CN103304900A - Flame-retardant whisker-enhanced polypropylene alloy material - Google Patents
Flame-retardant whisker-enhanced polypropylene alloy material Download PDFInfo
- Publication number
- CN103304900A CN103304900A CN201310242078XA CN201310242078A CN103304900A CN 103304900 A CN103304900 A CN 103304900A CN 201310242078X A CN201310242078X A CN 201310242078XA CN 201310242078 A CN201310242078 A CN 201310242078A CN 103304900 A CN103304900 A CN 103304900A
- Authority
- CN
- China
- Prior art keywords
- retardant
- parts
- alloy material
- fire
- whisker
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a flame-retardant whisker-enhanced polypropylene alloy material, belonging to the technical field of macromolecular materials. The alloy material is prepared from the following raw materials in parts by weight: 44.2-49.5 parts of polypropylene resin, 7.2-13.1 parts of rubber, 3-5 parts of nylon resin, 6-9 parts of compatibilizer, 11-19 parts of flame retardant, 5-8 parts of whisker enhancer, 0.4-0.8 part of antioxidant, 9-15 parts of glass fiber and 1.2-2 parts of carbon black. The flame-retardant whisker-enhanced polypropylene alloy material has the advantages that the bending strength is greater than 73-92 MPa, the izod notched impact strength is 14.5-18.3 kj/m<2>, the thermal deformation temperature is 155-170 DEG C, and the flame retardance V-0 is UL-94-V-0-1.6 mm, so that the use field of the flame-retardant whisker-enhanced polypropylene alloy material can be expanded.
Description
Technical field
The invention belongs to technical field of polymer materials, be specifically related to the polypropylene alloy material that a kind of fire-retardant whisker strengthens.
Background technology
Because polypropylene has good electrical performance characteristics, low temperature tolerance characteristics, chemical stability and workability etc., thereby extensively is used in automobile, building materials, textile equipment, food product pack etc.Because polypropylene is a kind of combustible material, easily forms wire drawing during burning and produce a large amount of molten drops, thereby limited to a certain extent polypropylene and used widely.Hence one can see that, polypropylene material carried out modification have positive effect.
Summary of the invention
Task of the present invention is to provide that a kind of intensity is high, heat resistance good and flame retardant effect is excellent and use the polypropylene alloy material that the fire-retardant whisker of expanding use range strengthens.
Task of the present invention is finished like this, the polypropylene alloy material that a kind of fire-retardant whisker strengthens, and its raw material by following parts by weight forms:
In one embodiment of the invention, described acrylic resin is the Co-polypropylene of 150 ℃ of fusing points.
In another embodiment of the present invention, described rubber is paracril
In yet another embodiment of the present invention, described nylon resin is that fusing point is at the NYLON610 resin more than 220 ℃.
In another embodiment of the present invention, described compatilizer is the maleic anhydride grafted polyethylene resin.
Also have among the embodiment of the present invention, described fire retardant is TDE.
More of the present invention and among embodiment, described whisker toughener is the calcium sulfate crystal whiskers of length 150-220 micron.
In of the present invention and then embodiment, described oxidation inhibitor is tricresyl phosphite (24-di-tert-butyl-phenyl) ester.
Of the present invention again more and among embodiment, described glass fibre is the alkali free glass fibre of length 3mm.
In again of the present invention and then embodiment, described carbon black is that carbonarius is female.
The polypropylene alloy material that fire-retardant whisker provided by the invention strengthens has following performance index after tested: flexural strength is greater than 73~92MPa, and the socle girder notched Izod impact strength is greater than 14.5~18.3kj/m
2, 155~170 ℃ of heat-drawn wires, flame retardant resistance V-0 (UL-94-V-0-1.6mm) can expand its use field.
Embodiment
Embodiment 1:
Embodiment 2:
Embodiment 3:
Embodiment 4:
The polypropylene alloy material that the fire-retardant whisker that is obtained by above-described embodiment 1 to 4 strengthens has following technique effect after tested:
Test event | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 |
Flexural strength MPa | 73 | 80 | 85 | 92 |
Notched Izod impact strength kj/m 2 | 14.7 | 16.7 | 17.3 | 18.3 |
Heat-drawn wire ℃ | 155 | 160 | 164 | 170 |
Flame retardant resistance (UL-94-V-0-1.6mm) | V-0 | V-0 | V-0 | V-0 |
Claims (10)
1. polypropylene alloy material that fire-retardant whisker strengthens is characterized in that its raw material by following parts by weight forms:
44.2~49.5 parts of acrylic resins;
7.2 ~ 13.1 parts of rubber;
3 ~ 5 parts of nylon resins;
6 ~ 9 parts of compatilizers;
11 ~ 19 parts of fire retardants;
5 ~ 8 parts of whisker tougheners;
0.4 ~ 0.8 part in oxidation inhibitor;
9 ~ 15 parts in glass fibre;
1.2 ~ 2 parts of carbon blacks.
2. the polypropylene alloy material that strengthens of fire-retardant whisker according to claim 1 is characterized in that described acrylic resin is the Co-polypropylene of 150 ℃ of fusing points.
3. the polypropylene alloy material that strengthens of fire-retardant whisker according to claim 1 is characterized in that described rubber is paracril.
4. the polypropylene alloy material that strengthens of fire-retardant whisker according to claim 1 is characterized in that described nylon resin is that fusing point is at the NYLON610 resin more than 220 ℃.
5. the polypropylene alloy material that strengthens of fire-retardant whisker according to claim 1 is characterized in that described compatilizer is the maleic anhydride grafted polyethylene resin.
6. the polypropylene alloy material that strengthens of fire-retardant whisker according to claim 1 is characterized in that described fire retardant is TDE.
7. the polypropylene alloy material that strengthens of fire-retardant whisker according to claim 1 is characterized in that described whisker toughener is the calcium sulfate crystal whiskers of length 150-220 micron.
8. the polypropylene alloy material that strengthens of fire-retardant whisker according to claim 1 is characterized in that described oxidation inhibitor is tricresyl phosphite (24-di-tert-butyl-phenyl) ester.
9. the polypropylene alloy material that strengthens of fire-retardant whisker according to claim 1 is characterized in that described glass fibre is the alkali free glass fibre of length 3mm.
10. the polypropylene alloy material that strengthens of fire-retardant whisker according to claim 1 is characterized in that described carbon black is that carbonarius is female.