CN103289562A - UV (Ultraviolet)-water-based spray coating matte finish - Google Patents
UV (Ultraviolet)-water-based spray coating matte finish Download PDFInfo
- Publication number
- CN103289562A CN103289562A CN2013102677163A CN201310267716A CN103289562A CN 103289562 A CN103289562 A CN 103289562A CN 2013102677163 A CN2013102677163 A CN 2013102677163A CN 201310267716 A CN201310267716 A CN 201310267716A CN 103289562 A CN103289562 A CN 103289562A
- Authority
- CN
- China
- Prior art keywords
- water
- mixture
- matte finish
- finish paint
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an UV (Ultraviolet)-water-based spray coating matte finish which comprises the following components by weight percentage: 75%-85% of 40% UV water-based resin, 0.1%-0.5% of defoamer, 1.0%-2% of dispersing agent, 1%-5% of flatting agent, 3%-5% of film-forming agent, 1%-3% of initiator, 0.1%-1% of wetting agent, 0.5%-1% of thickening agent and the balance of water, wherein the 40% UV water-based resin is polyurethane acrylic resin, or modified epoxy acrylic resin or a mixture thereof; and the flatting agent is an inorganic powder (silicon dioxide). The UV-water-based spray coating matte finish disclosed by the invention is fine in surface film, low in glossiness, soft and natural; the formed film is resistant to scratch, and also capable of highlighting the natural textures of wood; and therefore, a beautiful, scratch-resistant protective layer can be formed on wood products such as wood furniture and a wood floor; and as a result, lasting protection is formed on the surface of the wood furniture and the wood floor.
Description
Technical field
The present invention relates to a kind of UV-curable wood coating, specifically a kind of mute light or the UV-water-based spray paint of mute light entirely.
Background technology
UV is the english abbreviation of Ultraviolet (ultraviolet ray), and the UV lacquer is the ultraviolet light polymerization lacquer.Common plank, sheet materials such as calcium silicate board with microporous are by last UV lacquer, and the stone material plate that forms through UV photo solidification machine drying has glossy surfaces to handle again, bright in colour, have very strong visual impact, wear-resisting, anti-chemical is strong, long service life, nondiscoloration, easy to clean is more satisfactory sheet material maintenance treatment process.It is ultraviolet light polymerization lacquer maintenance treatment process that wood product surfaces such as existing wooden furniture, timber floor all adopt the UV lacquer, has formed industrialized production.Along with the development of application techniques, and the raising of people's living standard, people's aesthetic conceptions are also more and more diversified, and the floor is except the plane formula of routine, also extended a lot of other categories, comprising: style modelled after an antique, open, semi open model etc.Therefore the coating of UV oiliness just can not satisfy the requirement of this series products, and the UV water-based is with regard to growing up slowly.The UV water-borne coatings has its feature: environmental protection, easily delustring, nature, therefore when handling the floor of some open or semi open model styles, the characteristic property of its painting effect can highlight the natural texture of timber, keeps the natural aesthetic feeling of timber.
Summary of the invention
The purpose of this invention is to provide a kind of UV-water-based coated matte finish paint; this fine and smooth, low, soft nature of glossiness in finish paint surface; the paint film scrape resistant that forms well can highlight simultaneously the nature of timber; can form the protective layer of attractive in appearance and scrape resistant at wood product surfaces such as wooden furniture, timber floors; particularly at some on open or semi open model or the ancient imitation floor board, thereby wooden furniture and timber floor surface are formed lasting protection.
The objective of the invention is to be achieved through the following technical solutions:
A kind of UV-water-based coated matte finish paint, it is characterized in that: the component of this finish paint and weight proportion thereof are: 40% UV water-base resin 75 % one 85%, defoamer 0. 1 % 1. and 5 %, dispersion agent 1. 0 % one 2%, matting agent 1% 1 %, membrane-forming agent 3% 1 %, initiator 1% one 3%, wetting agent 0. 1 %-1 %, thickening material 0.5 % one 1 %, surplus is water; Described 40% UV-water-base resin is polyurethane acrylic resin or modified epoxy acrylate resin or their mixture.
Among the present invention, described defoamer is not for containing organosilicon polymer solution, polyacrylic acid superpolymer or their mixture; Described dispersion agent is high molecular weight block copolymer solution, modified acroleic acid block copolymer solution or their mixture; Described initiator is fragrant ketone, bitter almond oil camphor and derivative thereof or their mixture; Described wetting agent is acrylate copolymer, modified siloxane solution or their mixture; Described thickening material is polyurethane thickener, alkali swelling thickening material or their mixture; Described matting agent is organism modified gas aerosil class, aerosil, delustring wax slurry class or their mixture.Described membrane-forming agent is high boiling alcohol ether solvents, pure ester solvent or their mixture.
Surface finish, soften that the UV water-base resin that the present invention adopts and matting agent improve lacquer as woodenware finish have reduced glossiness simultaneously.Compared with prior art; lacquer painting exquisiteness of the present invention, low, the soft nature of glossiness; the paint film structure scrape resistant of Xing Chenging is good simultaneously, can form the protective layer of attractive in appearance and scrape resistant at wood product surfaces such as wooden furniture, timber floors, thereby wooden furniture and timber floor surface are formed lasting protection.
Embodiment
The present invention is further illustrated below in conjunction with embodiment.
Embodiment 1
A kind of UV-water-based coated matte finish paint of the present invention, its component and weight proportion thereof are: the component of this finish paint and weight proportion thereof are: 40% UV water-base resin 85 %, defoamer 0. 1 %, dispersion agent 1. and 0 %, matting agent 1%, membrane-forming agent 3%, initiator 1%, wetting agent 0. 5 %, thickening material 0.5 %, surplus is water.In the said components: described UV-water-base resin is polyurethane acrylic resin or modified epoxy acrylate resin or polyester acrylic resin or their mixture, produces as CYTEC, BASF, BAYER etc.; Described defoamer is not for containing organosilicon polymer solution, polyether siloxane copolymer or their mixture, as TEGO901W, the TEGO902W of Di Gao company production or their mixture; Described dispersion agent is high molecular weight block copolymer solution, alkane hydroxylammonium salts block copolymer solution or their mixture, as BYK180, the BYK190 of Bi Ke company production or their mixture; Described initiator is fragrant ketone, bitter almond oil camphor and derivative thereof or their mixture, the IRGACURE500 that produces as CIBA, 1173 or their mixture; Described wetting agent is acrylate copolymer, modified siloxane solution or their mixture, as BYK346, the BYK348 of Bi Ke company production or their mixture; Described matting agent can adopt organism modified gas aerosil class, as the flatting silica TS100 of DEGUSS company production; Delustring wax slurry class is as the FA115 of the modest company of moral production or their mixture.
During preparation, after the UV-water-base resin with 40%, defoamer, dispersion agent, initiator disperse, add matting agent and fully be uniformly dispersed, add wetting agent, membrane-forming agent, thickening material at last and be uniformly dispersed and get final product.During coating decoration, regulate the thickness that spraying machine is adjusted paint film; Regulate the temperature of the temperature control finish paint of constant temperature water bath, lacquer is applied to wood product surfaces such as furniture, timber floor by the mode that sprays.
After testing, the key technical indexes such as the following table 1 of UV-water-based coated matte finish paint of the present invention:
Table 1
| Sequence number | Interventions Requested | Assay | Inspecting standard |
| 1 | Appearance of film | Surfacing, smooth | Range estimation |
| 2 | Sticking power | 0-1 | EN ISO 2409 |
| 3 | Glossiness | 5°-6° | GB/T9754-1998 |
| 4 | Anti-steel wire lump test | By | - |
Coating surface exquisiteness of the present invention, glossiness is low, soften good, and the paint film structure scrape resistant of formation can form the protective layer of scrape resistant at wood product surfaces such as wooden furniture, timber floors, thereby wooden furniture and timber floor surface are formed lasting protection.
Embodiment 2
Another UV-water-based spray paint of the present invention, it is half mute lac varnish, compare with embodiment 1, it only is the weight proportion difference, should half component and the weight proportion thereof of making lac varnish mute be: the component of this finish paint and weight proportion thereof be: 40% UV water-base resin 75%, defoamer 0. 5 %, dispersion agent 2%, matting agent 5 %, membrane-forming agent 5 %, initiator 3%, wetting agent 1 %, thickening material 1 %, surplus is water.
Claims (8)
1. UV-water-based coated matte finish paint, it is characterized in that: the component of this finish paint and weight proportion thereof are: 40% UV water-base resin 75 % one 85%, defoamer 0. 1 % 1. and 5 %, dispersion agent 1. 0 % one 2%, matting agent 1% 1 %, membrane-forming agent 3% 1 %, initiator 1% one 3%, wetting agent 0. 1 %-1 %, thickening material 0.5 % one 1 %, surplus is water; Described 40% UV-water-base resin is polyurethane acrylic resin or modified epoxy acrylate resin or their mixture.
2. UV-water-based coated matte finish paint according to claim 1 is characterized in that: described matting agent is organism modified gas aerosil class, aerosil, delustring wax slurry class or their mixture.
3. UV-water-based coated matte finish paint according to claim 1 is characterized in that: described defoamer is not for containing organosilicon polymer solution, polyether siloxane copolymer or their mixture.
4. UV-water-based coated matte finish paint according to claim 1, it is characterized in that: described dispersion agent is high molecular weight block copolymer solution, modified acroleic acid block copolymer solution or their mixture.
5. UV-water-based coated matte finish paint according to claim 1, it is characterized in that: described initiator is fragrant ketone, bitter almond oil camphor and derivative thereof or their mixture.
6. UV-water-based coated matte finish paint according to claim 1, it is characterized in that: described wetting agent is acrylate copolymer, modified siloxane solution or their mixture.
7. UV-water-based coated matte finish paint according to claim 1, it is characterized in that: described thickening material is polyurethane thickener, alkali swelling thickening material or their mixture.
8. UV-water-based coated matte finish paint according to claim 1, it is characterized in that: described membrane-forming agent is high boiling alcohol ether solvents, pure ester solvent or their mixture.