CN103305075A - Waterborne anticorrosive paint and preparation method thereof - Google Patents
Waterborne anticorrosive paint and preparation method thereof Download PDFInfo
- Publication number
- CN103305075A CN103305075A CN201310258799XA CN201310258799A CN103305075A CN 103305075 A CN103305075 A CN 103305075A CN 201310258799X A CN201310258799X A CN 201310258799XA CN 201310258799 A CN201310258799 A CN 201310258799A CN 103305075 A CN103305075 A CN 103305075A
- Authority
- CN
- China
- Prior art keywords
- water
- anticorrosive paint
- defoamer
- ethylene glycol
- acrylic emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a waterborne anticorrosive paint which comprises a dispersant, a surfactant, a defoamer, ethylene glycol, aluminum tripolyphosphate, zinc phosphate, a pure acrylic emulsion, a polyurethane thickener, a coalescing agent and water. The invention further provides a method for preparing the waterborne anticorrosive paint. The method comprises the following steps: sequentially casting the dispersant, the surfactant, the defoamer, ethylene glycol, aluminum tripolyphosphate, zinc phosphate, the pure acrylic emulsion, the polyurethane thickener and the coalescing agent; casting the next material after uniformly stirring the material; stirring while casting; and detecting the viscosity after uniformly dispersing. The paint prepared by the formula and process has the advantages of continuous rust protection, corrosion prevention, environmental protection, water resistance and alkali resistance.
Description
Technical field
The present invention relates to a kind of coating and preparation method thereof, specifically is a kind of water-based anticorrosive paint and preparation method thereof.
Background technology
The metal current protective system is mainly based on oil paint, because oil paint a large amount of organic solvents volatilizations in coating process, and contaminate environment not only, and HUMAN HEALTH produced significant threat.In recent years, the waterborne metal anti-corrosive paint of pollution-free, energy conservation and economical and efficient more and more receives an acclaim, and especially possesses the water-borne coatings of antirust, anticorrosion, environmental protection lastingly, water-fast, alkaline-resisting advantage, can satisfy the personage to demand and the requirement of coating.
Summary of the invention
The present invention relates to a kind of water-based anticorrosive paint, described coating is made up of the component of following weight percent:
Dispersion agent 0.5～1.0%,
Tensio-active agent 0.1～0.2%,
Defoamer 0.4～0.8%,
Ethylene glycol 0.8～3.5%,
Aluminium triphosphate 2～12%,
Zinc phosphate 5～25%,
Pure-acrylic emulsion 30～65%,
Polyurethane thickening material 0.8～1.5%,
Film coalescence aid 1～2.5%
Surplus is water.
The invention still further relates to a kind of technology for preparing above-mentioned water-based anticorrosive paint, described technology is included as successively, and order drops into dispersion agent, tensio-active agent, defoamer, ethylene glycol, aluminium triphosphate, zinc phosphate, pure-acrylic emulsion, Polyurethane thickening material, film coalescence aid in water, after stirring, every kind of material casts a kind of material again, stir while feeding intake, the back of waiting to be uniformly dispersed is detected viscosity and is got final product.
Beneficial effect of the present invention is: the coating by this prescription and prepared possesses antirust, anticorrosion, environmental protection lastingly, water-fast, alkaline-resisting advantage.
Embodiment
Embodiment 1
A kind of water-based anticorrosive paint prescription, described coating is made up of the component of following weight percent:
Dispersion agent 1%,
Tensio-active agent 0.2%,
Defoamer 0.5%,
Ethylene glycol 2%,
Aluminium triphosphate 5%,
Zinc phosphate 15%,
Pure-acrylic emulsion 40%,
Polyurethane thickening material 1%,
Film coalescence aid 2%
Surplus is water.
In water, drop into dispersion agent, tensio-active agent, defoamer, ethylene glycol, aluminium triphosphate, zinc phosphate, pure-acrylic emulsion, Polyurethane thickening material, film coalescence aid successively in order, after stirring, every kind of material casts a kind of material again, stir while feeding intake, the back of waiting to be uniformly dispersed is detected viscosity and is got final product.
Embodiment 2
A kind of water-based anticorrosive paint prescription, described coating is made up of the component of following weight percent:
Dispersion agent 1%,
Tensio-active agent 0.1%,
Defoamer 0.6%,
Ethylene glycol 3%,
Aluminium triphosphate 10%,
Zinc phosphate 20%,
Pure-acrylic emulsion 50%,
Polyurethane thickening material 1%,
Film coalescence aid 2%
Surplus is water.
In water, drop into dispersion agent, tensio-active agent, defoamer, ethylene glycol, aluminium triphosphate, zinc phosphate, pure-acrylic emulsion, Polyurethane thickening material, film coalescence aid successively in order, after stirring, every kind of material casts a kind of material again, stir while feeding intake, the back of waiting to be uniformly dispersed is detected viscosity and is got final product.
Embodiment 3
A kind of water-based anticorrosive paint prescription, described coating is made up of the component of following weight percent:
Dispersion agent 1%,
Tensio-active agent 0.2%,
Defoamer 0.8%,
Ethylene glycol 3%,
Aluminium triphosphate 12%,
Zinc phosphate 25%,
Pure-acrylic emulsion 40%,
Polyurethane thickening material 1%,
Film coalescence aid 2%
Surplus is water.
In water, drop into dispersion agent, tensio-active agent, defoamer, ethylene glycol, aluminium triphosphate, zinc phosphate, pure-acrylic emulsion, Polyurethane thickening material, film coalescence aid successively in order, after stirring, every kind of material casts a kind of material again, stir while feeding intake, the back of waiting to be uniformly dispersed is detected viscosity and is got final product.
Claims (2)
1. water-based anticorrosive paint, it is characterized in that: described coating is made up of the component of following weight percent:
Dispersion agent 0.5～1.0%,
Tensio-active agent 0.1～0.2%,
Defoamer 0.4～0.8%,
Ethylene glycol 0.8～3.5%,
Aluminium triphosphate 2～12%,
Zinc phosphate 5～25%,
Pure-acrylic emulsion 30～65%,
Polyurethane thickening material 0.8～1.5%,
Film coalescence aid 1～2.5%
Surplus is water.
2. technology for preparing the described water-based anticorrosive paint of claim 1, described technology is for dropping into dispersion agent, tensio-active agent, defoamer, ethylene glycol, aluminium triphosphate, zinc phosphate, pure-acrylic emulsion, Polyurethane thickening material, film coalescence aid successively in order in water, after stirring, every kind of material casts a kind of material again, stir while feeding intake, the back of waiting to be uniformly dispersed is detected viscosity and is got final product.