CN103253901B - 一种混凝土桥面快速铺装砂浆及其制备方法 - Google Patents

一种混凝土桥面快速铺装砂浆及其制备方法 Download PDF

Info

Publication number
CN103253901B
CN103253901B CN201310222531.0A CN201310222531A CN103253901B CN 103253901 B CN103253901 B CN 103253901B CN 201310222531 A CN201310222531 A CN 201310222531A CN 103253901 B CN103253901 B CN 103253901B
Authority
CN
China
Prior art keywords
bridge deck
concrete bridge
mortar
fast spreading
deck fast
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310222531.0A
Other languages
English (en)
Other versions
CN103253901A (zh
Inventor
王朝杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI YUXI NEW MATERIAL TECHNOLOGY Co Ltd
Original Assignee
SHANGHAI YUXI NEW MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI YUXI NEW MATERIAL TECHNOLOGY Co Ltd filed Critical SHANGHAI YUXI NEW MATERIAL TECHNOLOGY Co Ltd
Priority to CN201310222531.0A priority Critical patent/CN103253901B/zh
Publication of CN103253901A publication Critical patent/CN103253901A/zh
Application granted granted Critical
Publication of CN103253901B publication Critical patent/CN103253901B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种混凝土桥面快速铺装砂浆及其制备方法。其中,砂浆由以下重量百分比的原料组成:高强度特种水泥20~30%、普通水泥20~35%、膨胀剂1~2.5%、减水剂0.1~0.2%、硬石膏1~5%、缓凝剂0.01~0.1%、抗裂纤维0.05~0.1%、可分散胶粉1~2%、消泡剂0.05-1%和水洗级配砂46~56%。本发明是一种在短时间内即可凝固并达到一定强度的高性能砂浆,其不但具有一定的操作时间,而且能在6小时内强度达到30Mpa以上,只需简单养护后即可满足使用要求,从而缩短工程交付时间,有效降低扰民。本发明的混凝土桥面快速铺装砂浆还具有施工方便、快硬早强、大流态、自密实和环保等优点。

Description

一种混凝土桥面快速铺装砂浆及其制备方法
技术领域
本发明属于建筑材料技术领域,具体的说是涉及一种混凝土桥面快速铺装砂浆及其制备方法。
背景技术
目前高速公路或普通公路在施工或维修桥面时普遍采用混凝土进行施工,由于现有技术中的普通混凝土存在凝结时间慢、养护时间长、通车时间久等缺点,所以造成施工或维修时间长而影响交通的诸多问题。我国至今仍缺乏相应的产品,市场上缺乏专门用于混凝土桥面的快速铺装砂浆,因此,必须结合我国混凝土桥面施工或维修铺装的实际和需要,开发性能优良的专用材料。如果能够提供一种凝结快速、养护时间短的混凝土桥面快速铺装砂浆及其制备方法将成为人们迫切的需求。
发明内容
本发明为了克服现有技术存在的不足,提供一种凝结快速、养护时间短的混凝土桥面快速铺装砂浆及其制备方法。
本发明是通过以下技术方案实现的:一种混凝土桥面快速铺装砂浆,其特征在于:所述混凝土桥面快速铺装砂浆由以下重量百分比的原料组成:高强度特种水泥20~30%、普通水泥20~35%、膨胀剂1~2.5%、减水剂0.1~0.2%、硬石膏1~5%、缓凝剂0.01~0.1%、抗裂纤维0.05~0.1%、可分散胶粉1~2%、消泡剂0.05-1%和水洗级配砂46~56%。
为了能使本发明用于低温环境下,还包括促凝剂0.02-0.08%和纤维素醚0.05-0.15%。
作为本发明的优选实施方式,所述混凝土桥面快速铺装砂浆由以下重量百分比的原料组成:高强度特种水泥21~28%、普通水泥22~31%、膨胀剂1.2~2%、减水剂0.13~0.19%、硬石膏1.5~4%、缓凝剂0.03~0.07%、抗裂纤维0.06~0.08%、可分散胶粉1.2~1.7%、促凝剂0.04-0.06%、纤维素醚0.08-0.12%、消泡剂0.8-1%和水洗级配砂47~50%。
作为本发明的最佳实施方式,混凝土桥面快速铺装砂浆由以下重量百分比的原料组成:高强度特种水泥22%、普通水泥23%、膨胀剂1.6%、减水剂0.18%、硬石膏1.8%、缓凝剂0.05%、抗裂纤维0.07%、可分散胶粉1.3%、促凝剂0.05%、纤维素醚0.1%、消泡剂1%和水洗级配砂48.85%。
一种混凝土桥面快速铺装砂浆的制备方法,其包括如下步骤:将所述高强度特种水泥和普通水泥按照各自的重量百分比混合搅拌在一起,在搅拌的同时按照各原料的重量百分比依次添加膨胀剂、减水剂、硬石膏、缓凝剂、抗裂纤维、可分散胶粉、促凝剂、纤维素醚、消泡剂和水洗级配砂,将所有原料混合搅拌均匀即可。
本发明采用高强度特种水泥和普通水泥按照一定比例复合,同时添加缓凝剂及其它化合物调整其凝结时间、抗压(抗折及粘结)强度、流动性及耐久性等性能。
本发明的有益效果是:本发明的混凝土桥面快速铺装砂浆是一种在短时间内即可凝固并达到一定强度的高性能砂浆,其不但具有一定的操作时间,而且能在6小时内强度达到30Mpa以上,只需简单养护后即可满足使用要求,从而缩短工程交付时间,有效降低扰民。本发明的混凝土桥面快速铺装砂浆还具有如下优点:1、施工方便:现场加水及石子后即可使用;2、快硬早强:6小时内强度即可达到30Mpa以上,高粘结(28天粘结强度达2.6Mpa以上)、韧性好;3、大流态、自密实:流动度为140mm,并且可根据自重均匀流动,自密实;4、环保:无毒、无害,对钢筋无腐蚀,对水质及周围环境无影响。
具体实施方式
以下结合具体实施例对本发明作详细描述。
实施例1:一种混凝土桥面快速铺装砂浆,其由以下重量百分比的原料组成:高强度特种水泥20%、普通水泥20%、膨胀剂1%、减水剂0.1%、硬石膏1.84%、缓凝剂0.01%、抗裂纤维0.05%、可分散胶粉1%、消泡剂1%、水洗级配砂55%。
本发明混凝土桥面快速铺装砂浆的制备方法包括如下步骤:将高强度特种水泥和普通水泥按照各自的重量百分比混合搅拌在一起,在搅拌的同时按照各原料的重量百分比依次添加膨胀剂、减水剂、硬石膏、缓凝剂、抗裂纤维、可分散胶粉、消泡剂和水洗级配砂,将所有原料混合搅拌均匀即可。
实施例2:一种混凝土桥面快速铺装砂浆,其由以下重量百分比的原料组成:高强度特种水泥21%、普通水泥22%、膨胀剂1.8%、减水剂0.15%、硬石膏3.5%、缓凝剂0.05%、抗裂纤维0.07%、可分散胶粉1.4%、促凝剂0.02%、纤维素醚0.05%、消泡剂0.5%、水洗级配砂49.46%。
实施例3:一种混凝土桥面快速铺装砂浆,其由以下重量百分比的原料组成:高强度特种水泥21%、普通水泥25.87%、膨胀剂2.5%、减水剂0.2%、硬石膏1%、缓凝剂0.1%、抗裂纤维0.1%、可分散胶粉2%、促凝剂0.08%、纤维素醚0.15%、消泡剂1%、水洗级配砂46%。
实施例4:一种混凝土桥面快速铺装砂浆,其由以下重量百分比的原料组成:高强度特种水泥22%、普通水泥23%、膨胀剂1.6%、减水剂0.18%、硬石膏1.8%、缓凝剂0.05%、抗裂纤维0.07%、可分散胶粉1.3%、促凝剂0.05%、纤维素醚0.1%、消泡剂1%和水洗级配砂48.85%。
最后应当说明的是,以上内容仅用以说明本发明的技术方案,而非对本发明保护范围的限制,本领域的普通技术人员对本发明的技术方案进行的简单修改或者等同替换,均不脱离本发明技术方案的实质和范围。

Claims (3)

1.一种混凝土桥面快速铺装砂浆,其特征在于:所述混凝土桥面快速铺装砂浆由以下重量百分比的原料组成:高强度特种水泥21~28%、普通水泥22~31%、膨胀剂1.2~2%、减水剂0.13~0.19%、硬石膏1.5~4%、缓凝剂0.03~0.07%、抗裂纤维0.06~0.08%、可分散胶粉1.2~1.7%、促凝剂0.04-0.06%、纤维素醚0.08-0.12%、消泡剂0.8-1%和水洗级配砂47~50%。
2.根据权利要求1所述的一种混凝土桥面快速铺装砂浆,其特征在于:所述混凝土桥面快速铺装砂浆由以下重量百分比的原料组成:高强度特种水泥22%、普通水泥23%、膨胀剂1.6%、减水剂0.18%、硬石膏1.8%、缓凝剂0.05%、抗裂纤维0.07%、可分散胶粉1.3%、促凝剂0.05%、纤维素醚0.1%、消泡剂1%和水洗级配砂48.85%。
3.根据权利要求1所述的一种混凝土桥面快速铺装砂浆的制备方法,其特征在于:所述混凝土桥面快速铺装砂浆的制备方法包括如下步骤:将所述高强度特种水泥和普通水泥按照各自的重量百分比混合搅拌在一起,在搅拌的同时按照各原料的重量百分比依次添加膨胀剂、减水剂、硬石膏、缓凝剂、抗裂纤维、可分散胶粉、促凝剂、纤维素醚、消泡剂和水洗级配砂,将所有原料混合搅拌均匀即可。
CN201310222531.0A 2013-06-06 2013-06-06 一种混凝土桥面快速铺装砂浆及其制备方法 Expired - Fee Related CN103253901B (zh)