CN103319837A - PC/ABS alloy used for automotive upholstery - Google Patents
PC/ABS alloy used for automotive upholstery Download PDFInfo
- Publication number
- CN103319837A CN103319837A CN 201210075436 CN201210075436A CN103319837A CN 103319837 A CN103319837 A CN 103319837A CN 201210075436 CN201210075436 CN 201210075436 CN 201210075436 A CN201210075436 A CN 201210075436A CN 103319837 A CN103319837 A CN 103319837A
- Authority
- CN
- China
- Prior art keywords
- abs
- automotive upholstery
- parts
- abs alloy
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a PC/ABS alloy used for automotive upholstery. The PC/ABS alloy comprises, by weight, 100 parts of ABS resin, 50-70 parts of PC resin, 5-15 parts of polytetrafluoroethylene, 3-5 parts of EPDM, and 0.1-0.5 parts of epoxy resin. The PC/ABS alloy for automotive upholstery is prepared by a process including the following steps of weighing each component according to the ratio above, mixing uniformly, melt-mixing, and extruding and granulating. According to the invention, ABS and PC are blended, and a toughener having a function of compatibilization is cooperatively used, and therefore impact resistance of ABS is greatly increased. The PC/ABS alloy provided by the invention can be easily processed into components of various shapes through an injection process, and can be used for producing automotive upholstery.
Description
Technical field
The present invention relates to a kind of plastic material, relate in particular to a kind of automotive upholstery PC/ABS alloy.
Background technology
ABS is the general thermoplastic engineering plastic that grows up 1940's, it is a plastics variety that comprehensive mechanical property is very outstanding, not only have good rigidity, hardness and processing fluidity, and have the high tenacity characteristics, can injection moulding, extrude or thermoforming.
All with injection molding forming method processing, the advantage of ABS resin is impact-resistance, sound-proofing, scratch-resistant to most of trolley part, and thermotolerance is better, and is more attractive in appearance than PP, is specially adapted to the comparatively strict parts of horizontal impact-resistance and use temperature.ABS resin is to use in the automobile to be only second to Polyurethane and polyacrylic the third-largest resin.ABS resin can be used for Che Nei and car outer enclosure, the widgets such as bearing circle, oil guide pipe and handle and button, and the car outside comprises front radiator grill and lampshade etc.
ABS resin is easily processed, finish size stability and surface luster are good, easily application, painted, can also carry out metallize, plating, welding and the suitability for secondary processing such as bonding, can be widely used in field of electronics, comprise various offices and consumer electronics/electrical equipment, office electrical equipment comprises electronic data processing machine, office equipment.In electronic apparatus market, ABS resin will keep its status in requiring fire-retardant and high heat-resisting electronics/electrical equipment market in recent years, fire-retardant and high heat-proof ABS resin with the competition of the engineering plastic alloys such as ABS/PC in have obvious advantage.
PC refers to polycarbonate, is the high molecular polymer that contains carbonate group in the molecular chain, can be divided into the broad varietys such as aliphatics, aromatic series, aliphatic-aromatic according to the structure of ester group.Wherein the mechanical property owing to aliphatics and aliphatic-aromatic polycarbonate is lower, thereby has limited its application aspect engineering plastics.Only have at present that aromatic copolycarbonate obtains suitability for industrialized production.Because the singularity on the polycarbonate structure has now become the fastest general engineering plastic of rate of growth in the five large-engineering plastics.
The PC/ABS alloy is the mixture of polycarbonate and acrylonitrile-butadiene-styrene copolymer, is the thermoplastic plastic rubber that is formed by polycarbonate and acrylonitrile-butadiene-styrene copolymer ABS alloy, combines the excellent specific property of bi-material.The typically used scope is phone housing, computer and business machine housing, electrical equipment, lawn horticultural machine, auto parts dashboard, inside fitting and wheel cover.
Summary of the invention
For above shortcomings in the prior art, technical problem to be solved by this invention provides a kind of automotive upholstery PC/ABS alloy.
The present invention seeks to be achieved through the following technical solutions:
A kind of automotive upholstery PC/ABS alloy is made of by weight following component: 100 parts of ABS resin, PC resin 50-70 part, tetrafluoroethylene 5-15 part, EPDM 3-5 part, Resins, epoxy 0.1-0.5 part.
Take by weighing each component by proportioning, after mixing, melting mixing, extruding pelletization namely obtain described automotive upholstery PC/ABS alloy.
The present invention is used in conjunction with the toughner with compatibilization with ABS and PC blend, has greatly improved the erosion-resisting characteristics of ABS.Automotive upholstery of the present invention PC/ABS alloy can be processed into easily with Shooting Technique the part of different shape, can be used for making the automobile inside gadget.
Embodiment:
100 kilograms of ABS resin, 60 kilograms of PC resins, 10 kilograms of tetrafluoroethylene, 4 kilograms of EPDM, 0.3 kilogram of Resins, epoxy.
Take by weighing each component by proportioning, after mixing, melting mixing, extruding pelletization namely obtain described automotive upholstery PC/ABS alloy.
The present invention is used in conjunction with the toughner with compatibilization with ABS and PC blend, has greatly improved the erosion-resisting characteristics of ABS.Automotive upholstery of the present invention PC/ABS alloy can be processed into easily with Shooting Technique the part of different shape, can be used for making the automobile inside gadget.
The above; it only is the specific embodiment of the present invention; but protection scope of the present invention is not limited to this; any those of ordinary skill in the art are in the disclosed technical scope of the present invention; variation or the replacement that can expect without creative work all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.
Claims (1)
1. an automotive upholstery PC/ABS alloy is made of by weight following component: 100 parts of ABS resin, PC resin 50-70 part, tetrafluoroethylene 5-15 part, EPDM 3-5 part, Resins, epoxy 0.1-0.5 part.