CN103266490A - Solution of coating polyether glycol composition inside woven bag - Google Patents
Solution of coating polyether glycol composition inside woven bag Download PDFInfo
- Publication number
- CN103266490A CN103266490A CN2012105652604A CN201210565260A CN103266490A CN 103266490 A CN103266490 A CN 103266490A CN 2012105652604 A CN2012105652604 A CN 2012105652604A CN 201210565260 A CN201210565260 A CN 201210565260A CN 103266490 A CN103266490 A CN 103266490A
- Authority
- CN
- China
- Prior art keywords
- coating
- woven bag
- parts
- weight portion
- described method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A solution of coating polyether glycol composition inside woven bag comprises the steps of: firstly, weaving warps and wefts made of fiber materials into a cylindrical fiber braid on a circular weaving machine; then spraying a coating prepared on site on the inner side of the braid to form a liner, wherein the coating comprises the following components in parts by mass: 21-25 parts of ethylene-vinyl acetate copolymer, 46-55 parts of polyvinyl alcohol, 16-25 parts of isocyanate, 16-25 parts of polyether glycol and 10-30 parts of diethyl methyl benzene diamine; and drying to obtain the woven bag which is inside coated with the coating.
Description
Technical field
The present invention relates to a kind of painting method, specifically, relate to apply in the woven bag polyether Glycols composition scheme.
Background technology
Woven bag is the packing of the widely used conveying powdered products of industry such as industry, agricultural, building.Woven bag is normally formed by interlacing silk braiding, has small slit in the crossover sites of braided wires.In order to remedy this defective, people once were used for the woven bag face coat with polyvinyl resin.This coating is aging coming off easily, and also not wear-resisting, service life is shorter.The manufacture method of this kind face coat woven bag is: first weaving fiber tubular article on circular loom, then coated with resins is joined in the extruder, and through extruder extruding and hot melting film, be coated to the outer surface of knitted cylindrical thing and become product.This production method needs more production equipment, and energy resource consumption is bigger, and factory building is also had requirement; Simultaneously environment and operating personnel's health is all brought adverse effect.
Summary of the invention
The technical problem to be solved in the present invention is the deficiency that overcomes existing woven bag surface coating process, provide a kind of wear-resisting, corrosion-resistant, intensity is high, long service life, production technology is simple simultaneously, efficient is high, free of contamination woven bag painting method.
The woven bag of manufacturing of the present invention is made of fibrage layer and inner liner, and improvements are that described inner liner forms lining by spraying method in fibrage layer inside.
Described fibrage layer is to be main raw material with polypropylene (English name pp), through extruding, stretch the formation flat filament, weaves, works out through circular loom again.The thickness of described inner liner is 0.1～0.6mm.
Woven bag preparation method of the present invention is: warp and the parallel that will adopt fibrous material to make on circular loom earlier are woven into tubular fibrage layer, then coating is sprayed on the inboard liner that forms of braid, described coating comprises following component (parts by mass) and content:
Ethylene-vinyl acetate copolymer 21-25
Polyvinyl alcohol 46-55
Isocyanates 16-25
Polyether Glycols 16-25
Diethyl toluene diamine 10-30.
After the above-mentioned coating component prepared abundant mixing at the scene, 45 ℃～60 ℃ of temperature, under the condition of pressure 10～15MPa, utilize spray gun to be sprayed on the inboard of fibrage layer, form lining coating, after the drying, product.
Above-mentioned warp and parallel are to adopt acrylic resin and are that to add weight portion be 0.4 part antioxidant 1010, the ultra-violet absorber UV-327 that weight portion is 0.5 part, the auxiliary antioxidant DLTP that weight portion is 0.6 part for 100 parts acrylic resin according to weight portion; The mixture that obtains is stretched by extruder and wire drawing machine; The polyacrylic fibres that rolling forms, it has high strength, high abrasion, good toughness, premium properties such as in light weight.The coating of above-mentioned spraying is a kind of novel environment friendly material, be sprayed on woven bag tubular article inboard, have coating densification, continuous, jointless characteristics, corrosion-resistant, high temperature resistant, shock resistance, be difficult for aging coming off, and the moisture in the air-isolation and the infiltration of oxygen fully, especially be fit to carry chemical industry raw material, agrochemical, pulverulent materials such as building building cement.Woven bag painting method provided by the invention has improved prior art and has used extruder at woven bag outer surface coated plastic film, utilizes another surface that bag overturning machine translates into woven bag complicated technology of coated plastic film more then.Its objective is that a kind of raw materials consumption is provided is few, cost is low, and is in light weight, woven bag manufacture method of long service life and products thereof.Not only technology is simple for this method, equipment less investment, production efficiency height, and is conducive to environmental protection.
The specific embodiment
Further specify the present invention below by embodiment.
Embodiment 1
Be that to add weight portion be 0.4 part antioxidant 1010, the ultra-violet absorber UV-327 that weight portion is 0.5 part, the auxiliary antioxidant DLTP that weight portion is 0.6 part for 100 parts acrylic resin according to weight portion; The mixture that obtains is stretched rolling and make polyacrylic fibres by extruder and wire drawing machine.Be woven into tubular fibrage layer with polyacrylic fibres as warp and parallel at circular loom, then coating be sprayed on the inboard liner that forms of braid, described coating comprises following component (parts by mass) and content:
Ethylene-vinyl acetate copolymer 21
Polyvinyl alcohol 46
Isocyanates 16
Polyether Glycols 25
Diethyl toluene diamine 10.
After the scene preparation fully mixes, 45 ℃ of temperature, under the condition of pressure 10MPa, utilize spray gun to be sprayed on the inboard of fibrage layer the above-mentioned coating component, form lining coating, coating thickness 0.1mm, the woven bag of spraying in namely obtaining after the heated-air drying.
Embodiment 2
Repeat embodiment 1, the coating processes of woven bag and embodiment 1 are roughly the same, and difference is that coating comprises following component (parts by mass) and content:
Ethylene-vinyl acetate copolymer 25
Polyvinyl alcohol 55
Isocyanates 25
Polyether Glycols 16
Diethyl toluene diamine 30
60 ℃ of spraying temperatures, spray pressure 15MPa, coating thickness 0.6mm.
Embodiment 3
Repeat embodiment 1, the coating processes of woven bag and embodiment 1 are roughly the same, and difference is that coating comprises following component (parts by mass) and content:
Ethylene-vinyl acetate copolymer 23
Polyvinyl alcohol 50
Isocyanates 20
Polyether Glycols 20
Diethyl toluene diamine 20
53 ℃ of spraying temperatures, spray pressure 13MPa, coating thickness 0.3mm.
Claims (5)
1. apply polyether Glycols composition scheme in the woven bag, this method may further comprise the steps: warp and the parallel that will adopt fibrous material to make on circular loom earlier are woven into tubular fibrage layer, then coating is sprayed on the inboard liner that forms of braid, described coating comprises following component (parts by mass) and content:
Ethylene-vinyl acetate copolymer 21-25
Polyvinyl alcohol 46-55
Isocyanates 16-25
Polyether Glycols 16-25
Diethyl toluene diamine 10-30
The woven bag product of spraying in obtaining after the drying.
2. according to the described method of claim 1, it is characterized in that described coating is on-the-spot preparation.
3. according to the described method of claim 1, it is characterized in that the temperature of described coating spraying is 45 ℃～60 ℃, pressure is 10～15MPa.
4. according to the described method of claim 1, it is characterized in that the thickness of described liner is 0.1～0.6mm.
5. according to the described method of claim 1, it is characterized in that described warp and parallel are to adopt acrylic resin and are that to add weight portion be 0.4 part antioxidant 1010, the ultra-violet absorber UV-327 that weight portion is 0.5 part, the auxiliary antioxidant DLTP that weight portion is 0.6 part for 100 parts acrylic resin according to weight portion; The mixture that obtains is stretched the polyacrylic fibres that rolling forms by extruder and wire drawing machine.