CN103286129A - Copper plate rolling method - Google Patents
Copper plate rolling method Download PDFInfo
- Publication number
- CN103286129A CN103286129A CN2013102716897A CN201310271689A CN103286129A CN 103286129 A CN103286129 A CN 103286129A CN 2013102716897 A CN2013102716897 A CN 2013102716897A CN 201310271689 A CN201310271689 A CN 201310271689A CN 103286129 A CN103286129 A CN 103286129A
- Authority
- CN
- China
- Prior art keywords
- substrate
- copper
- base
- copper coin
- rolling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of copper plate/strip production, in particular to a copper plate rolling method. The method including substrate production and copper billet casting includes the steps of A, producing a billet; preparing material, namely preparing two cast copper billets in the required width and cleaning the surfaces; combining, namely, sandwiching the cast copper billets between the two substrates and firmly attaching to obtain a combined billet; heating the combined billet, namely, heating to 700-900 DEG C; B, rolling, namely moving the combined billet to a rolling mill for rolling so as to produce a composite copper plate; C, cutting, namely, cutting the composite copper plate according to the size, removing the substrates after cutting, and clearing an anti-adhesion material layer to obtain the copper plate. The copper plate rolling method has the advantages that rolling force of rollers and temperature of the copper billet are uniformized by the two substrates, so that the influence of instable factors of the rolling mill upon the quality is avoided; neat edge and smooth surface are effectively guaranteed for the obtained copper plate.
Description
Technical field
The present invention relates to copper coin band production technical field, relate in particular to a kind of copper coin milling method.
Background technology
Carrying out the production of copper coin band in ingot casting hot rolling cogging mode is the main method that present copper coin band is produced.But along with the continuous development of industrial technology, especially required precision is more and more higher to the quality of copper coin material, and traditional milling method can not satisfy the requirement of high-quality copper coin.Major defect is as follows, and the one, because the temperature difference of ingot casting both sides, and copper base rapid heat dissipation, cause the roll-force inequality of copper base in the operation of rolling, and then cause the blemish of copper coin band or the lateral bending of copper coin band; The 2nd, since different with the roll-force at edge in the middle of the copper base, cause easily going up sled in the middle of the roll, and then cause copper coin band mass defect.Therefore, adopt existing techniques in realizing to the hot rolling production of high accuracy copper coin, milling train and rolling mill practice are had very high requirement usually, some also needs the face that mills, cold rolling, heat treatment and finishing procedure after hot rolling.Therefore, also improve the production and processing cost, restricted the development of copper coin hot rolling technology.
Summary of the invention
The present invention is directed to above-mentioned the deficiencies in the prior art, a kind of new copper coin milling method is provided.It utilizes conventional mill just effectively to improve efficient and the quality of copper coin hot rolling.
The technical scheme that the present invention solves the problems of the technologies described above is as follows: a kind of copper coin milling method, comprise substrate and casting copper base, and it is characterized in that, comprise the steps:
A: make base substrate:
(1), get the raw materials ready: width prepares to cast one of copper base respectively on request, two of substrates, the overall size of described substrate is equal to or greater than the overall size of casting copper base, and substrate and casting copper base surface are carried out cleaning respectively;
(2), combination: be clipped between described two substrates described casting copper base and firm fitting to together, and two substrate periphery edges are welded to connect, obtain making up base substrate, also scribble anti-jointing material layer on the two sides of described casting copper base;
(3), combination base substrate heating: will put into heating furnace through the combination base substrate that step (2) obtain and heat, and be heated to temperature at 700~900C °;
B: rolling: will make compound copper coin through being rolled on the combination base substrate immigration milling train after step (3) heating;
C: cutting: according to instructions for use compound copper coin is cut by size, substrate is removed in the cutting back, and obtains copper coin after removing anti-jointing material layer.
The invention has the beneficial effects as follows: the one, adopt described combination base substrate to be rolled, efficiently solve casting copper base temperature difference in course of hot rolling, thereby roll-force is even, gained copper coin surface smoothness height; The 2nd, the roll-force of roll of having utilized two substrate homogenizing, thus avoided because of the unstable lot of unstable factor of bringing of milling train, and then improved rolling quality; The 3rd, adopt anti-jointing material layer both to prevent the bonding of substrate and casting copper base, the copper base is freely extended in the operation of rolling, can also keep the temperature stabilization of copper base.In addition, compound copper coin is cut, avoided copper coin owing to the soft cutting inconvenience that causes, guaranteed that effectively gained copper coin edge is regular, reduced follow-up arranging process.
On the basis of technique scheme, the present invention can also do following improvement.
Further, described two substrate periphery are connected to of steps A clustered operation is tightly connected, and makes between two substrates and forms seal cavity, and described seal cavity is vacuumized processing.
Adopt the beneficial effect of above-mentioned further scheme to be, adopt seal cavity, can make the copper coin edge of moulding smooth, the sealing space is vacuumized processing, casting copper base was pined for guaranteeing process safety in follow-up adding, avoid air to expand to the influence of product quality, also help between substrate and the casting copper base and combine closely, also be conducive to that casting copper base extends smoothly when rolling simultaneously.
Further, also be included in isolating bar is placed at described casting copper base periphery before being welded to connect in two substrate periphery edges.
Adopt the beneficial effect of above-mentioned further scheme to be, adopt isolating bar can avoid when the upper and lower base plate edge is connected by the connecting plate weldering, causing and the weldering of described casting copper base mistake.
Further, the gained copper coin is heat-treated after also being included in described step C.
Adopt the beneficial effect of above-mentioned further scheme to be, this heat treatment step can make copper coin reach the hardness of regulation.
Further, described substrate is carbon steel material.
Adopt the beneficial effect of above-mentioned further scheme to be, carbon steel is drawn materials conveniently, is convenient to seam utilization repeatedly.
Further, described anti-jointing material layer is barrier film.
Adopt the beneficial effect of above-mentioned further scheme to be, can prevent substrate and the adhesion in the operation of rolling of casting copper base, also help casting copper base simultaneously and extend smoothly.
Description of drawings
Fig. 1 is combination blank structure schematic diagram of the present invention;
Fig. 2 is that the A-A of Fig. 1 is to cutaway view;
Fig. 3 is operation of rolling schematic diagram of the present invention.
In Fig. 1~Fig. 3,1, substrate; 2, casting copper base; 3, anti-jointing material layer; 4, isolating bar; 5, welded seal band; 6, combination base substrate; 7, milling train.
The specific embodiment
Below in conjunction with accompanying drawing principle of the present invention and feature are described, institute gives an actual example and only is used for explaining the present invention, is not for limiting scope of the present invention.
As Fig. 1~shown in Figure 3, a kind of copper coin milling method comprises substrate 1 and casting copper base 2, and it comprises the steps:
A: make base substrate:
(1), get the raw materials ready: width prepares to cast 2 one of copper bases respectively on request, 1 two of substrates, the overall size of described substrate 1 is equal to or greater than the overall size of casting copper base 2, and substrate 1 and casting copper base 2 surfaces are carried out cleaning respectively; Getting carbon steel substrate 1 in this example is of a size of: long 2500 millimeters, and wide 1500 millimeters, thick 400 millimeters.Casting copper base 2 is of a size of; Long 2490 millimeters, wide 1490 millimeters, thick 200 millimeters.The overall size of namely generally getting substrate 1 greater than 5~10 millimeters of the overall sizes of casting copper base 2 for well.
(2), combination: be clipped between described two substrates 1 described casting copper base 2 and firm fitting to together, and two substrate 1 periphery edges are welded to connect, obtain making up base substrate 6, also scribble anti-jointing material layer 3 on the two sides of described casting copper base 2.
(3), combination base substrate heating: will put into heating furnace through the combination base substrate 6 that step (2) obtain and heat, and be heated to temperature at 700~900C °;
B: rolling: will make compound copper coin through being rolled on the combination base substrate 6 immigration milling trains 7 after step (3) heating;
C: cutting: according to instructions for use compound copper coin is cut by size, substrate 1 is removed in the cutting back, and obtains copper coin after removing anti-jointing material layer 3.
Described two substrate 1 peripheries are connected to of steps A clustered operation is tightly connected, and makes between two substrates 1 and forms seal cavity, and described seal cavity is vacuumized processing.Described being tightly connected is that embedding is all welded at two substrates, 1 periphery edge place, forms welded seal band 5, to improve the constraint to casting copper base 2.Guarantee that rolling back copper coin is regular.
Also be included in two substrate 1 periphery edges are placed isolating bar 4 at described casting copper base 2 peripheries before being welded to connect.
After also being included in described step C the gained copper coin is heat-treated.
Described substrate 1 is carbon steel material.
Described anti-jointing material layer 3 is barrier film, as adopts magnesium oxide-based barrier film.
The above only is preferred embodiment of the present invention, and is in order to limit the present invention, within the spirit and principles in the present invention not all, any modification of doing, is equal to replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (5)
1. a copper coin milling method comprises substrate and casting copper base, it is characterized in that, comprises the steps:
A: make base substrate:
(1), get the raw materials ready: width prepares to cast one of copper base respectively on request, two of substrates, the overall size of described substrate is equal to or greater than the overall size of casting copper base, and substrate and casting copper base surface are carried out cleaning respectively;
(2), combination: be clipped between described two substrates described casting copper base and firm fitting to together, and two substrate periphery edges are welded to connect, obtain making up base substrate, also scribble anti-jointing material layer on the two sides of described casting copper base;
(3), combination base substrate heating: will put into heating furnace through the combination base substrate that step (2) obtain and heat, and be heated to temperature at 700~900C °;
B: rolling: will make compound copper coin through being rolled on the combination base substrate immigration milling train after step (3) heating;
C: cutting: according to instructions for use compound copper coin is cut by size, substrate is removed in the cutting back, and obtains copper coin after removing anti-jointing material layer.
2. copper coin milling method according to claim 1 is characterized in that, described two substrate periphery are connected to of steps A clustered operation is tightly connected, and makes between two substrates and forms seal cavity, and described seal cavity is vacuumized processing.
3. copper coin milling method according to claim 1 and 2 is characterized in that, also is included in isolating bar is placed at described casting copper base periphery before being welded to connect in two substrate periphery edges.
4. copper coin milling method according to claim 1 is characterized in that, described substrate is carbon steel material.
5. copper coin milling method according to claim 1 and 2 is characterized in that, described anti-jointing material layer is barrier film.