CN103242045A - Several-meter wide hollow ceramic board replacing steel boards, being sawed and drilled and being free from breakage - Google Patents
Several-meter wide hollow ceramic board replacing steel boards, being sawed and drilled and being free from breakage Download PDFInfo
- Publication number
- CN103242045A CN103242045A CN2012100359335A CN201210035933A CN103242045A CN 103242045 A CN103242045 A CN 103242045A CN 2012100359335 A CN2012100359335 A CN 2012100359335A CN 201210035933 A CN201210035933 A CN 201210035933A CN 103242045 A CN103242045 A CN 103242045A
- Authority
- CN
- China
- Prior art keywords
- ceramic
- porcelain mud
- board
- make
- hollow ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a hollow ceramic board which is free from breakage. The hollow ceramic board is formed by bonding ceramics and a ceramic straight board and a corrugated ceramic board. The hollow ceramic board has the beneficial effects that the bending resistance of the hollow ceramic paperboard is several times higher than that of the straight board, a square corrugated board, a sine corrugated board and a trough type board and the volume weight can be less than 0.1g/cm<3>; when the hollow ceramic board is impacted, the impact force is quickly transmitted to the ceramic fiber cloths and is absorbed by the ceramic fiber lines so that the hollow ceramic board is kept perfectly and can not be broken; the ceramic hardness is higher than hardness of steel so that the wear resistance of the ceramic board is greater than that of steel; ceramics have excellent acid-base resistance, so the ceramic fiber lines are not eaten by worms and ants and have service lives exceeding millennium; glass cloths are 0.2mm/m<2> thick and are cheap; the hollow ceramic board is resistant to impact, has service life of millennium, is resistant to acid-base, is light, has small thermal conductivity, is resistant to thousand-degree high temperature and is low in cost, so that the hollow ceramic board has obvious advantages in the industries of transportation, chemistry, heat preservation, architecture and the like for production of bridges, compartments, cabins, furniture, interior and exterior walls, plant tiling, decoration and the like; and if the 10cm thick hollow ceramic board serves as the interior or exterior wall, the number of floors can be more than doubled and the heat preservation energy consumption can be reduced manyfold.
Description
Pottery is not afraid of soda acid worm ant, but is afraid of bump, one bump namely broken; If there is not bump, it's thousand pasts the life-span, makes the metal sheet self-induction be not so good as.
" wide several meters replace steel plate can saw the hollow ceramic plate that brill does not rot " that present technique proposes, be called for short the hollow ceramic plate that does not rot, can solve above-mentioned pottery and be afraid of the bump problem.
" wide several meters replace steel plates can saw bore the hollow ceramic plate that does not rot ", its beneficial effect be, the saving metallic substance, and use in thousand, weight reduction, the bending resistance curvature of reinforcement plate reduces cost.
" wide several meters replace steel plate can saw the hollow ceramic plate that brill does not rot ", the technical scheme that its technical solution problem adopts is, by the pottery straight plate of (1) bonding pottery (2), corrugated ceramic plates (4) is formed, make porcelain mud wrap up ceramic cloth with facility, strike off unnecessary porcelain mud, make straight cardboard, the square wave cardboard, sinusoidal wave cardboard, the grooved cardboard, again straight cardboard is placed on the square wave cardboard, or sinusoidal wave cardboard, or the bottom surface of grooved cardboard cardboard is bonding, make cored slab, send into kiln after the drying and fire, obtain hollow ceramic plate (3), thereby make wide several meters to replace steel plates can saw the hollow ceramic plate that brill do not rot being moved; It is manufactured with 2 kinds:
1), with facility porcelain mud and water are mixed by a certain percentage and to make porcelain mud, with facility porcelain mud is wrapped up 1 ceramic cloth, strike off unnecessary porcelain mud, make porcelain mud pass ceramic cloth hole, porcelain mud thickness is preferably thick less than ceramic cloth; The ceramic cloth that polylith is wrapped up by porcelain mud is bonded into facility that denumerable rice is wide to be as thin as 0.3 millimeter ceramic cloth paper, be pressed into trough-type ceramic cloth paper with facility again, or square wave pottery cloth paper, or sinusoidal ceramic cloth paper, to be placed on square wave pottery cloth paper by the wide ceramic cloth paper that is as thin as 0.3 millimeter of the denumerable rice of porcelain mud parcel then, or sinusoidal wave ceramic cloth paper, or the bottom surface of trough-type ceramic cloth paper is bonding, make cored slab, can paint before and after dry, drawing, putting forward poem decorates, send into kiln then and fire, obtain corresponding hollow ceramic plate, thereby make wide several meters to replace steel plates can saw the hollow ceramic plate that brill do not rot being moved;
2), with facility porcelain mud and water are mixed by a certain percentage and to make porcelain mud, with facility porcelain mud is wrapped up 1 ceramic cloth, strike off unnecessary porcelain mud, make porcelain mud pass ceramic cloth hole, porcelain mud thickness is preferably thick less than ceramic cloth; It is generous to centimetre-sized pottery fabric swatch that the ceramic cloth that polylith is wrapped up by porcelain mud is bonded into denumerable rice with facility, be pressed into the trough-type ceramic fabric swatch with facility again, or square wave pottery fabric swatch, or sinusoidal ceramic fabric swatch, to be placed on square wave pottery fabric swatch by the generous ceramic fabric swatch to centimetre-sized of the denumerable rice of porcelain mud parcel then, or sinusoidal wave ceramic fabric swatch, or the bottom surface of trough-type ceramic fabric swatch is bonding, make cored slab, can paint before and after dry, drawing, putting forward poem decorates, send into kiln then and fire, obtain corresponding hollow ceramic plate, thereby make wide several meters to replace steel plates can saw the hollow ceramic plate that brill do not rot being moved.As Fig. 1
The hollow ceramic cardboard that existing combination principle introduction is not rotted:
It is reported that porcelain mud is fired into about 1200 ℃ of the temperature of ceramic plate; Hollow ceramic cardboard bending resistance curvature is than straight cardboard, square wave cardboard, or sinusoidal wave cardboard, or the grooved cardboard is strong; The unit weight of cored slab can be less than 0.1g/cm
3
Present technique is made cored slab with straight plate, with economical with materials and expand ceramic cardboard range of application.
The ceramic cloth that present technique is taken, anti-1700 ℃ of high temperature so when porcelain mud was fired into ceramic plate, ceramic cloth still kept original tensile property, make ceramic plate can not rupture; Present technique is on the ratio of ceramic cloth and porcelain mud, and based on ceramic cloth, porcelain mud only uses as a kind of tackiness agent, its thickness is thick less than ceramic cloth, and emphasize the ratio of porcelain mud and water to make porcelain mud just wrap up the ceramic wiring bar, do not enter the fibrous inside of ceramic lines, like this, burn till and be as thin as the thick pottery of 0.05mm and have elasticity, when very thin pottery was subjected to clashing into, impact force just passed on the ceramic lines rapidly, absorbed by ceramic lines, make ceramic plate be kept perfectly and can not rupture; The hardness ratio iron and steel height of pottery, so the resistance to abrasion of ceramic plate is stronger than iron and steel; Ceramic thread, pottery all possesses very good anti acid alkali performance energy, and the worm mosquito do not eat, and so long as not being subjected to too strong impact force, the usage period surpasses thousand and is out of question; Polylith pottery cloth is overlapping bonding, and former ceramic cloth width can be expanded and reach ten meters; Former ceramic cloth is thick to be as thin as 0.2 millimeter, can do 0.3 millimeter thick do not rot ceramic paper; In addition, the ceramic plate area of multilayer ceramic cloth reaches up to a hundred square metres, and also very light, because in the ceramic plate, ceramic thread is loose condition (of surface), and pottery just exists as tackiness agent, sealing agent, and the volumetric ratio pottery volume of ceramic cloth is a lot of greatly.
Figure of description:
The hollow ceramic plate that Fig. 1 does not rot
1 pottery, the straight plate of 2 potteries, 3 hollow ceramic plates, 4 corrugated ceramic plates.
Claims (1)
1. " wide several meters replace steel plate can saw the hollow ceramic plate that brill does not rot ", it is characterized in that, formed by the straight plate of the bonding pottery of pottery, corrugated ceramic plates, make porcelain mud wrap up ceramic cloth with facility, strike off unnecessary porcelain mud, make straight cardboard, square wave cardboard, sinusoidal wave cardboard, the grooved cardboard, again cardboard is placed on the square wave cardboard, or sinusoidal wave cardboard, or the bottom surface of grooved cardboard cardboard is bonding, make cored slab, send into kiln after the drying and fire, obtain the hollow ceramic plate, thereby make wide several meters to replace steel plates can saw the hollow ceramic plate that brill do not rot being moved; It is manufactured with 2 kinds:
1), with facility porcelain mud and water are mixed by a certain percentage and to make porcelain mud, with facility porcelain mud is wrapped up 1 ceramic cloth, strike off unnecessary porcelain mud, make porcelain mud pass ceramic cloth hole, porcelain mud thickness is preferably thick less than ceramic cloth; The ceramic cloth that polylith is wrapped up by porcelain mud is bonded into facility that denumerable rice is wide to be as thin as 0.3 millimeter ceramic cloth paper, be pressed into trough-type ceramic cloth paper with facility again, or square wave pottery cloth paper, or sinusoidal ceramic cloth paper, to be placed on square wave pottery cloth paper by the wide ceramic cloth paper that is as thin as 0.3 millimeter of the denumerable rice of porcelain mud parcel then, or sinusoidal wave ceramic cloth paper, or the bottom surface of trough-type ceramic cloth paper is bonding, make cored slab, can paint before and after dry, drawing, putting forward poem decorates, send into kiln then and fire, obtain corresponding hollow ceramic plate, thereby make wide several meters to replace steel plates can saw the hollow ceramic plate that brill do not rot being moved;
2), with facility porcelain mud and water are mixed by a certain percentage and to make porcelain mud, with facility porcelain mud is wrapped up 1 ceramic cloth, strike off unnecessary porcelain mud, make porcelain mud pass ceramic cloth hole, porcelain mud thickness is preferably thick less than ceramic cloth; It is generous to centimetre-sized pottery fabric swatch that the ceramic cloth that polylith is wrapped up by porcelain mud is bonded into denumerable rice with facility, be pressed into the trough-type ceramic fabric swatch with facility again, or square wave pottery fabric swatch, or sinusoidal ceramic fabric swatch, to be placed on square wave pottery fabric swatch by the generous ceramic fabric swatch to centimetre-sized of the denumerable rice of porcelain mud parcel then, or sinusoidal wave ceramic fabric swatch, or the bottom surface of trough-type ceramic fabric swatch is bonding, make cored slab, can paint before and after dry, drawing, putting forward poem decorates, send into kiln then and fire, obtain corresponding hollow ceramic plate, thereby make wide several meters to replace steel plates can saw the hollow ceramic plate that brill do not rot being moved.