜层夹在纸板内、外面纸之间或者将保鲜膜或真空镀铝膜复合到内外面纸上制成保鲜纸箱,此外也有人提出将泡沫塑料与瓦楞组合在一起制成保鲜包装箱。然而,前者由于果蔬食用时难于清洗,有时还引起肠道感染,因此存在安全隐患;而后者提到的瓦楞纸箱由于工艺的复杂程度、制造成本较高等特点,未能在市场上大范围的推广应用。
发明内容
本发明的目的是克服现有技术中存在的不足,提供一种涂布型远红外辐射保鲜包装纸板的制备方法,该包装纸板在常温条件下能辐射一定波长的远红外光波,有效地保持果蔬新鲜。
按照本发明提供的技术方案,所述涂布型远红外辐射保鲜包装纸板的制备方法,其特征是,包括以下工艺步骤:
(1)涂料制备:将远红外陶瓷粉、粘合剂和分散剂按质量比1:9~11:7~8混合搅拌均匀,静置20~25分钟,得到远红外辐射涂料;
(2)涂布:将远红外涂料均匀涂布在瓦楞纸里纸的表面,涂布量为850~950g/平方米,并控制涂布后的表面无直径大于1mm的颗粒状突起或空洞;
(3)将涂布远红外涂料的瓦楞纸在85~90℃进行干燥,使得到的瓦楞纸的水份控制在11±3%。
在一个具体实施方式中,所述粘合剂为聚醋酸乙烯乳液(白乳胶)、变性淀粉、聚乙烯醇或丙烯酸树脂胶。
在一个具体实施方式中,所述分散剂为质量百分浓度为0.02~0.03%的多聚磷酸钠溶液。
在一个具体实施方式中,所述远红外陶瓷粉的细度为1~2.5微米。
本发明与现有技术相比优点在于:工序简单、制造成本相对较低;制成包装容器用于包装水果、蔬菜,可以有效地维持细胞活性,保持果蔬新鲜。试验表明,相同条件下与普通包装纸箱对比,远红外包装纸箱保鲜效果良好,可将好果率提高20%~60%,具有很强的市场竞争优势。
附图说明
图1为本发明所述包装纸板的结构示意图。
图2为本发明所述包装纸板的使用示意图。
具体实施方式
下面结合具体附图对本发明作进一步说明。
如图1所示:所述涂布型远红外辐射保鲜包装纸板包括面纸1和里纸3,在面纸1和里纸3之间设置瓦楞纸芯2,在所述里纸3的外表面涂布远红外涂层4。
本发明所使用的远红外陶瓷粉为市售工业级陶瓷粉,主要成分为SiO2、MgO、Al2O3、氧化钛、氧化钙等,远红外发射率在0.85以上。
如图2所示,在使用时,采用本发明所述涂布型远红外辐射保鲜包装纸板制成保鲜包装盒,里纸3外表面的远红外涂层4可以发射远红外光波,远红外光波与果蔬细胞及果蔬中的水分子产生共振效应,促进果蔬细胞新陈代谢,增强细胞活力,维持果蔬新鲜;同时,远红外涂层4中的陶瓷粉可以吸附果蔬呼吸过程中产生的乙烯。
实施例一:一种涂布型远红外辐射保鲜包装纸板的制备方法,包括以下工艺步骤:
(1)涂料制备:将远红外陶瓷粉、粘合剂和分散剂按质量比1:9:7混合搅拌均匀,静置20分钟,得到远红外辐射涂料;所述粘合剂为聚醋酸乙烯乳液(白乳胶),所述分散剂为质量百分浓度为0.02%的多聚磷酸钠溶液,所述远红外陶瓷粉的细度为1微米;
(2)涂布:将远红外涂料均匀涂布在瓦楞纸里纸的表面,涂布量为850g/平方米,为控制涂布的均匀度,避免掉粉现象,需要控制涂布表面具有一定的粗糙度;在本实施例中控制涂布后的表面无直径大于1mm的颗粒状突起或空洞,涂布后不会出现掉粉的现象;
(3)将涂布远红外涂料的瓦楞纸在85℃进行干燥,使得到的瓦楞纸的水份控制在8%。
实施例二:一种涂布型远红外辐射保鲜包装纸板的制备方法,包括以下工艺步骤:
(1)涂料制备:将远红外陶瓷粉、粘合剂和分散剂按质量比1:11:8混合搅拌均匀,静置25分钟,得到远红外辐射涂料;所述粘合剂为变性淀粉;所述分散剂为质量百分浓度为0.03%的多聚磷酸钠溶液;所述远红外陶瓷粉的细度为2.5微米;
(2)涂布:将远红外涂料均匀涂布在瓦楞纸里纸的表面,涂布量为950g/平方米,为控制涂布的均匀度,避免掉粉现象,需要控制涂布表面具有一定的粗糙度;在本实施例中控制涂布后的表面无直径大于1mm的颗粒状突起或空洞,涂布后不会出现掉粉的现象;
(3)将涂布远红外涂料的瓦楞纸在90℃进行干燥,使得到的瓦楞纸的水份控制在14%。
实施例三:一种涂布型远红外辐射保鲜包装纸板的制备方法,包括以下工艺步骤:
(1)涂料制备:将远红外陶瓷粉、粘合剂和分散剂按质量比1:10:7.5混合搅拌均匀,静置24分钟,得到远红外辐射涂料;所述粘合剂为聚乙烯醇;所述分散剂为质量百分浓度为0.025%的多聚磷酸钠溶液;所述远红外陶瓷粉的细度为2微米;
(2)涂布:将远红外涂料均匀涂布在瓦楞纸里纸的表面,涂布量为900g/平方米,为控制涂布的均匀度,避免掉粉现象,需要控制涂布表面具有一定的粗糙度;在本实施例中控制涂布后的表面无直径大于1mm的颗粒状突起或空洞,涂布后不会出现掉粉的现象;
(3)将涂布远红外涂料的瓦楞纸在86℃进行干燥,使得到的瓦楞纸的水份控制在11%。
Claims (1)
1.一种涂布型远红外辐射保鲜包装纸板的制备方法,其特征是,包括以下工艺步骤:
(1)涂料制备:将远红外陶瓷粉、粘合剂和分散剂按质量比1:9~11:7~8混合搅拌均匀,静置20~25分钟,得到远红外辐射涂料;
(2)涂布:将远红外涂料均匀涂布在瓦楞纸里纸的表面,涂布量为850~950g/平方米,并控制涂布后的表面无直径大于1mm的颗粒状突起或空洞;
(3)将涂布远红外涂料的瓦楞纸在85~90℃进行干燥,使得到的瓦楞纸的水份控制在11±3%;
所述粘合剂为变性淀粉、聚乙烯醇或丙烯酸树脂胶;
所述分散剂为质量百分浓度为0.02~0.03%的多聚磷酸钠溶液;
所述远红外陶瓷粉的细度为1~2.5微米。