CN103243276A - 一种非调质自然预硬易切锻造模具用钢 - Google Patents
一种非调质自然预硬易切锻造模具用钢 Download PDFInfo
- Publication number
- CN103243276A CN103243276A CN2013101359680A CN201310135968A CN103243276A CN 103243276 A CN103243276 A CN 103243276A CN 2013101359680 A CN2013101359680 A CN 2013101359680A CN 201310135968 A CN201310135968 A CN 201310135968A CN 103243276 A CN103243276 A CN 103243276A
- Authority
- CN
- China
- Prior art keywords
- steel
- die
- hardening
- natural pre
- cut
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种非调质自然预硬易切锻造模具用钢,所述模具用钢由下述质量百分比的组分组成:C0.2-0.25%,Si0.25-0.30%,Mn1.6-1.8%,S≤0.007%,P≤0.015%,Cr1.6-2.0%,Mo0.22-0.32%,Cu0.13-0.18%,Ni0.15-0.25%,余量为Fe及不可避免的夹杂质。本发明具有与原美国钢P20模钢相同的使用功能,但是省去了热处理,并且成材后无需切割,可以从钢材毛胚直接下料,经过锻造后自然冷却,即可以达到29-33的HRC硬度。因此本发明非调质自然预硬易切锻造模具用钢具有加工周期短、能耗低、减少了原材料浪费的优点。
Description
技术领域
本发明属于炼钢技术,具体地,涉及一种非调质自然预硬易切锻造模具用钢。
背景技术
P20模钢是适用于制作塑料模和压铸低熔点金属的模具材料。此钢含有下述质量百分比的组分:碳C0.35-0.45%,硅Si0.2-0.4%,锰Mn1.3-1.6%,硫S≤0.035%,磷P≤0.005%,铬Cr1.8-2.1%,钼Mo0.25-0.5%。
现有技术的P20模钢具有如下缺陷:1、加工过程中需要进行锻造或回火,再进行调质热处理再回火,消除应力才能达到使用要求,因此加工工艺周期长、能耗大,极容易造成原材料的浪费。2、切削性能不理想,不能满足使用过程中对切削性能要求。
发明内容
本发明所要解决的技术问题是提供一种非调质自然预硬易切锻造模具用钢。它属于非调质钢,加工过程简单,具有HRC硬度29-33和优异的切削性能。
本发明解决上述技术问题所采用的技术方案是:一种非调质自然预硬易切锻造模具用钢,所述模具用钢由下述质量百分比的组分组成:C0.2-0.25%,Si0.25-0.30%,Mn1.6-1.8%,S≤0.007%,P≤0.015%,Cr1.6-2.0%,Mo0.22-0.32%,Cu0.13-0.18%,Ni0.15-0.25%,余量为Fe及不可避免的夹杂质。
本发明所述的非调质自然预硬易切锻造模具用钢采用锻造的方法加工而成,所述的锻造方法为直接锻造的方法,具体为:将含有上述组分的模具用钢在1250℃下锻造,然后冷却至室温(15-25℃)。
本发明与现有技术相比,具有如下优点:
(1)本发明具有与原美国钢P20模钢相同的使用功能,但是省去了热处理,并且成材后无需切割,可以从钢材毛胚直接下料,经过锻造后自然冷却,即可以达到29-33的HRC硬度。因此本发明非调质自然预硬易切锻造模具用钢具有加工周期短、能耗低、减少了原材料浪费的优点。
(2)本发明在原P20模钢的基础上降低了碳的含量,加入了铜的含量。这使得其可以在自然冷却下达到HRC硬度(29-33)的要求。
(3)本发明增加了0.13-0.18%的铜的含量,松化了钢材分子结构从而减去了钢材的应力,因此变得容易切削(并且在使用时不受其影响,可以符合使用的各项要求)。
具体实施方式
为了更好地理解本发明的内容,下面结合具体实施例作进一步说明。应理解,这些实施例仅用于对本发明进一步说明,而不用于限制本发明的范围。此外应理解,在阅读了本发明所述的内容后,该领域的技术人员对本发明作出一些非本质的改动或调整,仍属于本发明的保护范围。
实施例
一种非调质自然预硬易切锻造模具用钢,所述模具用钢由下述质量百分比的组分组成:C0.2-0.25%,Si0.25-0.30%,Mn1.6-1.8%,S≤0.007%,P≤0.015%,Cr1.6-2.0%,Mo0.22-0.32%,Cu0.13-0.18%,Ni0.15-0.25%,余量为Fe及不可避免的夹杂质。
本实施例模具用钢HRC硬度为29-33。
如上所述,便可以较好地实现本发明。
Claims (2)
1.一种非调质自然预硬易切锻造模具用钢,其特征在于,所述模具用钢由下述质量百分比的组分组成:C0.2-0.25%,Si0.25-0.30%,Mn1.6-1.8%,S≤0.007%,P≤0.015%,Cr1.6-2.0%,Mo0.22-0.32%,Cu0.13-0.18%,Ni0.15-0.25%,余量为Fe及不可避免的夹杂质。
2.根据权利要求1所述的非调质自然预硬易切锻造模具用钢,其特征在于,所述非调质自然预硬易切锻造模具用钢具有29-33的HRC硬度。