CN103264242A - Composite materials for aluminium base brazing and preparation method thereof - Google Patents
Composite materials for aluminium base brazing and preparation method thereof Download PDFInfo
- Publication number
- CN103264242A CN103264242A CN2013101992137A CN201310199213A CN103264242A CN 103264242 A CN103264242 A CN 103264242A CN 2013101992137 A CN2013101992137 A CN 2013101992137A CN 201310199213 A CN201310199213 A CN 201310199213A CN 103264242 A CN103264242 A CN 103264242A
- Authority
- CN
- China
- Prior art keywords
- brazing
- soldering
- composite
- coating
- aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides composite materials for aluminium base brazing. The composite materials comprise aluminium or aluminium alloy base materials, and a coating arranged on the base materials, wherein the coating comprises metal powder for brazing, brazing flux and thermoplastic methyl acrylic ester copolymers. According to the composite materials, the thermoplastic methyl acrylic ester copolymers serve as carriers to load the metal powder and the brazing flux and can volatilize or can be thermally decomposed before the brazing flux is melted, no residues exist, and influences on the brazing cannot be caused. In the brazing process, the brazing flux can eliminate oxides on surfaces of aluminium products, so proceeding of the brazing process is benefited. The metal powder is melted and exposed on the surfaces of aluminium products in the brazing process, the fact that the appropriate liquidus temperature promotes excellent brazing is guaranteed, and corrosion resistance in brazing positions is also improved because of existence of the metal powder. Therefore, the composite materials for the aluminium base brazing do not need to use a great amount of fluoride brazing flux, and has good brazing effects.
Description
Technical field
The present invention relates to technical field of soldering materials, relate in particular to a kind of aluminium base soldering composite and preparation method thereof.
Background technology
Aluminium has the intensity height, density is little, corrosion-resistant, and heat conduction, electric conductivity good (slightly inferior to copper) are even also can keep characteristics such as excellent mechanical performances under lower temperature.In aluminium, fuse into the aluminium alloy that elements such as Mn, Mg, Si are prepared into, be greatly improved again at aspects such as hardness, fusing points, therefore aluminium and alloy thereof occupy unique status in The modern industry, are applied to fields such as electronics, automobile, Aero-Space, machine-building widely.In manufacturings such as artificial satellite, rocket, guided missile, microwave device, aircraft, radiator or air-conditioning heat dissipation for weight reduction, force down energy consumption, raise the efficiency and strengthen mobility and all exhaust possibly with aluminium for copper, even Dai Gang.Along with the large-scale application of aluminum products, aluminium base soldering tech has also obtained development widely.
Soldering is to adopt to do solder than the low-melting metal material of mother metal, and weldment and solder are heated to above the solder fusing point, is lower than the mother metal fusion temperature, utilizes the wetting mother metal of liquid solder, fills the play movement and realizes being connected the method for weldment with the counterdiffusion of mother metal phase.The soldering heating-up temperature is low, does not relate to the fusing of parent metal, can alleviate matrix-wild phase interfacial reaction, reduces the destructiveness that strengthens body, significantly improves thermal deformation, is a kind of method of attachment that the important application prospect is arranged.Because the oxide-film of aluminium and alloy surface thereof is difficult to remove, it is poor making the braze ability of aluminium and alloy thereof compare with other common metal materials.
In order to obtain good soldering effect, be that the brazed aluminum alloy product needed of representative is removed the oxide layer that forms in its surface with the car heat exchanger after extrusion molding or calendering.Traditional handicraft is after the element assembling of want soldering, utilizes spraying or similar step the suspension of fluoride flux to be applied to the element surface of required soldering before soldering processes.In order to remove the element surface oxide, particularly baroque element needs to spray a large amount of fluoride fluxs, does like this to cause cost to increase.In addition in this technology, the viscosity difference of brazing flux after applying and therefore brazing flux float because of the hot-air that in stove, circulates and cause the condition of work of deterioration.
Summary of the invention
The object of the present invention is to provide a kind of aluminium base soldering composite and preparation method thereof, aluminium base soldering provided by the invention need not to spray a large amount of brazing fluxes with composite in use, has improved the soldering effect.
The invention provides a kind of aluminium base soldering composite, comprise the aluminum or aluminum alloy base material;
Be arranged at the coating on the described base material;
Described coating comprises soldering metal dust, brazing flux and thermoplastic methacrylic lipin polymer.
Preferably, the mass ratio of described metal dust and brazing flux is 1:1~1:4.
Preferably, the average grain diameter of described metal dust≤30 μ m.
Preferably, described metal dust comprises following component:
0.01 the Zn of ω t%~5 ω t%;
The Si of surplus.
Preferably, described brazing flux is fluoride.
Preferably, the average grain diameter of described brazing flux≤8 μ m.
Preferably, the mass content of thermoplastic methacrylic lipin polymer is 1 ω t%~15 ω t% in the described coating.
Preferably, the content of described coating is 10g/m
2~30g/m
2
The invention provides a kind of aluminium base soldering preparation method of composite, may further comprise the steps:
The thermoplastic methacrylic lipin polymer is dissolved in the organic solvent, to wherein adding brazing flux and metal dust, obtains coating then;
Described coating is coated in the surface of aluminum or aluminum alloy base material;
The composite of finishing coating is carried out drying, obtain aluminium base soldering composite.
Preferably, described organic solvent is ester type compound.
Preferably, describedly be applied to spraying, roller coat, brushing or dip-coating.
Preferably, the temperature of described drying is 80 ℃~150 ℃.
The invention provides a kind of aluminium base soldering composite, comprise the aluminum or aluminum alloy base material; Be arranged at the coating on the described base material; Described coating comprises soldering metal dust, brazing flux and thermoplastic methacrylic lipin polymer.The present invention arranges coating at the aluminum or aluminum alloy substrate surface, and described coating comprises metal dust, brazing flux and thermoplastic methacrylic lipin polymer.In the present invention, the thermoplastic methacrylic lipin polymer is as carrier, carried metal powder and brazing flux, and described thermoplastic methacrylic lipin polymer can volatilize or thermal decomposition before the brazing flux fusing, and noresidue can not impact the soldering effect; In the process of soldering, brazing flux can be removed the oxide of aluminium material surface, is conducive to the carrying out of brazing process; Metal dust is dissolved in exposed aluminium material surface in the process of soldering, guaranteed that suitable liquidus temperature facilitates outstanding soldering, and the existence of metal dust has also improved the corrosion resistance of soldering place.Therefore, aluminium base soldering provided by the invention need not to use a large amount of fluoride fluxs with composite, and has soldering effect preferably.
In addition, aluminium base soldering provided by the invention need not in brazing process to spray a large amount of fluoride fluxs with composite, also just can not influence the effect of soldering because of the viscosity difference of brazing flux, evaporates into and makes work under bad environment in the air nor have brazing flux.Aluminium base soldering provided by the invention also has lower production cost with composite, is conducive to its large-scale industrial production.
The specific embodiment
The invention provides a kind of aluminium base soldering composite, comprise the aluminum or aluminum alloy base material;
Be arranged at the coating on the described base material;
Described coating comprises soldering metal dust, brazing flux and thermoplastic methacrylic lipin polymer.
Aluminium base soldering provided by the invention can be volatilized or thermal decomposition before the brazing flux fusing with the thermoplastic methacrylic lipin polymer in the composite, and noresidue can not impact the soldering effect; Brazing flux is removed the oxide of aluminium material surface in the process of soldering, be conducive to the carrying out of brazing process; Metal dust is dissolved in exposed aluminium material surface in the process of soldering, guaranteed that suitable liquidus temperature facilitates outstanding soldering, and the existence of metal dust has also improved the corrosion resistance of soldering place.Therefore, aluminium base soldering provided by the invention need not to use in a large number fluoride flux with composite, and has soldering effect preferably.
Aluminium base soldering provided by the invention comprises the aluminum or aluminum alloy base material with composite.The present invention does not have special restriction to type, the source of described aluminum or aluminum alloy base material, adopts soldering well known to those skilled in the art to get final product with the aluminum or aluminum alloy base material.In the present invention, in order to make between coating and aluminum or aluminum alloy base material better the contact arranged, described aluminum or aluminum alloy base material is preferably the aluminum or aluminum alloy base material through surperficial degreasing.
Aluminium base soldering provided by the invention comprises the coating that is arranged on the described base material with composite.In invention, described coating preferably is arranged on a side of described aluminum or aluminum alloy base material at least, also can in the both sides of aluminum or aluminum alloy base material coating be set all according to the needs of brazing operation.
In the present invention, described coating comprises metal dust.In the present invention, described metal dust preferably includes following component:
0.01 the Zn of ω t%~5 ω t%;
The Si of surplus.
In the present invention, described metal dust more preferably comprises the Zn of 0.05 ω t%~4 ω t%, most preferably is 1 ω t%~3 ω t%, and surplus is Si.When soldering connected the aluminium surface, brazing flux was 600 ℃ of fusings, and fusion or eliminate and will connect original oxide-film on the aluminium surface, exposed the aluminium lamination that makes new advances and gave Si.Because Si has higher solubility in aluminium under this temperature, the very fast fusion of Si forms the Al-Si alloy surface in exposed aluminium lamination.In the present invention, the Zn in the metal dust can play the anodic protection effect, has improved the decay resistance of soldering place.The inventor discovers that when Zn contained quantity not sufficient 0.01 ω t%, this anodic protection effect was not obvious, and when Zn content surpassed 5 ω t%, this anodic protection effect can not increase and reduce the soldering effect on the contrary;
In the present invention, the particle of metal dust is excessive to cause metallic particles fusion difficulty easily, influence welding quality, the average grain diameter of described metal dust preferably≤30 μ m, more preferably≤20 μ m, most preferably≤10 μ m.
In the present invention, described coating comprises brazing flux, and the present invention does not have special restriction to the kind of described brazing flux, adopts brazing flux well known to those skilled in the art to get final product.In the present invention, described brazing flux preferred fluorinated thing, more preferably fluoaluminate most preferably is potassium fluoroaluminate.In the present invention, the average grain diameter of described brazing flux preferred≤8 μ m, more preferably≤5 μ m.In the process of carrying out soldering, described brazing flux can be removed the oxide that connects the aluminium surface.In the present invention, when the mass ratio of metal dust and brazing flux is big in the coating, the brazed seam slag inclusion can occur, weld problems such as stifled; The mass ratio of metal dust and brazing flux hour problems such as brazed seam does not weld, brazed seam does not fill up occur easily in the brazing process.Therefore, in the present invention, the mass ratio of described metal dust and described brazing flux is preferably 1:1~1:4, more preferably 1:2~1:3.
In the present invention, described coating comprises the thermoplastic methacrylic lipin polymer, and described thermoplastic methacrylic lipin polymer is as carrier, carried metal powder and brazing flux.In the present invention, heated volatile or the thermal decomposition before the brazing flux fusing of described thermoplastic methacrylic lipin polymer, noresidue exists.In the present invention, the content of thermoplastic methacrylic lipin polymer is preferably 1 ω t%~15 ω t% in the described coating, more preferably 5 ω t%~10 ω t%.
In the present invention, the content of described coating is crossed when low, occurs easily in the process of soldering that brazed seam does not weld, problems such as brazed seam does not fill up, rosin joint; If the too high levels of coating in the process of soldering, problems such as brazed seam slag inclusion, surface erosion, weldering be stifled occur easily.In the present invention, the content of described coating is preferably 10g/m
2~30g/m
2, 15g/m more preferably
2~20g/m
2, the aluminium base soldering that obtains under this coating levels has higher soldering effect with composite.
A kind of aluminium base soldering preparation method of composite may further comprise the steps:
The thermoplastic methacrylic lipin polymer is dissolved in the organic solvent, to wherein adding brazing flux and metal dust, obtains coating then;
Described coating is coated in the surface of aluminum or aluminum alloy base material, obtains aluminium base soldering composite after the drying.
The present invention is dissolved in the thermoplastic methacrylic lipin polymer in the organic solvent, to wherein adding brazing flux and metal dust, obtains coating then.In the present invention, the described thermoplastic methacrylic lipin polymer of described thermoplastic methacrylic lipin polymer, brazing flux and metal dust and technique scheme, brazing flux and metal dust are consistent, do not repeat them here.In the present invention, described organic solvent is preferably ester type compound, ethyl acetate more preferably, and ethyl acetate has good solvability, boiling point is low, has the characteristics of quick-drying in coating, therefore, in the process of carrying out soldering, ethyl acetate volatilizees easily, can not impact brazing process.The present invention does not have special restriction to the consumption of described organic solvent, can be with described thermoplastic methacrylic lipin polymer dissolving, and the coating of preparation desired concn gets final product, and those skilled in the art can select the consumption of organic solvent according to the concentration of required coating.
After obtaining coating, the present invention is coated in the surface of aluminum or aluminum alloy base material with described coating, obtains aluminium base soldering composite after the drying.The present invention has good effect in order to make between coating and the aluminum or aluminum alloy base material, preferably the aluminum or aluminum alloy base material is carried out surperficial ungrease treatment, the present invention does not have special restriction to the method for described surperficial degreasing, adopts the technical scheme of aluminum or aluminum alloy surface degreasing well known to those skilled in the art to get final product.The present invention does not have special restriction to the method for described coating, adopts the method for coating coating well known to those skilled in the art to get final product.In the present invention, described coating is preferably spraying, roller coat, brushing or dip-coating, more preferably spraying or roller coat;
The present invention does not have special restriction to the method for described drying, adopts the technical scheme of drying well known to those skilled in the art to get final product.In the present invention, it is slower that dry temperature is crossed the volatilization of low solvent, the too high waste that then causes the energy of baking temperature, and the temperature of described drying is preferably 80 ℃~150 ℃, more preferably 90 ℃~140 ℃, most preferably is 100 ℃~130 ℃.
The invention provides a kind of aluminium base soldering composite, comprise the aluminum or aluminum alloy base material; Be arranged at the coating on the described base material; Described coating comprises soldering metal dust, brazing flux and thermoplastic methacrylic lipin polymer.The present invention arranges coating at the aluminum or aluminum alloy substrate surface, and described coating comprises metal dust, brazing flux and thermoplastic methacrylic lipin polymer.In the present invention, the thermoplastic methacrylic lipin polymer is as carrier, carried metal powder and brazing flux, and described thermoplastic methacrylic lipin polymer can volatilize or thermal decomposition before the brazing flux fusing, and noresidue can not impact the soldering effect; Brazing flux is removed the oxide of aluminium material surface in the process of soldering, be conducive to the carrying out of brazing process; Metal dust is dissolved in exposed aluminium material surface in the process of soldering, guaranteed that suitable liquidus temperature facilitates outstanding soldering, and the existence of metal dust has also improved the corrosion resistance of soldering place.Therefore, aluminium base soldering provided by the invention need not to use a large amount of fluoride fluxs with composite, and has soldering effect preferably.
In addition, aluminium base soldering provided by the invention need not in brazing process to spray a large amount of fluoride fluxs with composite, also just can not influence the effect of soldering because of the viscosity difference of brazing flux, evaporates into and makes work under bad environment in the air nor have brazing flux.Aluminium base soldering provided by the invention also has lower production cost with composite, is conducive to its large-scale industrial production.
In order to further specify the present invention, below in conjunction with embodiment aluminium base soldering provided by the invention is described in detail with composite and preparation method thereof, but they can not be interpreted as restriction to protection domain of the present invention.
Embodiment 1
With average grain diameter less than the metal dust of 20 μ m, particle diameter less than the potassium fluoroaluminate of 8 μ m, thermoplastic methacrylic lipin polymer by mass percentage the ratio of 5:5:1 be dissolved in the ethyl acetate, obtain coating;
Coating is sprayed to aluminium material surface through degreasing, and coating surface content is controlled at 20g/m
2, 100 ° of C oven dry, obtain aluminium base soldering composite then.
The present invention carries out soldering with prepared composite, and the result is as shown in table 1, and the aluminium base soldering that table 1 obtains for the embodiment of the invention 1~4 and comparative example 1~2 is with the brazing property test result of composite.
Embodiment 2
Adopt the technical scheme of embodiment 1 to prepare aluminium base soldering composite, different is that the mass percent of metal dust, potassium fluoroaluminate and carrier is 3:7:1 in the present embodiment.
The present invention carries out soldering with prepared composite, and the result is as shown in table 1, and the aluminium base soldering that table 1 obtains for the embodiment of the invention 1~4 and comparative example 1~2 is with the brazing property test result of composite.
Embodiment 3
Adopt the technical scheme of embodiment 1 to prepare aluminium base soldering composite, different is that the mass percent of metal dust, potassium fluoroaluminate and carrier is 4:6:1 in the present embodiment.
The present invention carries out soldering with prepared composite, and the result is as shown in table 1, and the aluminium base soldering that table 1 obtains for the embodiment of the invention 1~4 and comparative example 1~2 is with the brazing property test result of composite.
Embodiment 4
Adopt the technical scheme of embodiment 1 to prepare aluminium base soldering composite, different is that the mass percent of metal dust, potassium fluoroaluminate and carrier is 2:8:1 in the present embodiment.
The present invention carries out soldering with prepared composite, and the result is as shown in table 1, and the aluminium base soldering that table 1 obtains for the embodiment of the invention 1~4 and comparative example 1~2 is with the brazing property test result of composite.
Comparative example 1
Adopt the technical scheme of embodiment 1 to prepare aluminium base soldering composite, different is that the mass percent of metal dust, potassium fluoroaluminate and carrier is 7:3:1 in the present embodiment.
The present invention carries out soldering with prepared composite, and the result is as shown in table 1, the aluminium base soldering that table 1 obtains for the embodiment of the invention 1~6 brazing property test result of composite.
Comparative example 2
Adopt the technical scheme of embodiment 1 to prepare aluminium base soldering composite, different is that the mass percent of metal dust, potassium fluoroaluminate and carrier is 1:9:1 in the present embodiment.
The present invention carries out soldering with prepared composite, and the result is as shown in table 1, and the aluminium base soldering that table 1 obtains for the embodiment of the invention 1~4 and comparative example 1~2 is with the brazing property test result of composite.
The aluminium base soldering that table 1 embodiment of the invention 1~4 and comparative example 1~2 the obtain brazing property test result of composite
As can be seen from Table 1, control in 1:1~1:4 when the mass ratio of metal dust and potassium fluoroaluminate, the soldering effect of the composite that obtains is better.
Embodiment 5
With particle diameter less than the metal dust of 20 μ m, particle diameter less than the potassium fluoroaluminate of 8 μ m and thermoplastic methacrylic lipin polymer by mass percentage the ratio of 3:7:1 be dissolved in the ethyl acetate, obtain coating;
Coating is sprayed to aluminium material surface through degreasing, and coating surface content is controlled at 10g/m
2, under 100 ° of C, dry then, obtain aluminium base soldering composite.
The present invention carries out soldering with prepared composite, and the result is as shown in table 2, and the aluminium base soldering that table 2 obtains for the embodiment of the invention 5~8 and comparative example 3~4 is with the brazing property test result of composite.
Embodiment 6
Adopt the technical scheme of embodiment 1 to prepare aluminium base soldering composite, different is that present embodiment floating coat surface content is 15g/m
2
The present invention carries out soldering with prepared composite, and the result is as shown in table 2, and the aluminium base soldering that table 2 obtains for the embodiment of the invention 5~8 and comparative example 3~4 is with the brazing property test result of composite.
Embodiment 7
Adopt the technical scheme of embodiment 1 to prepare aluminium base soldering composite, different is that present embodiment floating coat surface content is 20g/m
2
The present invention carries out soldering with prepared composite, and the result is as shown in table 2, and the aluminium base soldering that table 2 obtains for the embodiment of the invention 5~8 and comparative example 3~4 is with the brazing property test result of composite.
Embodiment 8
Adopt the technical scheme of embodiment 1 to prepare aluminium base soldering composite, different is that present embodiment floating coat surface content is 30g/m
2
The present invention carries out soldering with prepared composite, and the result is as shown in table 2, and the aluminium base soldering that table 2 obtains for the embodiment of the invention 5~8 and comparative example 3~4 is with the brazing property test result of composite.
Comparative example 3
Adopt the technical scheme of embodiment 1 to prepare aluminium base soldering composite, different is that present embodiment floating coat surface content is 5g/m
2
The present invention carries out soldering with prepared composite, and the result is as shown in table 2, and the aluminium base soldering that table 2 obtains for the embodiment of the invention 5~8 and comparative example 3~4 is with the brazing property test result of composite.
Comparative example 4
Adopt the technical scheme of embodiment 1 to prepare aluminium base soldering composite, different is that present embodiment floating coat surface content is 50g/m
2
The present invention carries out soldering with prepared composite, and the result is as shown in table 2, and the aluminium base soldering that table 2 obtains for the embodiment of the invention 5~8 and comparative example 3~4 is with the brazing property test result of composite.
The aluminium base soldering that table 2 embodiment of the invention 5~8 and comparative example 3~4 the obtain brazing property test result of composite.
As can be seen from Table 2, the control of the content of coating is at 10g/m
2~30g/m
2In, the soldering effect of the composite that obtains is better.
As seen from the above embodiment, the invention provides a kind of aluminium base soldering composite, comprise the aluminum or aluminum alloy base material; Be arranged at the coating on the described base material; Described coating comprises soldering metal dust, brazing flux and thermoplastic methacrylic lipin polymer.The present invention arranges coating at the aluminum or aluminum alloy substrate surface, and described coating comprises metal dust, brazing flux and thermoplastic methacrylic lipin polymer.In the present invention, the thermoplastic methacrylic lipin polymer is as carrier, carried metal powder and brazing flux, and described thermoplastic methacrylic lipin polymer can volatilize or thermal decomposition before the brazing flux fusing, and noresidue can not impact the soldering effect; Brazing flux is removed the oxide of aluminium material surface in the process of soldering, be conducive to the carrying out of brazing process; Metal dust is dissolved in exposed aluminium material surface in the process of soldering, guaranteed that suitable liquidus temperature facilitates outstanding soldering, and the existence of metal dust has also improved the corrosion resistance of soldering place.Therefore, aluminium base soldering provided by the invention need not to use a large amount of fluoride fluxs with composite, and has soldering effect preferably.
In addition, aluminium base soldering provided by the invention need not in brazing process to spray a large amount of fluoride fluxs with composite, also just can not influence the effect of soldering because of the viscosity difference of brazing flux, evaporates into and makes work under bad environment in the air nor have brazing flux.Aluminium base soldering provided by the invention also has lower production cost with composite, is conducive to its large-scale industrial production.
The above only is preferred embodiment of the present invention; should be pointed out that for those skilled in the art, under the prerequisite that does not break away from the principle of the invention; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (12)
1. aluminium base soldering composite comprises the aluminum or aluminum alloy base material;
Be arranged at the coating on the described base material;
Described coating comprises soldering metal dust, brazing flux and thermoplastic methacrylic lipin polymer.
2. composite according to claim 1 is characterized in that, the mass ratio of described metal dust and brazing flux is 1:1~1:4.
3. composite according to claim 1 is characterized in that, the average grain diameter of described metal dust≤30 μ m.
4. according to any described composite of claim 1~3, it is characterized in that described metal dust comprises following component:
0.01 the Zn of ω t%~5 ω t%;
The Si of surplus.
5. composite according to claim 1 is characterized in that, described brazing flux is fluoride.
6. according to claim 1 or 5 any described composites, it is characterized in that the average grain diameter of described brazing flux≤8 μ m.
7. composite according to claim 1 is characterized in that, the mass content of thermoplastic methacrylic lipin polymer is 1 ω t%~15 ω t% in the described coating.
8. composite according to claim 1 is characterized in that, the content of described coating is 10g/m
2~30g/m
2
9. an aluminium base soldering may further comprise the steps with the preparation method of composite:
The thermoplastic methacrylic lipin polymer is dissolved in the organic solvent, to wherein adding brazing flux and metal dust, obtains coating then;
Described coating is coated in the surface of aluminum or aluminum alloy base material, obtains aluminium base soldering composite after the drying.
10. preparation method according to claim 9 is characterized in that, described organic solvent is ester type compound.
11. preparation method according to claim 9 is characterized in that, describedly is applied to spraying, roller coat, brushing or dip-coating.
12. preparation method according to claim 9 is characterized in that, the temperature of described drying is 80 ℃~150 ℃.